• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.264-264
• /
• 2012

Zn-Mg 합금도금의 인산염 처리시 산성의 인산염 용액에 의해 도금층으로부터 용출된 마그네슘이온은 인산염 결정 형성에 참여하고, 이로인해 미세하고 치밀한 인산염 피막이 형성되었다. 마그네슘을 포함함 치밀한 인산염 피막은 우수한 내식성을 보였다. 마그네슘이온의 영향성 파악을 위해 인산염 용액내 추가적으로 마그네슘 이온을 투입하였으며, 마그네슘 함량증가에 따라 인산염 피막의 내식성이 향상됨을 확인하였다.

• Corrosion Science and Technology
• /
• 제12권6호
• /
• pp.295-303
• /
• 2013

Silane surface treatments have been developed as an alternative for toxic and carcinogenic chromate-based treatments for years. It is consistently observed that ultra-thin films offer excellent corrosion protection as well as paint adhesion to metals. The silane performance is comparable to, or in some cases better than, that of chromate layers. Based on the tetra-ethylorthosilicate(TEOS) and methlyl trieethoxysilane(MTES), inorganic sol was synthesized and formed hybrid networks with $SiO_2$ nano particle and polypropylene glycol(PPG) on Zn alloyed steel surface. According to SST results, addition of 10nm and 50nm $SiO_2$ nanoparticle in synthesized solution improved anti-corrosion property by its shear stress relaxation effect during curing process. Also, SST results were shown that anti-corrosive property was affected by the amounts of organic compounds.

• 한국표면공학회지
• /
• 제50권4호
• /
• pp.266-271
• /
• 2017

In this study, the corrosion resistance of Zn-3wt.%Mg coating was enhanced by controlling the density of coating. During the deposition the substrate temperature was controlled via an intermittent deposition process, resulting in the improvement of coating density. The maximum substrate temperature during this intermittent deposition process could be controlled from $200^{\circ}C$ to $80^{\circ}C$, depending upon the number of coating layer. The density of Zn-3 wt.%Mg coating increased from 76.1 % to 95.8 % as the substrate temperature was controlled. The salt spray test results revealed that the corrosion resistance of Zn-Mg coated steel could increase 3 times by increasing the density in coatings, while adhesion strength of coating was not changed significantly during 0-T bending test.

• Journal of Electrochemical Science and Technology
• /
• 제6권2호
• /
• pp.65-74
• /
• 2015

This work examines the characterization and corrosion behaviour of laser alloyed UNSG10150 steel with three different premixed composition Zn-Sn binary powders using a 4.4 kW continuous wave (CW) Rofin Sinar Nd:YAG laser processing system. The steel alloyed samples were cut to corrosion coupons, immersed in sulphuric acid (0.5 M H₂SO₄) solution at 30℃ using electrochemical technique and investigated for its corrosion behaviour. The morphologies and microstructures of the developed coated and uncoated samples were characterized by Optic Nikon Optical microscope (OPM) and scanning electron microscope (SEM/EDS). Moreover, X-ray diffractometer (XRD) was used to identify the phases present. An enhancement of 2.7-times the hardness of the steel substrate was achieved in sample A₁ which may be attributed to the fine microstructure, dislocations and the high degree of saturation of solid solution brought by the high scanning speed. At scanning speed of 0.8 m/min, sample A₁ exhibited the highest polarization resistance R_p (1081678 Ωcm² ), lowest corrosion current density i_corr (4.81×10⁻⁸A/cm² ), and lowest corrosion rate Cr (0.0005 mm/year) in 0.5 M H₂SO₄. The polarization resistance R_p (1081678 Ωcm² ) is 67,813-times the polarization of the UNSG10150 substrate and 99.9972% reduction in the corrosion rate.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2003년도 춘계학술발표대회 개요집
• /
• pp.99-101
• /
• 2003

This study deals with the resistance spot welding of aluminized steels. According to the test results it was clear that the weldability of aluminized steels was equivalent to or better than that of Zn coated steel. Microstructural inspection revealed that molten aluminum that was repelled from the weld during the process, piled up at the split zone. The test results also demonstrated that the weld metal of aluminized steels could hardly produce the weld crack even higher welding heat Input was applied.

• 대한금속재료학회지
• /
• 제46권8호
• /
• pp.495-505
• /
• 2008

With the high proportion of zinc coated steels in body-in-white assembly, newly developed surface roughness textured galvannealed steel sheets have been introduced. In this study, zinc coated and surface roughness textured steel sheets were welded by resistance spot welding to investigate its weldability including electrode wear test. Based on the results of tensile-shear test, nugget diameter changes, and electrode tip growth test, it was clear that both surface roughness textured steels (GA-T and GA-E) showed good weldability. Also, there was no large difference in weldability and electrode wear behavior between GA-T and GA-E steels which have different surface roughness morphology. An analysis of electrode degradation showed Fe and Zn penetration through the electrode tip surface at 2400 welds reached $55{\sim}60{\mu}m$ and $75{\sim}80{\mu}m$, respectively. Therefore, there is no significant effect of surface roughness morphology on spot weldability of surface roughness textured galvannealed steel sheets. However, slight difference in thickness of alloying layers existing on electrode tip was found between GA-T and GA-E steels.

• 한국표면공학회지
• /
• 제34권4호
• /
• pp.313-320
• /
• 2001

It is well known that the amount of hot-dip Zn coated sheet steels used for automotive is rapidly increasing. As hot-dip steel sheets show good corrosion resistance and excellent formability, the demand for outer panel of automotive has been increased in order to satisfy with the requirement of high surface qualify. There are many kinds of factors influencing on the surface quality and the dross control in the galvanising bath is regarded as one of the most important thing. In this study the characteristic and growing behavior of dross in the galvanizing bath were investigated and the effect of dross on the surface defect of GA was surveyed. The dross defects on the GA sheet steels result from bottom dross whose diameter are larger 50$\mu\textrm{m}$ in the Zn pot. Dross-free state exist for about 30 hours from starting time of GA production.

• 한국해양공학회지
• /
• 제24권5호
• /
• pp.60-66
• /
• 2010

Zinc has a number of characteristics that make it well suited for use as a coating to protecting iron and steel products from corrosion. Its excellent corrosion resistance in most environments accounts for its successful use as a protective coating on a variety of products and in many exposure conditions. The excellent field performance of zinc coatings results from their ability to form dense, adherent films that corrode at a rate that ranges from 1% to 10% of the corrosion rate of ferrous materials, depending on the environment. Recently, EU RoHS and EU ELV prohibited the use of materials that adversely affect the environment, such as Pb, Hg, Cd, and $Cr^{+6}$. In this study, environmentally-friendly, Cr-free solutions (epoxy solution, acrylic solution, and urethane solution S-700) and organic/inorganic solution with Si; LRO-317) were used to evaluate the corrosion resistance of zinc-coated steel subjected to a saltwater spray for 72 hours. The coating of urethane solution (S-700) was best among the three kinds of solution with heat treatment during five minutes at $190^{\circ}F$. Test specimens with S-700 and LRO-317 coating were heat treated in a drying oven at 170, 180, 190, 200, and $210^{\circ}C$ for five minutes. The results show that the optimum corrosion resistance was $190^{\circ}C$ in EGI and $170^{\circ}C$ in HDGI, respectively.

• 한국표면공학회지
• /
• 제34권4호
• /
• pp.297-302
• /
• 2001

As GA (Hot dip galvannealed steel sheet) has good corrosion resistance, weldability and paintability as well as excellent formability, it's demand is rapidly increasing for automotive panels. The GA coated layers are composed of several kinds of brittle Fe-Zn Metallic compounds which are susceptible to powdering during the press forming, however, very careful controls of manufacturing conditions such as galvannealing heat-treatment or bath composition are essential to meet with the required quality of automotive use. In this study the required characteristics of automotive panel are practically surveyed in detail and the appropriate manufacturing conditions of galvannealing or bath composition have experimentally investigated by using the various analyzing and simulating equipments. The result in this study indicated that the corrosion resistance at the cut edges was improved by increasing of coating weight and decreasing of thickness of sheet steels.

• Composites Research
• /
• 제37권3호
• /
• pp.238-245
• /
• 2024

본 연구에서는 강관의 효율적 유지관리를 위한 모니터링 시스템 개발 연구의 일환으로 개질 폴리에틸렌 코팅 처리된 강관의 성능 평가를 위한 실험적 연구를 수행하였다. 기존 방식인 기계적 전처리 코팅의 경우 확관시 폴리에틸렌 부착이 저하되는 현상이 발생하여 이를 해결하고자 칼슘 혼입 인산 아연 피막을 활용한 화학적 전처리 공정이 적용되었다. SEM 및 EDX 분석결과, Zn/Ca 비 1.0에서 가장 치밀한 구조가 확인되었다. 또한, 확관 시의 코팅 이탈 방지를 위한 그라프트 처리 무수말레산을 기반으로 엘라스토머, 금속산화물, 블로킹방지제, 슬립제를 각기 다른 조합으로 혼입하여 개질된 폴리에틸렌 코팅 강관에 대한 부착 및 연신율 평가를 실시하였다. 그 결과, 모든 개질 재료를 혼입한 시험체(S4)에서 금속산화물만 혼입한 시험체(S2)대비 25% 이상 향상된 성능을 확인하였다. 마지막으로, 공정이 완료된 코팅 파이프에 대하여 표면부 코팅 손상 방지를 위한 파이프 고정 부속 일부인 쐐기형 소켓링과 이탈 방지 압륜을 개발하고 성능평가를 수행하였다.