• 한국전기전자재료학회논문지
• /
• 제18권12호
• /
• pp.1111-1116
• /
• 2005

ZnO varistor ceramics added a glass-frit 0.03 $wt\%$ were fabricated with variation of sintering temperature. The sintering temperature and time were $1125^{\circ}C\~1200^{\circ}C$ and 2 h. The average grain sizes increased and the varistor voltage decreased with increasing the sintering temperature. The values of the specimen sintered at $1200^{\circ}C$ were $23.7\;{\mu}m$ and 329 V, respectively. The leakage current of all specimens was less than $1\;{\mu}A$ at DC $82\%$ of varistor voltage. The clamping voltage ratio of the specimen sintered at $1175^{\circ}C$ was 1.37. The endurance of surge current and the deviation of varistor voltage of the specimen sintered at $1175^{\circ}C$ were 6400 $A/cm^2$ and ${\Delta}-2.81\%$, respectively. After the High Temperature Load Test(HTLT) at $85^{\circ}C$ for 1000 h, the specimen sintered at $1175^{\circ}C$ showed the lowest deviation of varistor voltage of ${\Delta}-1.92\%$.

• 한국전기전자재료학회논문지
• /
• 제15권10호
• /
• pp.876-882
• /
• 2002

The microstructure and electrical characteristics of ZPCD (ZnO-$Pr_{6}O_{11}$-CoO-$Dy_2O_3$) -based varistor ceramics were investigated with various $Pr_{6}O_{11}$/CoO ratios and sintering temperatures. The density of varistor ceramics with $Pr_{6}O_{11}$=1.0 was almost constant with sintering temperature, whereas it was increased noticeably in $Pr_{6}O_{11}$=0.5. Increasing $Pr_{6}O_{11}$ content enhanced the densification for any CoO content and the density was greatly affected not by CoO content but by $Pr_{6}O_{11}$ content. The varistor ceramics with $Pr_{6}O_{11}$/CoO=0.5/l.0 exhibited a higher nonlinearity than any other composition ratios. In particular, the varistor ceramics sintered at $1350^{\circ}C$ exhibited the best electrical properties, with nonlinear exponent of 37.8, leakage current of 7.6 ${\mu}$A, and tan $\delta$ of 0.059.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.603-606
• /
• 2004

ZnO varistor ceramics were fabricated with variation of addition of $Nd_2O_3$ amount and the sintering temperature was $l150^{/circ}C$. The average grain sizes were showed decreased from $13.8{\mu}m$ to $4.7{\mu}m$, and varistor voltages were increased from 398 V to 657 V by added amount of $Nd_2O_3$. Nonlinear coefficient a of all were with increasing the amount of $Nd_2O_3$ more than 60, in case of added on 0.1mol% $Nd_2O_3$ was 87. And leakage current were less than $1_{\mu}A$ with applied at 82% of varistor voltage. The clamping voltage ratio of the specimes added 0.1mol% $Nd_2O_3$ was 1.38 at applied 25A [$8/20{\mu}s$]. In the specimen added 0.1mol% $Nd_2O_3$, endurence of surge current and deviation of varistor voltage were 7000A/$cm^2$, $\Delta-2.08%$, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.375-378
• /
• 2004

ZnO varistor ceramics were fabricated with variation of addition of glass-frit amount and the sintering temperature was $1150^{\circ}C$. The average grain sizes were showed decreased from $8.6\;{\mu}m$ to $10\;{\mu}m$, and varistor voltages were decreased from 506 V to 460 V by added amount of glass-frit. Nonlinear coefficient ${\alpha}$, of all were with increasing the amount of glass-frit more than 60, in case of added on 0.03wt% glass-frit was 83. And leakage current were less than $1{\mu}A$ with applied at 82% of varistor voltage. The clamping voltage ratio of the specimes added 0.03wt% glass-frit was 1.41 at applied 25A $[8/20{\mu}s]$. In the specimen added 0.03wt% glass-frit, endurence of surge current and deviation of varistor voltage were $6200A/cm^2$, $\Delta-1.67%$, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.307-308
• /
• 2005

ZnO varistor ceramics were fabricated as a function of the sintering temperature from $1125^{\circ}C$ to $1200^{\circ}C$ with glass-frit 0.03wt% addition. The average grain size was increased from 10.4 ${\mu}m$ to 23.7 ${\mu}m$, and varistor voltage was decreased from 538 V to 329 V with rising of the sintering temperature. The nonlinear coefficient a showed similar value from 75 to 80 and leakage current of all specimens exhibited the result of $1{\mu}A$ at 82% of varistor voltage. But the clamping voltage ratio of the specimens sintered at $1175^{\circ}C$ was 1.37 at 25A [$8/20{\mu}s$]. Also, endurance of surge current and deviation of varistor voltage of sintered specimens at $1175^{\circ}C$ were $6400A/cm^2$, $\Delta$-3.32%, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.625-628
• /
• 2002

The electrical properties of the praseodymium-based ZnO varistor ceramics, which are composed of Zn-Pr-Co-Cr-Dy oxides were investigated with $Dy_2O_3$ amount. The average grain size of varistor ceramics was greatly decreased from 18.2 to 4.6 pm with increasing $Dy_2O_3$ amount. The calculated nonlinear exponent$({\alpha})$ in varistor ceramics without $DY_2O_3$ was only 4.9, whereas the a value of the varistors with $DY_2O_3$ was abruptly increased in the range of 48.8 to 58.6. In particular, the maximum value of a was obtained by doping of 1.0 mol% $DY_2O_3$, reaching 58.6. The measured leakage current$(I_l)$ value in varistors without $DY_2O_3$ was $85.45{\mu}A$, whereas the $I_{\ell}$ value of the varistors with $DY_2O_3$ was very abruptly decreased in the range of 1.10 to $0.12{\mu}A$. In particular, the minimum value of $I_{\ell}$ was obtained by doping of 0.5 mol% $DY_2O_3$, reaching $0.12{\mu}A$. The tan $\delta$ varied in V-shape, with minimum 2.28% at 0.5 mol% $DY_2O_3$. The donor concentration and the density of interface states were decreased in the range of $(4.66{\sim}0.25){\times}10^{18}cm^3$ and $(5.70{\sim}1.39){\times}10^{12}/cm^2$, respectively, as $DY_2O_3$ amount is increased.

• 대한전기학회논문지
• /
• 제34권5호
• /
• pp.186-192
• /
• 1985

Co2O3 additive effects on the electrical properties in ZnO varistor are investigated. As the Co Cations being substituted and ionized normally to a divalent state for Zn in the lattice site increase, the leakage current in the prebreakdown region decreases and the so-called

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 춘계학술대회 논문집 반도체 재료 센서 박막재료 전자세라믹스
• /
• pp.179-182
• /
• 2004

ZnO varistor for transmission class arrester$({\Phi}65{\times}20mm)$ of 10kA(Class 3) grade was recently developed in korea and is tested for the properties by switching surge operating duty test to know the line discharge class and complex surge property in electric properties. To find out changing rate of residual voltage before and after lightning impulse residual voltage testing, the sample is cool to room temperature after finishing switching surge operating duty test, and the rate is good as 1.0~1.7%. The element had been considered as applicable ZnO varistor for electricity transmission from the test results of state conterl, switching surge operating duty, thermal stability and above test. But various test should be required for actual application because this is a part of the to be needed for application.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2004년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.67-69
• /
• 2004

ZnO varistor ceramics which were fabricated with variation of added of 0.01, 0.02, 0.03, 0.05, 0.1mol% $Nb_2O_5$ sintered at $1150^{\circ}C$. In the specimen added 0.05mol% $Nb_2O_5$, sintered density was $5.87g/cm^3$ and electrical properties were superior to any other components. The nonlinear coefficient was 75, and clamping voltage ratio was 1.40. And, endurance surge current in the specimen added 0.05mol% $Nb_2O_5$ was $6500A/cm^2$, and deviation of varistor voltage was -1.7%. As P.C.T and T.C.T environment test were succeed in all specimens, and deviation of varistor voltage in the specimen added 0.3mol% $Nb_2O_5$ was -0.81%. All specimens showed a good leakage current property in the High Temperature Continuous Load Test for 1000hr, at $85^{\circ}C$, and variation rate of the varistor voltage was -1.71%.

• 한국재료학회지
• /
• 제15권3호
• /
• pp.143-148
• /
• 2005

The microstructure, electrical properties, and clamping voltage characteristics of $ZnO-Pr_6O_{11}-CoO-Cr_2O_3-Y_2O_3(ZPCCY)-based$ varistor ceramics sintered at $1350^{\circ}C$ were investigated as a function of sintering time from 1 to 3 h. With increasing sintering time, the average grain size and density increased in the range of $11.4\~16.0\;{\mu}m$ and $5.34\~5.54g/cm^3$, respectively, in accordance of increasing sintering time. The nonlinear exponent decreased in the range of $60\~26$ and the leakage current increased in the range of $1.3\~10.7\;{\mu}A$ with increasing sintering time. The clamping voltage ratio increased in the range $1.58\~1.65$ for ratio surge current of 10 A as the sintering time increased.