• 한국세라믹학회지
• /
• 제25권5호
• /
• pp.552-560
• /
• 1988

ZnO low voltage varistor was obtained by varying a) the amount of seed grains, b) the size of seed grains, and c) sintering temperature. Also, the optimum condition for fabricating the ZnO seed grains was studied. Large ZnO seed grains were obtained by washing a ZnO sintered body containing 1m/of BaCO3 in boiling water. When the seed grains were added, abnormal grain growth occurred, and the varistor voltage sharply decreased. However, when more than 5w/o of seed grain content was added, the varistor voltage gradually increased. When 10w/o seed grains of 75~106${\mu}{\textrm}{m}$ were added and sintered for 2 hours at 1200 to 125$0^{\circ}C$, low voltage varistor properties with V1mA/mm of 19V/mm and nonlinear exponent ($\alpha$) of 12 occurred.

• 한국전기전자재료학회논문지
• /
• 제19권7호
• /
• pp.662-666
• /
• 2006

Microstructure and electrical properties of ZnO varistors as a function of sintering temperature and times were investigated. Sintering temperature and times greatly affected electrical properties and Bi-rich liquid phase of the microstructure. The varistor which were sintered at $1125^{\circ}C\sim1150^{\circ}C$, for 2 hr exhibited the varistor voltage$(V_c)$, nonlinear coefficient $(V_{10mA}/V_{1mA})$, leakage current$(I_L)$ dielectric constant and dissipation factor as $225\sim250V/mm,\;0.89\sim0.92,\;0.8\sim1.1{\mu}A,\;720\sim740\;and\;1.8\sim2.0%$, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.603-606
• /
• 2004

ZnO varistor ceramics were fabricated with variation of addition of $Nd_2O_3$ amount and the sintering temperature was $l150^{/circ}C$. The average grain sizes were showed decreased from $13.8{\mu}m$ to $4.7{\mu}m$, and varistor voltages were increased from 398 V to 657 V by added amount of $Nd_2O_3$. Nonlinear coefficient a of all were with increasing the amount of $Nd_2O_3$ more than 60, in case of added on 0.1mol% $Nd_2O_3$ was 87. And leakage current were less than $1_{\mu}A$ with applied at 82% of varistor voltage. The clamping voltage ratio of the specimes added 0.1mol% $Nd_2O_3$ was 1.38 at applied 25A [$8/20{\mu}s$]. In the specimen added 0.1mol% $Nd_2O_3$, endurence of surge current and deviation of varistor voltage were 7000A/$cm^2$, $\Delta-2.08%$, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.375-378
• /
• 2004

ZnO varistor ceramics were fabricated with variation of addition of glass-frit amount and the sintering temperature was $1150^{\circ}C$. The average grain sizes were showed decreased from $8.6\;{\mu}m$ to $10\;{\mu}m$, and varistor voltages were decreased from 506 V to 460 V by added amount of glass-frit. Nonlinear coefficient ${\alpha}$, of all were with increasing the amount of glass-frit more than 60, in case of added on 0.03wt% glass-frit was 83. And leakage current were less than $1{\mu}A$ with applied at 82% of varistor voltage. The clamping voltage ratio of the specimes added 0.03wt% glass-frit was 1.41 at applied 25A $[8/20{\mu}s]$. In the specimen added 0.03wt% glass-frit, endurence of surge current and deviation of varistor voltage were $6200A/cm^2$, $\Delta-1.67%$, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.307-308
• /
• 2005

ZnO varistor ceramics were fabricated as a function of the sintering temperature from $1125^{\circ}C$ to $1200^{\circ}C$ with glass-frit 0.03wt% addition. The average grain size was increased from 10.4 ${\mu}m$ to 23.7 ${\mu}m$, and varistor voltage was decreased from 538 V to 329 V with rising of the sintering temperature. The nonlinear coefficient a showed similar value from 75 to 80 and leakage current of all specimens exhibited the result of $1{\mu}A$ at 82% of varistor voltage. But the clamping voltage ratio of the specimens sintered at $1175^{\circ}C$ was 1.37 at 25A [$8/20{\mu}s$]. Also, endurance of surge current and deviation of varistor voltage of sintered specimens at $1175^{\circ}C$ were $6400A/cm^2$, $\Delta$-3.32%, respectively.

• Transactions on Electrical and Electronic Materials
• /
• 제16권6호
• /
• pp.308-311
• /
• 2015

V₂O₅/Mn₃O₄/Nb₂O₅ codoped zinc oxide varistor ceramics were sintered at a temperature range as low as 875~950℃. The voltage clamping characteristics of V₂O₅/Mn₃O₄/Nb₂O₅ codoped zinc oxide varistor ceramics were investigated at a pulse current range of 1~50 A. The sintering temperature had a significant effect on clamp voltage ratio, which exhibits surge protection capabilities. The varistor ceramics sintered at 875℃ exhibited the best clamping characteristics, in which the clamp voltage ratio was 2.69 at a pulse current of 50 A. The varistor ceramics sintered at 900℃ exhibited the highest electrical stability, where = 3,824 V/cm (initial 3,909 V/cm), and E_{1 mA/cm²} = 27 (initial 39) after application of a pulse current of 100 A.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 하계학술대회 논문집 E
• /
• pp.2161-2163
• /
• 1999

Generally, ZnO varistors have dynamic characteristics that the cut-off voltage increases as the time to crest of the varistor current decreases. Dynamic characteristics of ZnO varistor are the most important factor in region of the steep front discharge current particularly. Also, V-I characteristics of ZnO varistor have hysterisis loop in time domain and frequency dependency. This paper deals with ZnO varistor numerical equation and modeling method which takes the behavior of varying clamping voltage into consideration during the time to crest, in range of $1{\mu}m{\sim}50{\mu}m$, of impulse current applied to a ZnO varistor. The simulated results by the proposed model are compared with experimental results for each of the impulse current.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.328-329
• /
• 2005

ZnO 바리스터의 소결조건에 따른 바리스터 특성과 유전특성을 조사하였다. 소결조건에서 소결시간 및 시간에 따라 바리스터 전압의 변화를 볼 수 있었으며 적정소결온도에서 바리스터 전압 $V_{1mA}$ 및 $V_{10mA}/V_{1mA}$특성은 225 ~ 250. 0.85 ~ 0.9의 특성을 얻을 수 있었다. 특히, 유전특성의 경우 주파수에 따라 정전용량의 변화가 높은 온도에서 소결한 경우 높게 나타났으며 적정 소결온도에서는 유전율은 720 ~ 740, 유전손실은 2.5% 이하의 값을 얻을 수 있었다.

• 한국재료학회지
• /
• 제16권7호
• /
• pp.416-421
• /
• 2006

The varistor properties of ZPCCL-based ceramics were investigated at different $La_2O_3$ contents in the range of $0{\sim}2.0$ mol%. As $La_2O_3$ content increased, the ceramic density greatly increased in the range of $4.71{\sim}5.77\;g/cm^3$ and the varistor voltage greatly decreased in the range of $503.5{\sim}9.4$ V. The varistor with 0.5 mol% $La_2O_3$ exhibited good nonlinearity, in which the nonlinear exponent is 81.6 and the leakage current is 0.2 ${\mu}A$. Furthermore, the varistors exhibited the high electrical stability, with $%{\Delta}V_{1mA}=-1.1%,%{\Delta}{\alpha}=-3.7%$, and $%{\Delta}I_L=+100%$ for DC accelerated aging stress condition of 0.95 $V_{1mA}/150^{\circ}C/24$ h.

• 한국전기전자재료학회논문지
• /
• 제18권12호
• /
• pp.1111-1116
• /
• 2005

ZnO varistor ceramics added a glass-frit 0.03 $wt\%$ were fabricated with variation of sintering temperature. The sintering temperature and time were $1125^{\circ}C\~1200^{\circ}C$ and 2 h. The average grain sizes increased and the varistor voltage decreased with increasing the sintering temperature. The values of the specimen sintered at $1200^{\circ}C$ were $23.7\;{\mu}m$ and 329 V, respectively. The leakage current of all specimens was less than $1\;{\mu}A$ at DC $82\%$ of varistor voltage. The clamping voltage ratio of the specimen sintered at $1175^{\circ}C$ was 1.37. The endurance of surge current and the deviation of varistor voltage of the specimen sintered at $1175^{\circ}C$ were 6400 $A/cm^2$ and ${\Delta}-2.81\%$, respectively. After the High Temperature Load Test(HTLT) at $85^{\circ}C$ for 1000 h, the specimen sintered at $1175^{\circ}C$ showed the lowest deviation of varistor voltage of ${\Delta}-1.92\%$.