• Korean Journal of Materials Research
• /
• v.11 no.8
• /
• pp.664-664
• /
• 2001

The mechanical alloying (MA) effect in $\sigma$-VFe intermetallic compound was studied by neutron and X-ray diffraction. The structure of MA $\sigma$-VFe powders were characterized by the X- ray diffraction with Cu- $K\alpha$ radiation and neutron diffraction with monochromatic neutrons of $1.835\AA$ using a high resolution powder diffractometer (HRPD). Mechanical alloying of $\sigma$-VFe compound gives rise to a dramatic structural change. After 60 hours of MA, the Fe-Fe distribution of the $\sigma$- phase VFe tetragonal structure with 30 atoms in a unit cell is found to change into that of the $\sigma$-(V,Fe) solid solution with bcc structure, which is a stable phase at elevated temperature above $1200^{\circ}C$. A comparison of X-ray diffraction data for the $\alpha$-phase has been also made with the corresponding neutron diffraction data. The (101) and (111) diffraction peaks of the $\sigma$-phase was clearly observed only in neutron diffraction pattern, which is believed to be a characteristic feature due to the chemical atomic ordering of $\sigma$- VFe phase.

• Journal of dental hygiene science
• /
• v.22 no.3
• /
• pp.191-198
• /
• 2022

Background: The purpose of this study was to evaluate the composition of the crystal phases of various calcium silicate-based materials (CSMs): ProRoot white MTA^Ⓡ (mineral trioxide aggregate) (WMTA), Ortho MTA^Ⓡ (OM), Endocem MTA^Ⓡ (EM), Retro MTA^Ⓡ (RM), Endocem Zr^Ⓡ (EN-Z), Biodentine^TM (BD), EZ-seal^TM (EZ), and OrthoMTA III (OM3). Methods: In a sample holder, 5 g of the powder sample was placed and the top surface of the material was packed flat using a sterilized glass slide. The prepared slides were mounted on an X-ray diffraction (XRD) instrument (D8 Advance; Bruker AXS GmbH, Germany). The X-ray beam 2θ angle range was set at 10~90° and scanned at 1.2° per minute. The Cu X-ray source set to operate at 40 kV and 40 mA in the continuous mode. The peaks in the diffraction pattern of each sample were analyzed using the software Diffrac (version 2.1). Then, the peaks were compared and matched with those of standard materials in the corresponding Powder Diffraction File (PDF-2, JCPDS International Center for Diffraction Data). A powder samples of the materials were analyzed using XRD and the peaks in diffraction pattern were compared to the Powder Diffraction File data. Results: Eight CSMs showed a similar diffraction pattern because their main component was calcium silicate. Eight CSMs showed similar diffraction peaks because calcium silicate was their main component. Two components were observed to have been added as radiopacifiers: bismuth oxide was detected in WMTA, OM, and EM while zirconium oxide was detected in RM, EN-Z, BD, EZ, and OM3. Unusual patterns were detected for the new material, OM3, which had strong peaks at low angles. Conclusion: It was caused by the presence of Brushite, which is believed to have resulted in crystal growth in a particular direction for a specific purpose.

• YAKHAK HOEJI
• /
• v.8 no.2
• /
• pp.37-44
• /
• 1964

The relationships involving acid-consuming capacity and X-ray powder diffraction patterns of aluminum hydroxide gel were studied. The aging of antacid efficacy of aluminum hydroxide gel has also been characterized by using X-ray powder diffraction. The acid-consuming capacity decreased with progress of crystallization from amorphous alumino gel, and it was found that aged product at 80.deg. C had crystal structure of bohmite (.alpha.-Al.sub 2/O$_{2}$(OH)$_{2}$). It was also noted that the rate of aging decreased with decreasing pH of aluminum hydroxide gel.

• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1075-1079
• /
• 1999

LaSrCoO3 thin films were spin-coated onto the SrTiO3(100) substrates by the chemical solution process. X-ray diffraction $\theta$-2$\theta$ scans and X-ray diffraction $\beta$ scans were used to determine the crystallinity and in -plane alignment behavior of the films. The X-ray diffraction pattern showed the film obtained by annealing at 80$0^{\circ}C$ was highly oriented. The X-ray diffraction pole-figure analysis and reciprocal-space mapping (2$\theta$-$\Delta$$\omega$ scans) of the resulting film showed that the film comprising the pseduocubic phase had an epitaxial relationship with the SriO3 substrate.

• Tribology and Lubricants
• /
• v.20 no.1
• /
• pp.7-13
• /
• 2004

High strength steels are widely used as tribo-materials in the field. Previous study revealed that for mild steel, the states of strain on the worn surface measured by X-ray diffraction has a good relationship with the state of wear. The objective of this study is to identify the relationship between the state of strain on the worn surface and the state of wear in high strength steels. Sliding wear tests were carried out using several hardened steels. X-ray diffraction tests were conducted to analyze the state of strain on the worn surface during wear. The experimental results indicated that the state of strain on worn surface in the hardened steel shows the same tendency as in the mild steel. It is clear that change of half value width on the worn surface as a function of sliding speeds is broadly similar in shape to wear characteristics curve and its magnitude has a good relationship with the wear rate at two different wear modes in the hardened steel.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.73-75
• /
• 2005

The objective of this study is to estimate the feasibility of X-ray diffraction method application for fatigue life assessment of the high-temperature pipeline steel such as main steam pipe, reheater pipe and header etc. in power plant. In this study, X-ray diffraction tests using various types of specimen simulated low cycle fatigue damage were performed in order to analyze fatigue properties when fatigue damage conditions become various stages such as 1/4, 1/2 and 3/4 of fatigue life, respectively. As a result of X-ray diffraction tests for specimens simulated fatigue damages, we conformed that the variation of the full width at half maximum intensity decreased in proportion to the increase of fatigue life ratio.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.347-350
• /
• 1998

We studied relation of X-ray diffraction and charge/discharge capacity of LiMn$_2$O$_4$ cathode. LiMn$_2$O$_4$ is prepared by reacting stoichiometric mixture of LiOH.$H_2O$ and MnO$_2$ (mole ratio 1 : 2) and heating at $700^{\circ}C$, 80$0^{\circ}C$ for 24hr, 36hr, 48hr, 60hr and 72hr. Through X-ray diffraction pattern, it is analyzed that crystal structure and lattice parameter and peak ratio so on. We obtained X-ray diffraction pattern that varied lattice parameter and peak intensity by function of calcining temperature and time. Cathode active materials calcined at 80$0^{\circ}C$ for 36hr shown that (111)/(311) Peak ratio at X-ray diffraction pattern was 0.37. It means that crystal structure is formed very well in this temperature and time. In the result of charge/discharge test, cathode active material calcined at 80$0^{\circ}C$ for 36hr displayed excellent charge/discharge properties than that of cathode active materials calcined at other temperature and title. In this study, we certified that spinel structure basied cubic is formed very well at 80$0^{\circ}C$ for 36hr. In this case, (111)/(311) peak ratio at X-ray diffraction is 0.37, and charge/discharge properties is excellent than others.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.9
• /
• pp.1588-1590
• /
• 2007

• Environmental Engineering Research
• /
• v.9 no.3
• /
• pp.103-112
• /
• 2004

• Analytical Science and Technology
• /
• v.19 no.5
• /
• pp.407-414
• /
• 2006

An X-ray diffractometer for spatially resolved X-ray diffraction measurements was developed to identify phase in the narrow (micron-scaled) region of high burn-up fuels and some nuclear materials. The micro-XRD was composed of an X-ray microbeam alignment system and a sample micro translation system instead of a normal slit and a fixed sample stage in a commercial XRD. The X-ray microbeam alignment system was fabricated with a microbeam concentrator having two Ni deposited mirrors, a vertical positioner, and a tilt table for the generation of a concentrated microbeam. The sample micro translation system was made with a sample holder and a horizontal translator, allowing movement of a specimen at $5{\mu}m$ steps. The angular intensity profile of the microbeam generated through a concentrator was symmetric and not distorted. The size of the microbeam was $4,000{\times}20{\mu}m$ and the spatial resolution of the beam was $47{\mu}m$ at the sample position. When the diffraction peaks were measured for a $UO_2$ pellet specimen by this system, the reproducibility ($2{\Theta}={\pm}0.01^{\circ}$) of the peaks was as good as a conventional X-ray diffractometer. For the cross section of oxidized titanium metal, not only $TiO_2$ in an outer layer but also TiO near an oxide-metal interface was observed.