Al-doped ZnO (AZO) thin films were grown on glass substrates by radio-frequency magnetron sputtering. The effects of oxygen flow ratio, which was used for a sputtering gas, on the AZO thin films were investigated by using the X-ray diffraction (XRD), atomic force microscopy (AFM), and Hall effects measurement. The AZO thin film, deposited with oxygen flow ratio of 0% at the growth temperature of $400^{\circ}C$, showed a strongly c-axis preferred orientation and the lowest resistivity of $6.9{\times}10^{-4}{\Omega}cm$. The ZnO (002) diffraction peak indicated a tendency to decrease substantially with increasing the oxygen flow ratio. Furthermore, as the oxygen flow ratio was decreased, the carrier concentration and the hall mobility were increased, but the electrical resistivity was decreased.
Turquoise blue pigment of Vanadium-zircon blue (DCMA number 14-42-2), which was already commercialized, was stable to be reproduced but insufficient to give strong blue. However, it possible to obtain more intense blue by partially substituting cobalt ions into the willemite($Zn_2SiO_4$) lattice classified into DCMA number 7-10-2 for blue ceramic pigment. By the composition of willemite $Co_xZn_{2-x}SiO_4$(X=0.01, 0.03, 0.05, 0.07, 0.09 mole), this study used reagent grade zinc oxide, cobalt oxide and silicon dioxide as starting materials, carrying out the synthesis with solid reaction method by adding $H_3BO_3$ as a mineralizer. The firing temperature was between $1200^{\circ}C$ and $1400^{\circ}C$. The characteristics of synthesized pigment were analyzed by X-ray diffraction, Raman spectroscopy and SEM and the characteristics of color tones were analyzed by UV-Vis spectroscopy and CIE-$L^*a^*b^*$ measurement. As a result, the optimal composition was $Zn_{1.95}Co_{0.05}$ with 1wt% of $H_3BO_3$ as a mineralizer and firing condition was $1350^{\circ}C$/3 h. $L^*a^*b^*$ value was 29.25, 41.03, -59.93 for on glaze pigment and 37.03, 36.41, -60.03 for under glaze pigment.
Proceedings of the Korean Vacuum Society Conference
/
2013.02a
/
pp.313-313
/
2013
For high-performance TFT (Thin film transistor), poly-crystalline semiconductor thin film with low resistivity and high hall carrier mobility is necessary. But, conventional SPC (Solid phase crystallization) process has disadvantages in fabrication such as long annealing time in high temperature or using very expensive Excimer laser. On the contrary, MIC (Metal-induced crystallization) process enables semiconductor thin film crystallization at lower temperature in short annealing time. But, it has been known that the poly-crystalline semiconductor thin film fabricated by MIC methods, has low hall mobility due to the residual metals after crystallization process. In this study, Ni metal was shallow implanted using PIII&D (Plasma Immersion Ion Implantation & Deposition) technique instead of depositing Ni layer to reduce the Ni contamination after annealing. In addition, the effect of external magnetic field during annealing was studied to enhance the amorphous silicon thin film crystallization process. Various thin film analytical techniques such as XRD (X-Ray Diffraction), Raman spectroscopy, and XPS (X-ray Photoelectron Spectroscopy), Hall mobility measurement system were used to investigate the structure and composition of silicon thin film samples.
Proceedings of the Korean Institute of Surface Engineering Conference
/
2001.06a
/
pp.14-14
/
2001
Nitride films such as TiN, CrN etc. deposited on glass by PVD processes have been developed for many industrial applications. These nitride films deposited on glass were widely used for not only decorative and optical coatings but also wear and corrosion resistance coatings employed as dies and molds made of glass for the example of lens forming molds. However, the major problem of nitride coatings on glass by PVD process is non-uniform film owing to pin-hole and micro crack. It is estimated that nonuniform coating is influenced by a different surface energy between metal nitrides and glass due to binding states. In this work, therefore, for the evaluation of nucleation and growth mechanism of nitride films on glass TiN and CrN film were synthesized on glass with various nitrogen partial pressure by unbalanced magnetron sputtering. Prior to deposition, for the examination of relationship between surface energy and film microstructure plasma pre-treatment process was carried out with various argon to hydrogen flow rate and substrate bias voltage, duty cycle and frequency by using pulsed DC power supply. Surface energy owing to the different plasma pre-treatment was calculated by the measurement of wetting angle and surface conditions of glass were investigated by X-ray Photoelectron Spectroscopy(XPS) and Atomic Force Microscope(AFM). The microstructure change of nitride films on glass with increase of film thickness were analyzed by X-Ray Diffraction(XRD) and Scanning Electron Microscopy(SEM).
An, Ha-Rim;Baek, Seong-Ho;Park, Il-Kyu;Ahn, Hyo-Jin
Korean Journal of Materials Research
/
v.23
no.8
/
pp.469-475
/
2013
Al-doped ZnO(AZO) thin films were synthesized using atomid layer deposition(ALD), which acurately controlled the uniform film thickness of the AZO thin films. To investigate the electrical and optical properites of the AZO thin films, AZO films using ALD was controlled to be three different thicknesses (50 nm, 100 nm, and 150 nm). The structural, chemical, electrical, and optical properties of the AZO thin films were analyzed by X-ray diffraction, X-ray photoelectron spectroscopy, field-emssion scanning electron microscopy, atomic force microscopy, Hall measurement system, and UV-Vis spectrophotometry. As the thickness of the AZO thin films increased, the crystallinity of the AZO thin films gradually increased, and the surface morphology of the AZO thin films were transformed from a porous structure to a dense structure. The average surface roughnesses of the samples using atomic force microscopy were ~3.01 nm, ~2.89 nm, and ~2.44 nm, respectively. As the thickness of the AZO filmsincreased, the surface roughness decreased gradually. These results affect the electrical and optical properties of AZO thin films. Therefore, the thickest AZO thin films with 150 nm exhibited excellent resistivity (${\sim}7.00{\times}10^{-4}{\Omega}{\cdot}cm$), high transmittance (~83.2 %), and the best FOM ($5.71{\times}10^{-3}{\Omega}^{-1}$). AZO thin films fabricated using ALD may be used as a promising cadidate of TCO materials for optoelectronic applications.
Proceedings of the Korean Vacuum Society Conference
/
2014.02a
/
pp.367-367
/
2014
Transparent conductive oxides (TCOs) 박막은 가시광선영역에서의 높은 투과율과 낮은 저항 특성을 동시에 갖고 있어 최근 smart windows, solar cells, liquid crystal displays (LCD), organic light emitting devices (OLED)등과 같은 최첨단 기기에 필수적인 구성요소로 활발히 사용되고 있다. 따라서, 현재까지 FTO ($SnO_2:F$), ITO ($In_2O_3:Sn$), ATO ($SnO_2:Sb$)등과 같은 다양한 TCO들이 많은 연구자들에 의해 연구되고 있다. 그 중 ITO는 우수한 전기적(${\sim}10^{-4}{\Omega}cm$) 및 광학적(~85%) 특성 때문에 현재 상업적으로 활발히 응용되고 있는 대표적인 물질이다. 하지만 ITO의 주된 구성요소인 indium은 제한적인 매장량과 과도한 소비량 때문에 원가가 비싸다는 문제점이 있다. 반면에, ATO는 우수한 전기적(${\sim}10^{-3}{\Omega}cm$) 및 광학적(~80%) 특성뿐만 아니라 구성물질들의 매장량이 풍부하여 ATO의 원가가 저렴하다는 장점을 가지고 있어 현재 ITO을 대체 할 수 물질로 관심 받고 있다 [1]. 지금까지 우수한 특성을 갖는 ATO박막을 합성하는 방법으로 sol-gel spin coating, sputtering, spray pyrolysis, chemical vapor deposition (CVD)등이 알려져 있다. 이 중에서도, sol-gel spin coating과 spray pyrolysis은 solution기반의 합성법으로 분류되며 합성과정이 간단하고 비용이 저렴하다는 장점이 있고 현재까지 많은 연구가 보고되었다. 그러나, 진공기반이 아닌 우수한 특성을 갖는 solution기반의 ATO박막을 합성하기 위해서는 새로운 합성법의 개발이 학문적으로나 산업적으로도 매우 중요한 이슈이다. 따라서, 본 연구에서는 electrospray을 활용하여 solution기반의 ATO박막을 처음으로 합성하였다. 게다가 ATO박막에 열처리온도에 따른 구조, 화학, 전기, 광학적 특성을 확인하기 위하여 X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Scanning Electron Microscopy (SEM), transmission electron microscopy (TEM), Hall Effect Measurement System, UV spectrophotometer를 사용하였다. 이러한 실험 결과들을 바탕으로 electrospray을 통해 합성된 solution기반의 ATO박막에 자세한 특성을 본 학회에서 다루도록 하겠다.
Lee, Yelim;Phuoc, Cao Van;Park, Seung-Young;Jeong, Jong-Ryul
Korean Journal of Materials Research
/
v.25
no.12
/
pp.703-707
/
2015
In this study, we investigated the effect of annealing conditions on the ferromagnetic resonance(FMR) of yttrium iron garnet ($Y_3Fe_5O_{12}$, YIG) thin film prepared on gadolinium gallium garnet ($Gd_3Ga_5O_{12}$, GGG) substrate. The YIG thin films were grown by rf magnetron sputtering at room temperature and were annealed at various temperatures from 700 to $1000^{\circ}C$. FMR characteristics of the YIG thin films were investigated with a coplanar waveguide FMR measurement system in a frequency range from 5 to 20 GHz. X-ray diffraction(XRD) and X-ray photoelectron spectroscopy(XPS) were used to characterize the phase formation, crystal structure and composition of the YIG thin films. Field dependent magnetization curves at room temperature were obtained by using a vibrating sample magnetometer(VSM). The FMR measurements revealed that the resonance magnetic field was highly dependent on the annealing condition: the lowest FMR linewidth can be observed for the $800^{\circ}C$ annealed sample, which agrees with the VSM results. We also found that the Fe and O composition changes during the annealing process play important roles in the observed magnetic properties.
AZO thin films are grown on a p-Si(111) substrate by RF magnetron sputtering. The characteristics of various thicknesses and heat treatment conditions are investigated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Hall effect and room-temperature photoluminescence (PL) measurements. The substrate temperature and the RF power during growth are kept constant at 400 ℃ and 200 W, respectively. AZO films are grown with a preferred orientation along the c-axis. As the thickness and the heat treatment temperature increases, the length of the c-axis decreases as Al3+ ions of relatively small ion radius are substituted for Zn2+ ions. At room temperature, the PL spectrum is separated into an NBE emission peak around 3.2 eV and a violet regions peak around 2.95 eV with increasing thickness, and the PL emission peak of 300 nm is red-shifted with increasing annealing temperature. In the XPS measurement, the peak intensity of Al2p and Oll increases with increasing annealing temperature. The AZO thin film of 100 nm thickness shows values of 6.5 × 1019 cm-3 of carrier concentration, 8.4 cm-2/V·s of mobility and 1.2 × 10-2 Ω·cm electrical resistivity. As the thickness of the thin film increases, the carrier concentration and the mobility increase, resulting in the decrease of resistivity. With the carrier concentration, mobility decreases when the heat treatment temperature increases more than 500 ℃.
$TiO_2$ oxide semiconductor is being widely studied in various applications such as photocatalyst and photosensor. Pd/$TiO_2$ gas sensor is mainly used to detect $H_2$, CO and ethanol. This study focus on increasing hydrogen detection ability of Pd/$TiO_2$ in room temperature through Al-doping. Pd/$TiO_2$ was fabricated by the hydrothermal method. Contacting to Aluminum (Al) foil led to Al doping effect in Pd/$TiO_2$ by thermal diffusion and enhanced hydrogen sensing response. $TiO_2$ nanoparticles were sized at ~30 nm of diameter from scanning electron microscope (SEM) and maintained anatase crystal structure after Al doping from X-ray diffraction analysis. Presence of Al in $TiO_2$ was confirmed by X-ray photoelectron spectroscopy at 73 eV. SEM-energy dispersive spectroscopy measurement also confirmed 2 wt% Al in Pd/$TiO_2$ bulk. The gas sensing test was performed with $O_2$, $N_2$ and $H_2$ gas ambient. Pd/Al-doped $TiO_2$ did not response $O_2$ and $N_2$ gas in vacuum except $H_2$. Finally, the normalized resistance ratio ($R_{H2on}/R_{H2off}$) of Pd/Al-doped $TiO_2$ increases about 80% compared to Pd/$TiO_2$.
Proceedings of the Korean Vacuum Society Conference
/
2011.02a
/
pp.88-88
/
2011
ZnO는 직접 천이형 반도체로써, 상온에서 3.4eV에 해당하는 띠틈을 가지고 있다. 뿐만 아니라 60meV의 큰 엑시톤 결합에너지를 가지고 있어 단파장 광전 소자 영역의 LED(Light Emitting Diode)나 LD(Laser Diode)에 널리 사용되고 있다. 하지만 일반적으로 격자틈새 Zn(Zni2+)이온이나 O 빈자리(V02+)이온과 같은 자연적인 도너 이온이 존재하여 n-형 전도성을 나타낸다. 그러므로 ZnO계 LED와 LD의 개발에 있어서 가장 중요한 연구 과제는 재현성 있고 안정된 고농도의 p-형 ZnO박막을 성장시키는 것이다. 하지만, 자기보상효과나 얕은 억셉터 준위, 억셉터의 낮은 용해도로 인하여 어려움을 가지고 있다. 본 연구에서는 고품질의 p-형 ZnO박막을 제작하기 위해 AlN를 도핑시킨 ZnO박막을 RF 마그네트론 스퍼터링 법을 이용하여 Ar과 O2분위기에서 성장시켰다. ZnO와 AlN타겟을 동시에 사용하였으며, ZnO타겟에 걸어준 RF 파워는 80W, AlN타겟에 걸어준 RF 파워는 5~20W로 변화시켰다. 박막의 전기적, 광학적 특성은 XPS (X-ray Photoelectron Spectroscopy), REELS (Reflection Electron Energy Loss Spectroscopy), XRD (X-ray Diffraction), SIMS (Secondary Ion Mass Spectrometry), AES (Auger Electron Spectroscopy), Hall measurement를 이용하여 연구하였다. XPS측정결과, AlN를 도핑시킨 ZnO박막의 Zn2p3/2와 O1s피크는 undoped ZnO박막의 피크보다 낮은 결합에너지에서 측정되었다. 모든 박막이 결정화 되었으며, (002)방향으로 우선적으로 성장된 것을 확인할 수 있었다. 홀 측정 결과, 기판을 $200^{\circ}C$로 가열하면서 성장시킨 박막이 p-형을 나타내었으며, 비저항(Resistivity)이 $5.51{\times}10^{-3}{\Omega}{\cdot}m$, 캐리어 농도(Carrier Concentration)가 $1.96{\times}1018cm^{-3}$, 이동도(Mobility)가 $481cm^2$/Vs이었다. 또한 QUEELS -Simulation에 의한 광학적 특성분석 결과, 가시광선영역에서 투과율이 90%이상으로 투명전자소자로의 응용이 가능하다는 것을 보여주었다.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.