• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.2
• /
• pp.55-58
• /
• 2013

ITO thin films deposited on glass substrate with RF magnetron sputtering were vacuum annealed at 100, 200 and $300^{\circ}C$ for 30 minutes and then effect of annealing temperature on the structural, electrical and optical properties of ITO films were investigated. The structural properties are strongly related to annealing temperature. The annealed films above $100^{\circ}C$ are grown as a hexagonal wurtzite phase and the largest grain size is observed in the films annealed at $300^{\circ}C$. The electrical resistivity also decreases as low as $4.65{\times}10^{-4}{\Omega}cm$ with a increase in annealing temperature and ITO film annealed at $300^{\circ}C$ shows the lowest sheet resistance of $43.6{\Omega}/{\Box}$. The optical transmittance in a visible wavelength region also depends on the annealing temperature. The films annealed at $300^{\circ}C$ show higher transmittance of 80.6% than those of the films prepared in this study.

• Korean Journal of Materials Research
• /
• v.26 no.6
• /
• pp.347-352
• /
• 2016

ZnO with wurtzite structure has a wide band gap of 3.37 eV. Because ZnO has a direct band gap and a large exciton binding energy, it has higher optical efficiency and thermal stability than the GaN material of blue light emitting devices. To fabricate ZnO devices with optical and thermal advantages, n-type and p-type doping are needed. Many research groups have devoted themselves to fabricating stable p-type ZnO. In this study, $As^+$ ion was implanted using an ion implanter to fabricate p-type ZnO. After the ion implant, rapid thermal annealing (RTA) was conducted to activate the arsenic dopants. First, the structural and optical properties of the ZnO thin films were investigated for as-grown, as-implanted, and annealed ZnO using FE-SEM, XRD, and PL, respectively. Then, the structural, optical, and electrical properties of the ZnO thin films, depending on the As ion dose variation and the RTA temperatures, were analyzed using the same methods. In our experiment, p-type ZnO thin films with a hole concentration of $1.263{\times}10^{18}cm^{-3}$ were obtained when the dose of $5{\times}10^{14}$ As $ions/cm^2$ was implanted and the RTA was conducted at $850^{\circ}C$ for 1 min.

• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.664-668
• /
• 2012

ZnO nanorods were successfully fabricated on Zn foil by chemical bath deposition (CBD) method. The ZnO precursor concentration and immersion time affected the surface morphologies, structure, and electrical properties of the ZnO nanorods. As the precursor concentration increased, the diameter of the ZnO nanorods increased from ca. 50 nm to ca. 150 nm. The thicknesses of the ZnO nanorods were from ca. $1.98{\mu}m$ to ca. $2.08{\mu}m$. ZnO crystalline phases of (100), (002), and (101) planes of hexagonal wurtzite structure were confirmed by XRD measurement. The fabricated ZnO nanorods showed a photoluminescene property at 380 nm. Especially, the ZnO nanorods deposited for 6 h in solution with a concentration of 0.005M showed a stronger (101) peak than they did (100) or (002) peaks. In addition, these ZnO nanorods showed a good electrical property, with the lowest resistance among the four samples, because the nanorods were densely in contact and relatively without pores. Therefore, a ZnO nanorod substrate is useful as a highly sensitive biochip substrate to detect biomolecules using an electrochemical method.

• Korean Journal of Materials Research
• /
• v.21 no.3
• /
• pp.144-148
• /
• 2011

We have investigated the structural and optical properties of Ga-doped ZnO (GZO) thin films deposited by RF magnetron sputtering at various deposition temperatures from 100 to $500^{\circ}C$. All the GZO thin films are grown as a hexagonal wurtzite phase with highly c-axis preferred parameter. The structural and electrical properties are strongly related to deposition temperature. The grain size increases with the increasing deposition temperature up to $400^{\circ}C$ and then decreases at $500^{\circ}C$. The dependence of grain size on the deposition temperature results from the variation of thermal activation energy. The resistivity of GZO thin film decreases with the increasing deposition temperature up to $300^{\circ}C$ and then decreases up to $500^{\circ}C$. GZO thin film shows the lowest resistivity of $4.3{\times}10^{-4}\;{\Omega}cm$ and highest electron concentration of $1.0{\times}10^{21}\;cm^{-3}$ at $300^{\circ}C$. The mobility of GZO thin films increases with the increasing deposition temperature up to $400^{\circ}C$ and then decreases at $500^{\circ}C$. GZO thin film shows the highest resistivity of 14.1 $cm^2/Vs$. The transmittance of GZO thin films in the visible range is above 87% at all the deposition temperatures. GZO is a feasible transparent electrode for the application to the transparent electrode of thin film solar cells.

• Korean Journal of Materials Research
• /
• v.17 no.12
• /
• pp.629-633
• /
• 2007

This study examined the effect of growth temperature on the electrical and optical properties of hydrogenated Al-doped zinc oxide (AZO:H) thin films deposited by rf magnetron sputtering using a ceramic target (98 wt.% ZnO, 2 wt.% $Al_2O_3$). Various AZO films on glass were prepared by changing the substrate temperature from room temperature to $200^{\circ}C$. It was shown that intentionally incorporated hydrogen plays an important role on the electrical properties of AZO : H films by increasing free carrier concentration. As a result, in the 2% $H_2$ addition at the growth temperature of $150^{\circ}C$, resistivity of $3.21{\times}10^{-4}{\Omega}{\cdot}cm$, mobility of $21.9cm^2/V-s$, electric charge carrier concentration of $9.35{\times}10^{20}cm^{-3}$ was obtained. The AZO : H films show a hexagonal wurtzite structure preferentially oriented in the (002) crystallographic direction.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.24 no.2
• /
• pp.101-105
• /
• 2010

We fabricated FEDs(Filed emission devices) based on ZnO nanowires. The ZnO nanowires were synthesized on Au thin films by hydrothermal method at the temperature of 90[$^{\circ}C$] on hot plate. In order to form tips of the ZnO nanowire, SDS(Sodium Dodecyl Sulfate) was mixed in O.05-0.3[wt%] solution as capping material. After 2 hour growth, we obtained nanowires of chain form The high-purity nanowires showed sharp tip geometry with a wurtzite structure. The field emission properties of the ZnO nanowires were investigated in high vacuum chamber. The turn-on field for the ZnO nanowires was found to be about 4.1[V/${\mu}m$] at a current density of 0.1[${\mu}A/cm^2$].

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.176-179
• /
• 2009

ZnO:Al 투명전도막을 유리기판위에 in-line RF-magnetron sputtering법으로 증착온도 및 증착압력에 따라 제조하고, 습식식각에 따른 박막의 표면형상 및 광학적 특성변화를 조사하였다. 초기박막은 육방정계(Hexanonal wurtzite)의 결정 구조와 (002)면의 c-축 우선배향성을 갖으며 가시광 영역에서 높은 광 투과도(T $\geq$ 80%)와 낮은 비저항($\rho\;=\;5.2{\times}10^{-4}{\Omega}{\cdot}cm$)의 특성을 나타내었다. 습식 식각 후 박막의 표면형상은 식각 전 박막의 결정성에 큰 의존성을 보이며 본 연구에서는 1 mTorr의 낮은 증착압력과 $350^{\circ}C$의 높은 증착온도에서 증착된 결정성이 우수한 막에서 높고 균일한 형태의 crater를 갖는 표면형상을 얻을 수 있었다. 균일한 crater를 형성하는 ZnO:Al 박막은 hill 형태의 표면형상을 갖는 상용 Asahi-U glass에 비하여 높은 Haze ($T_{diffused}/T_{total}$)값과 넓은 산란각을 나타내어 향상된 광 산란특성을 갖으며 이는 실리콘 박막 태양전지내로 입사된 광의 산란경로를 증가시켜 태양전지 성능을 크게 향상시킬 수 있을 것으로 기대한다.

• Journal of Sensor Science and Technology
• /
• v.15 no.5
• /
• pp.323-327
• /
• 2006

Manganese, copper and chlorine-doped ZnS phosphors (ZnS:Mn,Cu,Cl) were synthesized through solid-state reaction. Manganese was added in the range of amount $1.4{\sim}5.3$ mol % to ZnS phosphors containing 0.2 or 1.0 mol % of copper and a small amount of chlorine. As-synthesized phosphors showed a spherical morphology with a mean size of ${\sim}20\;{\mu}m$ and structural properties of Wurtzite, which were identified by SEM and XRD, respectively. Optical properties of ZnS:Mn,Cu,Cl synthesized with various concentrations of activators were analysed by both of PL and EL spectra. Samples mainly showing only 580 nm-orange emission by 380 nm-UV excitation gave different EL spectra of blue, green, and orange emissions at 450, 480 and 580 nm, respectively, depending on concentrations of $Cu^{2+}$ and $Mn^{2+}$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.11-11
• /
• 2006

ZnO는 넓은 밴드갭(3.37eV)과 큰 액시톤(exciton) 결합에너지(60meV)를 가지는 II-VI족 화합물 반도체이다[1]. 이와같은 특성은 상온에서도 높은 재결합 효율이 기대되는 엑시톤 전이가 가능하여 자발적인 발광특성 및 레이저 발진을 위한 낮은 임계전압을 가져 일광효율이 큰 장점이 있다. 최근에는 ZnO의 전기적, 광학적, 자기적 특성을 높이기 위해 doping에 대한 연구가 많이 보고 되고 있다. 이중 ZnO내에 Mg을 doping하게 되면 Mg 조성에 따라 밴드갭이 3.3~7.7eV까지 변하게 된다. 그러나 이원계 상평형도에 따라 ZnO내에 고용될 수 있는 MgO의 고용도는 4at% 이하이다. 이는 ZnO는 Wurtzite 구조이고, MgO는 rocksalt 구조로 각각 결정구조가 다르기 때문이다. 본 연구는 열기상증착방법(thermal evaporation)으로 ZnO 템플레이트를 이용하여 MgZnO 나노막대를 합성하였고, Zn와 Mg의 서로 다른 녹는점을 이용해 2-step으로 성장을 하였다. 합성은 수평로를 사용하였으며, 반응온도 550, $700^{\circ}C$로 2-step으로 하였으며, 소스로 사용된 Zn(99.99%)과 Mg(99.99%) 분말을 산소를 직접 반응시켜 합성하였다. Ar 가스와 O2 가스를 각각 운반가스와 반응가스로 사용하였다. ZnO 템플레이트 위에 성장시킨 1차원 MgZnO 나노구조의 형태 및 구조적 특성을 FESEM과 TEM으로 분석하였다. 그리고 결정학적 특성은 XRD를 이용해 분석하였다.

• Korean Journal of Materials Research
• /
• v.21 no.4
• /
• pp.202-206
• /
• 2011

We have investigated the structural and electrical properties of Ga-doped ZnO (GZO) thin films deposited by an RF magnetron sputtering at various RF powers from 50 to 90W. All the GZO thin films are grown as a hexagonal wurtzite phase with highly c-axis preferred parameters. The structural and electrical properties are strongly related to the RF power. The grain size increases as the RF power increases since the columnar growth of GZO thin film is enhanced at an elevated RF power. This result means that the crystallinity of GZO is improved as the RF power increases. The resistivity of GZO rapidly decreases as the RF power increases up to 70 W and saturates to 90W. In contrast, the electron concentration of GZO increases as the RF power increases up to 70 W and saturates to 90W. GZO thin film shows the lowest resistivity of $2.2{\times}10^{-4}{\Omega}cm$ and the highest electron concentration of $1.7{\times}10^{21}cm^{-3}$ at 90W. The mobility of GZO increases as the RF power increases since the grain boundary scattering decreases due to the reduced density of the grain boundary at a high RF power. The transmittance of GZO thin films in the visible range is above 90%. GZO is a feasible transparent electrode for application as a transparent electrode for thin film solar cells.