Mechanical Properties of (Y, Nb)-TZP/Alumina Composites for Dental Implant Abutments

For abutment of dental implants, (Y, Nb)-TZP/Alumina composites were prepared by addition of 10-90 vol% alumina at an interval of 10 vol％ into tetragonal zirconia solid solution which consists of 90.24 mol% Zr $O_2$, 5.31 mol% Y$_2$ $O_3$, and 4.45 mol% Nb$_2$O$\_$5/. Biaxial flexure strength and fracture toughness of composite were optimized by adding 10 vol% alumina, which resulted in 900 MPa and 8.9 MPam$\^$1/2/, respectively. The composite did not undergo low temperature degradation even after autoclave treatment at 200$^{\circ}C$ for 10 h. 65 of (Y, Nb)-TZP/Alumina composite abutments were employed into 40 patients and any adverse reaction, screw loosing, or fracture of abutments was not observed for the span of 2 years, indicating that the ceramic abutments can be safely used for restorations.

치과 임플란트 상부구조물용 (Y, Nb)-TZP/알루미나 복합체의 기계적 물성

치과 임프란트의 상부구조물로 응용하기 위해 Zr $O_2$, $Y_2$ $O_3$, Nb$_2$ $O_{5}$를 각각 90.24, 5.31, 4.45mo1%씩 혼합한 정방정 지르코니아 고용체에 알루미나를 부피비로 10-90%를 10vo1%간격으로 첨가하여 (Y, Nb)-TZP/알루미나 복합체를 제조하였다. 최적의 기계적 물성은 알루미나를 10vo1% 첨가했을 때 이축 곡강도는 900MPa이었으며 파괴인성은 8.9MPam$^{1}$2/이었고 20$0^{\circ}C$ 오토크레이브하에서 10시간 열처리했을 때 저온열화가 관찰되지 않았다. 복합체를 임프란트 상부구조물로 제작하여 40명의 환자에게 총 65개를 시술한 후 2년 동안 관찰한 결과 부작용이나 나사의 풀림 또는 파절이 전혀 일어나지 않아 우수한 임상결과를 보였다.