• Polymer(Korea)
• /
• v.24 no.2
• /
• pp.201-210
• /
• 2000

To determine the effect of chain length of linear amine curing agents on the thermal and mechanical properties, standard epoxy resin, diglycidyl ether of bisphenol A (DGEBA) was cured with diethylenetriamine (DETA), triethylenetetraamine (TETA) and tetraethylenepentaamine (TEPA) in a stoichiometrically equivalent ratio. From this work, the effect of linear amine curing agents on the thermal and mechanical properties was significantly influenced by chain length of curing agents. In contrast, the results showed that the DGEBA/DETA system had higher values than the DGEBA/TETA and DGEBA/TEPA system in the density, shrinkage (%), thermal expansion coefficient, tensile modulus, and flexural strength. Whereas the DGEBA/DETA cure system had lower values than the DGEBA/TETA and DGEBA/TEPA cure system in the maximum exothermic temperature, conversion (%), and T$_{g}$. These findings imply that the differences in the maximum conversion about the chain length of curing agents affect the thermal and mechanical properties.s.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.164-165
• /
• 2021

To prepare the good-adherent and weather-resistant acrylic resin coatings, acrylic resin was prepared by a radical polymerization. Glass transition temperature(Tg) of the acrylic copolymer was fixed at 30℃ and the contents of tertiary amine monomer(DMAEMA) was varied to be 5, 10, 15, 20 wt% respectively. γ-Glycidoxypropyltrimethoxysilane(GPTMS) containing epoxy group was used for curing agents and di-n-butyltindilaurate(DBTDL) was used for drying accelerator. The equivalent ratio of amine to epoxy was 1:1. The prepared coatings exhibited excellent adhesion to various substrates, and various physical properties of the coatings were satisfactory. The gloss retention and color difference were improved at low tertiary amine concentration. The coatings containing 10wt% tertiary amine concentration have especially good weather resistant properties.

• Composites Research
• /
• v.17 no.6
• /
• pp.44-51
• /
• 2004

To determine the effect of numbers of nitrogen atom bonded at ethyl group included in main chain of linear amine curing agents of epoxy-cure systems on the thermal and mechanical properties, standard epoxy resin DGEBF was cured with DETA, TETA and TEPA in a stoichiometrically equivalent ratio. From this work, the effect of curing agents of the DGEBF/amine systems oil the thermal and mechanical properties was significantly influenced by numbers of nitrogen atom of curing agents. The results showed that heat of reaction increased, and maximum exothermic temperature decreased with the decrease of numbers of nitrogen atom. In case of cured systems, density and maximum conversion(%) had no relation to numbers of nitrogen atom, but flexural modulus and tensile modulus increased with the decrease of numbers of nitrogen atom in main chain. Thermal stability, shrinkage(%), Tg, tensile and flexural strength showed irregular tendency having nothing to do with numbers of nitrogem atom at a sight. This findings imply that the differences in the maximum conversion(%) about the chain length of curing agents affect the thermal and mechanical properties.

• Corrosion Science and Technology
• /
• v.9 no.5
• /
• pp.201-208
• /
• 2010

Epoxy coatings cured by different amine based curing agents have been prepared. Atomic force microscopy (AFM) has been used to monitor the surface topology changes of epoxy coatings before and after hygrothermal cyclic test. The glass transition temperature ($T_g$) and coefficient of thermal expansion (CTE) of the epoxy coating were measured by Thermo-mechanical Analysis (TMA). The Electrochemical impedance spectroscopy (EIS) with hygrothermal cyclic test has been introduced to evaluate the corrosion protection of the epoxy coatings. In conclusion, thermal properties of epoxy coatings were in good agreement with the results of corrosion protection of epoxy coated carbon steel obtained result by EIS with hygrothermal cyclic test. The relationship between thermal properties, surface roughness changes and corrosion protection of epoxy coatings are discussed in this study.

• Textile Coloration and Finishing
• /
• v.11 no.6
• /
• pp.7-17
• /
• 1999

Aminophosphazene derivatives were prepared from hexachlorocyclotriphosphazene and used for the curing agents of epoxy resins. The effect of the curing agent on the dynamic viscoelastic properties, flame proofing, and heat resistance of the cured epoxy resins were investigated and compared with those for the epoxy resins cured with aliphatic and aromatic amines. The epoxy resin cured by 1,1-diamino-3,3,5,5-tetrachlorocyclotriphosphazene showed the highest storage modulus and glass transition temperature when cured at 19$0^{\circ}C$ for 6 hours. The epoxy resins cured with phosphazene derivatives showed superior flame proofing to those with aliphatic amine and aromatic amine. Particularly it is an effective curing agent for epoxy resins to enhance the storage modulus, flame proofing and resistance to heat.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.162-163
• /
• 2021

To prepare the waterborne silicone acrylic resin coatings, acrylic resin was prepared by a radical polymerization. Glass transition temperature(Tg) of the acrylic copolymer was fixed at 30℃ and the contents of tertiary amine monomer(DMAEMA), were varied to be 5, 10, 15 and 20 wt%, hydroxyl monomer, and carboxyl monomer were fixed 10 wt%, and 4 wt% respectively. γ-Glycidoxypropyltrimethoxysilane(GPTMS) containing epoxy group was used for curing agents. The eqivalent ratio of amine to epoxy was 1:1. The prepared coatings exhibited excellent adhesion to various substrates, and various physical properties of the coatings were satisfactory. The gloss retension and color difference were improved at low tertiary amine concentration. The coatings containing 10wt% tertiary amine concentration have especially good weather resistant properties.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.04a
• /
• pp.214-217
• /
• 2004

The cure kinetics of blends of epoxy(tetraglycidyl-4,4'-diaminodiphenylmethane ; TGDDM)/curing agent(diaminodiphenyl sulfone ; DDS) resin with amine terminated polyetherimide-CTBN-amine terminated polyetherimide triblock copolymer(ABA) were studied using differential scanning calorimetry under isothermal conditions to determine the reaction parameters such as activation energy and reaction constants. By increasing the amount of ABA in the blends, the final cure conversion was decreased. Lower values of the final cure conversions in the epoxy/ABA blends indicated that ABA hinders the cure reaction between the epoxy and curing agents. 1be value of the reaction order, m, for the initial autocatlytic reaction was not affected by blending ABA with epoxy resin, and the value was approximately 1.0. The value of n for the nth order component in the autocatalytic analysis was increased by increasing the amount of ABA in the blends, and the value increased from 2.0-3.4. A diffusion controlled reaction was observed as the cure conversion increased and the rate equation was successfully analyzed by incorporating the diffusion control term for the epoxy/DDS/ABA blends.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.8
• /
• pp.2272-2278
• /
• 2010

A new hybrid thermosetting maleimido epoxy compound 4-(N-maleimidophenyl) glycidylether (N-MPGE) is prepared by reacting N-(4-hydroxyphenyl) maleimide (HPM) with Epichlorohydrin by using benzyltrimethylammonium chloride as a catalyst. The resulting compound possesses both the oxirane ring and maleimide group. The curing reaction of these maleimidophenyl glycidylether epoxy compound (N-MPGE) with amines as curing agents such as ethylendiamine (EDA), diethylentriamine (DETA) and triethylenetetramine (TETA), aminoethylpiperazine (AEP) and isophoronediamine, IPDA), are studied. Incorporation of maleimide groups in the epichlorohydrin provides cyclic imide structure and high cross-linking density to the cured resins. The cured samples exhibited good thermal stability, excellent chemical (acid/alkali/solvent) and water absorption resistance. Morphological studies by the SEM technique further confirmed the phase homogeneity net work of the cured systems.

• Composites Research
• /
• v.17 no.6
• /
• pp.37-43
• /
• 2004

To determine the effect of chain length and chemical structure of linear amine curing agents on thermal and mechanical properties, a standard bifunctional linear DGEBF epoxy resin was cured with EDA and HMDA having amine group at the both ends of main chain in a stoichiometrically equivalent ratio in condition of preliminary and post cure. From this work, the effect of linear amine curing agents on the thermal and mechanical properties is significantly influenced by numbers of carbon atoms of main chain. In contrast, the results show that the DCEBF/EDA system having two carbons had higher values in the thermal stability, density, shrinkage (%), grass transition temperature, tensile modulus and strength, flexural modulus and strength than the DGEBF/HMDA system having six carbons, whereas the DGEBF/EDA cure system had relatively low values in maximum ekothermic temperature, maximum conversion of epoxide, thermal expansion coefficient than the DGEBF/HDMA cure system. These findings indicate that the packing capability (rigid property) in the EDA structure affects the thermal and mechanical properties predominantly. It shows that flexural fracture properties have a close relation to flexural modulus and strength.

• Applied Chemistry for Engineering
• /
• v.10 no.7
• /
• pp.990-995
• /
• 1999

To determine the effect of chemical structure of linear amine curing agents on thermal and mechanical properties, standard epoxy resin DGEBA was cured with ethylene diamine(EDA) and hexamethylene diamine(HMDA) in a stoichiometrically equivalent ratio. From this work, the effect of linear amine curing agents on the thermal and mechanical properties is significantly influenced by the chemical structure or chain length of curing agents. In contrast, the results show that the DGEBA/EDA system having the two carbons had higher values in the thermal stability, maximum conversion of epoxide, density, glass transition temperature, tensile modulus, flexural strength, and flexural modulus than the DGEBA/HMDA system having the six carbons, whereas the DGEBA/EDA cure system had relatively low values in the shrinkage(%), thermal expansion coefficient, tensile strength, and had similar values in the maximum exothermic temperature, and conversion of epoxide compared to the DGEBA/HMDA cure system. This findings indicate that packing ability in the HMDA structure affects the thermal and mechanical properties.