• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.569-572
• /
• 2003

전력선 통신용 LC 공진필터에 사용되는 Ni-Zn 페라이트를 제조하기 위해 Ni0.8Zn0.2Fe2O4를 기본조성으로 선택하고 x (Co mol 비)를 변화시켜 전자기적 특성을 조사하였다. $Bi_2O_3$ CaO가 첨가됨으로써 균일한 입자성장과 입계에 고저항층이 형성되어 주파수 손실이 감소하였으며, $Ni_{0.8-x}Zn_{0.2}Co_xFe_2O_{\delta}$의 기본조성에 Co의 함량을 증가시키면 x = 0.05에서 투자율 75, 공진주파수 20 MHz의 특성을 나타내고 결정 입자 크기와 같은 구조적 특성에는 영향을 거의 미치지 않지만 자기이방성 변화에 따라 전자기적 특성에는 영향을 미친다. 또한, $Ni_{0.75}Zn_{0.2}Co_{0.05}Fe_2O_{4.017}$ 조성의 페라이트 코어의 발열량은 큐리온도 이하에서 일어난다.

• Journal of the Korean Ceramic Society
• /
• v.39 no.7
• /
• pp.669-674
• /
• 2002

Ni-Zn ferrite was sintered by microwave hybrid sintering method using microwave energy of 2.45 GHz, 700 W in the temperature range of 900$^{\circ}C$ ∼ 1070$^{\circ}C$. A high density (98%TD) Ni-Zn ferrite, added Bi$_2$O$_3$ and CuO, with a single phase was obtained by microwave sintering at 970$^{\circ}C$ for 15 min. All the sintered samples showed sintered density over 90% of TD. These results indicate that the processing time and energy consumption can be reduced significantly by microwave hybrid sintering method.

• Journal of Magnetics
• /
• v.18 no.4
• /
• pp.428-431
• /
• 2013

We demonstrate that a partial loading of $Ni_{0.5}Zn_{0.5}Fe_2O_4$ (Ni-Zn ferrite) film remarkably improves impedance matching of electrically small $Ba_3Co_2Fe_{24}O_{41}$ ($Co_2Z$) hexaferrite antenna. A 3 ${\mu}m$ thick Ni-Zn ferrite film was deposited on a silicon wafer by the electrophoresis deposition process and post-annealed at $400^{\circ}C$. The fabricated Ni-Zn ferrite film has saturation magnetization of $268emu/cm^3$ and coercivity of 89 Oe. A partial loading of the Ni-Zn ferrite film on the $Co_2Z$ hexaferrite helical antenna increases antenna return loss to 24.7 dB from 9.0 dB of the $Co_2Z$ antenna. Experimental results show that impedance matching and maximum input power transmission to the antenna without additional matching elements can be realized, while keeping almost the same size as the $Co_2Z$ antenna size.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05a
• /
• pp.92-95
• /
• 2003

전력선 통신용 LC 공진필터에 사용되는 Ni-Zn 페라이트를 제조하기 위해 $Ni_{0.8}Zn_{0.2}Fe_{2}O_{4}$를 기본조성으로 첨가제 $Bi_{2}O_{3}$, CaO와 x (co mol 비)를 변화시켜 전자기적 특성을 조사하였다. $Bi_{2}O_{3}$ CaO가 첨가됨으로써 균일한 입자성장과 입계에 고저항층이 형성되어 주파수 손실이 감소하였으며, $Ni_{0.8-x}Zn_{0.2}Co_{x}Fe_{2}O_{\delta}$의 기본조성에 Co의 함량을 증가시키면 x = 0.05에서 투자율 75, 공진주파수 20MHz의 특성을 나타내고 결정 입자 크기와 같은 구조적 특성에는 영향을 거의 미치지 않지만 전자기적 특성에는 영향을 미친다. 또한, $Ni_{0.75}Zn_{0.2}Co_{0.05}Fe_{2}O_{4.017}$ 조성의 페라이트 코어의 발열량은 큐리온도 이하에서 일어난다.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.11a
• /
• pp.109-113
• /
• 2002

본 연구에서는 공침법에 의한 초미세분말을 이용하여 제조된 (NiCuZn)-ferrite와 건식법을 이용하여 제조된 (NiCuZn)-ferrite의 저온소결 특성 및 전자기적 특성을 상호 비교 분석하였다. 조성은 (N $i_{0.4-x}$C $u_{x}$Z $n_{0.6}$)$_{1+w}$(F $e_2$ $O_4$/)$_{1-w}$에서 x의 값을 0.2, w의 값은 0.03으로 고정하였고, 소결은 공침법으로 합성된 분말의 경우 초기열처리과정을 거쳐 최종적으로 90$0^{\circ}C$에서, 건식법의 경우 11$50^{\circ}C$의 온도에서 진행하였다. 그 결과, 공침법으로 제조된 (NiCuZn)-ferrite는 건식법으로 제조된 (NiCuZn)-ferrite보다 20$0^{\circ}C$이상 낮은 소결온도에서 높은 소결밀도 값을 가졌으며, 품질계수 등 칩 인덕터에서 중요한 요소인 전자기적 특성이 우수하게 나타났다. 또한, 공침법으로 합성된 페라이트는 분말의 초기열처리온도에 따라 최종소결 특성이 크게 변하였다. 그밖에 공침법과 건식법으로 합성한 (NiCuZn)-ferrite의 결정성, 미세구조들을 XRD, SEM, TEM을 이용하여 비교 고찰하였다.하였다.다.

• Electrical & Electronic Materials
• /
• v.8 no.6
• /
• pp.744-751
• /
• 1995

This paper describes a study on absorption properties of electromagnetic wave by the composition ratio of Ni-Zn ferrite. Ni-Zn ferrite was composed of 48-52mol% Fe$\_$2/O$\_$3/, 18-22mol% NiO and 26-34mol% ZnO. The sintering of the composition was carried out at 1200.deg. C for 2 hours. Through the experiments, it was found that the resonance phenomenon occured at low frequency range for high permeability and vice versa. In the case of the composition of 49mol% Fe$\_$2/O$\_$3/, 20mol% NiO and 31mol% ZnO, the bandwidth ranged from 0.35GHz to 0.95GHz with the absorption thickness of 10mm. Also, in the case of the composition 51mol% Fe$\_$2/O$\_$3/, 22mol% NiO and 27mol% ZnO, the bandwidth ranged from 0.48GHz to 1.2GHz with the absorption thickness of 6mm.

• Journal of Fashion Business
• /
• v.4 no.1
• /
• pp.25-32
• /
• 2000

The purpose of this study was to suggest the knowlege and scientific information of the damage according to the heavy metal exposure level of hair coloring manipulations. The study was investigated variations of the heavy metal contents(Pb, Zn, Cu, Mn, Fe, Ni) in hairdye and human hairs by 1 and 2 times of hair coloring manipulations. The results were as follows; 1. Mean heavy metal contents in colorant of hairdye were 0.250ppm(Pb), 33.650ppm(Zn), 0.800ppm(Cu), 0.675ppm(Mn), 31.050ppm(Fe), 1.700ppm(Ni). In oxidant of hairdye, It were 0.225ppm(Pb), 35.450ppm(Zn), 0.575ppm(Cu), 0.075ppm(Mn), 16.600ppm(Fe), 1.500ppm(Ni). 2. Mean heavy metal contents were 2.950ppm(Pb), 29.000ppm(Zn), 9.400ppm(Cu), 1.075ppm(Mn), 40.775ppm(Fe), 1.950ppm(Ni) in virgin hairs, 3.025ppm(Pb), 40.250ppm(Zn), 9.650ppm(Cu), 1.350ppm(Mn), 42.900ppm(Fe), 2.200ppm(Ni) in 1 time of coloring hairs, 3.350ppm(Pb), 51.650ppm(Zn), 10.950ppm(Cu), 1.475ppm(Mn), 44.350ppm(Fe), 2.225ppm(Ni) in 2 times of coloring hairs.

• Journal of Magnetics
• /
• v.10 no.3
• /
• pp.84-88
• /
• 2005

Nanoparticles $Ni_{0.7}Zn_{0.3}Fe_2O_4$ is fabricated by a sol-gel method. The magnetic and structural properties of powders were investigated with XRD, SEM, $M\ddot{o}ssbauer$ spectroscopy, and VSM. $Ni_{0.7}Zn_{0.3}Fe_2O_4$ powders annealed at $300^{\circ}C$ have a spinel structure and behaved superparamagnetically. The estimated size of $Ni_{0.7}Zn_{0.3}Fe_2O_4$ nanoparticle is about 11 nm. $Ni_{0.7}Zn_{0.3}Fe_2O_4$ annealed at 400 and $500^{\circ}C$ has a typical spinel structure and is ferrimagnetic in nature. The isomer shifts indicate that the iron ions were ferric at the tetrahedral (A) and the octahedral (B). Blocking temperature $(T_B)\;of\;Ni_{0.7}Zn_{0.3}Fe_2O_4$ nanoparticle is about 260 K. The magnetic anisotropy constant of $Ni_{0.7}Zn_{0.3}Fe_2O_4$ annealed $300^{\circ}C$ were calculated to be $1.7X10^6\;ergs/cm^3$. Also, temperature of the sample increased up to $43^{\circ}C$ within 7 minutes under AC magnetic field of 7 MHz.

• Asian-Australasian Journal of Animal Sciences
• /
• v.1 no.2
• /
• pp.73-79
• /
• 1988

Experiments were conducted to determine whether supplemental cobalt (Co) or nickel (Ni) would prevent the signs of zinc (Zn) deficiency in chicks fed a high calcium (1.5%) corn-soybean diet and to examine the difference in $^{65}Zn$ absorption rates between inbred Ancona and crossbred New Hampshire X Single Comb White Leghorn chicks. In the initial experiment, the supplementation of 27 ppm Ni, 27 ppm Co or 54 ppm Co to a basal diet increased weight gain and reduced feather defects; 54 ppm Ni tended to increase weight gain but did not reduce feather defects. In further experiments, chicks fed the diet supplemented with 54 ppm Co usually showed increased weight gain and reduced feather defects; however, chicks fed a diet supplemented with 54 ppm Ni less frequently showed these effects. In another test, Ancona chicks fed a diet supplemented with 30 ppm Zn (except during a $^{65}Zn$ absorption study period) showed lower weight gain, more feather defects and less $^{65}Zn$ absorption than did New Hampshire X Leghorn cross chicks. Similar results were achieved with two strains of chicks fed the basal and 54 ppm Ni, 54 ppm Co or 60 ppm Zn supplemented diets. The sparing effects of Co on Zn which were commonly observed and the lesser effect of Ni or Zn were shown to be, at least in part, the result of increased availability of dietary Zn. That Ancona chicks required more Zn than New Hampshire cross chicks for the development of feathers and for growth is partly the result of decreased Zn absorption from the type of diets fed.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.85-85
• /
• 2012

NiO는 니켈 공공과 침입형 산소 이온에 의한 비화학적양론 특성 때문에 자발적으로 p-형 반도체 특성을 나타내는 것으로 알려져 있다. NiO는 3.7 eV 의 넓은 밴드갭을 가지고 있어 투명소자를 위한 hole injection layer 나 hole transport layer로 사용하기 위한 연구가 많이 이루어지고 있다. 또한, 안정적인 p-형 반도체 특성은 n-형 산화물 반도체와의 접합을 통해 복합소자의 구현이 용이하기 때문에, ZnO 등과의 접합을 통한 소자 구현이 가능하다.[1] 하지만, 기존의 많은 연구에서는 내부의 결함이 많이 존재하는 다결정 박막을 사용하였기 때문에, 전하의 이동에 제한이 발생해, 충분한 소자 특성을 나타내지 못하였다. 최근 Dutta의 연구에 의하면, 결정질 사파이어 기판위에 박막을 성장할 경우 [111] 방향으로 우선 배향성을 가진 NiO 박막을 얻을 수 있다고 알려져 있다.[2] 본 실험에서는 NiO 박막을 이용한 PN 접합소자 구현을 위해 사파이어 위에 p-NiO 박막을 에피택셜하게 성장한 후 구조적 특성을 분석하였으며, n-ZnO 박막을 그 위에 성장하여 소자를 제작하였다. 그 결과 ZnO 또한 에피택셜한 성장을 하는 것을 확인할 수 있었다. 성장순서에 따른 PN 접합구조 특성을 확인하기 위해 사파이어 위에 ZnO 를 성장시킨 후 NiO 를 성장시킨 결과 NiO 박막의 우선성장 방향이 [100]으로 변하는 것을 확인할 수 있었다.