• 한국세라믹학회지
• /
• 제28권9호
• /
• pp.675-682
• /
• 1991

Among many problems that need to be solved in the process of preparing multilayer chip LC filters, we studied the control of shrinkage in order to prevent the crack, warpage, and/or delamination which occurs at the interface between the inductance (L part) and the capacitance (C part). Shrinkage was controlled by compositions, powder size, calcining temperature and amount of organic binder. Capacitance sheet was prepared by mixing 65 wt% binder with the composition of 96 wt% TiO2 having an average particle size of 0.5 $\mu\textrm{m}$, 3 wt% CuO. After small amount of MnO2 and SiO2 added, it was calcined at 750$^{\circ}C$ for 2 hr. Inductance sheet was prepared by mixing 60 wt% binder with the composition of 49.5% mol% Fe2O3, 20.5 mol% ZnO, 20 mol% NiO and 10 mol% CuO which was calcined at 775$^{\circ}C$ for 2 hr. These sheets was laminated at 250 kg/$\textrm{cm}^2$, and cofired at 900$^{\circ}C$ for 2 hr to give rise to a multilayer chip LC filter without any warpage.

• 한국세라믹학회지
• /
• 제47권6호
• /
• pp.566-571
• /
• 2010

Dispersion behavior of the slurries consisted of bimodal-type AlN powders was examined in non-aqueous solvent system. Azotropic solvent system and copolymer acidic dispersant were applied to the slurries. Measurements of the sedimentation height and the viscosity of the each slurry, and the test of particle size distribution of the each powder sample were conducted as examinations for the dispersion behavior at the various dispersant contents. The bimodal-type particle size distribution was continued after addition of the dispersant and small particle portions were increased as the dispersant content increases. The density of the green sheet was also increased as the dispersant content increases and a green density of $2.114\;g/cm^3$ was obtained at the sample prepared from 2.4 wt% dispersant content. The increase of large particle portions resulted in the surface defects of the green sheets.

• 한국세라믹학회지
• /
• 제48권6호
• /
• pp.516-519
• /
• 2011

Indium tin oxide (ITO) coatings were made using an ITO slurry and an ITO sol. This was achieved by dispersing nanosized ITO powder in a mixed solvent without any dispersant and developing an adhesive ITO sol from indium acetate and tin tetrachloride in a mixture of DMF and n-butanol. Coating was carried out in one step by spin coating an ITO slurry, which was then followed by an ITO sol over it. Here, the sol penetrates into the nano ITO particle layers to make them adhere to each other as well as to a glass substrate. This is then followed by sintering at 500$^{\circ}C$ for 1 h to produce a uniform film consisting of ITO particles of about 50 nm and 10 nm. ITO films were obtained with sheet resistances from 450 to 1500 ohm/${\Box}$ by varying spin speed and concentration. Transmittance is higher than 90% at 550 nm.

• 한국세라믹학회지
• /
• 제46권6호
• /
• pp.708-712
• /
• 2009

ITO films were achieved by sintering at $500{\sim}550{^{\circ}C}$. This was possible by inducing a seeding effect on an ITO sol by producing crystalline ITO nanoparticles in situ during heat treatment. Two kinds of ITO sols (named ITO-A and ITO-B) were prepared at 2.0 wt% from indium acetate and tin(IV) chloride in different mixed solvents. The ITO-A sol showed a high degree of crystallinity of ITO without any detectable Sn$O_2$ on XRD at $350{^{\circ}C}$/1 h, but the ITO-B sol showed a small amount of Sn$O_2$ even after annealing at $600{^{\circ}C}$/1 h. The 10 wt% ITO-A//ITO-B showed the sheet resistance of 3600$\Omega$/□, while the ITO-B sol alone showed 5200 $\Omega$/□ by sintering at $550{^{\circ}C}$ for 30 min. Processing parameters were studied by TG/DSC, XRD, SEM, sheet resistance, and visible transmittance.

• 한국세라믹학회지
• /
• 제31권4호
• /
• pp.427-435
• /
• 1994

Cu-metallized low firing temperature substrates were synthesized by cofiring green sheet of cordierite-based glass with Cu. By Sol-Gel method, Cu powder was coated with borosilicate gel which should act as a glass frit in Cu paste during cofiring. Theoretical weight ratios of Glass/Cu were controlled to be 2.5, 5, 10 and 15% by varying alkoxide concentrations. Average particle size of coated Cu was 0.629~0.674 ${\mu}{\textrm}{m}$ in comparison to that of as-received Cu(0.596 ${\mu}{\textrm}{m}$), which increased with alkoxide concentration but did not increase above certain concentration. The weight ratios of coated layer were 2.11~5.37%. The properties of Cu-metallized low firing temperature substrate, cofired at 90$0^{\circ}C$ for 1h under H2/N2 atmosphere, were as follows; sheet resistance was 13~43 m{{{{ OMEGA }}/$\square$, adhesion strength was 1.0~2.1 kgf/$\textrm{mm}^2$. From the observations of SEM photographs, the gel coated on Cu performed excellently as a glass frit.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2007년도 춘계학술대회 논문집
• /
• pp.67-70
• /
• 2007

LTCC (Low Temperature Co-fired Ceramic) has been emerged as a promising technology in packaging industry. In this technology the lamination and the sintering process are very important because they change the permittivity of ceramics and the dimension of metal pattern which have influences on electric property. In this paper we studied on influence of the permittivity and the dimension change by lamination pressure and sintering temperature of LTCC process. As a results, permittivity increase along with increasing of lamination pressure and sintering temperature.

• 소성∙가공
• /
• 제16권5호통권95호
• /
• pp.396-400
• /
• 2007

LTCC(Low Temperature Co-fired Ceramic) which offers a good performance to produce multilayer structures with electronic circuits and components has emerged as an attractive technology in the electronic packaging industry. In LTCC module fabrication process, the lamination and the sintering are very important processes and affect the electrical characteristics of the final products because the processes change the permittivity of ceramics and the dimension of the circuit patterns which have influences on electronic properties. This paper discusses the influence of lamination pressure and sintering temperature on the permittivity and the dimensional change of LTCC products. In the present investigation, it is shown that the permittivity increases along with increasing of the lamination pressure and the sintering temperature.

• 한국세라믹학회지
• /
• 제47권4호
• /
• pp.276-282
• /
• 2010

There are the impregnating layer formation by surface protective materials or impregnants and the adhesion method by polymer, FRP sheet or steel plate in the surface protective method of concrete structure. The surface impregnation method by impregnants improves the durability of concrete structure by modifying the structure of the concrete surface and also have a merit that can be shortly applied in place without the decrease of concrete surface appearance and is easily applied again. This study is interested in manufacturing the concrete surface impregnants including lithium and potassium silicate for the repair of the exposed concrete and the color concrete requiring the advanced function in view of the concrete appearance. The durability and porosity properties was tested for the review of application. The result of this study show that the effective content of silicate ranges 5 to 20% and the separate application of the first impregnant and the second impregnant is effective for the optimum performance. The adhesion in tension is slightly increased but the reinforcement of concrete substrate is slight. So, the concrete impregnant of this study is more desirable for the improvement of durability rather than the reinforcement.

• 에너지공학
• /
• 제26권4호
• /
• pp.84-91
• /
• 2017

섬유강화플라스틱(glass fiber reinforced plastics)은 수지에 섬유상의 보강재를 복합화하여 고강도 특성을 나타내게한 대표적인 플라스틱 복합소재이다. 섬유강화플라스틱 성형제품의 기계적 물성을 결정하는 요소는 강화재로 사용되는 섬유상 소재이므로 섬유소재에 대한 연구는 관심이 높은 대상이나, 기지재를 구성하는 수지의 물성에 영향을 미치는 충진재의 영향에 관한 연구는 많지 않은 편이다. 그러나, 플라스틱 또는 수지 조성물의 물성은 미네랄 충진재에 의하여 결정되며, 기지재가 복합소재에 미치는 영향이 높은 만큼 본 연구에서는 $3-6{\mu}m$ 크기의 중질 탄산칼슘을 사용하여 충진재의 크기와 첨가량이 섬유강화복합체에 미치는 영향을 확인하고자 하였다. 시편은 시트몰딩 컴파운드(SMC, Sheet molding compound) 방법에 의하여 제조되었으며, 기계적 특성은 굴곡강도와 인장강도 결과를 비교 분석 하였다. 그 결과 탄산칼슘의 크기 또는 첨가량이 성형시편의 기계적 강도에 영향을 미칠 수 있음을 확인할 수 있었으며, 그 중에서도 가장 낮은 평균 입경 ($2.8{\mu}m$) 조건에서 가장 높은 기계적 특성을 나타냈다.

• 한국분말재료학회지
• /
• 제16권6호
• /
• pp.431-437
• /
• 2009

Various inorganic fillers improve the thermal conductivity and physical properties of organic products. Alumina has been used a representative filler in the heat radiation sheet for the heat radiation of electric device. The high filling rate of alumina increases the thermal conductivity and properties of products. We successfully developed the spherical alumina by flame fusion process using the oxygen burner with LPG fuel. In the high temperature flame (2500$\sim$3000$^{\circ}C$) of oxygen burner, sprayed powders were melting and then rotated by carrier gas. This surface melting and rotation process made spherical alumina. Especially effects of chemical composition and particle size of stating materials on the melting behavior of starting materials in the flame and spheroidization ratio were investigated. As a result, spheroidization ratio of boehmite and aluminum hydroxide with endothermic reaction of dehydration process was lower than that of the sintered alumina without dehydration reaction.