Flexural Modulus of Larch Boards Laminated by Adhesives with Reinforcing Material

  • Injeong LEE;Weontae OH
    • Journal of the Korean Wood Science and Technology
    • /
    • 제51권1호
    • /
    • pp.14-22
    • /
    • 2023
  • Economical use of larix (larch) boards (grade 3) in industries is lower than that of imported hardwood; thus, studies have been conducted toward performance improvement of larix boards. Herein, flexural modulus of larix board samples laminated with wood adhesives polyurethane resins, poly (vinyl acetate) resins, phenol-resorcinol-formaldehyde resins, melamine-formaldehyde resins, and urea-formaldehyde resins was compared with that of the samples bonded with adhesives reinforced with mesh-type basalt fibers. Moreover, the flexural moduli of the laminated samples bonded by mesh-type basalt fibers were compared with those of reinforced samples. The results showed that boards laminated with polyurethane and urea-formaldehyde resin adhesives had higher flexural modulus than those without the lamination. In particular, the increase in the flexural modulus was relatively significant for the 2- and 3-ply board structures laminated with polyurethane adhesives compared to those with reinforcement. The 3-ply board structure without reinforcement had the highest flexural modulus when the urea-formaldehyde resin adhesive was used.

수계형 아크릴 점착제의 합성 및 점착 특성 (Synthesis and Adhesion Characteristics of Water-Borne Acrylic Pressure Sensitive Adhesives(PSAs))

  • 함현식;곽윤철;황재영;안성환;김명수;박홍수
    • 한국응용과학기술학회지
    • /
    • 제22권2호
    • /
    • pp.191-199
    • /
    • 2005
  • Removable protective adhesives for automobiles were synthesized by an emulsion polymerization of monomers such as n-butyl acrylate (BA), n-butyl methacrylate (BMA), acrylonitrile (AN), acrylic acid (AA) and 2-hydroxyethyl methacrylate (2-HEMA), in which AA and 2-HEMA were functional monomers. Potassium persulfate (KPS) was used as an initiator and sodium lauryl sulfate (SLS) was used as an emulsifier, and polyvinyl alcohol (PVA) was used as a stabilizer. Emulsion polymerization was carried out in a semi-batch type reactor. Tensile strength, extension, peel strength, viscosity and solid content of the synthesized adhesives were tested. The optimum physical properties of the removable protective adhesives for automobiles were obtained with the composition of 0.43 mole BA, 0.57 mole AN, 0.21 mole BMA, 0.03 mole AA, and 0.03 mole 2-HEMA.

세라믹 브라켓과 교정용 접착제에 따른 전단 결합 강도의 비교 연구 (A COMPARATIVE STUDY OF THE SHEAR BOND STRENGTH OF DIFERENT CERAMIC BRACKETS AND ADHESIVES)

  • 이주원;유동환;김상철
    • 대한치과교정학회지
    • /
    • 제27권2호
    • /
    • pp.315-326
    • /
    • 1997
  • 여러 세라믹 브라켓과 접착제에 따른 전단 결합 강도를 비교하기 위하여, 영구 소구치 48개를 대상으로 베이스의 유지 형태가 다른 3종의 세라믹 브라켓을 광중합과 화학 중합을 포함한 3종의 교정용 접착제를 사용하여 접착하고 전단 결합 강도와 파절 양상을 관찰한 결과, 화학 중합형 레진으로 접착한 경우 광중합형으로 접착한 경우보다 결합강도가 높았으며, 화학적 결합을 하는 Starfire 브라켓이, 기계적 결합을 하는 Transcend나, 복합형 결합인 Fascination 보다 전단 결합 강도가 낮았다. Trascend는 주로 법랑질과 레진(E/R)에서, Fascination은 법랑질, 레진, 브라켓 베이스에 혼합(COMB)되어 파절되며, Starfire는 레진과 브라켓 베이스(R/B)에서 파절이 나타났다.

  • PDF

목공예품 보존용 송진 기반 에폭시 접착제 및 메움제의 제조와 적용성에 관한 연구 (A Study on the Manufacturing and Applicability of Rosin-based Epoxy Adhesives and Filling Material for Conservation of Wood Crafts)

  • 위광철;한원식;오승준
    • 보존과학회지
    • /
    • 제36권6호
    • /
    • pp.475-482
    • /
    • 2020
  • 송진을 기반으로한 2액형의 주제를 합성하고 이를 이용하여 접착제와 메움제를 제조하였다. 접착제 주제는 Maleic anhydride modified rosin에 epichlorohydrin을 반응시켜 epoxide group 이 형성되도록 제조하고 경화제는 상온 경화형 triethylenetetramine을 사용하였다. 제조된 접착제는 주제와 경화제의 비는 100 : 20이었으며, 메움제는 Filler를 혼합하여 주제와 경화제 모두를 점토형으로 제조하였다. 제조된 원액 접착제와 메움제는 우수한 접착 강도(3.06 MPa)와 자외선 조사에서 매우 안정한 결과(△E* ab 3.55, △b* 3.17)를 나타내어 기존 시판 복원용 접착제들에 비하여 우수한 결과를 나타내었다. 또 경화 완료 후에 acetone과 toluene 등의 유기 용매에 용해되어 가역성을 갖는 재료로 볼 수 있어 복원으로 인하여 발생될 수 있는 문제점의 일부를 해결한 결과를 나타내었다. 제조된 접착제 및 메움제를 이용해 실제 목공예품에 적용하여 작업성, 안정성, 제거성 등에서 우수한 결과를 나타내었으며 이를 이용할 경우 다양한 분야의 적용 가능성을 확인할 수 있었다.

인산염 종류에 따른 산화마그네슘 경화체의 강도 특성 (Strength properties of magnesium oxide matrix according to type of phosphate)

  • 임정준;편수정;김대연;이상수
    • 한국건축시공학회:학술대회논문집
    • /
    • 한국건축시공학회 2018년도 추계 학술논문 발표대회
    • /
    • pp.79-80
    • /
    • 2018
  • Recently, the interest in remodeling of new and old buildings is increasing worldwide. As a result, the frequency of use of architectural adhesives has increased. Currently, adhesives used in buildings are made of organic materials in most cases, and epoxy resin adhesives are most widely used. However, epoxy resin adhesives contain formaldehyde and VOCs in the room during construction, which can cause sick house syndrome. In case of building fire, it may cause damage due to carbon monoxide generated from organic materials. It is urgent to study the problem of epoxy fill adhesive made of such organic materials. Therefore, the purpose of this study is to investigate the effect of the adhesion of epoxy resin adhesive, which is a problem of epoxy resin adhesive, which is an existing organic adhesive by using inorganic materials such as magnesia and phosphate, And the inorganic adhesive which does not emit the release amount as an inorganic material.

  • PDF

목공예용 천연 및 합성 접착제의 특성 연구 (Study on the Physical Properties and Characteristics of Adhesives for Woodcraft)

  • 김성은;이진경;이채훈;정용재
    • 보존과학회지
    • /
    • 제35권6호
    • /
    • pp.681-688
    • /
    • 2019
  • 본 연구에서는 목공예품에 사용되는 천연 및 합성 접착제의 특성을 평가하고, 온습도 변화에 따른 접착제와 목재의 열화 양상을 비교하였다. 아교 1종, 폴리초산비닐계 접착제 3종, 에폭시계 접착제 1종와 느티나무 목재를 선정하여 물리적, 화학적 특성평가와 내후성, 건조속도 평가를 진행하였다. 접착제 특성평가를 통해 아교와 폴리초산비닐계 1종의 접착강도가 각각 6.54 N/㎟과 7.01 N/㎟으로 나타났으며, 아교는 pH 7.03, 폴리초산비닐계 접착제는 pH 3.32~3.59으로 접착제로써 사용가능한 범위인 것으로 확인되었다. 내후성 실험결과 에폭시계 접착제는 열화 후 접착강도 감소폭이 가장 높았다. 접착제에 대한 가역성 실험을 통해 에폭시를 제외하고 수용성용매인 NaOH에서 가역성이 높은 것으로 나왔으나 처리 시 목재에 변색이 나타날 수 있으므로 사용 시 주의가 필요하다.

관능성 단량체 종류에 따른 4원 용액형 아크릴계 점착제의 합성과 물성에 관한 연구 (The Effects of Functional Monomers on the Synthesis andPhysical Properties of Solution Type Quaternary Polymer Acrylic Pressure-Sensitive Adhesives)

  • 김남석;김성훈
    • 한국응용과학기술학회지
    • /
    • 제25권4호
    • /
    • pp.525-532
    • /
    • 2008
  • To prepare a solution type acrylic pressure-sensitive adhesive, quarter polymers were synthesized from butyl acrylate(BA), 2-ethylhexylacrylate(2-EHA) as a base monomer, methyl methacrylate(MMA) as a comonomer, each of methacrylic acid(MAA), acrylic acid(AA) as a functional monomer. Acrylic solution type pressure-sensitive adhesives(PSA's) of isocyanate derivative crosslinking PSA's were prepared by crosslinking of BEMM, BEMA with toluene-2,4-diisocyanate. The structure of adhesive was identified by FT-IR. The viscosity was measured by using Brookfield DV-III and molecular weight was measured by using gel permeation chromatography. The physical properties of polyethylene film coated with BEMMT, BEMAT were measured as a function of the concentration. As the result, BEMMT(0.6, 0.8), BEMAT(0.6) showed peel adhesion of $160{\sim}180\;g_f$/25 mm width and shear adhesion of more than 24 hours, and tackiness of $4/32{\sim}6/32$ which was relevant to commercial usage.

An investigation into the effect of denture adhesives on incisal bite force of complete denture wearers using pressure transducers - a clinical study

  • Kalra, Pawan;Nadiger, Ramesh;Shah, Farhan Khalid
    • The Journal of Advanced Prosthodontics
    • /
    • 제4권2호
    • /
    • pp.97-102
    • /
    • 2012
  • Study was conducted to determine and assess the effect of different type of denture adhesives on the incisal bite force of complete denture wearers until the dislodgement of upper denture, using pressure transducer. MATERIALS AND METHODS. 30 patients out of 100 were included in the study. Based on the Kapur's method of scoring denture retention and stability, these patients were divided into 3 groups-Group A - Clinically good dentures; Group B - Clinically fair dentures; and Group C - Clinically poor dentures. A custom made occlusal force meter was constructed based on the load cell type of pressure transducers. Different adhesives (powder, paste and adhesive strips) were used in the study. Complete denture wearers were asked to bite on the load cell and the readings of incisal bite force were recorded. The readings of incisal bite force were subjected to statistical analysis using Repeated measures ANOVA followed by post-hoc bonferroni test. RESULTS. The result suggests that denture adhesives improved the incisal bite force of complete denture wearers significantly The incisal bite force (in kg) in Group A without using adhesives, with powder adhesive, with paste adhesive and with adhesive strips was found to be 2.48 (${\pm}0.16$), 3.43 (${\pm}0.11$), 6.01 (${\pm}0.11$), 3.22 (${\pm}0.09$) respectively. The incisal bite force (in kg) in Group B without using adhesives, with powder adhesive, with paste adhesive and with adhesive strips was found to be 1.87 (${\pm}0.18$), 3.35 (${\pm}0.14$), 5.34 (${\pm}0.18$), 3.21 (${\pm}0.12$) respectively. The incisal bite force (in kg) in Group C without using adhesives, with powder adhesive, with paste adhesive and with adhesive strips was found to be 1.00 (${\pm}0.17$), 3.07 (${\pm}0.14$), 4.37 (${\pm}0.26$), 2.99 (${\pm}0.14$) respectively. CONCLUSION. Within the limitations of the study, it was concluded that the use of denture adhesive was found to be significantly effective in improving the incisal bite force of complete dentures until the dislodgement of upper denture. Fittydent paste adhesive was found to be more effective than the powder and strips adhesives. The improvement in incisal bite force was found to be higher in Group C in comparison to that of Group A and Group B.

옻과 아교를 이용한 토기 복원용 천연접착제 제조 및 특성 분석 (A Study on Preparation and Characteristics of Natural Adhesives with Lacquer and Animal Glue for Ceramics Conservation)

  • 김은경;박대우;장성윤
    • 접착 및 계면
    • /
    • 제14권3호
    • /
    • pp.128-134
    • /
    • 2013
  • 본 연구에서는 합성수지 접착제를 대체하여 토기 유물에 활용할 수 있는 천연접착제를 개발하기 위해 옻과 아교를 배합하여 시료를 제조하였고 이에 대한 구조적 물리적 특성을 분석하였다. 구조분석 결과 옻에 배합하는 아교의 비율이 높아질수록 carbonyl (C=O), amine (N-H), aromatic (C=C) 결합이 증가하는 것을 확인하였다. 또한 제조한 천연접착제를 합성수지 접착제와 비교하였을 때 낮은 접착강도를 가진 Paraloid B-72부터 높은 접착강도의 Araldite rapid type에 상응하는 다양한 점도와 접착강도를 가지고 있음을 확인하였다. 이를 바탕으로 하여 향후 체계적이고 심화된 분석이 이루어 진다면 훼손된 토기 유물의 접착 및 복원을 위한 친환경 천연접착제의 실용화가 가능할 것으로 사료된다.

인산염 종류와 붕사 첨가율에 따른 무기접착재의 특성 (Properties of Inorganic Adhesives according to Phosphate Type and Borax Ratio)

  • 송하영;임정준;길배수;이상수
    • 한국건축시공학회지
    • /
    • 제19권4호
    • /
    • pp.289-297
    • /
    • 2019
  • 현재 건축물에 사용되는 접착제는 주로 유기질 재료인 에폭시 수지 접착제가 사용되고 있다. 유기질 재료인 에폭시 수지 접착제는 유기성 물질로 접착제 생산 시 유해물질이 발생하며, 시공 후에도 유해물질이 실내거주공간에서 높게 나타난다. 또한 건축물 화재 시 유기 재료에서 발생되는 다량의 일산화탄소가 인명피해로 이어진다. 본 연구는 순수무기계 재료인 산화마그네시아, 인산염, 붕사를 사용한 무기 접착재에 대해 기존 유기 접착제를 대체 할 무기 접착재로의 활용가능성을 평가한 연구이다. 적정 인산염 선정에 관한 실험과 지연제로서 활용한 붕사의 첨가율에 대한 특성을 실험한 결과 적정 인산염으로 제1인산칼륨이 도출되었으며, 붕사 첨가율에 따른 특성을 측정한 결과 KS F 4923의 품질기준과 비교하여 경화수축률과 가열변화율은 품질기준을 만족하였으며, 인장강도는 붕사 첨가율 4% 이상에서 만족하는 결과가 나왔지만 접착강도의 경우 품질 기준을 충족하지 못하였다. 향후 접착강도 증진을 위한 추가적인 연구가 필요할 것으로 판단된다.