• 한국전기전자재료학회논문지
• /
• 제18권12호
• /
• pp.1117-1123
• /
• 2005

In this study, our varistors based on M. Matsuoka's composition were fabricated with ZnO nano-powder whose sizes were 50 nm and 100 nm. Before fabrication of ZnO nano-powder varistors, structure and Phase were analyzed by FE-SEM and XRD with size of ZnO nano-powders to obtain manufacturing information to fabricate the first ZnO varistors using by nano-powders. As a results of these analyses, calcination and sintering temperatures were respectively designed at $600^{\circ}C\;and\;1050^{\circ}C$. ZnO nano-powder varistors were analyzed by SEM and XRD to measure the changes of microstructures and phase after sintered by out process conditions. Also, electrical properties of ZnO nano-powder varistors were obtained by capacitance-voltage, frequency-teal impedance, and current-voltage corves. Our ZnO nano-powder varistors had about 2.5 times of electric field at varistor voltage as compared with normal ZnO varistors fabricated with micro-powder. Also, leakage current and non-liner coefficient respectively had $2.0{\times}10^{-6}A/cm^{-2}$ and 41 for ZnO nano-powder varistors with 50 nm.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.294-295
• /
• 2006

Varistor fabricated with ZnO nano-powder was studied about the characteristic of energy capability in this paper. ZnO nano-powder varistor were sintered in air at $1050\;^{\circ}C$. The electrical properties and residual voltage of ZnO nano-powder varistor were obtained. Our ZnO nano-powder varistor has about 3 times of electric field at varistor voltage as compared with commercial ZnO varistor fabricated with micro-powder. In the current impulse withstand test, our nano varistor has had better performance than micro varistor. To analysis energy capability take infrared images for pyrexia distribution of each varistor. ZnO Nano-powder varistor has shown much quick response property because of increasing effective cross-section.

• 한국전기전자재료학회논문지
• /
• 제19권9호
• /
• pp.862-867
• /
• 2006

Bi-based nano-varistors and micro-varistors fabricated with each ZnO nano-powder and micro-powder were studied about characteristics on the surge capability in this study. ZnO nano-varistors were sintered in air at $1050^{\circ}C$ for 2 hr. The voltage-current and residual voltage properties of ZnO nano-varistor were compared with their of ZnO micrio-varistor. As a result of these properties, our ZnO nano-varistor has about 3 times at operating voltage as compared with conventional ZnO varistor fabricated with micro-powder and the residual voltage was 8.06 kV at nominal discharge current 101kA in the lighting impulse current test. And then the residual voltage rate 1.72 of our nano-varistor has had better performance than the 1.79 of micro-varistor because ZnO nano-varistor has shown much quick response property because of increasing effective cross-section area. Also, to analysis surge capability took thermal images for pyrexia temperature distribution with each of the varistors after operating varistors. Nano-varistor doesn't have shown local overheating and can confirm accurate temperature grade on the surface of its.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.183-184
• /
• 2005

In this study, our varistors based on M.Matsuoke's composition were fabricated with ZnO nano-powder whose sizes were 50nm and 100nm. Electrical properties of ZnO nano-powder varistors were obtained by capacitance-voltage and frequency-real impedance. nano-powder varistors are indicated the change of the interface defects density $N_t$ at the grain boundaries and the donor concentration $N_d$ in the ZnO grains. Frequency analysis was accomplished to understand the equivalent circuit.

• 한국분말재료학회지
• /
• 제12권4호
• /
• pp.284-290
• /
• 2005

ZnO nanostructures with various shapes were synthesized under ambient pressure condition by a wet chemical reaction method. Nanorods of ZnO with hexagonal cross-section and their aggregates with radiate shape were synthesized. Precursor concentration affected considerably the shape evolution of ZnO nanorods. Low precursor concentration was proved to be more preferable to the growth of ZnO nanorods, which is attributed to the intrinsic characteristics of chemical reaction in the synthesis of ZnO from zinc compounds.

• 공업화학
• /
• 제24권4호
• /
• pp.391-395
• /
• 2013

본 연구에서는 자외선 흡수 물질로 잘 알려진 zinc oxide (ZnO) 나노분말을 세 가지 합성조건에서 수열합성법으로 합성하였다. 또한, 분산성을 향상시키기 위하여 합성된 ZnO 나노분말의 표면을 다양한 실란계 계면활성제를 사용하여 표면 개질하였고, 표면개질된 ZnO 나노분말을 분산제로 72 h 동안 볼밀링하여 분산 졸 시료를 제조하였다. 30 nm 크기로 합성된 ZnO 나노분말을 3-chloropropyl trimethoxy silane로 표면개질하여 폴리우레탄계 분산제로 제조한 분산 졸 시료가 가장 높은 자외선 차단 특성 및 가시광 투과율을 가지면서 분산 안정성이 가장 우수하였다.

• 한국재료학회지
• /
• 제12권10호
• /
• pp.784-790
• /
• 2002

For mass product of nanocrystalline ZnO ultrafine powders, self-sustaining combustion process(SCP) and ultrasonic spray combustion method(USCM) were applied at the same time. Ultrasonic spray gun was attached on top of the vertical type furnace. The droplet was sprayed into reaction zone of the furnace to form SCP which produces spherical shape with soft agglomerate crystalline ZnO particles. To characterize formed particles, fuel and oxidizing agent for SCP were used glycine and zinc nitrate or zinc hydroxide. Respectively, with changing combustion temperature and mixture ratio of oxidizing agent and fuel, the best ultrasonic spray conditions were obtained. To observe ultrasonic spray effect, two types of powder synthesis processes were compared. One was directly sprayed into furnace from the precursor solution (Type A), the other directly was heated on the hot plate without using spray gun (Type B). Powder obtained by type A was porous sponge shape with heavy agglomeration, but powder obtained using type B was finer primary particle size, spherical shape with weak agglomeration and bigger value of specific surface area. 9/ This can be due to much lower reaction temperature of type B at ignition time than type A. Synthesized nanocrystalline ZnO powders at the best ultrasonic spray conditions have primary particle size in range 20~30nm and specific surface area is about 20m$^2$/g.

• 한국전기전자재료학회논문지
• /
• 제23권1호
• /
• pp.14-17
• /
• 2010

$ZnGa_2O_4$ powder were prepared by combustion method and $Mn^{2+}$ ions, a green luminescence activator, and $Cr^{3+}$ ions, a red luminescence activator were separately doped into $ZnGa_2O_4$. The characteristics of the synthesized nano powder were investigated by means of X-ray diffraction (XRD), Scanning Electron Microscope (SEM), and photoluminescence (PL). The various $ZnGa_2O_4$ peaks, with the (311) main peak, appeared at all sintering temperature XRD patterns. The PL specctrums of $ZnGa_2O_4$ powder showed main peak of 425 nm, and maximum intensity at the sintering temperature of $1200^{\circ}C$. SEM images shown that nano sized particles(about 200 nm) were of spherical shape. The characteristics of $ZnGa_2O_4$ containing 0.004 mol $Mn^{2+}$(505 nm, green) and $ZnGa_2O_4$ containg 0.002 mol $Cr^{3+}$ (696 nm, red) were shown to be the best.

• 한국진공학회지
• /
• 제17권6호
• /
• pp.538-543
• /
• 2008

나노급 다이아몬드는 최근 폭발법이나 증착법에 의한 신공정으로 100 nm 이하의 분말형태의 제조가 가능하다. 나노급 다이아몬드의 소결을 이용하면 이상적인 연마기기의 제작이 가능하다. 이러한 나노급 다이아몬드의 소결 공정에서 생기는 비이상적인 나노결정의 결정립성장과 다이아몬드 결합장애를 방지하기 위해서 나노급 무기물을 균일하게 코팅하는 공정개발이 필요하다. 본 연구에서는 나노급 다이아몬드의 소결 특성을 향상시키기 위해서 ALD(atomic layer deposition)을 이용하여 진공에서 $20{\sim}30\;nm$ 두께의 ZnO 박막을 코팅해 보았다. 나노급 다이아몬드 분말 전면에 경제적으로 ZnO ALD를 위해서 기존의 기계적 진동효과 또는 전용 fluidized bed reactor를 대치하여 새로이 20 mm 석영튜브 안에 다이아몬드 분말을 넣고 다공성 유리필터로 막은 후 펄스와 퍼지 공정시의 압력에 의한 다이아몬드의 부유를 이용한 변형된 fluidized bed 공정을 채용하였다. 다공성 유리필터로 양쪽이 막힌 석영튜브 안에 전구체 DEZn (diethylzinc : $C_4H_{10}Zn$)와 반응기체 $H_2O$를 사용하여 ZnO 박막을 캐니스터 온도 $10^{\circ}C$에서 원자층증착하였다. 공정 순서 및 반응물질 주입 시간은 DEZn pulse-0.1초, DEZn purge-20초, $H_2O$ pulse-0.1초, $H_2O$ purge-40초와 같이 설정하였으며, 이 네 단계를 1 cycle로 정의하여 100 cycle 반복 실시하였다. 다이아몬드 분말과 ZnO 박막이 증착된 다이아몬드 분말의 미세구조를 확인하기 위하여 투과전자현미경 (transmission electron microscope)을 이용하였다. TEM 측정결과, ALD 증착 전 나노급 다이아몬드 분말의 직경이 약 $70{\sim}120\;nm$이었고 사면체, 육면체 등의 다양한 형태를 보임을 확인하였다. ZnO 박막이 ALD코팅된 다이아몬드 분말의 직경은 약 $90{\sim}150\;nm$이었고, 다이아몬드 분말과 ZnO의 명암차이에 의해 약 $20{\sim}30\;nm$ 두께의 균일한 ZnO 박막이 다각형 형태의 다이아몬드 파우더 표면에 성공적으로 증착되었음을 확인하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 추계학술대회 논문집 Vol.19
• /
• pp.203-204
• /
• 2006

Nano-Varistors fabricated with ZnO 30nm and 80nm powders were studied about the electrical characteristics with AC accelerated degradation in this paper Especially, ZnO nano-powder varistors were sintered m air at $1050^{\circ}C$ and analyzed the phenomenons of before and after AC degradation test. The stress conditions of AC degradation test were $1.0V_{1mA}$ $115{\pm}2^{\circ}C$ for 24h. 80nm-varistor was exhibited better performance than 30nm-varistor m the electrical stabilities. And then 80nm-varistor resulted m the degradation characteristics that the variation rate of operating voltage, nonlinear coefficient and leakage current was -0 3%, -0 4% and -3 3%, respectively.