• 한국전기전자재료학회논문지
• /
• 제18권9호
• /
• pp.810-814
• /
• 2005

[ $Pb(Zr_{0.2}Ti_{0.8})O_3/SrRuO_3$ ] heteroepitaxial thin films were deposited at various temperatures on single crystal $SrTiO_3$ substrates by pulsed laser deposition and characterized for the microstructural and ferroelectric properties. The $SrTiO_3$ substartes etched by buffered oxide etch $(pH{\thickapprox}5.8)$ solution for 20s followed by the thermal annealing at $1000^{\circ}C$ for 1h showed the terrace ledges with a 0.4nm height. The $SrRuO_3$ bottom electrodes with a thickness of 52nm grown on $SrTiO_3$ single crystal also exhibit a terrace ledge similar to that of $SrTiO_3$. The PZT thin films were grown with an epitaxial relationship and showed typical P-E hysteresis loops shown at the epitaxial films. The 56nm thick-PZT films deposited at $650^{\circ}C$ exhibit a remanent polarization $(p_r)$ of $80{\mu}C/cm^2$ and a coercive field $(E_c)$ of 160kV/cm.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1995년도 하계학술대회 논문집 C
• /
• pp.1022-1024
• /
• 1995

In this study, $Pb(Zr_xTi_{1-x})O_3$(x=0.65, 0.52, 0.35) thin films were fabricated by Sol-Gel method. A stock solution with excess Pb 10[mol.%] of $Pb(Zr_xTi_{1-x})O_3$ was made and spin-coated on the Pt/$SiO_2$/Si substrate at 4000[rpm] for 30[sec.]. Coated specimens were dried on the hot-plate at $400[^{\circ}C]$ for 10[min.]. Sintering temperature and time were $500{\sim}800[^{\circ}C]$ and $1{\sim}60$[min.]. To investigate crystallization condition, PZT thin films were analyzed with sintering temperature, time and composition by the XRD. The microstructure of thin films were investigated by SEM. The ferroelectric perovskite phases precipitated under the sintering of $700[^{\circ}C]$ for 1 hour. In the PZT(52/48) composition, dielectric constant and dielectric loss were 2133, 2.2[%] at room temperature, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.1
• /
• pp.67-69
• /
• 2004

The $Pb(Zr,Ti)O_3$ thin films were fabricated with $Pb(La,Ti)O_3$ buffers in-situ onto $Pt/Ti/SiO_2/Si$ substrates by pulsed laser deposition technique using a Nd:YAG laser with energy density of $2.5J/cm^2$, and deposited for 10 minutes at $550^{\circ}C$ of substrate temperature. And then, the films have been annealed at $550^{\circ}C$ in oxygen ambient pressure. The remanent polarization value is increased by using buffer layers but coercive field of films is slightly increased.

• 한국결정성장학회지
• /
• 제8권2호
• /
• pp.307-314
• /
• 1998

졸-겔법을 이용하여 PZT박막을 제조하였다. 출발물질로는 Pb-acetate trihydrate, Zr-normal propoxide와 Ti-ispropoxide를 사용하였으며, 용매로는 2-Methoxyethanol과 iso- Propanol을 사용하였다. 기판에 따른 Pb 이온 및 Si 이온의 확산을 고찰하기 위해 bare Si와 열산화된 $SiO_2/Si$ 그리고 산화된 기판 위에 졸-겔 spin-coating법으로 $TiO_2$를 입힌 $TiO_2/SiO_2/Si$ 기판을 사용하였다. 박막의 치밀화 및 기판과의 접착상태는 SEM을 이용하였고, 상생성 온도는 XRD, 그리고 Pb 이온 및 Si 이온의 확산 정도는 ESCA를 사용하였다. 기판으로 bare Si 및 $SiO_2/Si$를 사용한 경우, $700^{\circ}C$에서 perovskite상을 얻을 수 있었으며, SiO2/Si 기판을 사용하여 Si의 막으로의 확산을 다소 방지할 수 있었다. $TiO_2/SiO_2/Si$기판을 사용한 경우, $500^{\circ}C$에서 perovskite상을 얻을 수 있었고, Pb 이온 및 Si 이온의 확산을 방지할 수 있었다.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권8호
• /
• pp.836-850
• /
• 1996

In this study, we have analyzed structural analysis and measured ferroelectric characteristics of PZT thin films prepared by sol gel process with different sintering conditions and different Zr/Ti mot%. When the Zr mot% of PZT thin film was increased, it was found that the remanent. polarization and coercive field were decreased and increased, respectively. Also, the maxium dielectric constant of PZT(50/50) thin film was 786.8. We got double hysteresis(anti-fcrroelectric) curve from PbZrO$_{3}$ thin film. As heating rate goes up, pyrochlore phase of PZT thin film was decreased and dielectric and ferroelectric characteristics were improved. As a result of variation of sintering temperature and time 500.deg. C-800.deg. C and 5 sec.-8 hours, respectively, we got optimal sintering temperature and time. The optimium sintering temperature and time of conventional furnace method and rapid thermal processing method were 650.deg. C-700.deg. C for 30-60 minutes and 700.deg. C/20 seconds-2 minutes, respectively.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권5호
• /
• pp.606-610
• /
• 1995

In this study, Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ ceramic thin films were fabricated from an alkoxide-based by Sol-Gel method. Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ stock solution was made and spin-coated on the Pt/ $SiO_{2}$/Si substrate at 4000[rpm] for 30[sec.]. Coated specimens were chied at 400[.deg. C] for 10[min]. The coating process was repeated 6 times and then heat-treated at 500-800[.deg. C] and 1 hour. The final thickness of the thin films were about 4800[.angs.]. The ferroelectric perovskite phases precipitated under the sintering of 700[.deg. C] for 1 hour. Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ thin films sintered at 700[.deg. C] for 1 hour showed good dielectric and ferroelectric properties.

• E2M - 전기 전자와 첨단 소재
• /
• 제10권2호
• /
• pp.134-140
• /
• 1997

PbTiO$_{3}$-PbZrO$_{3}$-Pb(Ni$_{1}$3/Nb $_{2}$3/O$_{3}$)(PZT-PNN) thin films were prepared from corresponding metal organics partially stabilized with diethanolamine by the sol-gel spin coating method. Each mol rates of PT:PZ:PNN solutions were #1(50:40:10), #2(50:30:20), #3(45:35:20) and #4(40:40:20), respectively. The spin-coated PZT-PNN films were sintered at the temperature from 500.deg. C to 600.deg. C for crystallization. The P-E hysteresis curve was drawn by Sawyer-Tower circuit with PZT-PNN film. The coercive field and the remanent polarization of #4(40:40:20 mol%) PZT-PNN film were 28.8 kV/cm and 18.3 .mu.C/cm$^{2}$, respectively. Their dielectric constants were shown between 128 and 1120, and became maximum value in MPB(40:40:20 mol%). The leakage currents of PZT-PNN films were about 9.4x 10$^{-8}$ A/cm$^{2}$, and the breakdown voltages were about 0.14 and 1.1 MV/cm. The Curie point of #3(45:35:20 mol%, sintered at 600.deg. C) film was 330.deg. C.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2004년도 하계학술대회 논문집 C
• /
• pp.1618-1620
• /
• 2004

The $Pb(Zr_{0.4}Ti_{0.6})O_3/Pb(Zr_{0.6}Ti_{0.4})O_3$ [PZT(4060)/(6040)] multilayered thin films were deposited by RF Sputtering method on the Pt/Ti/$SiO_2$/Si substrate. This procedure was repeated several times to form PZT(4060)/(6040) heterolayerd thin films. The effects on the structural and dielectric properties of PZT multilayered thin films were investigated. The MFM(Metal Ferroelectric Metal) type capacitors were made using the PZT(4060)/(6040) multilayered thin films deposited with optimum deposition condition. An enhanced dielectric property was observed in the PZT(4060)/(6040) multilayered thin films. The relative dielectric constant and dielectric loss at 100Hz of the PZT(4060)/(6040)-5 multilayered thin films were about 1106 and 0.016, respectively.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2003년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.117-119
• /
• 2003

The $Pb(Zr_{0.3}Ti_{0.7)O_3/Pb(Zr_{0.7}/Ti_{0.3})O_3$ [PZT(30/70)/(70/30)] heterolayered thin films were deposited by RF sputtering method on the $Pt/TiO_2/SiO_2/Si$ substrate. Sputter gas ratio(AR/O2) was changed form 90/10 to 50/50. The structural properties and electrical properties of the PZT(30/70)/ (70/30) heterolayered thin films were studied. The relative dielectric constant and dielectric loss at 100Hz of the PZT(30/70)/PZT(70/30) heterolayered thin films with Ar/$O_2$(80/20) ratio were about 982 and 0.036, respectively.

• 한국진공학회지
• /
• 제17권2호
• /
• pp.138-147
• /
• 2008

RF 스퍼터링 시스템을 이용하여 $SiO_2/TiO_2/ZrO_2$ 광대역 반사방지막을 단계별로 제작하였고, 분광타원계와 $UV-V_{is}$ 분광광도계를 이용하여 박막의 두께, 굴절률 및 투과율 스펙트럼을 300$\sim$900nm의 파장 영역에 걸쳐 측정 및 분석하였다. 측정 및 분석된 박막의 두께, 굴절률 및 투과율 스펙트럼을 설계값과 비교 평가한 결과 각층의 두께, 굴절률의 차이에 따른 투과율의 변화를 분석할 수 있었고, 박막의 두께보다는 굴절률과 굴절률의 분산형태가 투과율의 변화에 더 크게 기여함을 알 수 있었다.