• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.6
• /
• pp.143-151
• /
• 2007

This study presents the experimental results of frost durability including resistance to freezing-thawing and surface scaling of concrete. Mixing design was proportioned with the various water-binder ratio between 0.37 and 0.47 and three different binder compositions corresponding to Type I cement without any supplementary cementitious materials(OPC), Type II cement with 50% blast-furnace slag replacement(BFS50), and ternary cement with Type III cement, 15% fly ash, and 35% slag replacement (BFS35%+FA15%). Test results showed that the mixing design with BFS50% and BFS35%+FA15% exhibited higher durability factor than that made with OPC only. Finally, the use of blend cement containing slag can be used effectively in terms of frost durability of the concrete exposed to severe condition under coastal environment like as flying salt, sea water spray, etc.

• Computers and Concrete
• /
• v.2 no.1
• /
• pp.19-30
• /
• 2005

We study the kinetics of absorption of water in Portland cement concretes added with 60, 70 and 80% of granulated blast furnace slag (GGBS) cured in water and at open air and preheated at 50 and $100^{\circ}C$. A mathematical model is presented that allows describing the process not only in early ages where the capillary sorption is predominant but also for later and long times where the diffusive processes through the finer and gel pores are considered. The fitting of the model by computerized methods enables us to determine the parameters that characterize the process: i.e., the sorptivity coefficient (S) and diffusion coefficient (D). This allows the description of the process for all times and offers the possibility to know the contributions of both, the diffusive and capillary processes. The results show the influence of the curing regime and the preheating temperature on the behavior of GGBS mortars.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.2
• /
• pp.149-156
• /
• 2016

It has been well known that concrete structures exposed to chloride and sulfate attack environments lead to significant deterioration in their durability due to chloride ion and sulfate ion attack. The purpose of this experimental research is to evaluate the long-term durability against chloride ion and sulfate attack of the alkali activated cementless concrete replacing the cement with ground granulated blast furnace slag. For this purpose, the cementless concrete specimens were made for water-binder ratios of 40%, 45%, and 50%, respectively and then this specimens were cured in the water of $20{\pm}3^{\circ}C$ and immersed in fresh water, 10% sodium sulfate solution for 28, 91, 182, and 365 days, respectively. To evaluate the long-term durability to chloride ion and sulfate attack for the cementless concrete specimens, the diffusion coefficient for chloride ion and compressive strength ratio, mass change ratio, and length change ratio were measured according to the NT BUILD 492 and JSTM C 7401, respectively. It was observed from the test results that the resistance against chloride ion and sulfate attack of the cemetntless concrete were comparatively largely increased than those of OPC concrete irrespective of water-binder ratio.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.3
• /
• pp.204-210
• /
• 2022

Cement is pointed out as the main cause of carbon dioxide emission in the construction industry. Many researchs are underway to use blast furnace slag, an industrial by-product, as a substitute for cement to reduce carbon dioxide emitted during the manufacturing the cement. When blast furnace slag is used as a substitute for cement, it has advantages such as long-term strength and chemical resistance improvement. However, blast furnace slag has a problem that makes initial strength low. This is due to the impermeable film on the surface created during the production of blast furnace slag. The created film is known to be destroyed in an alkaline environment, and based on this, previous studies have suggested a solution using various alkali activators. But, alkali activator is dangerous product since it is a strong alkaline material. And it has the disadvantage in price competitiveness. In this study, an experiment was conducted to improve the initial hydration reactivity of the blast furnace slag to secure the initial strength of the mortar substituted with the blast furnace slag and to check whether the carbonation resistance was increased. As a result of the experiment, it was confirmed that the mortar using alkaline water showed higher strength than the mortar using tap water, and there were more hydration products generated inside. In addition, it was confirmed that the mortar using alkaline water as a compounding water had high carbonation resistance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.4
• /
• pp.67-74
• /
• 2015

In this study, effects of micropores on the freezing-thawing resistance of high volume slag concrete are reviewed. Concrete was made with slag which contains the ground granulated blast furnace slag(GGBS) and the pig iron preliminary treatment slag(PS) by replacing 0, 40, 70 %, then compressive strength, freezing-thawing resistance, micropores were reviewed. Also, specified design strength, target air contents were set. Deterioration was induced by using 14-day-age specimen which has low compressive strength for evaluating deterioration by freeze-thawing action. As results of the experiment, despite of specified design strength which has been set similarly and ensured target air contents, the pore size distribution of the concrete showed different results. Micropores in GGBS70 specimen have small amount of water which is likely to freeze because there is small amount of pore volume of 10~100 nm size at 0 cycle which has not been influenced by freezing-thawing. For these reasons, it was confirmed that the freezing-thawing resistance performance of GGBS70 is significantly superior than other specimens because relatively small expansion pressure is generated compared to the other specimens.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.4
• /
• pp.313-320
• /
• 2016

The aim of this study is to look into the metakaolin replacement ratio of blast furnace slag based alkali activated slag mortar and its mechanical characteristics according to changes in stimulant concentration. Metakaolin has high fineness, and therefore the fluidity becomes lower as the replacement ratio becomes higher. So in this study, a sufficient value of mixing water was provided to secure fluidity for the characteristic experiment, and a different W/B was derived for each specimen in order to make the fluidity identical. A characteristic experiment was conducted according to the mol concentration of NaOH, which was used as the mixing water that affects fluidity. Additionally, compressive strength measurement, observation of inner microstructure through SEM, acid resistance experiment, and neutralization resistance was conducted. The results of this study revealed that for a high concentration NaOH solution to have even fluidity, a high W/B is necessary, and the functions were enhanced, not degraded.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.2
• /
• pp.97-106
• /
• 2009

self-loading, various problems related to construction can be solved as well as the save of construction cost. Thus, this study has an aim of applying foam concrete to structural purpose by adding bottom ash as a reinforcing material like fine aggregate, in contrast to conventional non-structural usage such as soundproofing or insulating materials. In addition, it was evaluated in terms of unit volume weight, flow value, air void, water absorption and dosage of foam agent wether replacement of cement by granulated blast furnace slag or fly-ash has an effect on the material characteristics of foam concrete. As results of experiments, it can be found that the increase of fine aggregate ratio, that is to say, the increase of bottom ash results in the increase of unit volume weight, while decreasing air void and flow value. But, appropriate addition of bottom ash to foam concrete makes it easy to control a homogeneous and uniform quality in foam concrete due to less sensitive to bubbles. As the replacement ratio of mineral admixtures such as granulated blast furnace slag and fly-ash increases, as unit volume weight tends to decrease. In the meanwhile, serious effects were shown on fluidity of foam concrete when more than limit of replacement ratio was applied.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.33-40
• /
• 2013

The cement industry brought very severe environment problems with massive carbon dioxide during its production. To solve this problem, attempts on Alkali-Activated Slag (AAS) concrete that perfectly substitutes industrial by-products such as ground granulated blast furnace slag (GGBFS) for cement are being actively made. AAS concrete is possible to have high strength development at room temperature, however, it is difficult to ensure the working time due to the fast setting time and the loss of workabillity because of the alkali reaction. In this study, the early age properties of alkali activated slag mortar are investigated to obtain the fundamental data for AAS concrete application to structural members. The water-binder ratio (W/B) was fixed at 0.35 and sodium hydroxide and waterglass as alkali activator was used. The compressive strength, the flow and the ultrasonic pulse velocity were measured according to the type of superplasticisers, which were naphthalene(N), lignin(L), melamine(M) and PC(P), up to a maximum of 2 percent by the mass of GGBFS. The results showed that adding melamine type of superplasticizer improved the fluidity of AAS mortar without decreasing the compressive strength, while naphthalene and polycarbonate type of superplasticizer had little effect on the fluidity of AAS mortar.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.6
• /
• pp.74-82
• /
• 2017

This research presents the results of the strength and drying shrinkage properties to study the effect of ground granulated blast furnace slag(GGBFS), fly ash(FA) and calcium sulfoaluminate(CSA) for activated ternary blended slag cement. The activated ternary blended cement(ATBC) mortar were prepared having a constant water-cementitious materials ratios of 0.4. The GGBFS contents ratios of 100%, 80%, 70% and 60%, FA replacement ratios of 10%, 20%, 30% and 40%, CSA ratios of 0%, 10%, 20% and 30% were designed. The superplasticizer of polycarboxylate type were used. The activator was used of 10% sodium hydroxide(NaOH) + 10% sodium silicate($Na_2SiO_3$) by weight of binder. Test were conducted for mini slump, setting time, V-funnel, water absorption, compressive strength and drying shrinkage. According to the experimental results, the contents of superplasticizer, V-funnel and compressive strength increases with an increase in CSA contents for all mixtures. Moreover, the setting time, water absorption ratios and drying shrinkage ratio decrease with and increase in CSA. One of the major reason for the increase of strength and decrease of drying shrinkage is the accelerated reactivity of GGBFS with alkali activator and CSA. The CSA contents is the main parameter to explain the strength development and decreased drying shrinkage in the ATBC.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.2
• /
• pp.171-175
• /
• 2010

This paper presents the experimental results of frost durability characteristics including freezing-thawing and de-icing salt scaling of the concrete for gutter of the road and marine structure. Mixtures were proportioned with the three level of water-binder ratio(W/B) and three binder compositions corresponding to Type I cement with 0%, 30% and 50% GGBS(Ground granulated blast furnace slag) replacement. Also, two different solutions of calcium chloride were used to evaluate their effect on the frost durability resistance. Specially, in case of complex of freezing and thawing with salt and carbonation, the deterioration of concrete surface is evaluated. Test results showed that the BFS30 and BFS50 mixture exhibited higher durability and lower mass loss values than those made with OPC mix and the use of GGBS can be used effectively in terms of economy and frost durability of the concrete to be in complex deterioration. Therefore, the resistance to complex deterioration with freezing-thawing was strongly influenced by the strength and the type of cement.