• 한국공작기계학회논문집
• /
• 제14권4호
• /
• pp.49-54
• /
• 2005

Measuring defects on the inside and on the surface of a steel structure is very important technology in order to predict the life span of the structure. In particular, a place with a high probability that it may contain defects is a welded part and it is very important to check defects in the part, absence/presence of non-uniform substances, its shape, and the location. Many non-destructive tests can be applied, but the ultrasonic flow detection test is widely used with some advantages. The ultrasonic flow detection test, however, cannot be applied when there is a problem by a contact medium between PZT and a specimen, in case of a small and complicated shape or a moving object or when the specimen is hot. In this study, to solve the problems of the contact ultrasonic flow detection test, the non-contact ultrasonic flow detection test for sending/receiving ultrasonic waves using lasers was described. I intended to develop a non-destructive detection system applying the laser application ultrasonic test to a steel structure by detecting the defects inside of and on the surface of the specimen.

• 한국해양공학회지
• /
• 제30권1호
• /
• pp.51-56
• /
• 2016

In this study, for the tube-to-tube friction welding of hose nipple materials, the main parameters of friction welding were investigated using tensile tests, Vickers hardness surveys of the bond area (HAZ), and observations of the microstructure to increase the quality of friction welding based on visual examination. As-welded and post weld heat treated (PWHT) specimens were tested. The optimal welding conditions were found to be n = 1000 rpm, HP = 10 MPa, UP = 15 MPa, HT = 9 s, and UT = 5 s when the metal loss (Mo) was 7.5 mm. Furthermore, the peak of the hardness distribution of the friction welded joints could be eliminated by PWHT. Moreover, the two materials of the friction weld were thoroughly mixed with a well-combined structure of micro-particles, without any molten material, particle growth, or defects.

• 대한기계학회논문집A
• /
• 제24권5호
• /
• pp.1331-1342
• /
• 2000

In power generation systems a variety of structural components typically operate at high temperature and pressure. Therefore a life assessment methodology accounting for gradual creep fracture is increasingly needed for these components. The most critical defects in such structure are generally found in the form of semi-elliptical surface cracks in the welded tubular joints. Therefore the analysis of a semi-elliptical surface crack in a plate or a shell is an important problem in engineering fracture mechanics. On this background, via shell/line-spring finite element analyses of such surface cracks in the welded T and L joints under various loadings, we investigate J-integral along the crack front We first develop T and L joints auto mesh generation program providing ABAQUS input file composed of shell/line-spring finite elements. We then further develop a T and L joints life assessment program based on the experimental creep crack growth law and auto mesh generation program in a graphical user interface format Finally the remaining life of T and L joints for various analytical parameters are assessed using the developed life assessment program.

• 한국재료학회지
• /
• 제21권7호
• /
• pp.410-414
• /
• 2011

This study was carried out to evaluate the microstructures and mechanical properties of a friction stir welded Ni based alloy. Inconel 600 (single phase type) alloy was selected as an experimental material. For this material, friction stir welding (FSW) was performed at a constant tool rotation speed of 400 rpm and a welding speed of 150~200 mm/min by a FSW machine, and argon shielding gas was utilized to prevent surface oxidation of the weld material. At all conditions, sound friction stir welds without any weld defects were obtained. The electron back-scattered diffraction (EBSD) method was used to analyze the grain boundary character distributions (GBCDs) of the welds. As a result, dynamic recrystallization was observed at all conditions. In addition, grain refinement was achieved in the stir zone, gradually accelerating from 19 ${\mu}m$ in average grain size of the base material to 5.5 ${\mu}m$ (150 mm/min) and 4.1 ${\mu}m$ (200 mm/min) in the stir zone with increasing welding speed. Grain refinement also led to enhancement of the mechanical properties: the 200 mm/min friction stir welded zone showed 25% higher microhardness and 15% higher tensile strength relative to the base material.

• 한국해양공학회지
• /
• 제17권1호
• /
• pp.47-54
• /
• 2003

In this study, the residual stress and the acoustic emission Charactreistics from fatigue crack propagation were investigated, bused on the welded material of STS316L. The residual stress of welding locations could be evaluated by ultrasonic parameters, such as L$_{CR}$ wave velocity and L$_{CR}$ wave frequency； the residual stress between base metal and weld metal was evaluated. In the fatigue tests, three types of signals were observed, regardless of specimen condition, base metal, and weld metal. Based on NDE analysis of AE signals by the time-frequency analysis method, it should also be possible to evaluate, in real-time, the crack propagation and final fracture process, resulting from various damages and defects in welded structural members.

• 한국정밀공학회지
• /
• 제24권5호
• /
• pp.35-43
• /
• 2007

Laser welding of metals has been widely used to improve a wear resistance and a corrosion resistance of the industrial parts. The objective of this research works is to investigate the influence of the process parameters, such as the welding for metals with CW Nd:YAG lasers. The bead-on-plate welding tests are carried out for several combinations of the experimental conditions. In order to quantitatively examine the characteristics of the butt welding, the welding quality of the cut section, stain-stress behavior and the hardness of the welded part are investigated. From the results of the investigation, it has been shown that the optimal welding condition without defects in the vicinity of the welded area and with a good welding quality is 1325W of the laser power, and 1.4m/min of laser welding speed.

• Journal of Welding and Joining
• /
• 제15권6호
• /
• pp.78-84
• /
• 1997

Friction welding technique was studied to weld the turbine wheel and shaft of a turbocharger. The welding parameters were selected to investigate the effects of variables on welding quality of Inconel 713C and SCM 440. Experimental results showed that the turbine wheel and shaft could be successfully welded by friction welding. The heat affected zone was identified to be 2 mm from the weld seam. After welding, the hardness profile was found to have sudden increase and decrease for inconel 713C and SCM 440 respectively. Tensile strength of welded specimens was higher than the required strength for all of the studied welding parameters. The central portion of fracture surfaces by bending had no defects such as crack.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2003년도 추계학술대회 논문집(III)
• /
• pp.85-90
• /
• 2003

Among rail defects, the transverse crack, which has been the most dangerous fatigue damage, is developed from shelling near the rail running face and grows perpendicular to the rail surface. Moreover, the crack has occurred frequently fatigue damage during winter. Therefore, to assure the safety of railway vehicles, it is necessary to investigate growth behavior of transverse crack for rail steel. In this study, fatigue crack growth behavior of rail steel and its gas pressure welded part at room and low temperature are performed. The fatigue crack growth rate of the welded part was lower than that of the base part within a lower ${\Delta}K$ region at both room and low temperature, and this difference decreases with increasing the ${\Delta}K$ due to the decrease of the fracture toughness.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1998년도 제2회 박판성형심포지엄 논문집 박판성형기술의 현재와 미래
• /
• pp.102-109
• /
• 1998

In this study, the side panels were developed using the laser-welded Tailored Blanks (TB) with both the same thickness and the different thickness. At first, the formability of the same thickness T.B was investigated to be compared with one of the non welded panel with respect to weldline movements and strain distribution on blank during the stamping. Based on these results, we selected candidates of T.B with different thickness for stamping experiments. That is, we determined the weld line positions and the die step. Then we made some stamping tryouts with selected types of blank designs to investigate the formability of T.B with different thickness. During the tryouts, the wrinkles were found in the a-pillar lower region which is under the deformation mode of the shrink flange. In the b-pillar region, the fractures were found also, these defects have been reduced and corrected by controlling the blank design and the die faces and process pamameters.

• 한국산학기술학회논문지
• /
• 제18권5호
• /
• pp.278-284
• /
• 2017

본 연구에서는 일정한 회전 속도에서 용접 속도를 제어하여 AZ61 마그네슘 합금에 적합한 입열량 조건을 도출하였다. 또한 산업적 측면에서는 더 빠른 용접 속도가 요구되기 때문에 용접 속도에 따른 효과를 연구하였다. 회전 속도 변수는 800rpm으로 일정하게 적용하였고, 용접 속도는 100 - 500mm/min 으로 변화시켜 용접부의 거동을 관찰 및 평가하였다. 기계적 물성 평가를 위하여 인장 및 경도 시험을 수행하였으며, 미세구조 관찰과 용접부의 건정성을 판단하기 위하여 광학현미경을 사용하였다. 용접 속도가 400mm/min 이상 적용되었을 때 용접부 내부에서 결함이 관찰되었다. 용접 속도가 증가할수록 교반부의 결정립 크기는 작아졌으며, 경도 또한 비례 증가하는 경향을 보였다. 회전속도 800rpm, 용접 속도 200mm/min과 300mm/min 일 때, 용접부 내 외부 적으로 결함이 없었으며, 우수한 기계적 물성이 기록되었다. 이때, 접합 효율은 각각 100.5%, 101.2%이었고, 최대인장강도가 모재의 강도와 유사하였다. 인장 시편의 파괴는 시편의 전진측과 교반부 사이에서 발생하였으며, 이는 횡단면부 경도 분포에서 경도가 일시적으로 감소하는 위치와 일치하였다.