• Journal of the Korean Applied Science and Technology
• /
• v.22 no.2
• /
• pp.191-199
• /
• 2005

Removable protective adhesives for automobiles were synthesized by an emulsion polymerization of monomers such as n-butyl acrylate (BA), n-butyl methacrylate (BMA), acrylonitrile (AN), acrylic acid (AA) and 2-hydroxyethyl methacrylate (2-HEMA), in which AA and 2-HEMA were functional monomers. Potassium persulfate (KPS) was used as an initiator and sodium lauryl sulfate (SLS) was used as an emulsifier, and polyvinyl alcohol (PVA) was used as a stabilizer. Emulsion polymerization was carried out in a semi-batch type reactor. Tensile strength, extension, peel strength, viscosity and solid content of the synthesized adhesives were tested. The optimum physical properties of the removable protective adhesives for automobiles were obtained with the composition of 0.43 mole BA, 0.57 mole AN, 0.21 mole BMA, 0.03 mole AA, and 0.03 mole 2-HEMA.

• Elastomers and Composites
• /
• v.44 no.3
• /
• pp.308-314
• /
• 2009

The acrylic rubber was synthesized by emulsion polymerization using n-butyl acrylate, n-butyl methacrylate, acrylonitrile, glycidylmethacrylate, and allyl methacrylate. When the contents of acrylonitrile were increased at fixed amount of crosslinking monomers, the Tg of polymers was increased with the contents of acrylonitrile, Mooney viscosity, hardness, and tensile strength also were increased. But the elongation was decreased due to the reduction of chain flexibility. The addition of the monomer for crosslinking, glycidylmethacrylate whose Tg is $56^{\circ}C$ resulted in the increased Tg of the polymer, and increased Mooney viscosity, hardness, and tensile strength, but the elongation at break was decreased with the glycidylmethacrylate contents. It was shown that this phenominon was attributed to the increment of crosslinking density by glycidylmethacrylate through the measurement of rheometer.

• Journal of the Korean Applied Science and Technology
• /
• v.22 no.4
• /
• pp.332-338
• /
• 2005

This study was conducted to prepare acrylic removable protective coatings by emulsion polymerization. Monomers used were n-butyl acrylate, acrylonitrile, butyl methacrylate. Emulsifiers used were sodium lauryl sulfate and polyoxyethylene lauryl ether, which are an anionic emulsifier and a nonionic emulsifier respectively. Potassium persulfate was used as an initiator and polyvinyl alcohol was used as a stabilizer. Emulsion polymerization was carried out in a semi-batch reactor at $70^{\circ}C$ and agitation speed was 200 rpm. Tensile strength, extension, peel strength, viscosity, and solid contents of the synthesized coatings were examined. The coatings prepared with BA:AN = 60:20 (in weight ratio) satisfied the standard for automobile in terms of extension and peel strength. When the concentration of BMA was in a range of $18{\sim}23$ wt%, the prepared coatings satisfied the standard for automobile in terms of peel strength and water resistance.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.45 no.2
• /
• pp.13-20
• /
• 2013

In this study, two biodegradable polymer(PLA, PBS) emulsions were treated on agricultural packaging paper such as fruit bagging paper. Water-repellency, mechanical properties, and SEM image with thermal aging were measured on the emulsion treated fruit bagging paper. Biodegradable polymers(such as poly lactic acid, poly butylene succinate) emulsion treated fruit bagging paper had higher water-repellency and strength than other water-repellent(such as acrylic repellent, linseed oil and paraffin wax) treated fruit bagging paper. According to FE-SEM results of polymer emulsion coated fruit bagging paper, the colloidal particles of emulsion after thermal treatment (looks like being) were adhered to the fibers. Thus, using biodegradable polymer emulsion is expected to protect a fruit for a long time.

• Applied Chemistry for Engineering
• /
• v.18 no.5
• /
• pp.444-448
• /
• 2007

The effects of intra-particle composition on the adhesive properties and water dispersity of acrylic emulsion type pressure sensitive adhesives (PSAs) were investigated. In the case of PSA having uniform intra-particle composition, the higher holding strength made the water dispersity lower. By changing the intra-particle composition in hard core/soft shell type, however, it was possible to get PSAs showing both high holding strength and water dispersity. When the weight ratio of MAA/AA is 4/1, high holding strength, but low initial tack and very low water dispersity were observed in both cases of higher contents of (AA+MAA) in core and shell area. When the weight ratio of MAA/AA is 1/4, however, higher water dispersity and lower holding strength were indicated in the case of higher contents of (AA+MAA) in shell area.

• Journal of IKEEE
• /
• v.21 no.1
• /
• pp.24-29
• /
• 2017

In this paper, we have developed the nano carbon tile and chip which is based on a reducing process of oxidation and the viscous fluid control, after hardening to the stylene monomer and methylol acrylamide monomer using an acrylic emulsion junction material. Then we can obtain the sphere form structure of diagonal 1~3 mm, they have mixture the acrylic emulsion junction material(45%) and the coconut carbon powder(55%) of size 300~500 mesh for 25~30 min. Finally, if we have dry for the formated carbon including 30~90 minute at $90{\sim}300^{\circ}C$, then be obtained for pure carbon formation of 95%. In order to identify the safety of the friendly circumstance carbon formation, we have tested the far-infrared ratio, energy analysis, gas density and anti-disease germs experiment.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.350-355
• /
• 1998

Preplaced aggregate concrete in the building fields has recently been used in the partial repair works for damaged reinforced concrete structures, and polymer-modified mortars have been employed as grouting mortars for the preplaced aggregate concrete. The objective of this study is to clear the properties of polymer-modified grouting mortars. Polymer-modified mortars using a polystyrene acrylic(St/Ac) emulsion as grouting mortars for preplaced aggregate concrete are prepared with various mix proportions, and tested for flexural and compressive strengths, adhesion in tension. The flexural strength of emulsion-modified grouting mortars does not give much variation with increasing fly ash replacement for cement and sand-binder ratio. With increasing polymer-binder ratio, the flexural strength and adhesion in tension of St/Ac emulsion-modified grouting mortars increases, become nearly constant or reaches a maximum at a polymer-binder ratio of 5%. From the test results, St/Ac emulsion-modified grouting mortar with a polymer-binder ratio of 5%, a fly ash replacement of 10% for cement and sand-binder ratio of 1.0 is recommended as a grouting mortar for preplaced aggregate concrete.

• Applied Chemistry for Engineering
• /
• v.7 no.4
• /
• pp.679-690
• /
• 1996

Acrylic copolymer was synthesized from 2-dimethylaminoethyl methacrylate and alkylmethacrylate containing long chain hydrocarbon group. To facilitate emulsification in water, acrylic copolymer was treated with acetic acid, and therefore acetated acrylic copolymer was produced. Acetated acrylic copolymer was perfectly emulsified in water and showed increased emulsion stability. Polymer as a cement dispersion agent(PDCM-PSD) was prepared by blending the newly synthesized acetates acrylic copolymer with sodium gluconate, oleic acid, and triethanolamine. The applicability of the blended polymer was examined, and it was found that the effects of dispersion and water-proof(0.3~0.5) were excellent.

• Journal of the Korean Applied Science and Technology
• /
• v.22 no.3
• /
• pp.289-297
• /
• 2005

In order to improve resistant properties of water-borne acrylic pressure sensitive adhesives(PSAs) for automobiles, this study was carried out. Removable PSAs for automobiles were synthesized by emulsion polymerization of monomers, n-butyl acrylate(BA), n-butyl methacrylate(BMA), acrylonitrile(AN), acrylic acid(AA) and 2-hydroxyethyl methacrylate(2-HEMA), and AA and 2-HEMA could act as functional monomers for crosslink. Emulsion polymerization was carried out in a semi-batch type reactor. Water resistance, heat resistance, acid resistance, alkali resistance and smoke resistance were examined. As a result, water resistance increased with the amount of BMA, however, the effect of BMA content on the water resistance was insignificant at a range of over 14 wt%. The water resistance also increased with the amount of functional monomers, AA and 2-HEMA. The prepared PSAs satisfied all the standard for automobiles except heat resistance. However, the heat resistance comes nearly up to the standard. Also, acid resistance, alkali resistance and smoke resistance of the prepared PSAs satisfied with the standard.

• Applied Chemistry for Engineering
• /
• v.5 no.4
• /
• pp.669-680
• /
• 1994

DMA-co-DAMA were synthesized from 2-diethylaminoethyl metacrylate and dodecyl-metacrylate containing long chain hydrocarbon group with hydrophilic and hydrophobic radicals. To facilitate water emulsification,acrylic copolymer was cationized by acetic acid to produce acetated acrylic copolymer. The structures of the synthesized copolymer and acetated copolymers were confirmed by IR, NMR, and molecular weight was measured by GPC, and C. H. N elemental analysis. Acetated acrylic copolymers were perfectly emulsified in water and showed increased emulsion stability. Polymer dispersion for cement modifier(PDCM-PDD) was prepared by blending of the guaternized acrylic copolymer synthesized above sodium silicate sodium gluconate oleic acid and triethanol amine. The result with prepared polymer dispersion of cement modfier was examined, and it was found that excellent waterproffing effect; Water permeability ratio is 0.44 under the water pressure of $100g/cm^2$ and 0.55 under $3kg/cm^2$, and water absorption ratio is 0.36~0.47 and 1.02 compressive strength ratio at mixed ratio of water/PDCM-PDD is 45 times.