• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.108-111
• /
• 2001

YBCO HTS thick films coated using powder, Y$_2$O$_3$+L, quenched over 1200$^{\circ}C$ was studied. Quenched powder was crushed and mixed well in order to obtain uniformly dispersed Y2ll. Also, the powder was prepared with various condition in other to acquire optimum micro structure. As a result, it was found that the quenched sample on 1300$^{\circ}C$, holding time of 30min, has a bettor characteristic than other sample. On the other hand, the effect of film thickness was investigated. We concluded that the initiate film thickness has to be over 150$\mu\textrm{m}$. Especially, it was found that the film coated over 3 times with 50$\mu\textrm{m}$ m was best quality.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.482-485
• /
• 2002

We synthesize a (Y,Sm)BCO(its composition is (Y/Sm123+0.4Y/Sm211)+1wt%CeO$_2$) powders using polymeric complex method. (Y,Sm)BCO powders are prepared as heated at 970$^{\circ}C$. For measurement of this characterization, We measure XRD and SEM. We use TSMG method for fabricatlon of (Y,Sm)BCO single crystal. The manufactured VBCO single crystal is measured by a magnetic distribution device using 0.5 Tesla magnet. As the result of this measurement, we find that a trapped magnet fields are 550 Gauss.