• Korean Journal of Materials Research
• /
• v.26 no.8
• /
• pp.430-437
• /
• 2016

Aluminum oxide ($Al_2O_3$) thin films were grown by atomic layer deposition (ALD) using a new Al metalorganic precursor, dimethyl aluminum sec-butoxide ($C_{12}H_{30}Al_2O_2$), and water vapor ($H_2O$) as the reactant at deposition temperatures ranging from 150 to $300^{\circ}C$. The ALD process showed typical self-limited film growth with precursor and reactant pulsing time at $250^{\circ}C$; the growth rate was 0.095 nm/cycle, with no incubation cycle. This is relatively lower and more controllable than the growth rate in the typical $ALD-Al_2O_3$ process, which uses trimethyl aluminum (TMA) and shows a growth rate of 0.11 nm/cycle. The as-deposited $ALD-Al_2O_3$ film was amorphous; X-ray diffraction and transmission electron microscopy confirmed that its amorphous state was maintained even after annealing at $1000^{\circ}C$. The refractive index of the $ALD-Al_2O_3$ films ranged from 1.45 to 1.67; these values were dependent on the deposition temperature. X-ray photoelectron spectroscopy showed that the $ALD-Al_2O_3$ films deposited at $250^{\circ}C$ were stoichiometric, with no carbon impurity. The step coverage of the $ALD-Al_2O_3$ film was perfect, at approximately 100%, at the dual trench structure, with an aspect ratio of approximately 6.3 (top opening size of 40 nm). With capacitance-voltage measurements of the $Al/ALD-Al_2O_3/p-Si$ structure, the dielectric constant of the $ALD-Al_2O_3$ films deposited at $250^{\circ}C$ was determined to be ~8.1, with a leakage current density on the order of $10^{-8}A/cm^2$ at 1 V.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.21.2-21.2
• /
• 2011

$Fe_3O_4$ having half metallic property is one of the efficient spin filtering materials which are widely used in spintronic research field and ZnO is wide band gap semiconductor which can be used by tunnel barrier or semiconductor channel in spin MOSFET. We investigated the magnetic and the electric properties of $Fe_3O_4$/ZnO multilayer fabricated on c-$Al_2O_3$ substrate by pulsed laser deposition (PLD). For multilayer films, PLD was performed at variable temperatures such as $200{\sim}750^{\circ}C$ and at target distance from 40 to 80 mm, KrF eximer laser of 1.5 $J/cm^2$ and a reputation rate of 2Hz. $Fe_3O_4$/ZnO multilayers were deposited at $4{\times}10^{-6}$ Torr. After fabricating $Fe_3O_4$/ZnO multilayers, $Fe_3O_4$/ZnO multilayers were treated by RTA(Rapid Thermal Annealing) at various temperature to change magnetic phase. The magnetism of the multilayer is changed by thickness of the ZnO tunnel barrier. Magnetic phase of FexOy showed a very small magnetism due to $Fe_2O_3$ ${\alpha}$-phase, but large magnetism from $Fe_3O_4$ or $Fe_2O_3$ ${\gamma}$-phase was observed. In the present study, effect of the ZnO thickness on the MR (magnetoresistance) ratio was investigated in detail.

• Solar Energy
• /
• v.17 no.2
• /
• pp.55-66
• /
• 1997

The structural and optoelectronic properties of polycrystalline CdS films up to several microns in thickness, fabricated by three different methods, are compared to one another for the purpose of preparing CdTe/CdS solar cells. All films were deposited on an indium tin oxide on glass substrate. The three methods are: 1) alternated spraying of cation and anion solution at room temperature; 2) spray pyrolysis with substrate temperature up to $500^{\circ}C$; 3) chemical bath deposition (CBD). Deposited films were thermally treated in various ways. All films showed a well-developed wurtzite structure. Films grown by the alternated-spray method and the chemical bath method consist of randomly-oriented crystallites with dimensions <0.5 microns. Annealing at $400^{\circ}C$ increases the crystallite size slightly. Films which were grown by pyrolysis at substrate temperatures from $400^{\circ}C\;to\;500^{\cir\c}C$ were oriented in the <002> direction. For growth by pyrolysis at $500^{\circ}C$, the surface is rough on a lateral scale of 0.1 to 0.3 microns. The optical band gap and defect states are investigated by optical absorption, photoluminescene, Raman, and photothermal deflection spectroscopies.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.3
• /
• pp.332-337
• /
• 2006

We prepared 100 nm-thick CoNi composite silicide on a 70 nm-thick polysilicon substrate. Composite silicide laye.s were formed by rapid thermal annealing(RTA) at the temperatures of $700^{\circ}C,\;900^{\circ}C,\;1000^{\circ}C$ for 40 seconds. A Focused ion beam (FIB) was used to make nano-patterns with the operation range of 30 kV and $1{\sim}100$ pA. We investigated the change of thickness, line width, and the slope angle of the silicide patterns by FIB. More easily made with the FIB process than with the conventional polycide process. We successfully fabricated sub-100nm etched patterns with FIB condition of 30kv-30pA. Our result implies that we may integrate nano patterns with our newly proposed CoNi composite silicides.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.34 no.3
• /
• pp.241-247
• /
• 2014

This study presents the ultrasonic nonlinearity of AISI316 austenitic stainless steels subjected to longterm isothermal aging. These steels are attractive materials for use in industrial mechanical structures because of their strength at high-temperatures and their chemical stability. The test materials were subjected to accelerated heat-treatment in an electrical furnace for a predetermined aging duration. The variations in the ultrasonic nonlinearity and microstructural damage were carefully evaluated through observation of the microstructure. The ultrasonic nonlinearity stiffly dropped after aging for up to 1000 h and, then, monotonously decreased. The polygonal shape of the initial grain structures changed to circular, especially as the annealing twins in the grains dissolved and disappeared. The delta ferrite on the grain boundaries could not be observed at 1000 h of aging, and these continuously transformed into their sigma phases. Consequently, in the intial aging period, the rapid decrease in the ultrasonic nonlinearity was caused by voids, dislocations, and twin annihilation. The continuous monotonic decrease in the ultrasonic nonlinearity after the first drop resulted from the generation of $Cr_{23}C_6$ precipitates and ${\sigma}$ phases.

• Journal of the Korean Vacuum Society
• /
• v.20 no.1
• /
• pp.57-62
• /
• 2011

We have studied the electrical and magnetic transport properties of tunneling device with FePt magnetic quantum dots. The FePt nanoparticles with a diameter of 8~15 nm were embedded in a $SiO_2$ layer through thermal annealing process at temperature of $800^{\circ}C$ in $N_2$ gas ambient. The electrical properties of the tunneling device were characterized by current-voltage (I-V) measurements under the perpendicular magnetic fields at various temperatures. The nonlinear I-V curves appeared at 20 K, and then it was explained as a conductance blockade by the electron hopping model and tunneling effect through the quantum dots. It was measured also that the negative magneto-resistance ratio increased about 26.2% as increasing external magnetic field up to 9,000 G without regard for an applied electric voltage.

• Journal of Powder Materials
• /
• v.13 no.4 s.57
• /
• pp.285-289
• /
• 2006

Co-Fe-Ni-B-Si-Cr based amorphous strips containing nitrogen were manufactured via melt spinning, and then devitrified by crystallization treatment at the various annealing temperatures of $300^{\circ}C{\sim}540^{\circ}C$ for up to 30 minutes in an inert gas $(N_2)$ atmosphere. The microstructures were examined by using XRD and TEM and the magnetic properties were measured by using VSM and B-H meter. Among the alloys, the amorphous ribbons of $Co_{72.6}Fe_{9.8}Ni_{5.5}B_{2.4}Si_{7.1}Cr_{2.6}$ containing 121 ppm of nitrogen showed relatively high saturation magnetization. The alloy ribbons crystallized at $540^{\circ}C$ showed that the grain size of $Co_{72.6}Fe_{9.8}Ni_{5.5}B_{2.4}Si_{7.1}Cr_{2.6}$ alloy containing 121 ppm of nitrogen was about f nm, which exhibited paramagnetic behavior. The formation of nano-grain structure was attributed to the finely dispersed Fe4N particles and the solid-solutionized nitrogen atoms in the matrix. Accordingly, it can be concluded that the nano-grain structure of 5nm in size could reduce the core loss within the normally applied magnetic field of 300A/m at 10kHz.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.12
• /
• pp.7283-7286
• /
• 2014

SiOC films were prepared as insulators for displays by sputtering at low temperatures, and the relationship with the electrical properties waaas examined. The electrical properties of SiOC films were affected by the annealing process, and SiOC films annealed at 100oC showed a significant increase in thickness and a decrease in the reflective index. XRD revealed an increase in the degree of the amorphous structure. Moreover, the capacitance and leakage current of the SiOC films annealed at 100oC decreased. These characteristics of SiOC films highlight their potential as ideal insulators. Amorphous SiOC films by the reduction of polarization are dependent on the elongation effect of the bonding lengths in the structure and the thickness. The properties of these SiOC films are suitable for low temperature displays.

• Journal of Powder Materials
• /
• v.12 no.4 s.51
• /
• pp.273-278
• /
• 2005

Nanostructured TiN/$TiB_2$/$TiSi_2$ and TiN/$TiB_2$/$Ti_5Si_2$ composite powders have been prepared by mechanochemical reaction from mixtures of Ti, BN, and $Si_3N_4$ powders. The raw materials have reacted to form a uniform mixture of TiN, $TiB_2$ and $TiSi_2$ or $Ti_5Si_3$ depending on the amount of $Si_3N_4$ used in the starting mixtures, and the reaction proceeded through so-called mechanically activated self-sustaining reaction (MSR). Fine TiN and $TiB_2$ crystallites less than a few tens of nanometer were homogeneously dispersed in the amorphous $TiSi_2$ or $Ti_5Si_3$ matrix after milling for 12 hours. These amorphous matrices became crystalline phases after annealing at high temperatures as expected, but the original microstructure did not change significantly.

• Journal of Korea Foundry Society
• /
• v.32 no.2
• /
• pp.104-108
• /
• 2012

The effect of heat treatment on mechanical properties of 0.4C-2.3Si(wt%) steel with bainitic ferrite matrix were investigated. This steel has been synthesized intergrating concepts from TRIP(Transformation Induced Plasticity) steel & Austempered Ductile Cast Iron(ADI) technology. The low alloy medium carbon (0.4 %C) steel with high silicon (2.3 %Si) was initially annealed for 60 min at $800^{\circ}C$, $820^{\circ}C$ and $840^{\circ}C$ respectively in the intercritical region and then subsequently austempered at various temperatures at $260^{\circ}C$, $320^{\circ}C$ and $380^{\circ}C$ for 30 min in a salt bath. The mechanical properties were measured by using a tensile test. A detailed study of the microstructure of this steel after heat treatment was carried out by means of electron back scattering diffraction (EBSD) technic. In this study, a new low alloy steel with high strength (780~1,050MPa) and exceptionally high ductility (20~40%) was obtained.