급속응고법으로 제작된 비정질 $Fe_{85-x}Co_{x}Zr_{7}B_{7}Cu_{1}$ 합금의 열처리에 따른 구조 및 자기특성이 조사되었다. 비정질 $Fe_{85-x}Co_{x}Zr_{7}B_{7}Cu_{1}$ 합금은 $600^{\circ}C$이하의 열처리온도에서 약 10 nm의 초미세결정립이 형성된다. $600^{\circ}C$이상의 열처리 조건에서는 결정립크기가 급격히 증가하여 자기특성을 열화시킨다. $Fe_{85-x}Co_{x}Zr_{7}B_{7}Cu_{1}$ 합금의 최적열처리온도는 Fe-Zr-B초미세결정립합금에 비하여 낮으며, 결정립크기 또한 감소한다. 이는 Cu의 첨가에 기인하는 것으로 판단된다. 최적열처리조건에서 $Fe_{80}Co_{5}Zr_{7}B_{7}Cu_{1}$ 초미세결정립합금의 포화자화 및 f=50 kHz, $B_{m}=0.2\;T$에서 측정한 투자율 및 철손은 각각 157.3 emu/g(1.5 T), $1.8{\times}10^{4}$ 및 13 W/kg으로 자기특성이 가장 우수하다.

• The Korean Journal of Ceramics
• /
• v.1 no.3
• /
• pp.143-146
• /
• 1995

Twins along(202) and (211) planes are observed in monoclinic $ZrO_2$ thin film, which is deposited on Si substrate by MOCVD at $350^{\circ}C$ and annealed at $1150^{\circ}C$ for 10 hours in air. These types of twin have not been reported in monoclinic $ZrO_2$. The twins seem to be originated from the two dimensional tensile stresses applied to the $ZrO_2$ thin film due to the different thermal expansions of $ZrO_2$ thin film and Si substrate.

• Journal of the Korean Ceramic Society
• /
• v.36 no.12
• /
• pp.1390-1395
• /
• 1999

Zr(Y,Ce)O2 TZP ceramics were prepared by sintering compacts of 3 mol% Y2O3-TZP(3Y-TZP) powders with different amount of 12 mol% CeO2-TZP(12Ce-TZP) in air at 140$0^{\circ}C$ for 2 h. The phase changes microstructure and mechanical properties of Zr(Y. Ce)O2 TZP after hydrothermal aging(20$0^{\circ}C$ 5h) were investigated. Although an addition of 12Ce-TZP accelerated the grain growth of Zr(Y, Ce)O2 TZP it restrained the transformation of tetragonal to the monoclinic phase during aging. The degradation in mechanical properties of sintered bodies was governed by the formed monoclinic phase and chemical composition. Induced Vickers indentation crack was propagated intergranually. From SEM observation of the fracture surfaces the pull-out of individual grain was confirmed.

• Journal of the Korean Ceramic Society
• /
• v.27 no.8
• /
• pp.1064-1070
• /
• 1990

ZrO2 fine powders were prepared by hydrolysis, adding 0.1, 0.2, 0.3, 0.4, 0.5, 0.6mol/1H2O/ethanol to 0.1 mol/l Zr(OC3H7)4/ethanol. When hydrolized by adding 0.1mol/l Zr(OC3H7)4/ethanol to 0.1, 0.2mol/l H2O/ethanol., spherical monodispersed ZrO2 fine powders were obtained. And in this condition average sizes were about 0.5, 0.3${\mu}{\textrm}{m}$, respectively. The more H2O/ethanol concentration increased, the more the particle size decreased and the particles were agglomerated strongly. Prepared powders were amorphous and hydrates. The calcined powders with 43$0^{\circ}C$ and 100$0^{\circ}C$ were showed tetragonal and monoclinic phase, respectively.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.189-189
• /
• 2011

CrZrN 박막은 CrN 박막에 비해서 향상된 기계적 특성과 우수한 표면 조도특성을 가지고 있다. 그러나 $500^{\circ}C$ 이상에서 기계적 특성이 급격히 감소하는 현상이 알려져 있다. 본 연구에서는 CrZrN 박막에 Si를 첨가하여 Si 함량에 따른 고온에서의 기계적 특성을 CrZrN 박막과 비교하였다. $500^{\circ}C$에서 마모 실험한 결과 CrZrN 박막에 비하여 소량의 Si의 첨가만으로 고온에서의 마모 특성이 향상되는 것을 확인하였다. 이것은 Si 첨가에 따라 고온에서 안정한 비정질상의 형성 영향으로 판단된다.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.53-54
• /
• 2006

Ti-Zr-Ni coatings deposited by low vacuum plasma spray technique consisted of nanometer-sized $W-Ti_{50}Zr_{35}Ni_{15}$ 1/1 cubic approximant and TiZrNi Laves phases as well as a low volume fraction of $ZrO_2$ phase. The shift of composition during deposition of the quasicrystalline powders and the presence of $ZrO_2$ phases are believed to be responsible for the reduced corrosion performances evaluated by means of electrochemical tests in a Hanks' Balance Salt Solution at $37^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.259-259
• /
• 2007

The low temperature sintering of dolomite type borates, $CaZr(BO_3)_2$[CZB] ceramics and their microwave dielectric properties were investigated The sintering temperature of CZB ceramics could be reduced from $1150^{\circ}C$ to $925^{\circ}C$ by the addition of sintering additive. $CaZrO_3$, $ZrO_2$ and $CaB_2O_4$ second phases were found in the CZB ceramics. The syntheses, sintering properties, microstructures, and dielectricnproperties of dolomite-type borates were examined by XRD, thermal analysis, electron microscopy, network analyzer, and the results are discussed intensively. The compatibility with silver electrode was also explored.

• Journal of the Korean Ceramic Society
• /
• v.25 no.1
• /
• pp.1-6
• /
• 1988

The IR edge absorption of the important pure components of ZrF4-based glasses, including two previously uncharacterized components(ZrF4 and AlF3), has been measured. Values of the glass IR edge absorption coefficients have been calculated from these results, assuming additivity, and are compared with experimental glass absorption coefficients. The calculated ${\alpha}$ values are about a factor of two lower than the experimental values for ZrF4-based glasses, and the ZrF4 makes the largest contribution to the calculated ${\alpha}$ value.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.1001-1006
• /
• 2002

Bond strength of $SrZrO_3$ resistive oxide barrier on Ag sheathed Bi(2223) tapes prepared by the sol-gel and dip-coating method was evaluated with an aid of Taguchi method and $L_18(2^1{\times}3^7)$ orthogonal arrays to determine the optimal process combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed optimal condition is as follows: Sr/Zr mol ratio(0.3/0.7), amount of organic vehicle(5 wt%), drying temperature and time(160${\circ}C$, 10 min), heat treatment temperature and time(500${\circ}C$, 20 min), respectively. ANOVA analysis suggested that the influence of the factors within ${\alpha}$=0.1 was significant with a 90% confidence level.

• Journal of the Korean Ceramic Society
• /
• v.27 no.2
• /
• pp.201-210
• /
• 1990

The mullite-15v/o ZrO2 composites were prepared by dispersing ZrO2-3m/o Y2O3 powders into the mullite matrix in order to improve the mechanical properties of the mullite. The densification and retention of t-ZrO2 in the matrix of synthetic mullite were also investigated. From IR spectroscopic analysis, the obtained amorphous SiO2-Al2O3 powder was observed to have Si-O-Al chemical bond in its structure which might result in the homogeneous mullite composition. The lattice parameter of the mullite powder calcined above 130$0^{\circ}C$ (a0=7.5468$\AA$) is nearly close to the value of stoichiometric mullite (71.8wt% Al2O3, a0=7.5456$\AA$). The sintering behavior, microstructure, flexural strength and fracture toughness of the mullite and mullite-15v/o ZrO2 composites have been studied. The mullite-15v/o ZrO2(+3m/o Y2O3) ceramics with relative densities of 96% were obtained when sintered at 1$600^{\circ}C$. The flexural strength and fractrue toughness of the composites sintered at 1$600^{\circ}C$(calcination temperature of mullite powders ; 125$0^{\circ}C$) had maximum values of 307MPa and 2.50MPa.m1/2, respectively. The fracture toughness improvement in the mullite-ZrO2 cmoposite is assumed to be resulted from the combined effect of the stress-induced phase transformation of tetragonal ZrO2 and the crack deflection due to microcracking by the monoclinic ZrO2 formation.