• Progress in Superconductivity
• /
• v.11 no.2
• /
• pp.118-122
• /
• 2010

Electrical transport properties were measured on $SmFeAsO_{0.85}$ single crystals along the c-axis for various temperatures and magnetic fields. For the measurements a mesa structure was fabricated on the surface of the single crystals. Samples showed a metallic temperature dependence of resistance and current-voltage curves without hysteretic multiple branch splitting that is usually observed in tunneling Josephson junctions. In addition, in ab-planar magnetic fields, samples did not show the Fraunhofer-type field modulation of the critical current. All these features indicate that the c-axis transport characteristics of $SmFeAsO_{0.85}$ single crystals are explained by the anisotropic bulk superconductivity rather than Josephson tunneling.

• 한국초전도학회:학술대회논문집
• /
• v.15
• /
• pp.40-40
• /
• 2005

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.2 no.1
• /
• pp.43-50
• /
• 1992

$ LiNbO_3$ single crystals were grown using the Czochralski Method at various pulling speeds. Macroscopic defects such as cracks, bubbles and cellular structures were observed in some crystals. Cracks and bubbles observed in the crystals depended on the pulling speed and cooling rate. $ LiNbO_3$ crystals of about 15mm diameter could be grown properly at 6-7mm/h pulling speed and $ 20^{circ}C/h$ cooling rate. In order to investigate dielectric properties and optical properties for device application, these properties were measured for the sample cut along a axis and c axis at different temperatures.

• Journal of the Korean Ceramic Society
• /
• v.27 no.4
• /
• pp.536-542
• /
• 1990

Single crystals of YBa2Cu3O7-x have been grown in BaCuO2 flux at temperature of 125$0^{\circ}C$ and examined using XRD, EDAX and light microscopy. The YBCO crystals were grown in a cavity which was formed by the reduction of CuO and became large by the directional solidification in the crucible. The observed crystal growth habit is square planar with the c-axis normal to the plane. The surface morphology of grown crystals were growth ledges and growth sprial paterns on a (001) face.

• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.711-716
• /
• 2012

Tungsten bronze structure $Sr_{1-x}Ba_xNb_2O_6$ (SBN) single crystals were grown primarily using the Czochralski method, in which several difficulties were encountered: striation formation and diameter control. Striation formation occurred mainly because of crystal rotation in an asymmetric thermal field and unsteady melt convection driven by thermal buoyancy forces. To optimize the growth conditions, bulk SBN crystals were grown in a furnace with resistance heating elements. The zone of $O_2$ atmosphere for crystal growth is 9.0 cm and the difference of temperature between the melt and the top is $70^{\circ}C$. According to the growth conditions of the rotation rate, grown SBN became either polycrystalline or composed of single crystals. In the case of as-grown $Sr_{1-x}Ba_xNb_2O_6$ (x = 0.4; 60SBN) single crystals, the color of the crystals was transparent yellowish and the growth axis was the c-axis. The facets of the crystals were of various shapes. The length and diameter of the single crystals was 50~70 mm and 5~10 mm, respectively. Tungsten bronze SBN growth is affected by the temperature profile and the atmosphere of the growing zone. The thermal expansion coefficients on heating and on cooling of the grown SBN single crystals were not matched. These coefficients were thought to influence the phase transition phenomena of SBN.

• Progress in Superconductivity
• /
• v.3 no.2
• /
• pp.140-145
• /
• 2002

An enhancement of the c-axis differential conductance around the zero-bias voltage near the superconducting transition temperature $T_{c}$ has been observed in $Au/Bi_2$$Sr_2$$CaCu_2$$O_{8+x}$ junctions. We attribute such an enhancement to the Andreev reflection (AR) between the surface Cu-O bilayer with suppressed superconductivity and the next superconducting Cu-O bilayer. The continuous evolution of the differential conductance, from gap like depression to an AR-like peak structure, around the zero-bias voltage points to weakening of the barrier strength of the nonsuperconducting layer between adjacent Cu-O bilayers as temperature approaches $T_{c}$ from below. The peak structure disappeared just below the bulk $T_{c}$ value of underdoped Bi2212 single crystals, whereas it survived up to ~1 K above $T_{c}$ in Junctions prepared on slightly overdosed crystals. According to a recently proposed theoretical consideration, a wider temperature range of the AR a bone $T_{c}$ is expected in the underdoped regime when phase-incoherent preformed pairs emerge in the pseudogap state. Our result is in contradiction to the preformed pair scenario. scenario.o.

• Korean Journal of Crystallography
• /
• v.7 no.1
• /
• pp.44-56
• /
• 1996

CuInTe2 synthesised in a horizontal electric furnace was found to be polycrystalline. Single crystals of CuInTe2 were grown with the vertical Bridgman technique. The structure, Hall effect of the crystals were measured in the temperature range 30 to 293K. Both the polycrystals and single crystals of CuInTe2 were tetragonal in structure. The lattice constants of the polycrytals were measured as a=6.168Å and c=12.499Å, with c/a=2.026, these of the single crystals were measured as a=6.186Å and c=12.453Å, with c/a=2.013. The growth plane of the oriented single crystals was confirmed to be a (112) plane from the back-reflection Laue patterns. The Hall effect of the CuInTe2 single crystals was measured with the method of van der Pauw The Hall data of the samples measured at room temperature showed a carrier concentration of 2.14×1023holes/m3, a conductivity of 739.58Ω-1m-1, and a mobility of 2.16×10 -2m 2/V·s for the sample perpendicular to the c-axis. Values of 1.51×1023holes/m3, 717.55Ω-1m-1, and 2.97×10-2 m2/V·s were obtained for the sample parallel to the c-axis. The Hall coefficients for the samples both perpendicular and parallel to the c-axis in the temperature range 30K to 293K were always positive values. Thus the CuInTe2 single crystal was determined to be a p-type semiconductor.

• Korean Journal of Crystallography
• /
• v.7 no.2
• /
• pp.183-190
• /
• 1996

Single crystals of ZnO were grown hydrothermally with KOH solution in silver lined autoclave. The effect of LiOH and NH4OH on the morphology of as-grown crystals was studied. As-grown crystals were pale green and the maximum size was 30×30×20mm3. Addition of LiOH reduced the density of flaws on the (0001) face of as-grown ZnO crystals. In highly concentrated KOH solution, ZnO had a strong tendency to grow along the c-axis. When 1.0-2.0 M of NH4OH was added into mineralizer, growth rate along the direction of a-axis increased. From this result, ZnO single crystals of equant-faced hexagonal prism could be grown with acicular seeds.

• 한국초전도학회:학술대회논문집
• /
• v.12
• /
• pp.36-36
• /
• 2002

• 한국초전도학회:학술대회논문집
• /
• v.11
• /
• pp.20-20
• /
• 2001