• Journal of the Korean Ceramic Society
• /
• v.37 no.6
• /
• pp.517-523
• /
• 2000

Effect of catalysts, which was catalyzed by acid(HCl and HNO3) and base(NH4OH), on characteristics of the mullite powders prepared by sol-gel methdo wa sinvestigated by XRD, TGA, SEm AND BET. As a result, weight loss as a function of catalysts was in order of HCl=32.6%>HNO3=25.44%>Non=24.0%>NH4OH=22.5%. The mullite powder dried at 100$^{\circ}C$ appeared spherical shape in acid catalyst and different shape in base catalyst, but sintering powder at 1400$^{\circ}C$ appeared very fine particle of 0.05∼0.1$\mu\textrm{m}$ regardless of catalysts. In all cae, the pore quantity, which was capable to adsoprtion, was decreased with increasing temperature. In base catalyst, no change of special surface area in mullite appeared.

• The Korean Journal of Ceramics
• /
• v.6 no.1
• /
• pp.58-63
• /
• 2000

The preparation of Y-doped $SrZrO_3$powder by ultrasonic spray pyrolysis was investigated as a representative system, in order to produce fine, single phase multicomponent oxide powders. A precursor solution containing metal nitrates, citric acid and ethylene glycol was atomized glycol was atomized with an ultrasonic spray nozzle. Gel particles formed by organic functional groups were pyrolyzed and subsequently calcined at $800^{\circ}C$ to obtain well-crystallized, single perovskite phase. Most of large particles exhibited macroscopic pores and weak agglomeration between primary particles. However, strong agglomeration was observed in the surfaces of large particles. The effect of the microstructures of these particles on size reduction to submicron particles was described.

• Journal of the Korean Ceramic Society
• /
• v.30 no.1
• /
• pp.17-24
• /
• 1993

Sol-gel spin-coating technique was used to produce Nb2O5 thin films on silicon substrates from Nb(OC2H5)5 precursor. The films were heat-treated at temperatures between $600^{\circ}C$ and 100$0^{\circ}C$ in oxygen atmosphere and their crystalline phases, chemical states, and dielectric characteristics were investigated by X-ray diffractometry (XRD), Auger electron spectroscopy (AES), and C-V measurements, respectively. After 1 hour heat-treatment at 80$0^{\circ}C$, T-type Nb2O5 was formed, and its chemical composition was homogeneous with no appreciable SiO2 oxide at interfaces between the films and substrates. The films heat-treated at temperatures between $600^{\circ}C$ and 80$0^{\circ}C$ exhibit dielectric constant of less than 20 while the films heat treated at 100$0^{\circ}C$ show dielectric constant of 28.

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.636-640
• /
• 2011

Nano-sized cobalt (II) oxide nanoparticles with a high crystallinity were synthesized using thermolysis of a $Co^{2+}$-oleate precursor at 310$^{\circ}C$. The phase and morphology of as-prepared cobalt oxide nanoparticles were characterized using X-ray diffraction, high-resolution transmission electron microscopy, and Brunauer-Emmett-Teller surface area measurements. The cobalt oxide nanoparticles were found to be spherical nanoclusters with an average diameter of approximately 200 nm, consisting of tiny nanocrystals (10-20 nm). Furthermore, the Li electroactivites of the cobalt oxide nanoparticles were investigated using cyclic voltammetry and galvanostatic cycling. The cobalt oxide nanoparticles could deliver high capacities over 420 mA h $g^{-1}$ at a C/5 current rate.

• Journal of the Korean Ceramic Society
• /
• v.40 no.10
• /
• pp.985-990
• /
• 2003

By heat treating coal tar pitch between 450∼500$^{\circ}C$, mesophase pitch could be obtained. Subsequently, this pitch was oxi-stabilized between 160∼240$^{\circ}C$ in air for the purpose of reducing swelling and distortion. The mechanism of stabilization was analysed using the thermo-gravity and FT-IR. To investigate the effect of oxi-stabilization, the shore hardness and bending stress were measured with carbonized green body which was made from oxi-stabilized coal tar pitch.

• Journal of the Korean Ceramic Society
• /
• v.25 no.1
• /
• pp.49-53
• /
• 1988

Polycarbosilane was synthesized from the pyrolysis of polydimethylsilane, which is dechlorinated from dimethyldichlorosilane. The pyrolysis temperature was varied at 280-480$^{\circ}C$ for 2 hours. FT-IR, FT-NMR and GPC measurement were studied on the residue inside the reaction crucible and viscous solution inside the cooling zone respectively. From the viscous solution in the cooling zone at 420$^{\circ}C$, the synthesis of polycarbosilane wa well detected.

• Journal of the Korean Ceramic Society
• /
• v.31 no.9
• /
• pp.1030-1036
• /
• 1994

The ceramics in the system 0.5[Pb(Ni1/3Nb2/3)O3]-0.5[0.65PbTiO3-0.35PbZrO3] were prepared by conventional solid state reaction method, double calcined method (columbite precursor method) and flux method using NaCl-KCl. Amount of pyrochlore phase for the calcined powders, sintering charateristrics, dielectric and piezoelectric properties were then investigated. Sintering temperature was 1000~120$0^{\circ}C$ and in case of flux method, the amount of flux to oxide was 1 : 1 mole ratio. The dielectric and piezoelectric properties of ceramics prepared by double calcined method and flux method were found to be better than those by conventional method. It was also possible to lower sintering temperature and reduce the amount of pyrochlore phase either by double calcined method or flux method. But with increasing sintering temperature, the difference in characteristrics due to diffrent fabrication method gradually.

• Journal of the Korean Ceramic Society
• /
• v.32 no.7
• /
• pp.853-857
• /
• 1995

ZrSiO4 powders were prepared from partially hydrolyzed solution of Si(OC2H5)4 and ZrOCl2.8H2O solution by the sol-gel method and formation rate of ZrSiO4 on the reaction parameter was investigated. In order to prepare homogeneous ZrSiO4 precursor gels, the H2O/Si(OC2H5)4 molar ratio of about 2, the pH of the ZrOCl2.8H2O solution fo about 4 and stirring time of the mixed solutions of about 2 hrs were appropriate. Formation of temperature of ZrSiO4 reduced about 15$0^{\circ}C$ by milling and formation of ZrSiO4 at 1300~135$0^{\circ}C$ showed an accelerative increase through the hedvall effect by silica.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.995-1002
• /
• 1995

The alumina fiber was obtained by extruding the TEA complexed polymeric sol, synthesized by the alkoxide sol-gel method, through nozzle. The purpose of this study was to investigate the properties of fiber spun by TEA complexed sol. The analysis of sol indicated that TEA was bonded at alkoxide precursor and the optimum molar ratio for spinning was 0.5 mole of TEA, 3 mole of H2O. The cross section of the fiber from circular nozzle was not circular but oval, which indicated that the shape of nozzle did not affect the shape of fiber. The diameter of the fiber was about 100 ${\mu}{\textrm}{m}$ in the state of dried gel fiber, 60${\mu}{\textrm}{m}$ in calcined fiber, and the tensile strength of the fiber calcined at 90$0^{\circ}C$ was 2.1$\times$108 Pa.

• Journal of the Korean Ceramic Society
• /
• v.31 no.1
• /
• pp.17-24
• /
• 1994

Al2O3-ZrO2(ZTA) composites were fabricated by a surface-induced coating of the precursor for the ZrO2 phase on the kinetically stable colloid particles of Al2O3. The fabricated composites were characterized by a uniform spatial distribution of the dispersed ZrO2 phase and by the absence of large ZrO2 grains throughout the Al2O3 matrix. The fracture toughness (KIC) and the bending strength of ZTA composites sintered at 1$600^{\circ}C$, respectively, were 5.6 MPa.m1/2 (for 20 wt% ZrO2) and 600 MPa (for 15wt% ZrO2). The fraction of tetragonal ZrO2 phase decreases as the total content of ZrO2, suggesting that both the stress-induced tlongrightarrowm transformation and the microcrack nucleation contribute to the toughening of the ZTA composites fabricated by the surface-induced coating.