• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 1991년도 춘계연구발표회 논문개요집
• /
• pp.71-72
• /
• 1991

• 한국분말재료학회지
• /
• 제10권2호
• /
• pp.136-141
• /
• 2003

In the present study, $TiO_2$ imbedded copper matrix powders have been successfully prepared from the ($CuSO_4+TiO_2+Zn$) composite salt solution. The composite $Cu/TiO_2$ powders were formed by drying the solution at $200{\sim}~400^{\circ}C$ in the hydrogen atmosphere. Photocatalytic characteristics was evaluated by detecting TOC (total organic carbon) amount with TOC analyzer (model 5000A Shimadzu Co). Phase analysis of $Cu/TiO_2$ composite powders was carried out by XRD, DSC and powder size was measured with TEM. The mean particle size of composite powders was about 100 nm and a few zinc and copper oxide phases was included. The reduction ratio of TOC amount was 60% by the composite $Cu/TiO_2$ powders under the UV irradiation for 8 hours.

• 한국분말재료학회지
• /
• 제9권1호
• /
• pp.25-31
• /
• 2002

The efects of mechanical aloying conditions and the type of reducing agent on the solid state reductionof haematite $Fe_2O_3$ have been investigated at room temperature. Aluminium titanium zinc and copper were used as reducing agent. Nanocomposites of metal-oxide in which oxide particles with nano size were dispersed in Fe matrix were obtained by mechanical alloying of $Fe_2O_3$ with aluminium and titanium respectively However the reduction of $Fe_2O_3$ by coppe was not occurred Composite materials of iron with $Al_2O_3$ and $TiO_2$ were obtained from the system of $Fe_2O_3-Al$ and $Fe_2O_3-Ti$ after ball milling for 20 hrs and 30 hrs respectively. And the system of $Fe_2O_3-Zn$ resulted in the formationof FeO with ZnO after ball milling of 120 hrs. The final grain sizes of iron estimated by X-ray diffraction line-width measurement were in the ranges of 24~33 nm.

• 한국세라믹학회지
• /
• 제34권3호
• /
• pp.289-295
• /
• 1997

저손실 Mn-Zn 페라이트의 제조공정과 첨가제가 코아의 미세구조와 전기적 특성에 미치는 영향을 조사하였다. C\ulcorner와 SiO2를 원료분체혼합시에 첨가하는 경우보다 하소분체의 재분쇄시에 첨가할 때가 작고 균일한 소결체를 얻을 수 있었다. 산소분압(Po2)이 높아짐에 따라 미세구조가 불균일해졌고 DF(disaccomodation fac-색)가 증가하였다. 또한 하소온도가 높고 분쇄시간이 짧은 소결체의 경우 치밀한 속도가 감소하여, 130$0^{\circ}C$까지 정상입성장거동을 보였고, 따라서 높은 소결온도에서도 비교적 저손실 Mn-Zn 페라이트를 얻을 수 있었다. 장시간 분쇄하거나 하소온도가 낮은 시편의 경우는 치밀화속도의 증가에 기인하여 120$0^{\circ}C$이하의 저온 소결시 미립자의 저손실 Mn-Zn 페라이트를 얻을 수 있었으나 소결온도 125$0^{\circ}C$이상에서는 비정상 입성장을 유발시켰다.

• 해양환경안전학회지
• /
• 제20권5호
• /
• pp.468-473
• /
• 2014

본 연구에서는 정제되지 않은 ZnO 및 $TiO_2$나노입자를 M4배지에 노출시켜 두 나노입자가 어느 정도 크기의 응집체로 변화되는지를 살펴보고 또한 두 나노입자가 수생태계 생물종인 Daphnia magna에 어떠한 영향을 초래하는지 유영저해 및 폐사율을 통해 살펴보았다. ZnO 및 $TiO_2$나노입자의 분말상태 크기는 각각 20 nm와 40 nm였지만, M4배지에서는 1333 nm와 1628 nm로 약 40~70배의 크기로 응집되었다. 유영저해의 경우 ZnO와 $TiO_2$나노입자 모두 시간 및 농도가 높아질수록 D.magna가 유영하는데 영향을 미친 것으로 나타났으며, 특히 ZnO나노입자가 $TiO_2$나노입자에 비해 더 큰 영향을 미치는 것으로 나타났다. 폐사율의 경우 ZnO나노입자에서는 시간 및 농도가 높아질수록 폐사되는 비율이 높았으며, $TiO_2$나노입자에서는 72시간이 경과된 시점의 10 ppm 이상의 농도에서 폐사하는 것으로 관찰되었다. 이는 나노입자가 해양에 유입됨으로 인해 원래의 크기에 비해 응집되어 증가되어진다는 것을 알 수 있으며, 또한 그 응집체로 인해 수생태계 생물에 영향을 주는 것으로 나타났다.

• 한국전기전자재료학회논문지
• /
• 제30권12호
• /
• pp.794-799
• /
• 2017

Ga-doped ZnO (GZO) films were deposited by an RF magnetron sputtering method on glass substrates using ZnO as a target containing 5 wt% $Ga_2O_3$ powder (for Ga doping). The structural, electrical, and optical properties of the GZO thin films were investigated as a function of the substrate temperatures. The deposition rate decreased with increasing substrate temperatures from room temperature to $350^{\circ}C$. The films showed typical orientation with the c-axis vertical to the glass substrates and the grain size increased up to a substrate temperature of $300^{\circ}C$ but decreased beyond $350^{\circ}C$. The resistivity of GZO thin films deposited at the substrate temperature of $300^{\circ}C$ was $7{\times}10^{-4}{\Omega}cm$, and it showed a dependence on the carrier concentration and mobility. The optical transmittances of the films with thickness of $3,000{\AA}$ were above 80% in the visible region, regardless of the substrate temperatures.

• 한국결정성장학회지
• /
• 제19권1호
• /
• pp.11-14
• /
• 2009

Micro-pulling down(${\mu}-PD$)법을 이용하여 직경 2mm, 길이 $15{\sim}25\;mm$의 Zn와 Yb가 첨가된 near-stoichiometric 조성의 $LiNbO_3$ 단결정을 성장하였다. 일정 직경의 매끄럽고 결함이 없는 양질의 단결정임을 확인하였고, 결정 내 첨가된 Zn와 Yb의 조성이 고루 분포되었음을 알 수 있었다. Raman spectra를 통해 나타난 모든 peak은 $LiNbO_3$ power의 peak과 일치함을 알 수 있었고, 이를 통해 Hexagonal 구조의 $LiNbO_3$가 성장되었음을 확인할 수 있었다. Zn의 첨가량 증가에 따른 IR 영역의 투과도 비교를 통해 광손상을 억제에 효과가 있는 Zn 첨가의 역치량이 1 mol%임을 알 수 있었다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1993년도 정기총회 및 추계학술대회 논문집 학회본부
• /
• pp.222-224
• /
• 1993

In this paper, The optimum oxidation conditions for the formation of Cu-Zn ferrite were investigated using precipitates obtained by the mixture of $CuCl_2{\cdot}2H_2O$, $ ZnCl_2$, $FeCl_3{\cdot}6H_2O$ and NaOH. The precipitates were prepared by coprecipitation method on various temperatures and oxidation conditions. The oxidation products were examined by SEM, XRD, and VSM. The particles obtained at 70($^{\circ}C$) were more spherical and fine than that of prepared at 25($^{\circ}C$), 50($^{\circ}C$), 60($^{\circ}C$), respectively. By $H_2O_2$ oxidation, the saturation magnetization of the powders was little influenced, But, by air oxidation the saturation magnetization of the powders was influenced intricately. According to our experimental data, the saturation magnetization of the powders increased with reaction time and was saturated at 9 hours.

• 한국응용과학기술학회지
• /
• 제24권4호
• /
• pp.369-376
• /
• 2007

우리는 마이카, boron nitride, bismuthoxychloride와 같은 판상 분체에 ZnO 나노입자를 코팅한 고 기능성 무기 분체를 합성하였다. 본 실험에서 우리는 수열침전법을 이용하여 합성 분체를 합성하였다. 출발물질은 $ZnCl_2$를 사용하였고 침전제로는 hexamethylenetetramine(HMT)와 urea를 사용하였다. 본 실험의 반응변수로는 출발물질의 농도, 침전제 및 반응온도를 변화시켜 실험하였다. 합성물의 형태, 결정성 및 UV-차단능은FE-SEM, XRD, FT-IR, TGA-DTA, in vitro SPF 테스트를 활용해 분석하였다. 본 실험의 결과, 나토입자 크기를 갖는 ZnO는 동일한 최적의 합성조건하에서 다양한 판상 분체의 종류에 관계없이 균일하게 코팅되었다.

• 한국세라믹학회지
• /
• 제29권7호
• /
• pp.539-543
• /
• 1992

The continuous growth method was developed for Mn-Zn Ferrite single crystals. It is a new process that the polycrystalline MnχZn1-χFe2O4 raw materials are supplied continuously from the powder feeding system to the crucible heated by R.F. induction and melted in the crucible, and after the single crystals seed is attached to crucible's hole, the crystals are pulled downward with rotation. Growing the crystals by using the growth method different from the conventional Bridgman or Floating Zone method, we defined the factors having effect on the crystal growing through the pre-experiments. They are temperature distribution in the crucible, melt velocity according to its height, wettability between the crucible's bottom and melt. Therefore, Mn-Zn Ferrite single crystals were to be grown by attaining the appropriate melt height in the crucible, powder feeding rate, temperature gradient between the crucible and interface, crystal growing speed, and this method was confirmed to have possibility for single crystal growing.