• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.1322-1325
• /
• 2005

The main objectives of this research work are to develop conductive glass fiber woven roving and carbon fiber unidirectional fabric composite materials and to determine their electromagnetic shielding effectiveness(EMSE). Epoxy is the matrix phase and glass, carbon fiber are the reinforcement phase of the composite material. Carbon black are incorporated as conductive fillers to provide the electromagnetic shielding properties of the composite material. The amount of carbon black in the composite material is varied by changing the carbon black composition, woven roving and unidirectional (fabric) structure. The EMSE of various fabric composites is measured in the frequency range from 300MHz to 800MHz. The variations of EMSE of woven roving and unidirectional composites with fabric structure, metal powder composite are described. Suitability of conductive fabric composites for electromagnetic shielding applications is also discussed.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.7 no.4
• /
• pp.10-16
• /
• 2008

This study investigated electromagnetic interference(EMI) shielding effectiveness(SE) of the aluminum film, conductive fabric and nano carbon black carbon fiber reinforced composites. We fabricated carbon fiber reinforced composites filled with nano carbon black where they bonded aluminum film and conductive fabric. The measurements of SE were carried out frequency range from 300MHz to 1.5GHz. It is observed that the SE of the bonded aluminum film and conductive fabric composites is the frequency dependent, increase with the increase in filler nano carbon black content. The aluminum film bonded composites showed higher SE compared to that of carbon black and conductive fabric. The aluminum film bonded epoxy composite was shown to exhibit up to 80dB of SE. The result that aluminum film bonded composite can be used for the purpose of EMI shielding as well as for some microwave applications.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.2
• /
• pp.48-56
• /
• 1997

This work has been investigated in order to study the influence of the moisture absorption on the mechanical pf the glass fiber/epoxy resein composites and the carbon fiber/epoxy resein composites. The types of glass fiber used in the glass fiber/epoxy resein composites were randomly oriented fiber and plain fabric fiber. And carbon fiber.epoxy resein composites was laminated with fabric prepreg which was formed with carbon fiber and epoxy resein. Both composites were immersed up to 100 days in distilled water at $80^{\circ}C$, and then dried up to 3 days in an oven at 80$80^{\circ}C$. Both composites were measured for the weight gain of water(wt.%) and tensile strength through immersion and dry time. Consequently, it was found that the tensile strength of thw glass fiber/epoxy resein composites and the carbon fiber/epoxy resein composites were reduced proportionally to the moisture absortion rate. Also, the tensile strength of glass fiber composites was decreased more than that of the carbon fiber composites. Additionally, it was found that the tensile strength of all composites which decreased by moisture absorption were partly recovered by drying in an oven at 80$80^{\circ}C$.

• Korean Journal of Metals and Materials
• /
• v.49 no.10
• /
• pp.760-765
• /
• 2011

This paper presents a study of the tensile behavior of carbon and glass fiber reinforced epoxy hybrid laminates manufactured by vacuum assisted resin transfer molding (VARTM). The objective of this study was to develop and characterize carbon fiber reinforced plastic hybrid composite material that is low cost and light-weight and that possesses adequate strength and stiffness. The effect of position and content of the glass fabric layer on the tensile properties of the hybrid laminates was examined. The strength and stiffness of the hybrid laminates showed a steady decrease with an increase of the glass fabric content this decrease was almost linear. Fracture strain of these laminates showed a slight increasing trend when glass fabric content was increased up to 3 layers, but at a glass fabric content > 3 layers the strain was almost constant. When glass fabric layers were at both outer surfaces, the hybrid laminate exhibited a slightly higher tensile strength and elastic modulus due to the small amount of glass yarn pull-out.

• Journal of the Korean Ceramic Society
• /
• v.45 no.9
• /
• pp.561-566
• /
• 2008

Carbon fiber fabric-silicon carbide composites were fabricated by liquid silicon infiltration (LSI) process. The porous two-dimensional carbon fiber fabric performs were prepared by 13 plies of 2D-plain-weave fabric in a three laminating method, [0/90], [${\pm}45$], [$0/90/{\pm}45$] lay-up, respectively. Before laminating, a thin pyrolytic carbon (PyC) layer deposited on the surface of 2D-plain weave fabric sheets as interfacial layer with $C_3H_8$ and $N_2$ gas at $900^{\circ}C$. A densification of the preforms for $C_f-Si-SiC$ matrix composite was achieved according to the LSI process at $1650^{\circ}C$ for 30 min. in vacuum atmosphere. The bending strength of the each composite were measured and the microstructural consideration was performed by a FE-SEM.

• Composites Research
• /
• v.12 no.3
• /
• pp.8-16
• /
• 1999

Carbon woven fabric/C/SiC composites were fabricated by multiple impregnations of carbon woven fabric/carbon preform with the polymer precursor of SiC, i.e., polycarbosilane. In addition, two kinds of low density carbon/carbon preforms which had different fiber volume fraction and fiber orientation, i.e., a carbon woven fabric(${\thickapprox}$55 vol%)/carbon and a chopped carbon fiber${\thickapprox}$40 vol%)/carbon composites, were reaction-bonded with a silicon melt at 1$700^{\circ}C$ in a vacuum to fabricate dense carbon fiber/Si/SiC composites. The reaction-bonding process increased the density to ~2.1 g/$cm^3$ from 1.6 g/$cm^3$ and 1.15 g/$cm^3$ of a carbon woven and a chopped carbon preforms, respectively. All of the composites fractured with extensive fiber pull-out. The higher the density the higher the stiffness and proportional limit stress. The mechanical properties obtained from a three-point bend and tension tests were compared. The ratios of the peak tensile stresses to the bending strengths of a carbon woven and a chopped carbon composites were about one-third, respectively. The carbon woven fabric/Si/SiC composites with density of 2.06 g/$cm^3$ showed ~120 MPa of ultimate strength and ~80 MPa of proportional limit in bend testing.

• Transactions of Materials Processing
• /
• v.25 no.6
• /
• pp.402-408
• /
• 2016

A manufacturing technology of carbon fiber composites with thermoplastic polymer pellets and continuous woven fiber was investigated using a compression molding process. To secure the impregnation of resin into the porosity of fabric the composite specimens were prepared with general injection-molding grade polypropylene pellets and low viscosity polycarbonate pellets. Tensile tests of polypropylene and polycarbonate composites were performed. Polycarbonate composites showed higher fracture strength than that of polypropylene composites because of the difference of matrix properties. However, the increase rate of strength was lower than that of polypropylene composites due to the difference of coherence between matrix and reinforcement. To investigate the effect of carbon fiber volume fraction on the fracture strength variation polypropylene composites with different volume fraction were compression molded and tensile tests were performed together. It was shown that the fracture strength of the polypropylene composites increased by 3.2, 5.4 and 6.9 times with the increase of carbon fabric volume fraction of 0.256, 0.367, and 0.480, respectively.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.10a
• /
• pp.29-32
• /
• 2002

The mechanical and thermal properties of spun carbon fabric/continuous carbon fabric interplay hybrid composite materials have been studied. The properties of the hybrid composites are compared with those of the continuous carbon fabric/phenolic composites and spun carbon fabric /phenolic composites. Through hybridization, tensile strength and flexural strength of hybrid composites were increased by about 17%, and 10%, respectively compared with spun carbon composites. The thermal conductivity of the hybrid composite is lower approximately 4~6% along the direction parallel to the laminar plane than that of the continuous carbon/phenolic composite.

• Journal of the Korean Society of Safety
• /
• v.34 no.6
• /
• pp.1-6
• /
• 2019

Carbon fiber has excellent specific strength, corrosion resistance and heat resistance. And p-Aramid fiber has high toughness and heat resistance and high elasticity, and is used in various fields such as industrial protective materials, bulletproof helmets and vests, as well as industrial fields. However, carbon fiber is relatively expensive, and is susceptible to brittle fracture behavior due to its low fracture strain. On the other hand, the aramid fiber tends to decrease in elastic modulus and strength when applied to the epoxy matrix, but it is inexpensive and has higher elongation and fracture toughness than carbon fiber. Thus the twill hybrid carbonaramid fiber reinforced composite laminate composite was investigated for a delamination fracture toughness under Mode I loading by 2 kinds of MBT and MCC deduction. The specimen was fabricated with 20 hybrid fabric plies. The initial crack was made by inserting the teflon tape in the center plane with a₀/W=0.5 length. The results show that SERR(Strain Energy Release Rate) as the critical and stable delamination fracture toughness were 0.09 kJ/㎡, 0.386 kJ/㎡ by MBT deduction, and 0.192 kJ/㎡, 0.67 kJ/㎡ by MCC deduction, respectively.

• Transactions of the Korean Society for Noise and Vibration Engineering
• /
• v.26 no.4
• /
• pp.375-382
• /
• 2016

The mechanical property of a carbon-fiber-reinforced plastic (CFRP) is subjected to two elements, carbon fiber and polymer resin, in a first step and the selection of multi-layered structure is second one. Many combination of fabric layers, i.e. plainweave, twillweave, can be derived for candidates of test specimen used for a basic mechanical components so that a reliable identification of dynamic nature of possible multi-layered structures are essential during the development of CFRP based component system. In this paper, three kinds of multi-layered structure specimens were prepared and the dynamic characteristics of service specimens were conducted through classical modal test process with impact hammer. In addition, the design sensitivity analysis based on transmissibility function was applied for the measured response data so that the response sensitivity for each resonance frequency were compared for three CFRP test specimens. Finally, the evaluation of CFRP specimen over different multi-layered fabric structures are commented from the experimental consequences.