• The Journal of the Korea Contents Association
• /
• v.21 no.3
• /
• pp.609-615
• /
• 2021

The aim of the present study was to investigate the mechanical properties of melt-injected poly lactic acid (PLA) composites with β-tricalcium phosphate (β-TCP). The PLA mixed with calcined PLA/β-TCP powder to be contents of 0, 10, 30, 50 wt%, respectively, was dissolved in chloroform solvent under stirring for 24 h. Then the liquid mixtures were dropped into ethanol to extract solvent. After drying, the well-dispersed PLA/β-TCP composites were granulated and melt-injected to prepare specimens for various mechanical testing. PLA/β-TCP induced the precipitation of an apatite bone-mineral phase on the surface after immersion in a human simulated body fluid (SBF) for 90 days, showing in bioactivity. Mean various mechanical properties PLA/β-TCP composite were increased up to 10-30 wt% with significantly in part and composite were decreased 50 wt% of showing in mechanical properties. In conclusion, Over 30 wt% addition of β-TCP to PLA may be not advisable to improve the mechanical properties of melt-injected polymeric composites. Results indicated that β-TCP can be used considered as potential reinforcing agent for increasing mechanical properties for PLA. Therefore, it was suggest that the additional effects of β-TCP and research on a wide range of substances.

• The Journal of the Convergence on Culture Technology
• /
• v.9 no.3
• /
• pp.587-592
• /
• 2023

Cobalt oxide (Co₃O₄·CoO) ultra fine particles were synthesized by liquid phase precursor method. cobalt(II) chloride hexahydrate (CoCl₂·6H₂O) was as a starting material. A plant-derived crystalline cellulose was used as impregnating materials. A impregnated precursor was calcined at a temperature of 350 to 900℃ to obtain cobalt oxide particles having a particle size of 1 to 10㎛. The crystallization process and morphology according to the calcination temperature were examined, and the properties of the synthesized powder were evaluated using SEM and XRD. It was confirmed that a crystal phase of Co₃O₄ began to form around 350℃ and crystal growth occurred up to 900℃. At a temperature above 500℃, the Co₃O₄ crystal was changed to another crystal phase CoO.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.1
• /
• pp.5-9
• /
• 2008

Cordierite has a very low thermal expansion coefficient, but has problem that it has a weak mechanical strength and is apt to be attacked by acid such as sulfur for using as a diesel particulate filter support. The physical properties of $ZrTiO_4$ modified with $SiO_2,\;Al_2O_3$, MoOx, $Cr_2O_3\;and\;Nb_2O_5$ were investigated with XRD, SEM, UTM and thermal expansion, etc. in this paper. $ZrTiO_4$ powder was synthesized as a monoclinic structure with processes that starting materials of $TiO_2\;and\;ZrO_2$ were mixed with ball mill and calcined above $1240^{\circ}C$ for 3 hr. Additive modified $ZrTiO_4$ specimens for flexural strength and thermal expansion measurement were obtained by mixing $ZrTiO_4$ powder with additives, pressing and firing at $1300^{\circ}C$ for 3 hr. The porosity of additive modified $ZrTiO_4$ decreased monotonically with increasing additive content by 5 wt% regardless of additive types and saturated for further increase of additive by 10wt. The flexural strength of $Al_2O_3$ (5, 10 wt%) modified $ZrTiO_4$ shows a large increase, but that of other additives modified $ZrTiO_4$ decreased. The thermal expansion coefficient of additive modified $ZrTiO_4$ except $Nb_2O_5$ decreased continuously with the content of additive. In particular, the lowest thermal expansion coefficient of $ZrTiO_4$ was obtained for the additive of $SiO_2$.

• Clean Technology
• /
• v.24 no.4
• /
• pp.371-379
• /
• 2018

The objective of this study is to develop a platinum/hexaaluminate pellet catalyst for the decomposition of eco-friendly liquid propellant. Pellet catalysts using hexaaluminate prepared by ultrasonic spray pyrolysis as a support and platinum as an active metal were prepared by two methods. In the case of the pellet catalyst formed by loading the platinum precursor onto the hexaaluminate powder and then adding the binder (M1 method catalyst), the mesopores were well developed in the catalyst after calcination at $550^{\circ}C$. However, when this catalyst was calcined at $1,200^{\circ}C$, the mesopores almost collapsed and only a few macropores existed. On the other hand, in the case of a catalyst in which platinum was supported on pellets after the pellet was produced by extrusion of hexaaluminate (M2 method catalyst), the surface area and the mesopores were well maintained even after calcination at $1,200^{\circ}C$. Also, the catalyst prepared by the M2 method showed better heat resistance in terms of platinum dispersion. The effects of preparation method and calcination temperature of Pt/hexaaluminate pellet catalysts on the decomposition of liquid propellant composed mainly of ammonium dinitramide (ADN) or hydroxyl ammonium nitrate (HAN) were investigated. It was confirmed that the decomposition onset temperature during the decomposition of ADN- or HAN- based liquid propellant could be reduced significantly by using Pt/hexaaluminate pellet catalysts. Especially, in the case of the catalyst prepared by the M2 method, the decomposition onset temperature did not show a large change even when the calcination temperature was raised at $1,200^{\circ}C$. Therefore, it was confirmed that Pt/ hexaaluminate pellet catalyst prepared by M2 method has heat resistance and potential as a catalyst for the decomposition of the eco-friendly liquid propellants.