• Nuclear Engineering and Technology
• /
• v.41 no.2
• /
• pp.149-154
• /
• 2009

The microstructure, the corrosion behavior and the oxide properties were examined for Zr-1.5Nb-0.4Sn-0.2Fe-0.1Cr (HANA-4) alloys which were subjected to two different final annealing temperatures: $470^{\circ}C$ and $570^{\circ}C$. HANA-4 was shown to have $\ss$-enriched phase with a bcc crystal structure and Zr(Nb,Fe,Cr)$_2$ with a hcp crystal structure with $\ss$-enriched phase being more frequently observed compared with Zr(Nb,Fe,Cr)$_2$. The corrosion rate of HANA-4 was increased with an increase of the final annealing temperature in the PWR-simulating loop, $360^{\circ}C$ pure water and $400^{\circ}C$ steam conditions, which was correlated well with a reduction in the size of the columnar grains in the oxide/metal interface region. The oxide growth rate of HANA-4 was considerably affected by the alloy microstructure determined by the final annealing temperature.

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1133-1138
• /
• 2003

The pressure tubes, which contain high temperature heavy water and fuel, are within the core of a CANDU nuclear reactor, and are thus subjected to high stresses, temperature gradient, and neutron flux. Further, it is well known that pressure tubes of cold-worked Zr-2.5Nb materials result in hydrogen diffusion, which create fully-hydrided regions (frequently called Blister). Thus a proper investigation of hydrogen diffusion within zirconium-alloy nuclear components, such as CANDU pressure tube and fuel channels is essential to predict the structural integrity of these components. In this respect, this paper presents numerical investigation of hydrogen diffusion to quantify the hydrogen concentration for blister growth of CANDU pressure tube. For this purpose, coupled temperature-hydrogen diffusion analyses are performed by means of two-dimensional finite element analysis. Comparison of predicted temperature field and blister with published test data shows good agreement.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.354-358
• /
• 2000

Tetragonal (t)-ZrO2/Al2O3 composites doped with Y2O3, Nb2O5, and Fe2O3 ((Y, Nb, Fe)-TZP/Al2O3) were prepared over the range containing Fe2O3 from 0.1 to 0.5 mol% with 0.1 mol% intervals to evaluate the effect of Fe2O3 addition on chromaticity, hydrothermal stability, and mechanical property of the composites. After autoclaving for 20 h at 18$0^{\circ}C$ under 3.5 MPa water vapor pressure, no tlongrightarrowm phase transformation was observed probably due to the preferential solid solubility of Fe2O3 in Al2O3, the presence of the rigid Al2O3 particles, and the inherent phase stability of (Y, Nb)-TZP. The optimized strength and the fracture toughness of the composite were 700 MPa and 8.5 MPa.m1/2, respectively, when 0.1 mol% Fe2O3 was added. The composites have shown a gradual color change from a slightly white ivory to a pale yellowish brown with increasing the Fe2O3 concentration.

• Journal of the Korean Ceramic Society
• /
• v.41 no.7
• /
• pp.508-512
• /
• 2004

For abutment of dental implants, (Y, Nb)-TZP/Alumina composites were prepared by addition of 10-90 vol% alumina at an interval of 10 vol％ into tetragonal zirconia solid solution which consists of 90.24 mol% Zr $O_2$, 5.31 mol% Y$_2$ $O_3$, and 4.45 mol% Nb$_2$O$\_$5/. Biaxial flexure strength and fracture toughness of composite were optimized by adding 10 vol% alumina, which resulted in 900 MPa and 8.9 MPam$\^$1/2/, respectively. The composite did not undergo low temperature degradation even after autoclave treatment at 200$^{\circ}C$ for 10 h. 65 of (Y, Nb)-TZP/Alumina composite abutments were employed into 40 patients and any adverse reaction, screw loosing, or fracture of abutments was not observed for the span of 2 years, indicating that the ceramic abutments can be safely used for restorations.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05a
• /
• pp.101-104
• /
• 2003

The maximum coercive force of SmCo thin film was obtained at the Sm=28.2% and dc bias field was generated to CoZrNb, soft magnetic thin film, deposited on the SmCo thin film. DC field point having the maximum permeability for CoZrNb was shifted to higher dc field. DC field strength increased as the length of easy direction of magnetization decreased and 60Oe was measured for $3mm{\times}0.5mm$ sample.

• Journal of the Korean Magnetics Society
• /
• v.16 no.2
• /
• pp.136-139
• /
• 2006

The tunneling magnetoresistance (TMR) ratios of magnetic tunnel junctions (MTJs), in general, decrease abruptly above 250$^{\circ}C$ due to Mn interdiffusion from an antiferromagnet IrMn layer to a ferromagnetic CoFe and/or a tunnel barrier. To improve thermal stability, we prepared MTJs with nano-oxide layers. Using a MTJ structure consisting of underlayer CoNbZr 4/bufferlayer CoFe 10/antiferromaget IrMn 7.5/pinned layer CoFe 3/tunnel barrier AlO/freelayer CoFe 3/capping CoNbZr 2 (nm), we placed a nano-oxide layer (NOL) into the underlayer or bufferlayer. Then, the thermal, structural and magneto-electric properties were measured. The TMR ratio, surface flatness, and thermal stability of the MTJs with NOLs were promoted.

• Journal of the Korean Ceramic Society
• /
• v.48 no.5
• /
• pp.471-478
• /
• 2011

Investigations of crystal structure and phase transition of $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics doped with A-site substitution impurity (La, Nd) or B-site substitution impurity (Sb, Nb) at 2 mol% concentration were carried out. X-ray diffraction patterns of impurities doped $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics have been measured at pressures up to ~5 GPa with diamond anvil cell and synchrotron radiation. The patterns were obtained at room temperature using methanol-ethanol mixture as pressure-transmitting media. In order to refine the crystal structure, Rietveld analysis has been performed. The structures of impurities doped $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics are tetragonal in space group P4mm at ambient pressure and are transformed into a cubic phase in space group Pm$\bar{3}$m as the pressure increases. In this study, when A-site substitution donor $La^{3+}$ or $Nd^{3+}$ ion was added to $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics, the phase transition phenomena showed up at the pressure of 2.5~4.6 GPa, but when B-site substitution donor $Nb^{5+}$ or $Sb^{5+}$ ion was added to it, the phase transition appeared at relatively lower pressure of 1.7~2.6 GPa.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2001.05a
• /
• pp.310.2-310
• /
• 2001

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.519-523
• /
• 1995

The Fe-TM-C-N nanocrystalline films (TM : Hf, Zr and Nb) are investigated to examine the relation between microstructure and soft magnetic properties. In these films, as the atomic radius of TM element increases, $P_{N2}$ which was added to get good soft magnetic properties was decreased and the maximum value of the permeability shifted to the high Fe range in the composition diagram. The best soft magnetic properties achieved in these films are : Hc of 0.15 Oe, $\mu_{eff}$ of 7800 (1MHz) and $4{\pi}M_{s}$ of 17.5 kG in Fe-Hf-C-N film ; Hc of 0.06 Oe, $\mu_{eff}$ of 2750 (1MHz) and $4{\pi}M_{s}$ of 16.8 kG in Fe-Zr-C-N film and Hc of 0.31 Oe; $\mu_{eff}$ of 2100 (1MHz) and $4{\pi}M_{s}$ of 15.5 kG in Fe-Nb-C-N film. It was considered that the stronger the bonding force between TM and C(N), the finer TM(C,N) phase is precipitated and therefore, the finer $\alpha$-Fe grains are formed. The effective permeability of the Fe-Zr-C-N films and Fe-Nb-C-N films remains nearly constant up to 10 MHz.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.657-661
• /
• 2002

PZT powder was prepared by partial oxalate method using $(Zr_{0.53}Ti_{0.47})O_2$, $Pb(NO_3)_2$ and $(COOH)_2{\cdot}2H_2O$ as a precipitant. $Nb_2O_5$ additive effect on microstructure and piezoelectric properties of PZT ceramics were investigated. The coexistence of rhombohedral and tetragonal phases of PZT ceramics at the sintering temperature of $1100^{\circ}C$ was revealed from the X-ray diffraction patterns. The grain size PZT ceramics was decreased with the increase $Nb^{5+}$. and the sinterbility of PZT ceramics was decreased with the increase $Nb^{5+}$ addition. The electromechanical coupling factors $K_p$ show above 0.60 at $1100^{\circ}C$ sintering temperature by $Nb_2O_5$ addition above 0.6mol%.