• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2001년도 제33회 춘계학술대회 개최
• /
• pp.319-326
• /
• 2001

The sliding wear characteristics of carbon steel castings were Investigated using a ball on disk type tester. The experiment was conducted using high carbon steel wire rods as ball material and carbon steel castings as disk material and different operating conditions, at room temperature under a lubrication and dry conditions. The results showed that the carbon steel castings appeared average wear volume Is lowed after annealing under a lubrication conditions and wear curve linear Increased. The specific wear rate of carbon steel castings Increased with wire diameter lubrication and dry also Increased 125 times In Ory. The sliding wear mechanism were Investigated due to fatigue wear lubrications and abrasive wear dries also wire Included fatigue and abrasive wear by plastic flow.

• 한국주조공학회지
• /
• 제15권6호
• /
• pp.604-615
• /
• 1995

Austenitic stainless steel castings using expandable polystylene(referred to hereafter as EPS) patterns are often affected by distinctive defects associated with incomplete decomposition of the EPS as the molds are filled with metal. The quality of the castings, with particular reference to carbon pick-up in austenitic stainless steel is further influenced to a significant extent by such factors as reduced pressure, the additive by adding $Na_2CO_3$ in coating. The steel composition and microstructure were examined at the surface layer of castings, at depths of 1mm, by taking successive layers of swarf and analysis. In experiments, the carburizing atmosphere was neutralized, showing that the coating performed efficiently by decomposing almost instantly on heating and liberating $CO_2$. The upper parts of castings obtained using EPS patterns were slightly higher in carbon pick-up than other parts. Comparing the 316L and 304 stainless steel castings, qualitative and quantative differences could be found between the carbon pick-up behaviours as influence of the carbon content and alloying elements. Carbide former such as Cr makes carbon more soluble in the steel. This must make carbon pick-up in the surface layer but at the same time richer in carbon especially in the 304 stainless steel castings.

• Tribology and Lubricants
• /
• 제19권4호
• /
• pp.223-229
• /
• 2003

The sliding wear characteristics of the crane sheave were investigated using a pin-on-disk rig tester. The experiment was conducted using a high carbon steel wire that was upper material, also carbon steel castings that was disk material. There are various operating conditions in this work. At the room temperature, we carried out the wear test under a grease lubrication and dry condition. The results of wear test showed that an annealed-casted have lower, also the wear curves are linearly increased with increasing of sliding distance. For the specific wear rate of annealed-casted, the wear resistance was increased with decreasing diameter of wire. The wear of a wire and a disk have a different mechanism, the one is the abrasive wear due to fatigue wear under lubrication, another is the adhesion wear under dry condition.

• 한국주조공학회지
• /
• 제23권2호
• /
• pp.86-93
• /
• 2003

It has been a major concern in the foundry that steel castings manufactured by the evaporative pattern casting process encounter the carbon pick-up problem. A carbon rich layer at the evaporative pattern cast surface is a result of interactions between the gaseous products from foamed polystyrene and the molten metal. The carburized layer with a high hardness makes it difficult to machine the casting. In this study, the influence of the density of EPS pattern and coatings on carbon pick-up phenomena of S25C and S45C commercial carbon cast steel were investigated. As the density of EPS pattern is increased, the carbon concentration of decomposed pattern is increased and the thickness of carburized layer at the surface of steel castings is increased. Also as the density of coatings is increased, the permeability of coatings is decreased and the thickness of carburized layer at the surface of steel castings is increased. S25C steel which has lower original carbon content compared to S45C steel exhibited severe carburization.

• 한국주조공학회지
• /
• 제12권4호
• /
• pp.305-316
• /
• 1992

Steel and iron castings made with expandable polystylene (referred to hereafter as EPS) patterns are often affected by distinctive defects associated with incomplete decomposition of the EPS as the molds are filled with metal. The effects of practical factors on carbon pick-up were investigated on the specimens, by taking successive layers of swarf and analysis, whereas the lustrous carbon is determined by using combustion analysis. The quality of the castings, with particular reference to carbon pick-up in low carbon steel and lustrous carbon on gray iron, is further influenced to a significant extent by such practical factors as reduced pressure, the pouring temperature, the density of EPS pattern, the additive in coating and in pattern and the casting thickness. The rate at which carbon pick-up and lustrous carbon deposites are formed can be reduced by reducing the density of the pattern and also reducing pressure, especially by adding $Na_2CO_3$ in coating and in pattern to promote $CO_2$ evolution. The upper parts of castings obtained using EPS patterns are slightly higher in carbon pick-up and in lustrous carbon than other parts.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2004년도 학술대회지
• /
• pp.306-311
• /
• 2004

The sliding wear characteristics of the crane sheave were investigated using a pin-on-disk rig tester The experiment was conducted using a high carbon steel wire that was upper material, also carbon steel castings and carbon steel for machine structural use that was disk material. There are various operating conditions in this work. At the room temperature, we carried out the wear test under a grease lubrication. The results of wear test showed that carbon steel for machine structural use have lower wear volume, also the wear curves are linearly increased with increasing of sliding velocity The wear mechanism of a disk is the abrasive, adhesion, and fatigue wear under lubrication.

• 대한금속재료학회지
• /
• 제49권1호
• /
• pp.73-78
• /
• 2011

Weldability, especially HAZ cold cracking, weld metal solidification cracking, and HAZ liquation cracking susceptibilities, of ASTM A356 CA6NM martensitic stainless steel casting was investigated and compared with that of 9-12% Cr ferritic steel castings. Irrespective of the Cr and Ni content in the castings, the HAZ maximum hardness increased with an increase of carbon content. CA6NM steel, which has the lowest carbon content, had the lowest HAZ hardness and showed no cold cracking in y-slit cracking tests. CA6NM steel, meanwhile, showed the largest weld metal solidification cracking susceptibility in varestraint tests because of its higher amount of impurity elements, phosphorus, and sulfur. All castings investigated had good high temperature ductility in hot ductility tests and showed little difference in liquation cracking susceptibility.

• 대한기계학회논문집A
• /
• 제27권11호
• /
• pp.1873-1880
• /
• 2003

The sliding wear characteristics of the crane sheave were investigated using a pin on disk rig tester. The experiment was conducted using a high carbon steel wire that was upper material, also carbon steel castings that was disk material. There are various operating conditions in this work. At the room temperature, we carried out the wear test under a grease lubrication and dry condition. The results of wear test showed that an annealed-casted have lower, also the wear curves are linearly increased with increasing of sliding distance. For the specific wear rate of annealed-casted, the wear resistance was increased with decreasing diameter of wire. The wear of a wire and a disk have a different mechanism, the one is the abrasive wear due to fatigue wear under lubrication, another is the adhesion wear under dry condition.

• 한국주조공학회지
• /
• 제7권spc호
• /
• pp.284-293
• /
• 1987

• 한국주조공학회지
• /
• 제15권5호
• /
• pp.494-506
• /
• 1995

Test castings in plate, disc, and cubic shaped castings for 0.2wt.% carbon and stainless steel have been poured to examine the effects of the riser dimensions including riser neck on the casting soundness. Three empirical methods were chosen in risering of steel castings. A computer program of solidification analysis considering liquid and solidification contraction was developed to apply for riserdesign calculated by using their methods in plate, disc, and cubic shaped castings, and to calculate the position and dimension of shrinkage cavity in complex shaped casting. The potential of present method has been successfully demonstrated by comparing predicted cavity shapes with those obtained in a series of experimental castings. Three empirical methods can be used in a practical way to make a rapid estimation of tie minimum riser diameter, but they can not provide a criterion of casting soundness with shape and material on all occasions. The shape and position of shrinkage cavity can be successfully predicted both using the present method and using risering calculated by their methods regardless of the shape and cast material.