Abstract
In this study, we investigated the effect of annealing conditions on the ferromagnetic resonance(FMR) of yttrium iron garnet ($Y_3Fe_5O_{12}$, YIG) thin film prepared on gadolinium gallium garnet ($Gd_3Ga_5O_{12}$, GGG) substrate. The YIG thin films were grown by rf magnetron sputtering at room temperature and were annealed at various temperatures from 700 to $1000^{\circ}C$. FMR characteristics of the YIG thin films were investigated with a coplanar waveguide FMR measurement system in a frequency range from 5 to 20 GHz. X-ray diffraction(XRD) and X-ray photoelectron spectroscopy(XPS) were used to characterize the phase formation, crystal structure and composition of the YIG thin films. Field dependent magnetization curves at room temperature were obtained by using a vibrating sample magnetometer(VSM). The FMR measurements revealed that the resonance magnetic field was highly dependent on the annealing condition: the lowest FMR linewidth can be observed for the $800^{\circ}C$ annealed sample, which agrees with the VSM results. We also found that the Fe and O composition changes during the annealing process play important roles in the observed magnetic properties.