• 한국표면공학회지
• /
• 제45권6호
• /
• pp.242-247
• /
• 2012

Yb-doped ITO (ITO:Yb) films were deposited on unheated non-alkali glass substrates by magnetron cosputtering using two cathodes (DC, RF) equipped with the ITO and $Yb_2O_3$ target, respectively. The composition of the ITO:Yb films was controlled by adjusting the RF powers from 0 W to 480 W in 120 W steps with the DC power fixed at 70 W. The ITO:Yb films had a higher crystallization temperature ($200^{\circ}C$) than that of the ITO films ($170^{\circ}C$), which was attributed to both larger ionic radius of $Yb^{3+}$ and higher bond enthalpy of $Yb_2O_3$, compared to ITO. This amorphous ITO:Yb film post-annealed at $170^{\circ}C$ showed a resistivity of $5.52{\times}10^{-4}{\Omega}cm$, indicating that a introduction of Yb increased resistivity of the ITO film. However, these amorphous ITO:Yb films showed a high etching rate, fine pattering property, and a very smooth surface morphology above the crystallization temperature of the amorphous ITO films (about $170^{\circ}C$). The transmittance of all films was >80% in the visible region.

• 한국세라믹학회지
• /
• 제39권8호
• /
• pp.795-800
• /
• 2002

융액인상법으로 질소분위기 하에서 $Yb^{3+}$ 이온이 20at% 고용된 $Yb:YCa_4O(BO_3)_3$ (Yb:YCOB) 단결정을 이리듐 도가니를 사용하여 성장시켰다. 양질의 단결정을 성장시키기 위한 인상속도와 회전속도는 각각 1.5∼2 mm/h와 10∼20 rpm이었다. 분광물성 측정 결과, 흡수단이 236 nm에 있었으며, 전형적인 $Yb^{3+}$ 이온의 흡수 스펙트럼이 관찰되었다. Yb:YCOB의 열팽창계수는 320∼650 K의 측정범위에서 결정학적 축 a, b 그리고 c에 대해 12.1×$10^{-6}$ /K, 5.9${\times}10^{-6}$/K, 12.9${\times}10^{-6}$이었다. 비열은 330 K에서 0.162 $cal/g{\cdot}K$이었다.

• 한국결정성장학회지
• /
• 제4권1호
• /
• pp.57-62
• /
• 1994

FZ법을 이용하여 $YbFeCoO_4$ 단결정을 성장하였다. 결정 성장은 공기분위기 중에서 이루어졌으며, 성장 속도는 1~2mm/hr로 조절하였으며, 성장 초기는 $YbReO_3$와 CoO로 분해 되었으나 용융 후 액상의 조성이 변화됨에 따라 $YbFeCoO_4$ 단일사의 단결정이 육성되었다.결정의 성장 방향은 c축에 수직으로 성장하였으며 다결정의 종자 결정을 이용하여 용이성장축으로 성장된 결정의 성장 방향은[110]방향이었다.

• 한국항해항만학회:학술대회논문집
• /
• 한국항해항만학회 2000년도 추계학술대회논문집
• /
• pp.129-132
• /
• 2000

Perdeuterated hexaflouroacetyIacetonato-ytterbium $[Yb(HFA-D)_3]$ complexes were synthesized by the keto-en01 tautomerism reaction of $Yb(HFA-D)_3$ in methanol-$d_4$ in order to reduce the radiationless transition to the ligands. The luminescence properties of $Yb(HFA-D)_3$ complex were measured in the following anhydrous deuterated organic solvents ; Acetone-$d_6$, Methanol -$d_4$, THF-$d_6$, PO$(OHC_3)_3$ and DMSO-$d_6$. The intensity, lifetime and quantum efficiency of the luminescence in DMSO-$d_6$ were superior to those in other deuterated solvents. It was suggested that the anhydrous DMSO-$d_6$ might be the most appropriate solvent for the liquid laser material of $Yb(HFA-D)_3$ complex.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1997년도 춘계학술대회 논문집
• /
• pp.49-53
• /
• 1997

In this paper, YbBa$_{2}$Cu$_{3}$O$_{x}$ superconductor was sintered by means of conventional solid reaction and the textured YbBa$_{2}$Cu$_{3}$O$_{x}$ was prepared by the Melted-Condensed Process in which SmBa$_{2}$Cu$_{3}$O$_{x}$ crystal was used as seed crystal to introduce the YbBa$_{2}$Cu$_{3}$O$_{x}$ crystal growth. The texture of YbBa$_{2}$Cu$_{3}$O$_{x}$ was examined by X-ray diffraction, and the fracture of YbBa$_{2}$Cu$_{3}$O$_{x}$ sample was observed by SEM, which proved the sample was well oriented. After oxygen absorption of the textured YbBa$_{2}$Cu$_{3}$O$_{x}$ sample, it's critical temperature was measureed to be 86K.eed to be 86K.

• 한국결정학회지
• /
• 제11권3호
• /
• pp.151-156
• /
• 2000

Yb/YAG single crystals were grown from the melt composition of Y/sub 1-x/Yb/sub x/)₃Al/sub 5/O/sub 12/ where x equal to 5, 10, 15, 20, 25, 33, 50, 75 and 100 at % by floating zone method. Optimum growth parameters to get high quality single crystals were 3.5 mm/h of growth rate and 20 rpm of rotation rate under the N₂ atmosphere. After the growth, color of crystals was appeared with pale blue due to the lack of oxygen, but it was disappeared after annealing at 1450℃ for 2 hr. Absorption coefficients were linearly increased depending on the concentration of Yb/sup 3+/ ions. Broad emission band was measured in the range of 1020 to 1050 nm with the peak intensity at 1031 nm and 1051 nm because of ²F/sub 5/2/(1)→²F/sub 7/2/(3) and ²F/sub 5/2/(1)→²F/sub 7/2/(4) transition respectively. When Yb/sup 3+/ ions were substituted with high rates, there were tendency to decrease the measured fluorescent lifetime for Yb ions depending on the concentration of Yb/sup 3+/ ions.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.129-132
• /
• 2000

Perdeuterated hexafluoroacetylacetonato -ytterbium [$Yb (HFA -D)$_3$_3$] complexes were synthesized by the koto-enol tautomerism reaction of $Yb(HFA-H)_3$ in methanol-$d_4$, in order to reduce the radiationless transition to the ligands. The luminescence properties of $Yb(HFA-D)_3$ complex were measured in the following anhydrous deuterated organic solvents : Acetone-$d_6$, Methanol-$d_4$, THF-$d_8$, $PO(OC$H_3$)_3$ and DMSO-$d_6$. The intensity, lifetime and quantum efficiency of the luminescence in DMSO-$d_6$ were superior to those in other deuterated solvents. It was suggested that the anhydrous DMSO-d$_{6}$ might be the most appropriate solvent for the liquid laser material of $Yb(HFA-D)_3$ complex.x.

• 한국광학회:학술대회논문집
• /
• 한국광학회 2000년도 하계학술발표회
• /
• pp.246-247
• /
• 2000

Yb$^{3+}$ 이온은 InGaAs LD 및 Ti:sapphire 레이저로 펌핑할 수 있는 940 nm에서의 흡수대를 가지고 있고, 1.03 $mu extrm{m}$의 형광방출 특성을 가지고 있으며, 지금까지 알려진 1 $\mu\textrm{m}$ 파장대의 레이저 활성이온 중에서 가장 적게 열을 발생하는 특성을 가지고 있음이 알려져 최근에는 Yb$^{3+}$ 이온을 첨가한 여러 가지 레이저 매질이 연구되고 있다.[1] 그 중에서도 Yb$^{3+}$ ion doped yttrium aluminum garnet (Yb:YAG) 단결정은 충분하게 넓은 흡수선폭, 좋은 열광학적 특성, 고출력 작동을 하게 하는 stokes shift, 그리고 LD에 의한 펌핑을 가능하게 하는 940 nm 영역에서의 흡수 및 긴 여기시간을 가진 이상적인 매질로 알려져 있다.[2] 이러한 특성으로 인해 Yb:YAG 단결정은 femtosecond 레이저 등 각종 레이저 시스템의 소형화[3]를 가져왔으며, 레이저 결정의 양산 가능성 및 레이저 기기의 소형화에 따르는 시스템의 가격 감소가 가능하므로 Yb:YAG microchip 레이저는 향후 고출력 레이저 기기 산업의 중추가 될 것으로 기대된다. (중략)

• 공업화학
• /
• 제26권3호
• /
• pp.319-325
• /
• 2015

분무열분해법을 이용하여 서브 미크론 크기의 $CeO_2:Er^{3+}/Yb^{3+}$ 상향 변환 형광체 입자를 합성하고 $Er^{3+}$ 및 $Yb^{3+}$ 농도 변화에 따른 발광특성을 조사하였다. 합성한 $CeO_2:Er^{3+}/Yb^{3+}$는 $Er^{3+}$ 활성이온의 $^4S_{3/2}/^2H_{11/2}{\rightarrow}^4I_{15/2}$ 및 $^4F_{9/2}{\rightarrow}^4I_{15/2}$ 전이에 기인한 강한 녹색 및 적색 발광을 보였다. 가장 높은 발광을 보이는 활성제 농도는 Er = 1.0% 그리고 Yb = 2.0%이며, 농도소광 현상은 쌍극자-쌍극자 상호작용을 통해 일어남이 확인되었다. 레이저 다이오드 여기 광 세기에 대한 발광강도 의존성을 활성이온 농도에 따라 조사하였고, 발광 중간 에너지 레벨의 주 소멸과정을 고려하여 발광 메커니즘을 조사하였다. $Yb^{3+}$에서 $Er^{3+}$으로 에너지 전달은 바닥 상태 흡수(ground state absorption, GSA)에 기여하고, $Yb^{3+}$ 도핑은 $^4I_{11/2}{\rightarrow}^4I_{13/2}$ 전이를 가속화시켜 적색/녹색 발광세기 비를 상승시킨다. 최종적으로 분무열분해법으로 제조된 $CeO_2:Er^{3+}/Yb^{3+}$ 형광체의 발광은 선형 감쇠가 중간 에너지 레벨의 고갈을 지배하는 2 광자 프로세스에 의해 일어남을 확인하였다.

• 대한핵의학회지
• /
• 제22권1호
• /
• pp.77-81
• /
• 1988

Tumor localizing properties of $^{67}Ga$ citrate and $^{169}Yb$ citrate were studies with sarcoma 180 bearing mice. To compare precisely the accumulation of $^{67}Ga$ citrate and $^{169}Yb$ citrate in tumor tissue itself, $^{67}Ga$ and l63yb were administered simultaneously as a mixture of same chemical form of citrate. The yield of $^{169}Yb$ labeled citrated and the of radiopharmaceuticals purity was identified more than 90% by chromatography on silica gel plates. $^{67}Ga$ and $^{169}Yb$ were injected into mice and the mice were killed at 3, 24, and 48 hours following intraperitoneal injection of the radiopharmaceuticals. The retention value of $^{67}Ga$ and $^{169}Yb$ in tumor was similar but they differ from each other markedly in normal tissue distribution. $^{169}Yb$ citrate is cleared up from blood more rapidly than $^{67}Ga$ citrate, and a high tumor to blood ratio is achieved shortly after injection.