• Journal of Biomedical Engineering Research
• /
• v.20 no.1
• /
• pp.99-106
• /
• 1999

Ultra-high molecular weight polyethylene (UHMWPE) was crosslinked in the melt state to enhance wear resistance, Dicumyl peroxide (DCP) and triallyl cyanurate (TAC) was used as a crosslinking agent and a promoter, respectively. With increasing amount of DCP and TAC used, gel content of crosslinked UHMWPE (XUMPE) increased, while the melting temperature, crystallizaiton temperature, crystallinity, and tensile properties decreased. The results of pin-on-disk wear test and ball-on-disk test with small applied load showed reduced wear volumes of XUMPE from that of the unmodified UHMWPE. As the wear mechanism effected in the experimental condition of this study was thought to be deformation rather than adhesion or fatigue, a new parameter, the ratio of maximum contact stress to yield stress, was proposed to correlate well with observed wear resistance. In ball-on-disk wear test with larger applied load, XUMPE showed higher wear volumes than that of the unmodified UHMWPE which were accompanied with increased friction coefficients and surface roughness of the wear tracks. When contact stress was well above yield stress, the failure of XUMPE, as well as deformation, was thought to be much accelerated.

• Tribology and Lubricants
• /
• v.16 no.1
• /
• pp.9-14
• /
• 2000

It has been cleared in previous author's paper that the fatigue life before the pitting on the rolling contact surface with lubricant are influenced by the wear amount. In this study, the wear type has been clarified when wear amount is extremely large such as the case without lubricant. The test of rolling contact fatigue has been conducted under two different of herzian pressures and three different of slide ratios without lubricant. In addition, residual stress and half-value breadth using X-ray diffraction on worn surface have been measured as well as the wear amount. The results show that the pitting type wear by rolling contact fatigue has not been occurred when the wear amount is considerably large. Thus this type of wear has been deduced by the fatigue wear depending on delamination theory.

• Tribology and Lubricants
• /
• v.20 no.1
• /
• pp.7-13
• /
• 2004

High strength steels are widely used as tribo-materials in the field. Previous study revealed that for mild steel, the states of strain on the worn surface measured by X-ray diffraction has a good relationship with the state of wear. The objective of this study is to identify the relationship between the state of strain on the worn surface and the state of wear in high strength steels. Sliding wear tests were carried out using several hardened steels. X-ray diffraction tests were conducted to analyze the state of strain on the worn surface during wear. The experimental results indicated that the state of strain on worn surface in the hardened steel shows the same tendency as in the mild steel. It is clear that change of half value width on the worn surface as a function of sliding speeds is broadly similar in shape to wear characteristics curve and its magnitude has a good relationship with the wear rate at two different wear modes in the hardened steel.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.12
• /
• pp.1383-1392
• /
• 2009

A disadvantage in the design of a hypotrochoidal gear pump as in a gerotor pump is a lack of parts that can be adjusted to compensate for wear in the rotor set, and as a consequence, it causes a sharp reduction of volumetric efficiency. In this paper, an attempt has been made to reduce the wear rate between the rotors of a hypotrochoidal gear pump. Using the knowledge of shape design on the rotors, the contact stresses without hydrodynamic effect between the rotors' teeth are evaluated through the calculation of the Hertzian contact stress. Based on the above result and the sliding velocity between the rotors, a genetic algorithm (GA) is used as an optimization technique for minimizing the wear rate proportional factor (WRPF). The result shows that the wear rate or the WRPF can be reduced considerably, e.g. approximately 12.8% in this paper, throughout the optimization using GA.

• Tribology and Lubricants
• /
• v.15 no.1
• /
• pp.39-45
• /
• 1999

The wear behavior of $Al_2$O$_3$-40%TiO$_2$deposited on casted aluminum alloy (ASTM A356) by APS (Air Plasma Spray) against SiC ball has been investigated in this work. Wear tests were carried out at room temperature. The friction coefficient of $Al_2$O$_3$-40%TiO$_2$coating is lower than that of pure $Al_2$O$_3$coating(APS). $Al_2$O$_3$-40%TiO$_2$coating indicated the existence of the optimal coating thickness. It is found that voids and pores of coating surface resulted in the generation of cracks, and the cohesive of splats and the porosity of surface play a role in wear characteristics. It is suggested that the mismatch of thermal expansion of substrate and coating play an important role in wear performance. Tension and compression under thermo-mechanical stress may be occurred by the mismatch between thermal expansion of substrate and coating. The crack propagation above interface is observed in SEM.

• Tribology and Lubricants
• /
• v.10 no.2
• /
• pp.51-55
• /
• 1994

Rolling friction test was carried out to investigate the effect of the wear amount on rolling contact fatigue process in lubrication oil. The methods of this process were conducted at two Hertzian contact pressure and three slide ratio in each case by employing normalized and annealed carbon steel. During process of the rolling contact fatigue, the number of rotation until surface damage was occurred, the wear amount of rolling contact surface, and residual stress and half-value breadth using X-ray reflection on rolling contact surface were investigated. The result of this study shows that rolling contact fatigue process was directly influenced by wear trend and was confirmed by change of residual stress and half-value breadth on rolling contact surface.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.9 no.4
• /
• pp.25-33
• /
• 2000

The reorientations of the atoms by frictional shear deformation at the surface induce cracks at the boundary of the grain. The cracks grow and propagate in regions where the hydrostatic component of stress is least compressive because the compressive component restores the cracks by three-dimensional crystallizing $\pi$-bondings. The materials with Lder's band have very small amount of wear at the initial state. It suggests that initial frictional shear deformation be consumed to the formation of the Lder's band. The average wear amounts of the materials increase very steeply as the øu the stress-strain ratio at the ultimate point, decreases.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.5
• /
• pp.1468-1476
• /
• 1996

Surface integrity is dictated by the fabrication process of the metal part. In this work, steel specimens were prepared under various mechine conditions to achieve different degrees of deformation state. The tribological characteristics of the speciments were tested using a pin-on-disk type apparatus and other surface characterization tools. It is shown that though frictional characteristics are similar, the wear rate is significantrly affected by the properties of the surface. In the case of steel, surface cracks resulted in high wear despite the relatively high hardness of the specimen. Also, the sliding action were found to reduce the residual stress on the surface. These results indicate that there is a strong relationship between surface integrity and the tribological properties of steel, and therefore the machining condition should be optimized woth respect to tribological performance of a steel part.

• Tribology and Lubricants
• /
• v.10 no.3
• /
• pp.71-77
• /
• 1994

Rolling friction test was carried out to investigate the effect of the wear amount on rolling contact fatigue process in lubrication oil. The methods of this process were conducted at two Hertzian contact pressure and three slide ratio in each case by employing normalized and annealed carbon steel. During process of the rolling contact fatigue, the number of rotation until surface damage was occurred, the wear amount of rolling contact surface, and residual stress and half-value breadth using X-ray reflection on rolling contact surface were investigated. The result of this study shows that rolling contact fatigue process was directly influenced by wear trend and was confirmed by change of residual stress and half-value breadth on rolling contact surface.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.11a
• /
• pp.322-330
• /
• 2001

The plasma-sprayed 8％Y$_2$O$_3$-Zirconia coating was studied to know the relationship between phase transformation and wear properties after several heat treatment. Wear tests were carried out with ball on disk on 50N, 70N, 90N. The specimen in this study was cast iron and tests were performed on room temperature. The transformation of phase and residual stress was measured by x-ray diffraction method(XRD) and worn surface were observed by SEM.