Affect of Varistor Properties by Glass Frit Addition

Glass-Frit 첨가가 바리스터의 특성에 미치는 영향

ZnO varistor ceramics were fabricated with variation of addition of glass-frit amount and the sintering temperature was $1150^{\circ}C$. The average grain sizes were showed decreased from $8.6\;{\mu}m$ to $10\;{\mu}m$, and varistor voltages were decreased from 506 V to 460 V by added amount of glass-frit. Nonlinear coefficient ${\alpha}$, of all were with increasing the amount of glass-frit more than 60, in case of added on 0.03wt% glass-frit was 83. And leakage current were less than $1{\mu}A$ with applied at 82% of varistor voltage. The clamping voltage ratio of the specimes added 0.03wt% glass-frit was 1.41 at applied 25A $[8/20{\mu}s]$. In the specimen added 0.03wt% glass-frit, endurence of surge current and deviation of varistor voltage were $6200A/cm^2$, $\Delta-1.67%$, respectively.