• Progress in Superconductivity and Cryogenics
• /
• v.10 no.1
• /
• pp.6-9
• /
• 2008

We have investigated the MOD process successfully for the fabrication of the YBCO thick film on the $LaAlO_3$(001) single crystalline substrate. The cracking problem in YBCO thick film, a serious problem in the conventional TFA-MOD method, could be overcome with a careful control of precursor materials. Thus coating solution was prepared for the YBCO thick film by using fluorine-free precursor material. The precursor solutions were coated on the LAO(001) single crystalline substrate using the dip coating method, calcined at the temperature up to $500^{\circ}C$, and fired at various high temperatures for 2 h in a reduced oxygen atmosphere. Optimally processed YBCO thick film exhibited high critical current($I_c$) over 200 A/cm-width at 77K in self-field.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.1
• /
• pp.32-36
• /
• 2017

The Ag thin film of YBCO (yttrium barium copper oxide) CC (coated conductor) protect the YBCO layer and, at the same time, affects the electrical characteristics of the YBCO CC. Therefore, YBCO CC with the commercialization of the Ag thin film layers makes it easy to establish a process, it can lead to a variety of characteristic changes in YBCO CC. In this paper, plasma surface treatment was carried out to facilitate the deposition of the Ag thin film and the deposition process of YBCO CC. Surface roughness from the test results was increased as the time of the plasma surface treatment increased from 5 to 20 minutes. On the other hand, the surface roughness was decreased for the time of the plasma surface treatment over 20 minutes. Furthermore, after depositing, the increasing of deposit amount and reduced lifting phenomenon showed a similar tendency with the rise time of surface roughness.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.4
• /
• pp.5-8
• /
• 2004

A low cost MOD processing using YBCO oxide powder as a starting precursor was employed for fabrication of YBCO thin films. YBCO oxide is advantageous over metal acetates or TFA salts which are popular starting precursors for conventional MOD-TFA process. YBCO thin films were prepared by oxide-precursor-based MOD process and annealing condition was optimized. The YBCO thin film annealed at 78$0^{\circ}C$ shows no transport $I_c$ and poor microstructure. However, the YBCO thin film annealed at higher temperature shows improvement in microstructure and current transport property. In order to improve critical current, YBCO thin film was prepared by double coating method. YBCO thin film prepared with double coating approach shows enhanced superconducting performance ($I_c$>100A/cm-w).

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.27-32
• /
• 2006

[$YBa_2Cu_3O_{7-x}$] thin films were deposited on various buffered-templates by a metal organic chemical vapor deposition(MOCVD). Three different templates of $CeO_2/YSZ/CeO_2/pure-Ni(CYC),\;CeO_2/YSZ/Y_2O_3/Ni-3at.%W(YYC)$ and $CeO_2/IBAD-YSZ$/stainless steel were used. The Ni and Ni-W alloy tapes were biaxially textured by cold rolling and annealing heat treatment. The dense YBCO films were grown on both the IBAD and YYC templates with no microcrack, while the YBCO films on the CYC templates were grown with the formation of microcracks and NiO. The YBCO film on the YYC template showed the higher $I_c$ than that on CYC template. Especially, the IBAD templates with a thin $CeO_2$(type I) and thick $CeO_2$(type II) top layer were used to compare the deposition nature of the YBCO on them. Comparing the current property of the YBCO films on IBAD templates, the YBCO film deposited on thick $CeO_2$ layer was better than the film on thin $CeO_2$ layer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.617-619
• /
• 2001

The effect of the superconducting film thickness on the substrate temperature has been investigated. Superconducting YBCO thin films have been grown on MgO substrates by pulsed laser deposition. The dependence of the orientation of YBCO film on thickness has been investigated by X-ray diffraction technique. X-ray diffraction indicated that the film orientation was changed by increasing the film thickness and by changing the substrate temperature.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.3
• /
• pp.6-11
• /
• 2004

YBa$_2$Cu$_3$$O_{7-x}$ (YBCO) films were deposited on MgO(100) and SrTiO$_3$(100) single crystal substrates by cold-wall type MOCVD method using continuous source supplying system. Under the deposition temperature of 740∼76$0^{\circ}C$, c-axis oriented YBCO films were obtained. In case of the YBCO films deposited on MgO (100) single crystal substrate, the critical temperature (T$_{c}$) was under 81 K regardless of the deposition conditions, whereas T$_{c}$ of the YBCO films deposited on SrTiO$_3$(100) single crystal substrate was 83∼84 K. The critical current (I$_{c}$) of the YBCO film deposited on SrTiO$_3$(100) single crystal substrate for 30 min was 49 A/cm-width and the critical current density (J$_{c}$) was 0.82 MA/$\textrm{cm}^2$ to film thickness of 0.6 ${\mu}{\textrm}{m}$. I$_{c}$ increased to 84.4 A/cm-width as the deposition time increased to 50 min, but J$_{c}$ decreased to 0.53 MA/$\textrm{cm}^2$ to film thickness of 1.8 ${\mu}{\textrm}{m}$.rm}{m}$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.11
• /
• pp.959-962
• /
• 2000

We have fabricated good quality superconducting YBa$_2$Cu$_3$$O_{7-x}$(YBCO) thin films on Hastelloy(Ni-Cr-Mo alloys) metallic substrates with CeO$_2$and BaTiO$_3$buffer layers in-situ by pulsed laser deposition in a multi-target processing chamber. YBCO film with CeO$_2$single buffer layer shows T$_{c}$ of 71.64 K and the grain size less than 0.1${\mu}{\textrm}{m}$. When BaTiO$_3$ is used as a single buffer layer, the grain size of YBCO is observed to be larger than that of YBCO/CeO$_2$by 200 times and the transition temperature of the film is enhanced to be about 84 K. CeO$_2$/BaTiO$_3$double buffer layer has been adopted to enhance the superconducting properties, which results in the enhancement of the critical temperature and the critical current density to be about 85 K and 8.4$\times$10$^4$ A/$\textrm{cm}^2$ at 77 K, respectively mainly due to the enlargement of the grain size of YBCO film.ilm.

• Progress in Superconductivity and Cryogenics
• /
• v.15 no.4
• /
• pp.15-20
• /
• 2013

We investigated the flux pinning properties of both 10 mol% Zr-and Sn-doped $YBa_2Cu_3O_{7-{\delta}}$ (YBCO) films with the same thickness of ~350 nm for a comparative purpose. The films were prepared on the $SrTiO_3$ (STO) single crystal substrate by the metal-organic deposition (MOD) process. Compared with Sn-doped YBCO film, Zr-doped one exhibited a significant enhancement in the critical current density ($J_c$) and pinning force density ($F_p$). The anisotropic $J_{c,min}/J_{c,max}$ ratio in the field-angle dependence of $J_c$ at 77 K for 1 T was also improved from 0.23 for Sn-doped YBCO to 0.39 for Zr-doped YBCO. Thus, the highest magnetic $J_c$ values of 9.0 and $2.9MA/cm^2$ with the maximum $F_p$ ($F_{p,max}$) values of 19 and $5GN/m^3$ at 65 and 77 K for H // c, respectively, could be achieved from Zr-doped YBCO film. The stronger pinning effect in Zr-doped YBCO film is attributable to smaller $BaZrO_3$ (BZO) nanoparticles (the average size ${\approx}28.4$ nm) than $YBa_2SnO_{5.5}$ (YBSO) nanoparticles (the average size ${\approx}45.0$ nm) incorporated in Sn-doped YBCO film since smaller nanoparticles can generate more defects acting as effective flux pinning sites due to larger incoherent interfacial area for the same doping concentration.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2002.02a
• /
• pp.219-220
• /
• 2002

In this paper, we propose non-soldered current lead was introduced which has low contact resistivity for fault current limiters of YBCO film. Carbon/Cu has good thermal conductivity, electrical conductivity and chemically stable, and so forth. Therefore it seems to be suitable material of current lead for current limiters of YBCO film. We have investigated electric field-current in field of 0-130 mT and quench characteristics of a YBCO film. Experimental results show that characteristics of transport is all right using Carbon/Cu-current lead.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.6
• /
• pp.539-542
• /
• 2002

The effect of the superconducting film thickness on the surface resistance has been investigated. Superconducting YBCO thin films have been grown on MgO substrates by pulsed laser deposition. The dependence of the orientation of YBCO film on thickness has been investigated by X-ray diffraction technique. X-ray diffraction indicated that the film orientation was changed by increasing the film thickness and by changing the substrate temperature. The microwave properties of the films with mixed orientations of a-axis and c-axis will be reported for the applications of microwave devices.