• Korean Journal of Materials Research
• /
• v.14 no.6
• /
• pp.402-406
• /
• 2004

$WSi_2$, $TiSi_2$, $CoSi_2$, and $TaSi_2$ are general silicides used today in semiconductor devices. $WSi_2$ thin films have been proposed, studied and used recently in CMOS technology extensively to reduce sheet resistance of polysilicon and $n^{+}$ region. However, there are several serious problems encountered because $WSi_2$ is oxidized and forms a native oxide layer at the interface between $WSi_2$ and $Si_3$$N_4$. In this study, we have introduced 20 $slm-N_2$ gas from top to bottom of the furnace in order to control native oxide films between $WSi_2$ and $Si_3$$N_4$ film. In resulting SEM photographs, we have observed that the native oxide films at the surface of $WSi_2$ film are removed using the long injector system.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.1
• /
• pp.3-14
• /
• 1996

High temperature anneal of W-rich silicides, inferior to adherence compared with Si-rich silicides, resulted in the film peeling off from the Si-substrate when WSix thickness reached more than critical thickness. Investigation of the W-rich silicide films peeling off from the substrate revealed that the voids underneath the $WSi_2$ produced through silicide reaction were responsible for the poor adherence of W-rich silicide. In addition, internal stress in the film increased as the silicide thickness increased. In order to promote the adhesion of WSix to Si-substrate, thin Ti-layer was formed between WSi and Si-substrate(WSix/Ti/Si). No voids were observed in $WSi_2$/Ti/Si $N_2$-annealed at $1000^{\circ}C$, thereby leading to an increase of the critical thickness from ～1700$\AA$ to more than 2500$\AA$. However, higher resisiti-vity was obtained in WSix/Ti/Si than in WSix/Si. Finally, different silicide reaction mechanism for the structures(WSix/Si, WSix/Ti/Si) was proposed to explain the formation of voids as well as the role of thin Ti-layer.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.52 no.4
• /
• pp.173-178
• /
• 2003

In this paper, we studied the physical and electrical characteristics of $\textrm{WSi}_{x}$ thin film with respect to the adoption of the DCS (dichlorosiliane) post flow and the variation of deposition temperature. XRD measurements show that as deposited thin film has a hexagonal structure regardless of deposition Process. However, we find that the phase of thin film has changed to a tetragonal structure after the heat treatment at $680^{\circ}C$. Adoption of DCS post flow and increment of deposition temperature result in the increments of Si/W composition ratio. These conditions also result in the increment of sheet resistance by the amount 3.0~4.2$\Omega$/$\square$, but give the tendency in the decrement of stress by 0.27~0.3 E10dyne/$\textrm{cm}^2$. We also find that the contact resistance of word line and bit line interconnection was decreased by the amount 5.33~16.43$\mu$$\Omega$-$\textrm{cm}^2$, when applying DCS post flow and increasing deposition temperature.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.7
• /
• pp.17-25
• /
• 1999

Tungsten nitride($WN_x$) films were deposited by PECVD method on silicon nitride($WSi_3N_4$) substrate. The characteristics of $WN_x$ film were investigated with changing various processing parameters ; substrate temperature, gas flow rate, rf power, and different nitrogen sources. The nitrogen composition in $WN_x$ film varied from 0 to 45% according to the $NH_3$ and $N_2$ flow rate. The highest deposition rate of 160 nm/min was obtained for the $NH_3$ gas and relatively low deposition rate of $WN_x$ films were formed by $N_2$ gas. $WN_x$ films deposited on $WSi_3N_4$ substrate had higher deposition rate than that of TiN and Si substrates. The purity of $WN_x$ film were analyzed by AES and higher purity $WN_x$ films were deposited using $NH_3$ gas. The XRD analysis indicates a phase transition from polycrystalline tungsten(W) to amorphous tungsten nitride($WN_x$), showing improved etching profile of $WN_x$ films Thick $WN_x$ films were deposited on various substrates such as Tin, NiCr and Al and maximum thickness of $1.6 {\mu}m$ was obtained on the Al adhesion layer.