• Transactions of the Korean Society of Automotive Engineers
• /
• v.17 no.3
• /
• pp.15-21
• /
• 2009

The anisotropic mechanical properties were measured for the three orthogonal orientations of plain weave glass fabric reinforced epoxy resin laminate. In tensile and flexural tests, axial and edge type specimens failed by pull-out of warp and fill yarns, respectively. In contrast, the thickness type specimens failed by adhesive failure process. Longitudinal cracking occurred in several of the edge type specimens during tensile test. That cracking caused pop-in in the stress-strain curve. Defects induced by improper coupon machining caused that cracking.

• Journal of the korean Society of Automotive Engineers
• /
• v.12 no.2
• /
• pp.29-42
• /
• 1990

Three dimensional frame structures with such nonlinearities as large displacements, medium rotations, plastic hinges and local defects are efficiently analyzed by introducing the nonlinear rotational spring. Formulations are based on the incremental updated Lagrangian descriptions and the virtual work principle, Axial displacement and twisted angle in beam elements are interpolated linearly, while bending displacements are approximated by the Hermite polynomials. The modified are length method is used as a solution method. The moment-angle of rotation relationship obtained analytically or experimentally can be easily incorporated into the solution procedure. Several examples tested show that the present method can be used efficiently in analyzing nonlinear frame structures with plastic hinges or local defect.

• Journal of Korean Neurosurgical Society
• /
• v.64 no.5
• /
• pp.837-842
• /
• 2021

An atlantoaxial subluxation from the unstable Os odontoideum by the failure of proper integrations between the embryological somites might be a commonly reported pathology. However, its suspicious origin or paralleled occurrence with other congenital anomalies of vertebral body might be a relatively rare phenomenon. The authors present two cases, who simply presented with clinical signs of prolonged, intractable cervicalgia without any neurological deficits, revealed this rare feature of C1-2 subluxation from the unstable, orthotropic type of Os odontoideum that coincide with congenitally fused cervical vertebral bodies between C2-3. Surprisingly, in one case, when traced from the lower cervical down to the thoracic-lumbar levels during the preoperative work-up process, was also compromised with multi-level butterfly vertebrae formations. Presented cases highlight the association of various congenital vertebrae anomalies and the rationale to fuse only affected joints.

• International Journal of Fluid Machinery and Systems
• /
• v.6 no.2
• /
• pp.105-112
• /
• 2013

The application of contra-rotating rotors for higher specific speed pump has been proposed in our studies, which is in principle effective for reducing the rotational speed and/or the pump size under the same specification of conventional axial flow pump. In the previous experiments of our prototype, the cavitation inception at the tip region of the rear rotor rather than that of the front rotor and the strong potential interaction from the suction surface of the rear rotor blade to the pressure surface of the front one were observed, indicating the possibility to further improve the pump performance by optimizing rotational speed combination between the two rotors. The present research aims at the design of rear rotor with lower rotational speed. Considering the fact that the incoming flow velocity defects at the tip region of the rear rotor, an integrated inflow model of 'forced vortex' and 'free vortex' is employed. The variation of maximum camber location from hub to tip as well as other related considerations are also taken into account for further performance improvement. The ideas cited above are separately or comprehensively applied in the design of three types of rear rotor, which are subsequently simulated in ANSYS CFX to evaluate the related pump performance and therefore the whole low speed design idea. Finally, the experimental validation is carried out on one type to offer further proofs for the availability of the whole design method.

• Journal of Technologic Dentistry
• /
• v.41 no.4
• /
• pp.255-262
• /
• 2019

Purpose: Recently, the production technology of dental prosthesis using 3D Printer workpeices has been developed. However, the lack of information on the work processes and casting techniques of materials for 3D printing casting is expected to require research. Therefore, in this study, we intend to cast a Dental DLP 3D Printer workpiece, which is being commercialized, to identify its appearance and internal clearance, and to observe its castability. Methods: Castability of the 3D Printer workpiece was evaluated. The specimen is prepared in a cylindrical shape and in a 1 mm thick coping shape. The control specimen is made of wax and the experimental specimen is made of resin using two types of 3D printers. After casting, the appearance of the casting body was observed and the internal clearance of the coping was measured. Results: RP1 and RP2, cylindrical specimens, were partially cast or fin. When coping-type specimens were measured before casting, the internal clearance of PE2 was more accurate than that of PC and PE1. When coping-type specimens were measured after casting, CE1 was the most accurate in occlusal clearance and CE2n was the most accurate in axial clearance. Conclusion: 1. Exterior observations of the casting body indicated casting defects and fins. 2. Internal clearance observations show that the occlusal clearance of the castings is larger after casting, and the axial clearance of the castings is smaller after casting. 3. It is judged that the RP2 specimen is more likely to be applied for casting than the RP1 specimen.

• Proceeding of KASS Symposium
• /
• 2008.05a
• /
• pp.184-188
• /
• 2008

Performance degradation of concrete structures is generally caused by structural deteriorations, such as cracks. It may result in serious defects of concrete structures. Methods of damage detection are used a visual angle of human or non-destructive test, and they are using various sensors. Problems of crack damage detection are occurred to directions of cracks by using 1 axial type of accelerometer in concrete element. In addition, these sensors are not used to occurring fire in RC building. Thermocouple sensors are able to using measurement of temperature in fire, and then deformations of main element and structures are not used. In this study, fundamental studies for development of multiple function sensor using 3 axial type of accelerometer and electric resistance property of thermocouple sensors are discussed estimation to stability of structures when happened form active load or fire, and so on.

• Journal of Power System Engineering
• /
• v.13 no.5
• /
• pp.52-58
• /
• 2009

A gas turbine consists of an upstream compressor and a downstream turbine with a combustion chamber, and also the compressor and the turbine are generally coupled using a single shaft. Many casing bolts are used to assemble two horizontally separated casings, the gas turbine casing and the compressor casing, in both of axial and vertical directions. Because drilled holes for casing bolts in vertical direction are often too close to drilled holes for casing bolts in axial direction, one can observe cracks in the area frequently during operations of a gas turbine. In this study of the root cause analysis for the cracking initiating from the drilled holes of the casings of a gas turbine, the finite element analysis(FEA) was applied to evaluate the thermal and mechanical characteristics of the casings. By applying the field operation data recorded from combined cycle power plants for FEA, thermal and thermo-mechanical characteristics of a gas turbine are analyzed. The crack is initiated at the geometrical weak point, but it is found that the maximum stress is relieved when the same type of cracks is introduced on purpose during FEA. So, it is verified that the local fracture could be delayed by machining the same type of defects near the hole for casing flange bolts of the gas turbine, where the crack is initiated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.22-23
• /
• 2005

In order to increase the critical current of coated conductor, highly Bi-axially textured substrates are required. Texture uniformity of substrate is also important to fabricate high quality superconducting coated conductor because the amount of current flow along the coated conductor is limited by the defects such as bad textured area. Therefore, we need to evaluate the distribution of texture of Ni substrate along the length before buffer layer deposition on Ni tape. R2R(reel-to-reel) XRD system was used to measure the texture of long Ni substrate continuously. $\theta-2\theta$ scan of 10 m long Ni tape was measured and indicates that some of Ni(111) planes equally remain on Ni(002) textured substrate. The results of continuous Ni(220) $\Phi$-scan indicate that average FWHM is 9$^{\circ}$ within $\pm$1.

• Journal of the Korean Institute of Gas
• /
• v.6 no.1 s.17
• /
• pp.10-16
• /
• 2002

This paper introduces developed prototype intelligent pig which detects corrosion on pipeline by using Magnetic Flux Leakage technology. The 8 inch developed MFL(Magnetic Flux Leakage) pig is composed of 5 yokes which magnetize pipeline wall and 45 Hall sensors which detect MFL signal. The designed MFL modules are analyzed by using magnetic circuit method in order to confirm whether pipeline wall is fully saturated. A variety of artificial defects are manufactured on 8 inch diameter steel pipeline in order to acquire MFL signals. So leakage flux of the axial, radial and circumferential component was acquired as defects. The results of this paper show that design technique for 8 inch MFL pig can be applied to large diameter MFL pig and 0.5mm defect depth can be detected.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1996.06a
• /
• pp.526-526
• /
• 1996

The single crystal of LiTaO3 is well known eletro-optic material as well as the piezoelectric one applied to SAW filter. LiTaO3 has large electro-optic effects, so applied to optical switch, acosto-optic deflector, and optical memory device using photorefractive effects. The crystal growth of SAW-grade LiTaO3 has been studied many aspects, but there is no detail research about optic-grade crystal growth. The conditions of optic-grade LiTaO3 single crystal are as below. The optical transmittance must be over 75%, and axial and radial concentratiom uniformity below 1%. The variation of Curie temperature depending on Li/Ta ratio must be also below 2$^{\circ}C$ and no internal no internal cracks and defects. Because of the limitation of crystal quality, the growing of optic-grade LiTaO3 single crystal is very difficult compared with the growing of SAW-grade. In this research, upper conditions of optic-grade single crystal was investigated after growing of 1 inch diameter and 1.5 inch length LiTaO3 single crystal having no internal cracks and defects using Czochralski method. Curie temperature was determined with DSC and measuring capacitance and lattice parameter was calculated about the grown crystal and ceramic powder samples of various Li/Ta ratio. The result of Tc variation was below 1.2$^{\circ}C$ all over the grown crystal, so it is confirmed that LiTaO3 was grown under congruent melting composition having optical homogeniety. Also, the optical transmittance was about 78%, which was sufficient for optical device.