The acid catalytic reactions of toluene with n-propylalcohol were investigated and the adsorption experiments of dialkylbenzene isomers were carried out at 100$^{\circ}C$ over modified HZSM-5 zeolites. ZSM-5 zeolite was synthesized by the hydrothermal reaction using 4-propylammonium ion, sodium aluminate and colloidal silica etc., and several zeolite catalysts, including H-, K-, Sr-, P-Mg-HZSM-5, H-Y and H-mordenite, were prepared by conventional methods. The main reaction products of toluene with n-propylalcohol over HZSM-5 catalyst include not only xylenes, propyltoluenes, but also ethyltoluenes and high para-selectivity among dialkylbenzene isomers was observed on P-Mg-HZSM-5 zeolite. The diffusion coefficients of various p-dialkylbenzenes are nearly the same, about 1 ${times}$ 10$^{-10}$ cm$^2$/sec and that of m-xylene was about one tenth of o-xylene. These reaction and adsorption characteristics were interpreted in the light of the shape-selectivity related to related to the zeolite pore structure and the zeolitic acidity.

• Journal of the Korean Ceramic Society
• /
• v.47 no.5
• /
• pp.461-466
• /
• 2010

In this study, $Al_2O_3/TaAlO_4/SiO_2$ (A/TAlO/S) structures with tantalum aluminate charge trap layer were fabricated for Nand flash memory device. We evaluated the memory window and retention characteristic as the thickness of the tunnel oxide was varied among 3 nm, 4 nm, and 5 nm. All tunnel oxide thicknesses were measured by ellipsometer and TEM (Transmission Electron Microscope). The A/TAlO/S multi-layer film consisted of 5 nm tunnel oxide showed the best result of memory window of 1.57 V and retention characteristics. After annealing the 5 nm tunnel oxide A/TAlO/S multi-layer film at $900^{\circ}C$. The memory window decreased to 1.32 V. Moreover, the TEM images confirmed that the thickness of multi-layer structure decreased 14.3% after annealing and the program conditions of A/TAlO/S multi-layer film decreased from 13 V to 11 V for 100 ms. Retention properties of both as-deposited and annealed films stably maintained until to $10^4$ cycles.

• Journal of the Korean Ceramic Society
• /
• v.51 no.6
• /
• pp.618-622
• /
• 2014

Oxide phosphorescent phosphor has an wide application in ceramic art and decoration due to its chemical and mechanical properties. Here, phosphorescent properties of strontium aluminate phosphor ($SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$) emitting yellowish-green light was investigated with thermal treatment at $1250^{\circ}C$ under air and reducing atmosphere. The characterizations of thermally treated samples were analyzed using X-ray fluorescence (XRF), X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), fluorescence spectrometer. $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ still showed a good phosphorescent properties after annealing process in reducing atmosphere, while phosphorescence of $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ annealed in air seriously degraded, due to oxidation of $Eu^{2+}$ to $Eu^{3+}$ ions. It was also observed that $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ annealed in reducing atmosphere emitted yellowish-green light during 3 h after being exposed to sunlight.

• Journal of Powder Materials
• /
• v.19 no.1
• /
• pp.25-31
• /
• 2012

In this study, a high energy ball milling process was employed in order to improve the densification of direct nitrided AlN powder. The densification behavior and the sintered microstructure of the milled AlN powder were investigated. Mixture of AlN powder doped with 5 wt.% $Y_2O_3$ as a sintering additive was pulverized and dispersed up to 50 min in a bead mill with very small $ZrO_2$ beads. Ultrafine AlN powder with a particle size of 600 nm and a specific surface area of 9.54 $m^2/g$ was prepared after milling for 50 min. The milled powders were pressureless-sintered at $1700^{\circ}C-1800^{\circ}C$ for 4 h under $N_2$ atmosphere. This powder showed excellent sinterability leading to full densification after sintering at $1700^{\circ}C$ for 4 h. However, the sintered microstructure revealed that the fraction of yitttium aluminate increased with milling time and sintering temperature and the newly-secondary phase of ZrN was observed due to the reaction of AlN with the $ZrO_2$ impurity.

• Resources Recycling
• /
• v.3 no.3
• /
• pp.27-31
• /
• 1994

We tested the limestone sludge produced in Pohang Iron & Steel Co., Ltd. as a filler powder for the effective use of portland cement. Hydration process was investigated by measuring the hydration rate, the amounts of non-evaporable water and compressive strength of cement-limestone sludge paste prepared by mixing limes-tone sludge with cement. The results obtained in this study can be summarized as follows: 1. There is no significant difference between the cases of adding up to 10% limestone sludge and those of unmixed cement system. However the reaction rate increases in the 5% limestone sludge system(due to the effects of fine). 2. The compressive strength increases proportionally with increasing the measured amount of non-evaporable water, Adding 5% limestone sludge also increases the strength a little higher, and the compressive strength and calcium silicate hydrates. In the case of the mixed limestone sludge, $2\theta$=$11.7^{\circ}$ peak appears in the samples of 28 days hydration. This peak indicted the presence of calcium carboaluminate hydrate. Although limestone sludge is generally regarded as a inert materials, some kinds of cement can produce a calcium carboaluminate by reacting with aluminate in cement pastes.

• Korean Journal of Materials Research
• /
• v.17 no.10
• /
• pp.560-566
• /
• 2007

AlN plates were fabricated by hot pressing at $1700-1900^{\circ}C$ using yttria and alumina (3 and $10\;{\mu}m$ particle size) powders as additives and characterized: density, thermal conductivity, transverse rupture strength, and grain size measurement by SEM and EDS. Density values of $3.31-3.34\;g/cm^3$ are largely attributed to hot pressing of powder mixtures in carbon mold under $N_2$ atmosphere which caused effective degree of oxygen removal from yttrium-aluminate phase expected to form at $1100^{\circ}C$. The grain size of hot pressed AlN was almost homogeneous, with size approximately from 3.2 to $4.0\;{\mu}m$ after hot pressing. $Al_2O_3$ powder of $3\;{\mu}m$ particle size resulted in better transverse rupture strength and finer grain size compared to $10\;{\mu}m$ $Al_2O_3$ powder. The thermal conductivity of AlN ranged between $83-92.7\;W/m{\cdot}K$ and decreased with $Al_2O_3$ addition. Fine grain size is preferred for better mechanical properties and thermal conductivity.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.41 no.4
• /
• pp.341-345
• /
• 2021

Known to improve resistance to chloride ingress, blast furnace slag is a widely used supplementary cementitious material. However, a detailed characterization of cements blended with slag exposed to seawater remains unavailable. This study employs thermodynamic modeling as a toolkit for assessing the long-term phase evolution of slag cement in seawater. The modeling result shows that slag incorporation leads to the formation of phases that are less prone to structural alteration in seawater. Formation of more ettringite is expected to induce expansion in both plain and blended cements, while brucite is unstable in the blended systems. Despite this, the porosity is expected to increase in the blended cements, and aluminate hydrates with a higher chloride binding capacity are more abundant in the blended cements. The results suggest that the use of slag in concrete improves the durability performance of concrete in marine environments.

• Resources Recycling
• /
• v.28 no.2
• /
• pp.54-61
• /
• 2019

In order to recover pure alumina from black dross, leaching of mechanically activated black dross with NaOH solution resulted in an aluminate solution containing a small amount of Si(IV). Selective adsorption of Si(IV) onto hydrotalcite was investigated from 5 M NaOH solution where the concentration of Al(III) and Si(IV) was 13000 and 150 mg/L, respectively. Only Si(IV) was selectively loaded onto hydrotalcite, while Al(III) remained in the solution. Effect of the calcination treatment of hydrotalcite and concentration of calcined hydrotalcite and NaOH on the loading of Si(IV) was investigated. Although the loading percentage of Si(IV) was low from 5 M NaOH solution, most of the Si(IV) was removed by adjusting the concentration of NaOH by 48 times dilution with water when the concentration of calcined hydrotalcite was higher than 4.5 g/L. The loading of Si(IV) onto calcined hydrotalcite followed Freundlich adsorption isotherm.

• Resources Recycling
• /
• v.28 no.4
• /
• pp.23-29
• /
• 2019

In order to recover pure alumina from balck dross, precipiatation experiments were done to the NaOH leaching solution of mechanically activated black dross. In this work, hydrogen peroxide was added to the synthic solution as a precipitating agent. Among some variables, the concentration of $H_2O_2$ and the volume ratio of $H_2O_2$ to solution showed a remarkable effect on the precipitation of aluminum hydroxide. At the optimum conditions, most of the aluminate was precipitated. Calcination of the aluminum hydroxide at $1200^{\circ}C$ led to the formation of ${\theta}$ and ${\alpha}$-alumina. The charactistics of the synthesized activated alumina was measured by XRD and EDS. The average particles size of the alumina was $3.73{\mu}m$.

• The Korean Journal of Nuclear Medicine
• /
• v.38 no.5
• /
• pp.338-343
• /
• 2004

Purpose: The purpose of this study was to develop a small animal PET using dual layer phoswich detector to minimize parallax error that degrades spatial resolution at the outer part of field-of-view (FOV). Materials and Methods: A simulation tool GATE (Geant4 Application for Tomographic Emission) was used to derive optimal parameters of small PET, and PET was developed employing the parameters. Lutetium Oxyorthosilicate (LSO) and Lutetium-Yttrium Aluminate-Perovskite(LuYAP) was used to construct dual layer phoswitch crystal. $8{\times}8$ arrays of LSO and LuYAP pixels, $2mm{\times}2mm{\times}8mm$ in size, were coupled to a 64-channel position sensitive photomultiplier tube. The system consisted of 16 detector modules arranged to one ring configuration (ring inner diameter 10 cm, FOV of 8 cm). The data from phoswich detector modules were fed into an ADC board in the data acquisition and preprocessing PC via sockets, decoder block, FPGA board, and bus board. These were linked to the master PC that stored the events data on hard disk. Results: In a preliminary test of the system, reconstructed images were obtained by using a pair of detectors and sensitivity and spatial resolution were measured. Spatial resolution was 2.3 mm FWHM and sensitivity was 10.9 $cps/{\mu}Ci$ at the center of FOV. Conclusion: The radioactivity distribution patterns were accurately represented in sinograms and images obtained by PET with a pair of detectors. These preliminary results indicate that it is promising to develop a high performance small animal PET.