• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.33 no.6
• /
• pp.234-243
• /
• 2023

Zinc crystals of ZnO and SiO₂ in glaze raw materials, developed according to composition and firing requirements, are preferred because of their high decorative properties. However, most zinc crystal glazes have a high firing temperature and a narrow firing temperature range, making it difficult to use them as commercial glazes in ceramics. Therefore, in this study, it was expected that the firing temperature of a typical zinc crystal glaze could be lowered to below 1270℃ by using the eutectic effect through mixing frit, the main raw material used in manufacturing zinc crystal glaze. As a result, not only was the formation temperature of zinc crystals lower in the mixed frit glaze, but also the firing temperature range was widened to 1230~1270℃, making it possible to develop a glaze that produces crystals stably. The firing temperature was lowered to 1230~1250℃ and the holding temperature during cooling was lowered to about 950℃, resulting in the development of an economically effective glaze. When using a combination of frit, it has been shown that the holding temperature during cooling affects the recrystallization of zinc crystals depending on the composition of the glaze, and the crystal structure can be adjusted at this time. Additionally, the amount and shape of crystals can be controlled by using a nucleating agent.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.05a
• /
• pp.46-50
• /
• 1996

In this paper, xPb(Zn$\_$1/3/Nb$\_$2/3/)O$_3$-yPbTiO$_3$-zPbZrO$_3$-zPbZrO$_3$ (0.5wt%)MnO$_2$ ceramics were fabricated by the mixed oxide method sintered at 1250$^{\circ}C$ for 2[hrs] and then the dielectric and pyroelectric properties were investigated. In 0.10PZN-0.45PT-0.47PZ sample, dielectric constant was 829 and in the case of 01.5PZN-0.45PT-0.40PZ sample, pyroelectric current and pyroelectric coefficient were 0.95 x 10$\^$-7/ [A] and 7.6 x 10$\^$-1/ [C/$\textrm{cm}^2$$.$$^{\circ}C$]. Figure of merits of pyroelectric current and voltage and detectivity, in same sample, has shown good properties, that were 2.4 x 10$\^$-8/[C$.$cm/J], 5.5 x 10$\^$-11/[C$.$cm/J], 1.6 x 10$\^$-8/ [C$.$cm/J].

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.9
• /
• pp.776-782
• /
• 2002

The microstructure, V-Ι characteristics, and stability of ZnO-P $r_{6}$ $O_{11}$ CoO-C $r_2$ $O_3$- $Y_2$ $O_3$-based varistor ceramics were investigated with cooling rate in the range of 2~8$^{\circ}C$/min. The cooling rate relatively weakly affected the microstructure, the varistor voltage, and the leakage current in the V-Ι characteristics. But the nonlinear exponent relatively strongly affected by cooling rate. The cooling rate also greatly affected the stability of V-Ιand dielectric characteristics for DC accelerated aging stress. On the whole, the varistors cooled with 4$^{\circ}C$/fin exhibited the highest performance in the densification, nonlinearity, and stability. Especially, they exhibited a high stability, in which the variation rate of the varistor voltage( $V_{1㎃}$), the nonlinear exponent($\alpha$), and the dissipation factor(tan $\delta$) is -1.4%, -4.9%, and ＋60.0%, respectively, under DC accelerated aging stress such as 0.95 $V_{1㎃}$15$0^{\circ}C$/12 h)

• Korean Journal of Materials Research
• /
• v.24 no.5
• /
• pp.236-242
• /
• 2014

Fabrication of reaction-bonded $Al_2O_3$ (RBAO) ceramics using Al-Zn-Mg alloy powder was studied in order to improve traditional RBAO ceramic processing using Al powder. The influence on reaction-bonding and microstructure, as well as on physical and mechanical properties, of the particulate characteristics of the $Al_2O_3$-Al alloy powder mixtures after milling, was revealed. Variation of the particulate characteristics of this $Al_2O_3$-Al alloy powder mixture with milling time was reported previously. To start, the $Al_2O_3$-Al alloy powder mixture was milled, reaction-bonded, post-sintered, and characterized. During reaction-bonding of the $Al_2O_3$-Al alloy powder mixture compacts, oxidation of the Al alloy took place in two stages, that is, there was solid- and liquid-state oxidation of the Al alloy. The solid-state oxidation exhibited strong dependence on the density of surface defects on the Al-alloy particles formed during milling. Higher milling efficiency resulted in less participation of the Al alloy in reaction-bonding. This was because of its consumption by chemical reactions during milling, and subsequent powder handling, and could be rather harmful in the case of over-milling. In contrast to very little dependence of oxidation of the Al alloy on its particle size after milling, the relative density, microstructure, and flexural strength were strongly dependent on particle size after milling (i.e., on milling efficiency). The relative density and 4-point flexural strength of the RBAO ceramics in this study were ~98% and ~365 MPa, respectively, after post-sintering at $1,600^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.32 no.5
• /
• pp.635-641
• /
• 1995

The effects of A-site substitution with alkaline-earth ions (Ca, Sr and Ba) on the perovskite-phase formation and dielectric properties for Pb1-xMx(Zn1/3Nb2/3)O3 (0.0 x 0.5)-based relaxors were studied. Considerable improvements in the sinterability and the extent fo perovskite formation were observed with increasing the A-site substitution (x) and sintering temperature. The maximum dielectric permittivity appeared at x=0.1 for Sr and Ba substitutiion, while the relative dielectric permittivity was almost invariant in the case of Ca ion substitution. Curie temperature decreased with increasing relative amount of Sr and Ba ions but was almost invariant in case of Ca ion substitution. With increasing the amount of x, the diffuseness parameter ($\delta$) increased but the maximum dielectric constant decreased, demonstrating an enhanced diffuse phase transition (DPT) in the presence of alkaline-earth cations.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.10
• /
• pp.796-801
• /
• 2001

Ferroelectric 0.05PZN-xPZT(90/10)-(0.95-x)PZT(10/90) (x=0.65, 0.85) specimens were fabricated by the solid-state reaction method, and especially PZT(90/10) and PZT(10/90) powders were derived by the sol-gel method. All specimens showed a uniform ferroelectric grain without the presence of the pyrocholre phase. Average grain size increased with an increased in sintering temperature, the values for the x=0.65 and x=0.85 specimens sintered at 125$0^{\circ}C$ were 14.4$\mu$m and 9.8$\mu$m, respectively. The dielectric constant and dielectric loss of the x=0.65 specimen sintered at 125$0^{\circ}C$ were 1247. 2.06%, respectively. The coercive field and the remanent polarization of x=0.65 and x=0.85 specimens sintered at 125$0^{\circ}C$ were 8.5kV/cm, 13$\mu$C/$\textrm{cm}^2$ and 17.2kV/cm, 28 $\mu$C/$\textrm{cm}^2$, respectively. The pyroelectric coefficient of the x=0.65 and x=0.85 specimens sintered at 125$0^{\circ}C$ were 5.64$\times$10$^{-8}$ C/$\textrm{cm}^2$K and 2.76$\times$10$^{-8}$ C/$\textrm{cm}^2$K, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.543-546
• /
• 2000

Ferroeleclric 0.05PZN-xPZT(90/10)-(0.95-x)PZT(10/90) (x=0.65, 0.85) specimens were fabricated by the mixed-oxide method and cold-pressing method using sol-gel derived PZT(90/10) and PZT(10/90) powders. All specimens show a uniform ferroelectric grain without the presence of the pyrocholre phase. Average grain size increased with an increase in sintering temperature, the value for the x=0.65 specimen sintered at 125$0^{\circ}C$ was 14.4$\mu$m. The dielectric constant and dielectric loss of the x=0.65 specimen sintered at 125$0^{\circ}C$ were 1247, 2.06%, respectively. All specimens showed fairly good temperature and frequency stability of dielectric constant with the range from -2$0^{\circ}C$ to 6$0^{\circ}C$ and 100Hz to 10MHz. The coercive field and the remanent polarization of x = 0.65 specimen sintered at 125$0^{\circ}C$ were 8.5 kV/cm and 13 $\mu$C/cm$^2$, respectively. The pyroelectric coefficient of the x=0.65 specimen sintered at 125$0^{\circ}C$ was 5.64$\times$10$^{-8}$ C/cm$^2$K, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.138-141
• /
• 2004

[ $MnO_2$ ]가 첨가된 $0.9Pb(Zr_{0.5}Ti_{0.5})O_3-0.2Pb[(Zn_{0.8}Ni_{0.2})_{1/3}Nb_{2/3}]O_3$(0.8PZT-0.2PZNN) 세라믹스는 그 압전특성과 유전특성이 뛰어나지만 $1000^{\circ}C$ 이하의 낮은 소결 온도에서는 소결되지 않는다. $1000^{\circ}C$이하의 낮은 소결온도에서 소결하기 위해 CuO를 첨가한 결과, 소결온도 $920^{\circ}C$에서 소결성은 우수하였으나 그 압전 특성의 저하가 두드러졌다. 이는 XRD에서 확인한 결과에 따르면 CuO의 첨가가 우수한 MPB 조성으로 판명된 $MnO_2$ 가 첨가된 0.8PZT-0.2PZNN 세라믹스의 결정구조를 Rhombohedral 구조로 바꾸기 때문인 것으로 보였으며 이러한 문제는 PZNN의 비율을 조절하여 0.875PZT-0.125PZNN 세라믹스를 선택함으로 인해 해결할 수 있었다. 그러나 여전히 낮은 $Q_m$값을 높이기 위해서 $Al_2O_3$를 첨가하였고 그 결과 시편의 tetragonality 감소와 $Q_m$값의 증가를 확인할 수 있었으나 그 첨가량이 0.2wt% 이상일 경우에는 밀도의 감소로 인한 압전특성의 저하가 나타났다. 밀도의 향상을 위해 Zn and Ni excess 조성을 선택하였고 그 결과 0.5wt% $MnO_2$와 0.2wt% CuO 그리고 0.3wt% $Al_2O_3$를 첨가한 0.875PZT-0.125PZNN 세라믹스(Zn and Ni excess 조성)를 $920^{\circ}C$에서 소결한 경우 $k_p=0.581,\;Q_m=809,\;d_{33}=345\;pC/N\;and\;{\varepsilon}_{33}/{\varepsilon}_0=1345$의 빼어난 압전 및 유전특성과 $330^{\circ}C$의 높은 $T_c$를 보였고 그 조성의 vibration velocity는 약4.5 m/s로 나타났다.

• Applied Microscopy
• /
• v.27 no.2
• /
• pp.217-223
• /
• 1997

New type of ordering along 1110] direction was found In BZT sintered at $1400^{\circ}C$ for 90 hours by using X-ray diffraction analysis and high resolution transmission electron microscopy. The wavelength of the modulated structure was 0.9 nm which is three times larger than the interplanar distance of (110) plane. New type of ordering is considered to be formed as a result of Zn vancacy ordering and new structural model was proposed. The computer simulated electron diffraction and the structural images are in good agreement with those obtained by experiments.

• Journal of the Korean Ceramic Society
• /
• v.31 no.9
• /
• pp.981-988
• /
• 1994

Crystallizable glasses with precipitation of celsian were prepared for the purpose of insulating dielectric layers for the devices such as integrated circuit substrates. Crystallization behavior of these glasses were studied by DTA, SEM, XRD analysis and by the measurement of dielectric properties. The base composition of the glass-ceramic consists in weight percent of 30% SiO2, 10% Al2O3, 26% BaO, 10% CaO, 10% ZnO, 8%TiO2 and 6% B2O3. 2-6 wt% Y2O3 were selected as the nucleating agent to promote monoclinic celsian formation. As a result, in barium-rich glasses containing 4~6wt% Y2O3 , monoclinic celsian was developed as major crystalline phase in the temperature range of 850~90$0^{\circ}C$. Also, the dielectric constant and quality factor of these glass-ceramics were about 9 and more than 1000, respectively.