• Progress in Superconductivity
• /
• 제7권2호
• /
• pp.158-161
• /
• 2006

Superconducting YBCO films were successfully fabricated by MOD process using chemically modified precursor solution. In this study, a chemically modified precursor solution for MOD processing was synthesized using metal-organic salts and organic additives. It was shown that crack-free and uniform precursor films were formed after calcination in humidified Oxygen atmosphere. Less than 3 hours are required to finish the calcination process. XRD measurement shows that $BaF_2,\;CuO,\;Y_2O_3$ are major constituent of precursor films. Furthermore, YBCO films without any secondary phases were successfully fabricated after annealing in wet $Ar/O_2$ atmosphere. The YBCO film prepared on a $LaAlO_3$ single crystal substrate ($10mm{\times}10mm$) gives transport $I_c$ of 10A at 77K. This chemical modification approach is a possible candidate for improving MOD-processing of YBCO coated conductor.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 제37회 하계학술대회 논문집 B
• /
• pp.693-694
• /
• 2006

In order to develop a high temperature superconducting(HTS) coil for the fault current limiter(FCL), the over-current characteristics in YBCO coated conductor(CC) with Ni-W alloy substrate are analyzed. The HTS wire is wound by bifilar winding method for resistive current limitation and it is operated in 65K sub-cooled nitrogen. In order to analyze the resistance and the temperature characteristics of the CC wire, an analysis program is developed considering all the composition materials except the buffer layer. Using this program, the temperature rise, the resistance development and the current limitation of CC are calculated depending on the applied voltage and the stabilizer materials. According to the analysis results, under the temperature restriction of 300K, the maximum voltage per meter is determined as 40V/m if the stabilizer is $25{\mu}m$ thick stainless steel at each side. Finally, the wire length needed for the distribution level HTS FCL is estimated.

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2003년도 추계학술대회 논문집
• /
• pp.106-108
• /
• 2003

We fabricated Ni and Ni-W alloys for use as a substrate in YBCO coated conductor applications and evaluated the effect of W in Ni on texture, microstructure and surface morphology, and hardness of substrate. Pure Ni, Ni-2 at.％W, and Ni-5at.％W alloy substrates were prepared by plasma arc melting, cold rolling, and the recrystallization heat treatment at various temperature (700- 130$0^{\circ}C$). It was observed that Ni-W alloy substrates had stronger cube texture and maintained it at higher annealing temperature, compared to pure Ni substrate : The full-width at half- maximums of in-plane texture was 13.40$^{\circ}$ for Ni substrate and 4.42$^{\circ}$-5.57$^{\circ}$ for Ni-W substrate annealed at 100$0^{\circ}C$. In addition, it was observed that the Ni-W substrate had smaller grain size, shallower boundary depth, and higher hardness, compared to those of pure Ni substrate.

• 한국전기전자재료학회논문지
• /
• 제28권10호
• /
• pp.625-629
• /
• 2015

The second-generation HTS wire its YBCO coated conductor is widely used in the superconducting power apparatus. The YBCO coated conductor uses the normal-superconducting junction to increase the transport capacity of superconducting power apparatus when it is applied. The normal-superconducting junction can be a cause of reducing the stability of the superconducting power apparatus when a fault current is applied. Thus, in this study we have conducted the effect analysing normal-superconducting junction for the fault current using transport current and quench resistance. From the experimental results when a fault current is applied, the effect on the normal-superconducting junction is reduced the larger the amplitude of the fault current and is helpful to maintain the thermal stability of the HTS wire.

• Transactions on Electrical and Electronic Materials
• /
• 제10권2호
• /
• pp.62-65
• /
• 2009

YBCO-coated conductors, called "second-generation wires," show a remarkably greater increase in the amount or speed of their resistance than BSCCO wires when a quench occurs. This is probably because of the specific resistance at their stabilizer layer, which also affects their voltage grade. YBCO coated conductors with copper as a stabilizer layer have a voltage grade of 1.5-2 V/cm, and those with stainless steel as a stabilizer layer have a voltage grade of about 0.5-0.6 V/cm. The voltage grade of YBCO coated conductors is important in selecting and applying superconducting wires to power instruments later. In this study, two kinds of YBCO-coated conductors with different stabilizer layers and one kind of BSCCO wire were prepared. Among them, based on the YBCO coated conductors that had a stainless steel stabilizer layer with a low voltage grade, five kinds of experimental samples for joining were prepared with the remaining two kinds of wires. Using the prepared samples, the current application properties and the resistance increase in the flux-flow and the quench states of the single wire and the joined wires were compared.

• Progress in Superconductivity
• /
• 제11권2호
• /
• pp.128-134
• /
• 2010

The magnetic flux profiles in SmBCO and YBCO coated conductors(CC) in the presence of the external field were comparatively investigated by magneto-optic image and scanning hall probe measurements. The current distributions calculated by using the inversion method from measured field profiles show that the decrease of current densities near the edges of SmBCO CC is more significant than those of YBCO CC. Through the comparison of the numerical analysis based on Kim's critical state model and the Brandt and Indenbom's solution, we found that this feature is related to their different field dependant properties of the critical current densities.

• 한국초전도ㆍ저온공학회논문지
• /
• 제11권3호
• /
• pp.40-45
• /
• 2009

Many superconductor applications such as MRI and SMES must be operated in persistent current mode to eliminate the electrical ohmic loss. This paper presents the characteristic analysis of the high temperature superconducting (HTS) power supply made of YBCO coated conductor (CC). In this research, we have manufactured the HTS power supply to charge the 0.73 mH HTS double-pancake magnet made of YBCO CC. Among the all design parameters, the heater triggerring time and magnet applying time were the most important factors for the best performance of the HTS power supply. In this paper, three-dimensional simulation through finite element method (FEM) was used to study the heat transfer in YBCO CC and the magnetic field of the magnetic circuit. Based upon these results, the final operational sequence could be determined to generate the pumping current. In the experiment, the maximum pumping current reached about 16 A.

• 한국전기전자재료학회논문지
• /
• 제17권1호
• /
• pp.94-100
• /
• 2004

We fabricated textured Ag substrates for YBCO coated conductor and evaluated the effects of annealing temperature on microstructural evolution, texture formation, and surface morphology. Ag ingot, as an initial specimen, was prepared by plasma arc melting(PAM). Subsequently, the ingot was cold rolled to 100 ${\mu}{\textrm}{m}$ thick tape and annealed at temperatures of 600-80$0^{\circ}C$. The texture and surface morphology of the substrate were characterized by pole-figure and atomic force microscopy(AFM) profile, respectively. It was observed that a strong ｛110｝<110> texture was formed after annealing and its symmetry improved as annealing temperature increased. The full-width at half-maximum(FWHM) of ｛110｝<110> pole was as sharp as 10$^{\circ}$ for the substrate annealed at 80$0^{\circ}C$. On the other hand, it was found that the thermal grooving and faceting became remarkable as annealing temperature increased : root-mean-square(RMS) roughness of the substrate annealed at 80$0^{\circ}C$ was 39.2 nm. The substrate of strong texture and smooth surface, fabricated in our study, is considered to be suitable for use as a substrate for the epitaxial deposition of superconductor film.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2005년도 제36회 하계학술대회 논문집 B
• /
• pp.1285-1287
• /
• 2005

고온초전도 선재 중에서 YBCO 박막을 금속테이프에 증착하여 제조되는 coated conductor는 높은 자기장에서도 임계전류밀도의 감소가 크지 않아 고자장용 초전도 자석을 제조하는데 많이 활용될 것으로 기대되고 있다. coated conductor를 고자장용 초전도 자석제작에 활용하기 위해서는 긴 길이의 도체를 제조하는 것과 함께, 도체의 접합기술이 필요하다. 이는 초전도 자석을 영구전류모드로 운전하기 위해서는 도체의 접촉저항이 충분히 적어야 하기 때문이다. 그러나 박막형 coated conductor는 아직 긴 길이의 선재제조기술이 확립되어 있지 않고, 또 박막형 coated conductor의 형태와 사용되는 제조기술이 본질적으로 초전도 접합을 형성시키기에 매우 어려워서 아직 까지 초전도 접합에 대한 연구결과가 발표되지 않고 있으며, 접합 특성을 측정하는 기술도 개발되지 않았다. 본 연구에서는 coated conductor의 접합특성을 측정하기 위한 기본적인 시험방법을 제안하고, 전도성 금속접합재를 이용한 접합시료를 제작하여 그 특성을 평가한 결과를 발표한다.

• 전기학회논문지
• /
• 제56권2호
• /
• pp.282-288
• /
• 2007

Magnetization loss of high temperature superconductoring BSCCO tape and YBCO coated conductor(YBCOCC) is most important issue in the development of superconducting power devices. In this paper, the measured results of magnetization losses under various angles of external magnetic field in BSCCO tape stacked conductors and YBCO CC stacked conductors are presented and compared with each other. Also, we present the compared results of magnetization losses measured at arbitrary reaction magnetic fields and analyzed with perpendicular magnetic field components of those. The results show that magnetization losses of YBCO CC single and stacked conductors agree well with the analyzed value by it's perpendicular magnetic field component, but BSCCO single and stacked conductors are not.