• The korean journal of orthodontics
• /
• v.39 no.6
• /
• pp.393-401
• /
• 2009

Objective: The purpose of this study was to compare the shear bond strength (SBS) of brackets and microleakage of a tooth-adhesive-bracket complex bonded with a direct and an indirect bonding technique after thermocycling. Methods: Fifty non-carious human premolars were divided into two equal groups. In the direct bonding group a light-cured adhesive and a primer (Transbond XT) was used. In the indirect-bonding group, a light-cured adhesive (Transbond XT) and chemical-cured primer (Sondhi Rapid Set) were used. After polymerization, the teeth were kept in distilled water for 24 hours and thereafter subjected to thermal cycling (500 cycles). For the microleakage evaluation, 10 teeth from each group were further sealed with nail varnish, stained with 0.5% basic fuchsin for 24 hours, and examined under a stereomicroscope. Fifteen teeth from each group were used for SBS testing with the universal testing machine and adhesive remnant index (ARI) evaluation. Data were analyzed using the Mann-Whitney U test, Chi-square test, and Fisher's exact test. Results: There were no statistical differences on SBS and microleakage between the two bonding techniques. The indirect bonding group had a significantly lower ARI score. Bracket failures were obtained between enamel-resin interfaces. Conclusions: The type of bonding technique did not significantly affect the amount of microleakage and SBS.

• Journal of Korean Society of Forest Science
• /
• v.60 no.1
• /
• pp.51-57
• /
• 1983

Properties and glue shear strength of each water soluble rues-phenol copolymer adhesive and phenolic resin adhesive were examined as a high temperature curing binder through the manufacture of plywood made of Kapur veneer. The former has different molar ratio and the latter was made from different catalyst method. The results are summarized as follows: 1) Specific gravities of air dried plywood manufactured from each adhesive ranged from 0.67 to 0.82 and their moisture contents met the K.S. standard 2) In dry and wet shear strength, adhesives with 60 percent of non volatile content showed higher values than those with 50 percent except phenolic resin. Urea-phenol copolymer resin with 20 percent of phenol content exhibited the highest, and that with 70 percent the lowest. Filling effect of wood flour on the bonding strength is great in urea-phenol copolymer resin with more than 50 percent of phenol content, especially significant in 50 percent of non volatile content including alkali catalyst phenolic resin. Alkali and acid catalyst methods were the highest among the adhesive manufacture methods. In wet strength, urea resin belongs to the lowest group. 3) In glue shear strength after boiling and drying test, no method for manufacturing phenolic formaldehyde resin adhesive was stronger than alkali and acid catalyst methods. Phenolic resin made from alkali catalyst method needs a wood flour filler to improve the bonding quality. Urea-phenol copolymer resin with 10 percent of phenol content showed the reasonable water resistance.

• Restorative Dentistry and Endodontics
• /
• v.42 no.2
• /
• pp.125-133
• /
• 2017

Objectives: This study compared the effect of hexamethyldisiloxane (HMDSO) and ammonia ($NH_3$) plasmas on the bond strength of resin cement to fiber posts with conventional treatments. Materials and Methods: Sixty-five fiber posts were divided into 5 groups: Control (no surface treatment); $H_2O_2$ (24% hydrogen peroxide for 1 min); Blasting (blasting with aluminum oxide for 30 sec); $NH_3$ ($NH_3$ plasma treatment for 3 min); HMDSO (HMDSO plasma treatment for 15 min). After the treatments, the Ambar adhesive (FGM Dental Products) was applied to the post surface (n = 10). The fiber post was inserted into a silicon matrix that was filled with the conventional resin cement Allcem Core (FGM). Afterwards, the post/cement specimens were cut into discs and subjected to a push-out bond strength (POBS) test. Additionally, 3 posts in each group were evaluated using scanning electron microscopy. The POBS data were analyzed by one-way analysis of variance and the Tukey's honest significant difference post hoc test (${\alpha}=0.05$). Results: The Blasting and $NH_3$ groups showed the highest POBS values. The HMDSO group showed intermediate POBS values, whereas the Control and $H_2O_2$ groups showed the lowest POBS values. Conclusion: Blasting and $NH_3$ plasma treatments were associated with stronger bonding of the conventional resin cement Allcem to fiber posts, in a procedure in which the Ambar adhesive was used.

• Restorative Dentistry and Endodontics
• /
• v.32 no.4
• /
• pp.343-355
• /
• 2007

The objectives of this study was to evaluate the durability of 4 resin cements by means of microtensile bond strength test combined with thermocycling method and fractographic FE-SEM analysis. Experimental groups were prepared according to thermocycling (0, 1,000, 5,000) and the kind of resin cements, those were Variolink II, Multilink, Panavia F 2.0, Rely X Unicem. Flat dentin surfaces were created on mid-coronal dentin of extracted third molars. Then fresh dentin surface was grounded with 320-grit silicon carbide abrasive papers to create uniform smear layers. Indirect composite block (Tescera, Bisco Inc., Schaumburg, IL, USA) was fabricated ($12\;{\times}\;12\;{\times}\;6\;mm^3$). It's surface for bonding to tooth was grounded with silicon carbide abrasive papers from 180- to 600-grit serially, then sandblasted witk $20\;-\;50\;{\mu}m$ alumina oxide. According to each manufacturer's instruction, dentin surface was treated and indirect composite block was luted on it using each resin cement. For Rely X Unicem, dentin surface was not treated. The bonded tooth-resin block were stored in distilled water at $37^{\circ}C$ for 24 hours. After thermocycling, the bonded tooth-resin block was sectioned occluso-gingivally to 1.0 mm thick serial slabs using all Isomet slow-speed saw (Isomet, Buehler Ltd, Lake Bluff, IL, USA). These sectioned slabs were further sectioned to $1.0\;{\times}\;1.0\;mm^2$ composite-dentin beams. The specimens were tested with universal testing machine (EZ-Test, Shimadzu, Japan) at a crosshead speed of 1.0 mm/min with maximum load of 500 N. The data was analyzed using one-way ANOVA and Duncan's multiple comparison test at $p\;{\leq}\;0.05$ level. Within the limited results, we conclude as follows; 1. The bond strength of Variolink II was evaluated the highest among experimental groups and was significantly decreased after 1,000 thermocycling (p < 0.05). 2. The bond strength of Multilink was more affected by thermocycling than the other experimental groups and significantly decreased after 1,000 thermocycling (p < 0.05). 3. Panavia F 2.0 and Rely X Unicem showed the gradually decreased tendency of microtensile bond strength according to thermocycling but there was no significant difference (p > 0.05). 4. Adhesive based-resin cements showed lower bond strength with or without thermocycling than composite based-resin cements. 5. Variolink II & Multilink showed high bond strength and mixed failure, which was occurred with a thin layer of luting resin cement before thermocycling and gradually increased adhesive failure along the dentin surface after thermocycling. The bonding performance of resin cement can be affected by application procedure and chemical composition. Composite based-resin cement showed higher bond strength and durability than adhesive based-resin cement.

• Restorative Dentistry and Endodontics
• /
• v.35 no.2
• /
• pp.106-115
• /
• 2010

The purpose of this study was to evaluate the microtensile bond strength (${\mu}TBS$), failure modes and bonding interfaces of self-etching and three self-adhesive resin cements to dentin and indirect composite resin. Cylindrical composite blocks (Tescera, Bisco Inc.) were luted with resin cements (PA: Panavia F 2.0, Kuraray Medical Inc., RE: RelyX Unicem Clicker, 3M ESPE., MA: Maxem, Kerr Co., BI: BisCem, Bisco Inc.) on the prepared occlusal dentin surfaces of 20 extracted molars. After storage in distilled water for 24 h, $1.0\;mm\;{\times}\;1.0\;mm$ composite-dentin beams were prepared. ${\mu}TBS$ was tested at a cross-head speed of 0.5 mm/min. Data were analyzed with one-way ANOVA and Tukey's HSD test. Dentin sides of all fractured specimens and interfaces of resin cements-dentin or resin cements-composite were examined at FESEM (Field Emission-Scanning Electron Microscope). In conclusion, PA and RE showed higher bond strength and closer adaptation than MA and BI when indirect composite blocks were luted to dentin using a self-etching and three self-adhesive resin cements.

• Composites Research
• /
• v.24 no.6
• /
• pp.56-63
• /
• 2011

The objective of this study is to investigate appropriate bonding methods of solar cells in order to apply solar cells, which have been receiving particular attention as a renewable energy due to fossil energy depletion and environment issues, to composite structures. Back-contact solar cells with approximately 24.2% energy conversion efficiency were used in this study. Since silicon-based solar cells are mechanically fragile, the secondary-bonding methods using adhesive were examined in this study. The experiment was conducted with three kinds of bonding materials such as EVA film, Resin film and elastic adhesive. The performance of solar cells for three types of adhesives under mechanical loading on test specimens is conducted. In addition, the measuring equipment was designed to evaluate the performance of the solar cells under mechanical loading in real time and the fracture characteristics depending on bonding materials were evaluated. The reason decreasing solar cells efficiency were analyzed and considered by Fractography. The results show that the solar cell performance is largely affected by bonding techniques. Moreover, the bonding method using elastic adhesive shows best solar cell efficiency.

• Restorative Dentistry and Endodontics
• /
• v.33 no.6
• /
• pp.526-536
• /
• 2008

The purpose of this study was to compare the effect of various dentin bonding systems on microtensile bond strength of immediate dentin sealing (IDS) and delayed dentin sealing (DDS). Eighteen extracted permanent molars were used in this study. The teeth for DDS group were restored with a provisional restorations, and immersed in saline solution for 1 week, and divided into 3 subgroups according to various dentin bonding adhesives; SB subgroup (3 step total-etch adhesive), SE subgroup (2 step self-etch adhesive), XE subgroup (1 step self-etch adhesive). In IDS group, the teeth were divided into 3 subgroups, and applied with bonding adhesives as in DDS group. The teeth were restored with provisional restorations, and immersed in saline solution for 1 week. Indirect composite disc was cemented with resin cement, and all specimens were subjected to microtensile bond strength. The data were statistically analyzed with oneway ANOVA and Student t-test. The results were as follows: 1. The IDS group showed significantly higher ${\mu}TBS$ than DDS group in 3 step total-etch and 2 step selfetch adhesive (p < 0.05). 2. In IDS and DDS group, 3 step total-etch adhesive showed the highest ${\mu}TBS$ value, followed by 2 step self-etch, and 1 step self-etch adhesive. In IDS group, the ${\mu}TBS$ value for 1 step self-etch adhesive was significantly different from those of the other subgroups (p < 0.05), and in DDS group, there were statistical differences in all subgroup (p < 0.05). 3. Failure modes of tested dentin bonding adhesives were mostly mixed failure and only 1 step self-etch adhesive showed adhesive failure.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.3
• /
• pp.36-44
• /
• 2007

The purpose of this study was to investigate thermal stability, reactivity, and bonding strength of existing epoxy resin mixed with the epoxidized soybean oil (ESBO) in order to use soybean oil economically. In the dry shear test, the marked strengths showed $30.5kgf/cm^2$ at the ratio of ESBO to epoxy resin 9 : 1 and $6.2kgf/cm^2$ at the ratio 8 : 2. The bonding strengths of the others, except mixing ratios 2 : 8 and 1 : 9, exceeded the requirement of Korean plywood standard of $7.0kgf/cm^2$. In the wet shear test, the result was $5.8kgf/cm^2$ at the ratio 9 : 1. There were no thickness swelling and moisture absorption in the water resistance of the film. The value of activation energy, Tg (${\Delta}E$), by DSC analysis showed between $110^{\circ}C$ and $120^{\circ}C$ through all ratios. Epoxy in the epoxy resin fully reacted with the hardener (TETA), but it is difficult to decide that epoxys in the ESBO were reacted directly with the hardener from FT-IR analysis. As the mixing ratio of ESBO increased, the thermal stabilities dropped from TGA analysis. From the comprehensive view on the results of above experiments, it could be confirmed through experiments that the ESBO in the mixed adhesive of epoxy resin/ESBO played a role as an extending agent level of epoxy adhesive, and we were able to know that in order to utilize ESBO as an adhesive, a study should be performed on the condition of hardening, inducible of the hardening reaction.

• Restorative Dentistry and Endodontics
• /
• v.18 no.1
• /
• pp.38-53
• /
• 1993

The purpose of this study was to observe the resin infiltration pattern into dentin by various dentin bonding agents. Freshley extracted 36 sound human molars were used in this study. They were stored at $4^{\circ}C$ physiologic saline solution before experiment. All the teeth were cross-sectioned to expose dentin below about 3.0mm at the cusp tip and above 2.0mm at the cemento-enamel junction with Crystal Cutter (MC411 D, Maruto Co., Japan), and were made into specimens for this study (Fig. 1). The specimen experimental groups were divided into 9 groups by dentin surface treatment as following procedures: Group I: Treated with Gluma Cleanser followed by Gluma Primer and Sealer Group 2. Treated with Gluma Cleanser followed by Scotch bond 2 Adhesive Group 3: Treated with Gluma Cleanser followed by Tenure Solution A, Band Visar Seal Group 4: Treated with Scotchprep followed by Scotch bond 2 Adhesive Group 5: Treated with Scotchprep followed by Gluma Primer and Sealer Group 6: Treated with Scotch prep followed by Tenure Solution A, Band Visar Seal Group 7: Treated with Tenure Conditioner followed by Tenure Solution A, Band Visar Seal Group 8: Treated with Tenure Conditioner followed by Scotchbond 2 Adhesive Group 9: Treated with Tenure Conditioner followed by Gluma Primer and Sealer 27 specimens of 36 specimens were divided into 9 groups (Group 1-9), and were used for observation of resin tags. Remaining 9 specimens were divided into 3 groups (Group 1,4 and 7), and were used for observation of fractured dentin surfaces. Specimens to observe the resin tag were demineralized with 20% HCl for 14 hours, specimens to observe the fractured dentin surfaces were demineralized with 10% HCl for 3 minutes. All the specimens were gold-coated with Eiko ion coater (Eiko-engineering Co.), and observed under Scanning electron microscope (Hitachi S-2300) at 20 KV. The following results were obtained: 1. In group 1 treated with Gluma Cleanser, Gluma Primer, and Sealer, most resin tags were more than $100{\mu}m$. 2. In group 4 treated with Scotch prep and Scotchbond 2 Adhesive, most resin tags were about $10{\mu}m$. 3. In group 7 treated with Tenure conditioner, Tenure Solution A, B, and Visar Seal, most resin tags were about $10{\mu}m$ but occasionally resin tags were more than $100{\mu}m$. 4. In groups 2,3,5,6,8 and 9, the lengths of resin tags were inconsistent and the amount of resin tags were reduced.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.23 no.4
• /
• pp.283-292
• /
• 2007

Two-step or one-step bonding systems generally inhibit curing process of dual-cured core build-up resin composite for their adhesive acidity. In addition this dual-cured core build-up resin composite can be applied to dentin of pulp chamber and root at the time that complete the endodontic treatment. The purpose of this investigation was to determine the influence of sodium hypochlorite on rnicrotensile bond strength of dual-cured core build-up resin composite. Extracted human molars were horizontally sectioned with 1mm thickness using low speed diamond saw. After the sectioned specimens were divided into 8 groups, adhesive systems (Clearfil SE-Bond, Prime&Bond NT[2-step, 1-step], Adper Prompt L-Pop) were then applied with or without sodium hypochlorite pretreatment. The treated specimen was filled with dual-cured core build-up resin composite (Luxacore, DMG corp., German). Then light cured for 40 seconds and soaked in $37^{\circ}C$ water bath for 24 hours. After the treated specimen was grinded with 1mm width and measured rnicrotensile bond strength by testing machine. Additionally 8 teeth were prepared for SEM evaluation. The results were as follows. : NaOCl treated groups generally had lower rnicrotensile bond strength but did not show any difference statistically except Adper Prompt L-Pop. When the teeth were treated by NaOCl, though the difference of applied adhesive system, it had no statistically significant difference within the NaOCl treated groups except the relation of between ClearFil SE-Bond adhesive system and Adper Prompt L-Pop adhesive system. In the SEM evaluation, NaOCl treated groups presented relatively long resin tags and incomplete hybrid layer formation generally.