• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.256-257
• /
• 2014

Concrete made with ground granulated blast-furnace slag(GGBS) has many advantage, including improved durability, workability and economic benefits. GGBS concrete is that its strength development is considerably slower under standard 20℃ curing conditions than that of portland cement concrete, although the ultimate strength is higher for same water-binder ratio. GGBS is not therefore used in application where high early age strength is required. However, hydration of GGBS is much more sensitive to temperatures, the strength development of GGBS concrete is significantly enhanced.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.363-364
• /
• 2010

Recently, various researchers have studied alkali-activated concrete that do cementless as the binder. This study analyzed the effect on cementless mortar by flay ash and blast furnace slag of blast slag as the binder with no use of cement, by observing compressive strength and micro-structure.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.55 no.6
• /
• pp.11-17
• /
• 2013

This study was performed to evaluate the chlorine ion penetration resistance, chemical resistance and freezing and thawing resistance used ordinary portland cement, crushed coarse aggregate, crushed sand, river sand, fly ash, limestone powder, blast furance slag powder and superplasticizer to find optimum mix design of low carbon green concrete for structures. The performance of low carbon green concrete used fly ash, limestone powder and blast furnace slag powder were remarkably improved. This fact is expected to have economical effects in the manufacture of low carbon green concrete for offshore structures. Accordingly, the fly ash, limestone powder and blast furnace slag powder can be used for offshore structure materials.

• Advances in concrete construction
• /
• v.4 no.2
• /
• pp.107-121
• /
• 2016

This concrete is one of the most versatile construction material widely used for almost a century now. It was considered to be very durable material and required a little or no maintenance since long time. The assumption is very true, except when it is subjected to highly aggressive environments. The deterioration of concrete structures day by day due to aggressive environment is compelling engineers to assess the loss in advance so that proper preventive measure can be taken to achieve required durability to concrete structures. The compounds present in cement concrete are attacked by many salt solutions and acids. These chemicals are encountered by almost all concrete structures. The present study has been undertaken to investigate the effect of attack of chlorides and sulphates with varying severity on compressive strength of ground granulated blast furnace slag (GGBFS) concrete after immersion in salt solution for 28 days. The results indicate that the durability of GGBFS concrete increases with the increase in percentage replacement of cement by GGBFS for 20% and then gradually decreases with increases in percentage of GGBFS with cement (as in the study for 40% and 60%). Also there is increase in strength of GGBFS concrete with increase in age. Thus the durability of concrete improves when GGBFS is added as partial replacement of cement. In this study the strength of GGBFS concrete is less affected by chemicals as compared to conventional concrete when exposed to aggressive environment.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.63-71
• /
• 2011

Portland cement production is under critical review due to high amount of $CO_2$ gas released to the atmosphere. Attempts to increase the utilization of a by-products such as fly ash and ground granulated blast-furnace slag to partially replace the cement in concrete are gathering momentum. But most of by-products is currently dumped in landfills, thus creating a threat to the environment. Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. In this study, we investigated the influence of alkali activator and superplasticizer on the flowability and compressive strength of the alkali-activated mortar in oder to develop cementless alkali-activated concrete using blast furnace slag. In view of the results, we found out that the type and mixture ratio of alkali activator, the type and adding order of superplasticizer results to be significant factors. When cementless alkali-activated mortar using blast furnace slag manufactured with 1:1 the mass ratio of 9M NaOH and sodium silicate, and added superplasticizer before alkali activator in the mixer, we can be secured workability with 180 mm of flow during 1 hours and compressive strength of about 50 MPa under $20^{\circ}C$ curing condition at age of 28days.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.1
• /
• pp.29-36
• /
• 2019

This study investigated the self-healing properties of blast furnace slag cement paste sample with $Na_2SO_4$ as a blast furnace slag activator after conducting the permeability test. Self-healing properties were examined by crack filling ratio and quantification of self-healing products. The degree of self-healing was evaluated by the crack filling ratio, and the crack filling ratio was analyzed by panoramic analysis using BSE-DIP for objectivity. The average crack filling ratio showed a tendency of decreasing from the upper part of the specimen to the lower part as the average of the top part was 18%, the middle part was 7% and the bottom part was 5% on average. The maximum crack filling ratio was 44% and the minimum crack filling ratio was 3%. The residual self-healing product after the permeability test contained a large amount of Ca element and Al element derived from the blast furnace slag, and the Si element was mainly present near the crack surface. The most abundant minerals in self-healing products were about 68% C-A-H. $CaCO_3$ was about 13% and C-A-S-H was about 8%. Three minerals accounted for 90% of self-healing products. C-A-H was mainly present at a part slightly distant from the crack surface and showed an angular or acicular shape. The C-A-S-H was generated on the surface naturally connected to the existing specimen, and the $CaCO_3$ was generally observed on the surface of the specimen or the inside of the crack.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.3 no.3
• /
• pp.177-185
• /
• 1999

In this study, study about fly ash and blast-furnace slag used as substitutive materials for cement, and the influence on the neutralization of high flow concrete durability with these substitutive materials was performed and analyzed. The results are as follows 1) Aggregate segregation was partially improved with the progress of the admixture input at the mix proportion above slump flow 65 cm 2) Compressive strength with the progress of the increasement of fly ash input was decreased in early age, but decrease range was improved in long term age. Also, in case of blast-furnace, similar or improved compressive strength was appeared. 3) The neutralization depth with fly ash input was noticeably increased. But blast-furnace slag was effective to prevent. 4) In this experiment, high powder content was advantageously affected on preventive effect of the neutralization, and the relationship between the compressive strength and the neutralization depth was inversely proportional.

• Journal of the Korea Institute of Building Construction
• /
• v.22 no.6
• /
• pp.641-649
• /
• 2022

This study aims to completely develop a non sintered cement mortar using industrial by-products. To replace Portland cement, blast furnace slag, circulating fluidized bed fly ash, and pulverized coal fly ash were used, and natural aggregates were substituted with ferronickel slag. To understand the characteristics of the non sintered cement mortar to which ferronickel slag is applied, an experiment was conducted by classifying the particle size. Fluidity and workability were confirmed through the flow test, and bending and compressive strength tests were conducted at 3, 7, and 28 days of age. In addition, durability was identified through a chloride ion penetration test. Through the study, it is judged that the binder, which completely replaced cement and aggregate, has high potential of being used as a construction material. Notably, it was confirmed to be advantageous for strength and durability.

• Journal of the Korean Geotechnical Society
• /
• v.30 no.1
• /
• pp.93-101
• /
• 2014

In this study, a blast furnace slag having latent hydraulic property with an alkaline activator for resource recycling was used to solidify sand without using cement. Existing chemical alkaline activators such as $Ca(OH)_2$ and NaOH were used for cementing soils. An alkaliphilic microorganism, which is active at higher than pH 10, is tested for a new alkaline activator. The alkaliphilic microorganism was added into sand with a blast furnace slag and a chemical alkaline activator. This is called the microorganism alkaline activator. Four different ratios of blast furnace slag (4, 8, 12, 16%) and two different chemical alkaline activators ($Ca(OH)_2$ and NaOH) were used for preparing cemented specimens with or without the alkaliphilic microorganism. The specimens were air-cured for 7 days and then tested for the experiment of unconfined compressive strength (UCS). Experimental results showed that as a blast furnace slag increased, the water content and dry density increased. The UCS of a specimen increased from 178 kPa to 2,435 kPa. The UCS of a specimen mixed with $Ca(OH)_2$ was 5-54% greater than that with NaOH. When the microorganism was added into the specimen, the UCS of a specimen with $Ca(OH)_2$ decreased by 11-60% but one with NaOH increased by 19-121%. The C-S-H hydrates were found in the cemented specimens, and their amounts increased as the amount of blast furnace slag increased through SEM analysis.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.3A
• /
• pp.407-415
• /
• 2008

Hydration reaction of Free-CaO is thought to be the main reason of expansion failure of slag. A lot of research institutions are conducting studies on solutions to this problem, and moreover it has been carried out how to make use of aggregates for concrete. While studies covering wide rage of blast furnace slag have been accomplished in the country, studies on steelmaking slag are insufficient. Therefore, this study aimed at analyzing basic physical properties of electric arc furnace oxidizing slag, which is the main material, and furthermore it focused on how to make use of aggregates for concrete examining chemical mechanism, which can be put to practical use. To address this issue, components of electric arc furnace oxidizing slag were analyzed with measurement of physical properties, followed by long-term strength and detailed durability analysis, which can evaluate the appropriateness of application of cement concrete. Besides the environmental conservation and recycling which can be obtained by application of industry byproducts, commercializing of electric arc furnace oxidizing slag as fine aggregates for cement concrete are expected.