• Journal of Powder Materials
• /
• v.22 no.4
• /
• pp.240-246
• /
• 2015

Anodic aluminum oxide (AAO) has been widely used for the development and fabrication of nano-powder with various morphologies such as particle, wire, rod, and tube. So far, many researchers have reported about shape control and fabrication of AAO films. However, they have reported on the shape control with different diameter and length of anodic aluminum oxide mainly. We present a combined mild-hard (or hard-mild) anodization to prepare shape-controlled AAO films. Two main parameters which are combination mild-hard (or hard-mild) anodization and run-time of voltage control are applied in this work. The voltages of mild and hard anodization are respectively 40 and 80 V. Anodization was conducted on the aluminum sheet in 0.3 mole oxalic acid at $4^{\circ}C$. AAO films with morphologies of varying interpore distance, branch-shaped pore, diameter-modulated pore and long funnel-shaped pore were fabricated. Those shapes will be able to apply to fabricate novel nano-materials with potential application which is especially a support to prevent volume expansion of inserted active materials, such as metal silicon or tin powder, in lithium ion battery. The silicon powder electrode using an AAO as a support shows outstanding cycle performance as 1003 mAh/g up to 200 cycles.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.14 no.4
• /
• pp.923-928
• /
• 2010

Anodic aluminum oxide (AAO) nanotemplates for nano electronic device applications have been attracting increasing interest because of ease of fabrication, low cost process, and possible fabrication in large area. The size and density of the nanostructured materials can be controlled by changing the pore diameter and the pole density of AAO nanotemplate. In this paper, nano porous alumina films AAO nanotemplate was fabricated by second anodization method using sputterd Al films. In addition, effects of electrolyte temperature and anodization voltate on the microstructure of porous alumina films were investigated. As the electrolyte temperature was increased from $8^{\circ}C$ to $20^{\circ}C$, the growth rate of nanoporous alumina films was increased from 86.2 nm/min to 179.5 nm/min. The AAO nanotemplate fabricated with optimal condition had the mean pore diameter of 70 nm and the pore depth of $1\;{\mu}m$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2003.07a
• /
• pp.867-869
• /
• 2003

Vacuum tube arrays (VTA) with a submicron dimension were fabricated by using anodic aluminum oxide (AAO) nano-templates. The field emission characteristics of Ni nanowires show a turn-on voltage in the range of 11.0-14.0 V and a field enhancement factor in the range of 560-2790. The distance between the tips of Ni nanowires and the anode was much smaller than that between the tips and the anode of conventional designs.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.9
• /
• pp.2447-2448
• /
• 2010

• Journal of the Korean institute of surface engineering
• /
• v.50 no.6
• /
• pp.427-431
• /
• 2017

Anodic aluminum oxide (AAO) film has recently attracted much attention as a key material for the fabrication of various nanostructures. A control of anodizing voltage (U) was employed to render different anodic aluminum oxide (AAO) nanostructures with pore diameter ($D_p$) and interpore distance ($D_{int}$) in oxalic acid. In this work, we study the effect of stepwise modulation of anodizing voltages on the shape and dimension of porous structures along the vertical direction and demonstrate the fabrication of hierarchical layers of systematically controlled three-dimensional (3D) pore profile.

• Tribology and Lubricants
• /
• v.33 no.6
• /
• pp.275-281
• /
• 2017

In this work, we have fabricated anodic aluminum oxide (AAO) with ordered nanoscale porosity through an anodization process. We deposited gold and nano-organic thin films on the porous AAO surface to protect its structure and reduce friction. We investigated the tribological characteristics of the porous AAO with respect to the protective surface coatings using tribometers. While investigating the frictional characteristics of the samples by applying normal forces of the order of micro-Newton, we observed that AAO without a protective coating exhibits the highest friction coefficient. In the presence of protective surface coatings, the friction coefficient decreases significantly. We applied normal forces of the order of milli-Newton during the tribotests to investigate the wear characteristics of AAO, and observed that AAO without protective surface coatings experiences severe damage due to the brittle nature of the oxide layer. We observed the presence of several pieces of fractured particles in the wear track; these fractured particles lead to an increase in the friction. However, by using surface coatings such as gold thin films and nano-organic thin films, we confirmed that the thin films with nanoscale thickness protect the AAO surface without exhibiting significant wear tracks and maintain a stable friction coefficient for the duration of the tribotests.

• Transactions of the Korean hydrogen and new energy society
• /
• v.29 no.5
• /
• pp.434-441
• /
• 2018

The pore size of nickel (Ni) bottom electrode layer (BEL) for low-temperature solid oxide fuel cells embedded with ultrathin-film electrolyte was controlled by changing the substrate surface morphology and deposition process parameters. For ~150-nm-thick Ni BEL, the upper side of an anodic aluminum oxide (AAO) substrate with ~65-nm-sized pores provided ~1.7 times smaller pore size than the lower side of the AAO substrate. For ~100-nm-thick Ni BEL, the AAO substrate with ~45-nm-sized pores provided ~2.6 times smaller pore size than the AAO substrate with ~95-nm-sized pores, and the deposition pressure of ~4 mTorr provided ~1.3 times smaller pore size than that of ~48 mTorr. On the AAO substrate with ~65-nm-sized pores, the Ni BEL deposited for 400 seconds had ~2 times smaller pore size than the Ni BEL deposited for 100 seconds.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.05a
• /
• pp.368-370
• /
• 2007

AAO(Anodic Aluminum Oxidation) method has been known that it is practically useful for the fabrication of nano-structures and makes it possible to fabricate the highly ordered nano masters on large surface and even on the 2.5 or 3D surface at low cost comparing to the expensive e-beam lithography or the conventional silicon processing. In this study, by using the multi-step anodizing and etching processes, highly ordered nano patterned master with concave shapes was fabricated. By varying the processing parameters, such as initial matter and chemical conditions; electrical and thermal conditions; time scheduling; and so on, the size and the pitch of the nano pattern can be controlled. Consequently, various alumina/aluminum nano structures can be easily available in any size and shape by optimized anodic oxidation in various aqueous acids. The resulting good filled uniform nano molded structure through hot embossing molding process shows the validity of the fabricated nano pattern masters.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.1
• /
• pp.15-21
• /
• 2020

In this study, growth and burning behavior of 6061 aluminum alloy was studied under constant anodic voltages at various temperatures and magnetic stirring rates in 20% sulfuric acid solution by analysing I-t curves, measuring thickness and hardness of aluminum anodic oxide (AAO) films, observations of surface and cross-sectional images of AAO films. AAO films were grown continuously at lower voltages than 18.5V but burning occurred when a voltage more than 19V was applied in 20% H₂SO₄ solution at 20±0.5℃ and 200 rpm of magnetic stirring. The burning was always related with an extremely large increase of anodic current density with anodizing time, suggesting that high heat generation during anodizing causes deteriorations of AAO films by chemical reaction with acidic solutions. The burning resulted in decreases of film thickness and hardness, surface color brightened and formation of porous defects in the AAO films. The burning voltage was found to decrease with increasing solution temperature and decreasing magnetic stirring rate. The decreased burning voltages seem to be closely related with increased chemical reactions between AAO films and hydrogen ions.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.2
• /
• pp.130-134
• /
• 2016

The anodization of ADC12 aluminum alloy was investigated in the metal anionic acid media. Anodic oxide films containing foreign elements were formed on ADC12 Al alloy by anodization in the anion complex solution. Furthermore, the rough surface and cracks were considerably smoothened by the deposit of metal anions. When the size of metal anion was small, relatively large amount of metal anions was loaded in anodic films. Existence of $MoO_3$, $TiO_2$ and MgO was confirmed by XPS. According to the results of Tafel analysis, Mo oxide represented the most noble anti-corrosion potential due to $MoS_2$ formation. Corrosion current densities were generally higher than that of pristine anodic oxide without anion complexes.