• Tribology and Lubricants
• /
• v.11 no.5
• /
• pp.26-30
• /
• 1995

Sliding experiments have been conducted on alumina and silicon carbide ceramics. Wear and friction data of both materials indicate that wear proceeds in two distinct stages. The wear occurs by a relatively mild plastic-grooving process in the initial stage, but eventually gives way to a severe grain pull-out process after a defined period of sliding test. The datails of the transition mechanism are presented. The effects of grain size and second phase particle on the wear transition are also presented.

• Journal of the Korean Ceramic Society
• /
• v.25 no.2
• /
• pp.89-94
• /
• 1988

Alumina gel was prepared by the hydrolysis of aluminum isopropoxide Al(OC3H7i)3 at low temperature. Sample were calcined at the various temperatures for 10 houres in the electric furnace, respectively. In order to investigate the various propertis-thermal properties, pore size and distribution, and the transition of crystals, infrared spectroscopy, thermal analysis, particle size analysis, scanning electron microscopy, and porosimetry were employed. Transparent alumina gel was opalized at 1200$^{\circ}C$. Porosity was about 87% with pores below 0.7$\mu\textrm{m}$ and 55% at 1200$^{\circ}C$. The gel was transformed along the rising of temperature as follows; Boehmite\longrightarrow$\delta$-Al2O3\longrightarrow$\theta$\longrightarrowAl2O3\longrightarrow${\alpha}$-Al2O3.

• Bulletin of the Korean Chemical Society
• /
• v.25 no.6
• /
• pp.843-846
• /
• 2004

Pt nanoparticles loaded on alumina through an impregnation at room temperature was prepared using $K_2PtCl_4$ and acrylic acid as capping material. Transmission electron microscopy showed that the deposited Pt particles indicate ca. 80% cubic shapes with a narrow distribution of 8-10 nm in size. Propylene hydrogenation over the catalyst has been carried out to evaluate their catalytic performance by the values of activation energy. It is determined from the initial rate, reaction order, and rate constant and is found to be $9.7{\pm}0.5$ kcal/mol. This value has been discussed by comparing to those of encapsulated- and truncated octahedral Pt nanoparticles deposited on alumina, respectively, to study influence of the particle size and shape, and capping material used on the activation energy.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.875-876
• /
• 2006

For dry machining of mineral materials the Institute of Materials Engineering pursues a novel thermal protection shield concept for diamond tools, in which thermal insulating materials in diamond composite structures act as heat shield, which protects diamonds in deeper layers against high temperature and graphitisation. Before the effectiveness of this concept could be investigated suitable composites have to be manufactured. In this paper the powder metallurgical production processes of diamond-alumina-cobalt-composites with varying alumina and cobalt particle sizes, their microstructures and porosities are described. It could be observed that the distribution of small-sized alumina particles ($<70{\mu}m$) in the cobalt matrix is uniform and the porosity of the composite decrease.

• Korean Journal of Materials Research
• /
• v.2 no.1
• /
• pp.3-11
• /
• 1992

Aluminum sulfate hydrate was prepared using sulfuric acid from Ha-dong kaolin. The effects of calcination-temperature and calcination-time of kaolin, reaction-temperature and reaction-time, and sulfuric acid concentration on the formation of aluminum sulfate hydrate were investigated. The precipitation condition of aluminum sulfate hydrate from sulfuric acid solution was determined. Also, the products heat-treated at different temperatures have been investigated by X-ray diffraction, thermogravimetry, differential thermal analysis, Fourier transform infrared spectrophotometer, scanning electron microscopy, particle size distribution analysis and chemical analysis. In the optimum condition, the conversion of aluminum oxide in kaolin to aluminum sulfate hydrate was 60%. From the results of XRD, TG-DTA, and FT-IR, it is suggested that the aluminum sulfate hydrate is thermally decomposed as follows ; $Al_2(SO_4)_3{\cdot}18H_2O{\rightarrow}Al_2(SO_4)_3{\cdot}6H_2O{\rightarrow}Al_2(SO_4){\rightarrow}\;amorphous\;alumina{\rightarrow}{\gamma}-alumina{\rightarrow}{\delta}-alumina{\rightarrow}{\theta}-alumina{\rightarrow}{\alpha}-alumina$. The purity of alumina powder prepared by calcining aluminum sulfate hydrate at $1200^{\circ}C$ was 99.99 percent.

• Journal of Powder Materials
• /
• v.5 no.3
• /
• pp.199-209
• /
• 1998

A new low melting inorganic binder, monoclinic $HBO_2$, has been developed for Selective Laser Sintering (SLS) of alumina powder by dehydration process of boron oxide powder in a vacuum oven at $120^{\circ}C$. It led to better green SLS parts and higher bend strength far green and fired parts compared to other inorganic binders such as aluminum and ammmonium phosphate. This appeared to be due to its low viscosity and better wettability of the alumina particle surface. A low density single phase ceramic, aluminum borate ($Al_{18}B_4O_{33}$), and multiphase ceramic composites, $A_{12}O_3-A_{14}B_2O_9$, were successfully developed by laser processing of alumina-monoclinic $HBO_2$ powder blends followed by post-thermal processing; both $Al_{18}B_4O_{33}$ and $A_{14}B_2O_9$ have whisker-like grains. The physical and mechanical properties of these SLS-processed ceramic parts were correlated to the materials and processing parameters. Further densification of the $A_{12}O_3-A_{14}B_2O_9$ ceramic composites was carried out by infiltration of colloidal silica, and chromic acid into these porous SLS parts followed by heat-treatment at high temperature ($1600^{\circ}C$). The densities obtained after infiltration and subsequent firing were between 75 and 80% of the theoretical densities. The bend strengths are between 15 and 33 MPa.

• Membrane and Water Treatment
• /
• v.14 no.1
• /
• pp.11-18
• /
• 2023

This work addresses the development of microfiltration ceramic membrane from alumina using extrusion method. The membranes were sintered at different temperatures ranging between 1000 and 1300℃. The alumina was characterized with thermogravimetric analysis, particle size distribution, X-ray diffraction, Fourier transform infrared spectrometer and scanning electron microscope analysis. Subsequently, the effect of sintering temperature on the membrane properties such as porosity, flexural strength, and pure water permeability was investigated and optimized for the sintering temperature. It is observed that with increasing sintering temperature, the porosity of the membranes decreases and the flexural strength, and pure water permeability of the membranes increase. The uncoated and coated membranes were compared at constant flux mode of filtration. Under the turbidity solution recirculation alone at 100 NTU, trans-membrane pressure (TMP) of uncoated membrane remained constant when the filtration flux was below 121 Lm^-2 h ^-1 , while the coated membrane was 111 Lm_-2 h ^-1 . Although suction pressure increased more rapidly at higher turbidity, coated membrane filtration showed better removal efficiency of the turbidity.

• Korean Chemical Engineering Research
• /
• v.49 no.5
• /
• pp.664-668
• /
• 2011

Spherical alumina precursors represented by $AlO_xCl_y(OH)_z$, 30~200 nm in particle diameter, were prepared by partial hydrolysis of $AlCl_3$ vapor in a 500 ml reactor. Investigated on the particle morphology and size were the effects of the reaction time, the stirring speed and the reaction temperature. The particle morphology and size was insensitive to the reaction time in the range 20 to 300 s. The variation of the stirring speed from 0 to 300 and 800 rpm showed that the particle size was the largest at 0 rpm. As the temperature was varied from 180 to 190, 200, $140^{\circ}C$, the particle size showed a maximum at $190^{\circ}C$. By calcination of the as-produced particles at $1,200^{\circ}C$ for 6h with a heating rate of $10^{\circ}C$/min, ${\alpha}$-alumina particles 45 nm in surface area equivalent diameter were obtained. The particle shape after calcination turned wormlike due to sintering between neighboring particles. A rapid calcination at $1400^{\circ}C$ for 0.5 h with a higher heating rate of $50^{\circ}C$/min reduced the sintering considerably. An addition of $SiCl_4$ or TMCTS(2,4,6,8-tetramethylcyclosiloxane) to the $AlCl_3$ reduced the sintering effectively in the calcination step; however, peaks of ${\gamma}$ or mullite phase appeared. An addition of $AlF_3$ to the particles obtained from the hydrolysis resulted in a hexagonal disc shaped alumina particles.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.3
• /
• pp.157-161
• /
• 2000

In order to investigate the substrate effect on the electrochemical properties of thin-film electrode, $LiCoO_2$ was deposited onto the alumina, chemically etched-Si and flat-Si substrates. After annealing at $800^{\circ}C$ in $O_2$ for 30min, the film deposited on the alumina consisted of large particles with several cracks, whereas the film deposited on the flat-Si substrate was composed of very small and uniform particles. The films deposited on the flat-Si showed improved electrochemical properties such as peak potential divergence and rate-capability, over those deposited on the alumina and chemically etched-Si substrate, which can be attributed to the differences of the particle size surface morphology, and the electrical resistance of the current collector.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.1288-1291
• /
• 2004

In this study, physical characteristics of alumina slurry on variation of pH value and the effect of non-ionic surfactants on alumina slurry for copper chemical mechanical planarization (CMP) slurry have been investigated. After pH value of the slurry with alumina abrasive was changed by adding various amount of $HNO^3$ or KOH, the differences of settling rate, particle size, and zeta-potential were estimated. Better settling rates were shown in slurries with alumina abrasive at near pH 1. Higher zeta-potential was shown at around pH 2 in alumina slurry and the point of zero charge (PZC) was measured at about pH $9\sim10$. Non-ionic surfactant was added in the slurry with 5wt% alumina abrasive to get its effect on slurry practically. Abrasive size was smaller increased when amount of surfactant increased in slurry with P-4 as abrasive; on the other side, it was smaller when amount of surfactant decreased with AES-12. Variation of zeta-potential has no tendency with adding surfactant; however, values of zeta-potential were between $35\sim50mV$. The proper amount of surfactant was $0.1\sim1.0wt%$ in slurry with P-4 and $0.5\sim1.0wt%$ in slurry with AES-12 respectively. Excellent dispersion stabilization was obtained by addition of non-ionic surfactant