Growth And Characterization of $LiNbO_3$ Single Crystals

$LiNbO_3$단결정성장 및 특성 연구

  • 손진영 (한국과학기술원 무기재료공학과) ;
  • 노광수 (한국과학기수원 무기재료공학과) ;
  • 이진형 (학국과학기수원 재료공학과)
  • Published : 1992.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

$ LiNbO_3$ single crystals were grown using the Czochralski Method at various pulling speeds. Macroscopic defects such as cracks, bubbles and cellular structures were observed in some crystals. Cracks and bubbles observed in the crystals depended on the pulling speed and cooling rate. $ LiNbO_3$ crystals of about 15mm diameter could be grown properly at 6-7mm/h pulling speed and $ 20^{circ}C/h$ cooling rate. In order to investigate dielectric properties and optical properties for device application, these properties were measured for the sample cut along a axis and c axis at different temperatures.

인상속도를 변수로 Czochralski법을 이용하여 $ LiNbO_3$결정들을 성장시켰다. 성장된 단결정에 균열, 기포, 셀 구조 등의 결함들이 관찰되었다. 균열들은 인상속도와 냉각속도에 매우 민감하였는데 6~7mm/h의 인상속도와 20^{circ}C/h의 냉각속도가 직경 15mm정도의 결정성장에 적당한 조건임을 알 수 있었다. 소자응용에 필요한 유전적 성질 및 광학적 성질 등을 알아보기 위하여 a축, c축방향에 따라 절삭된 시편을 온도를 변화시켜가며 측정하였다.

Keywords