• Journal of Korean Society of Steel Construction
• /
• v.14 no.5 s.60
• /
• pp.647-656
• /
• 2002

High-strength steel in steel bridges is the key to achieving cost-efficiency because it facilitates lightweight construction and rationalizes structure. The future of high-strength steel is bright, with its use projected to expand. As such, it is necessary to evaluate precisely various factors affecting the process of fabricating high-strength steel, i.e., welding heat, strain hardening, and weldability and performance of the welded joints. This study therefore performed the maximum hardness test and y-groove weld crack test using welding processes such as SAW, FCAW, and GMAW, in order to investigate the welding performance and characteristics of welded Joints or high-strength steel produced in Korea such as SM570, POSTEN60, and POSTEN80. In addition, a series of welding tests was carried out to estimate the tensile strength, bending characteristics, absorbed energy, and hardness in welded joints.

• Journal of Korean Society of Steel Construction
• /
• v.12 no.3 s.46
• /
• pp.231-238
• /
• 2000

There was extreme improvement in the processing result of weld toe, but there is possibility that the fatigue failure occurs from the weld root part where the fatigue strength became low relatively. This study did the fatigue test at the cross rib specimens which implemented a partial penetration weld to improve the fatigue strength of the weld root part. As a result of the fatigue test of the partial penetration weld and the fillet weld specimens, almost the same fatigue strength appeared. Because the fatigue failure began from toe, there was not a reinforcement effect in the weld root part by the partial penetration weld. So, it examined fatigue strength at the partial penetration welding specimens which processed toe to stop the fatigue failure of toe part. As a result, there was big fatigue strength improvement from the partial penetration weld than the fillet weld. Therefore, if fatigue crack occurrence can be restrained from toe, it thinks that the fatigue strength of the root part can improve by the partial penetration weld, after all, it thinks that the overall fatigue life can improve.

• 대한공업교육학회지
• /
• v.31 no.1
• /
• pp.200-210
• /
• 2006

This C-ring test, normally employed for evaluating susceptibility to stress-corrosion cracking, was determined to be a suitable small scale test to evaluate PWHT(Post-Weld Heat Treatment) cracking susceptibility. This test is possible to incorporate an actual weld, to introduce a notch into the coarse grained HAZ(Heat Affected Zone), to load the coarse grained HAZ any level of stress ad, most importantly, since the C-ring is an approximately constant strain type test, the stress decreases with time at temperature in a manner similar to that of an actual steel weldment. The procedure employed in making the C-ring was presented in the experimental procedure section, however, several points deserve further discussion. The walls of the weld groove are made along radial lines form the center of th var in order to obtain an HAZ which is oriented perpendicular to the walls of the machined C-ring. Therefore, the plane of maximum stress will be aligned through the HAZ and, therefore, crack propagation will not be forced to deviate form the plane of maximum stress in order to remain in the coarse grained HAZ as is the case with the Y groove test.

• Journal of Power System Engineering
• /
• v.11 no.3
• /
• pp.41-46
• /
• 2007

The microstructure and electrochemical analysis of welds of electric resistance welding(ERW) pipe were investigated. The direction of metal flow line in HAZ of ERW pipe shifted to the inner(or outer) surface of pipe by plastic deformation during welding. The lowest heat input welds of ERW pipe was showed crack by liquid penetrant testing. Accelerated corrosion test by constant current density of 20mA/$cm^{2}$ developed groove at the welds of ERW pipe and the measured grooving factors were about $1.2{\sim}1.5$. Corrosion potential of base metal obtained by cyclic polarization in artificial sea water(3.5wt.% NaCl solution) was 100mV higher than that of weld metal of ERW pipe.

• Journal of Korean Society of Steel Construction
• /
• v.24 no.1
• /
• pp.129-136
• /
• 2012

This study seeks to evaluate the welding characteristics of SHN400 steel, which is suitable for the steel material used in building structures in KS. For this purpose, the Y-groove weld crack test and hardness, tensile, bending, cross tensile, and charpy V notch tests at the welding point were conducted with specimens taken from the highest, the thickest and the commonly used H-beams for girder or beam members. Each test was conducted under the KS test conditions. All tests results satisfied the requirements of KS and the welding requirements for the proper inelastic behavior of structure, indicating that SHN400 can be used for the building structure as a structural material.

• Journal of the Korean Institute of Gas
• /
• v.2 no.1
• /
• pp.7-13
• /
• 1998

In this study, for the safety performance of LNG storage tank, the fracture toughness in X-grooved weld HAZ(heat-affected zone) of $9\%$ Ni steel was evaluated qualitatively and quantitatively, and the relation with the change in microstructure was analyzed. The toughness assessment was peformed through the modified CTOD test proposed for thick weldment with X-groove. Additionally, microstructures of HAZ were evaluated by OM, SEM and XRD. From the results, HAZ toughness of SMA(shielded metal arc)-welded $9\%$ Ni steel decreased as the evaluated region approached the fusion line. The decrease in toughness was apparently caused by the increase in the fraction of coarse-grained zone within HAZ. On the other hand, toughness drop with decreasing test temperature in F.L.(fusion line) ${\~}$F.L.+3mm was larger than that in F.L.+5mm${\~}$F.L.+7mm region due to the fact that in the former regions, retained austenite had poor stability.