• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.68-69
• /
• 2005

Low temperature ($\leq900^{\circ}C$) sintering piezoelectric ceramics $0.01Pb(Mg_{1/2}W_{1/2})O_3$-0.41Pb$(Ni_{1/3}Nb_{2/3})O_3-0.35PbTiO_3-0.23PbZrO_3+0.1wt%Y_2O_3+xwt%ZnO$ $(0{\leq}x{\leq}2.5)$ have been developed and investigated. The electromechanical coupling coefficient ($k_p$), piezoelectric constant ($d_{33}$), and mechanical quality factor ($Q_m$) have been measured to characterize the piezoelectric materials system. When 2.0 wt% ZnO is added, the properties of the system, $d_{33}$ = 559 pC/N, $k_p$ = 55.0 % and $Q_m$ = 73.4 are obtained which are very suitable for piezoelectric actuators. A bending mode multilayer actuator has been also developed using the materials which size is $27(L)\times9(W)\times1.07(t)mm^3$. The actuators are fabricated by multilayer ceramic (MLC) process and consist of24 layers and each layer thickness is $35{\mu}m$. At this time, the displacement of actuator was $100{\mu}m$ at 28V.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.77-86
• /
• 2008

The reliability of leaded and lead-free solders of BGA type packages on a printed circuit board was investigated by employing the standard drop test and 4-point bending test. Tested solder joints were examined by optical microscopy to identify associated failure mode. Three-dimensional finite element analysis(FEM) with ANSYS Workbench v.11 was carried out to understand the mechanical behavior of solder joints under the influence of bending or drop impact. The results of numerical analysis are in good agreement with those obtained by experiments. Packages in the center of the PCB experienced higher stress than those in the perimeter of the PCB. The solder joints located in the outermost comer of the package suffered from higher stress than those located in center region. In both drop and bending impact tests, the lead-free solder showed better performances than the leaded solders. The numerical analysis results indicated that stress and strain behavior of solder joint were dependent on various effective parameters.

• Journal of the Korean Society of Radiology
• /
• v.15 no.6
• /
• pp.781-788
• /
• 2021

Due to the high sensitivity to radiation, excessive exposure needs to be prevented by accurately measuring the dose irradiated to the skin during radiation therapy. Although clinical trials use dosimeters such as film, OSLD, TLD, glass dosimeter, etc. to measure skin dose, these dosimeters have difficulty in accurate dosimetry on skin curves. In this study, to solve these problems, we developed a skin dosimeter that can be attached according to human flexion and evaluated its response characteristics. For the manufacture of the dosimeter, lead oxide (PbO) with high atomic number (Z_Pb: 82, Z_O: 8) and density (9.53 g/cm³) and silicon binders that can bend according to human flexion were used. In the case of a dosimeter made of PbO material, the performance degradation has been prevented by using parylene and others due to the presence of degradation due to oxidation, but the previously used parylene is affected by bending, so a new form of passive layer was produced and applied to the skin dosimeter. The characteristic evaluation of the skin dosimeter was evaluated by analyzing SEM, reproducibility, and linearity. Through SEM analysis, bending was evaluated, reproducibility and linearity at 6 MeV energy were evaluated, and applicability was assessed with a skin dosimeter. As a result of observing the dosimeter surface through SEM analysis, the parylene passive layer PbO dosimeter with the positive layer raised to the parylene produced cracks on the surface when bent. On the other hand, no crack was observed in the silicon passive layer PbO dosimeter, which was raised to silicon passive layer. In the reproducibility measurement results, the RSD of the silicon passive layer PbO dosimeter was 1.47% which satisfied the evaluation criteria RSD 1.5% and the linearity evaluation results showed the R² value of 0.9990, which satisfied the evaluation criteria R² 9990. The silicon passive layer PbO dosimeter was evaluated to be applicable to skin dosimeters by demonstrating high signal stability, precision, and accuracy in reproducibility and linearity, without cracking due to bending.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.27 no.8
• /
• pp.958-968
• /
• 2003

The purpose of this study was to clarify the different mechanical properties of fabrics among the theme groups classified by fashion fabric trend. This study can be useful for fabric marketers and planners to design new products. In order to carry out this study, the fabric samples of representative theme for‘2002/03 F/W fashion fabric trend were collected from a fashion company and were measured to analyze the mechanical properties, hand value(H.V) and total hand value(T.H.V) by KES-FB System. The results were as follows. 1. The theme-A of‘Luxury, Elegance’was consisted of wool, rayon and PET and had a lower B, 2HB of bending properties and a lower G and 2HG5 of shear properties. The theme-B of‘Technical, Functional’was consisted of synthetic fibers such as PET, PA, PU and elastic fiber and had a higher MIU and a lower MMD, SMD of surface properties. The theme-C of‘Vintage, Aged’was consisted of mostly cotton and had the highest B and 2HB. The theme-D of‘Fancy, Airy’was consisted of mostly woolen wool, polyacryl and polyamide and had a high MMD and SMD of surface properties and a high LC and RC of compression properties. 2. As the results of analyzing H.V and T.H.V through KES-FB system, the theme-A showed a higher Smoothness and lower Stiffness. The theme-B had a lower Smoothness, Fullness, Soft feeling and T.H.V and the theme-C had the highest Stiffness. The theme-D showed the highest Fullness and Soft Feeling but the lowest Stiffness.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.487-487
• /
• 2011

Recently graphene has emerged as a fascinating 2D system in condensed-matter physics as well as a new material for the development of nanotechnology. The unusual electronic band structure of graphene allows it to exhibit a strong ambipolar electric field effect with high mobility. These properties lead to the possibility of its application in high-performance transparent conducting films (TCFs). Compared to indium tin oxide (ITO) electrodes, which have a typical sheet resistance of ${\sim}60{\Omega}$/sq and ~85 % transmittance in the visible range (400?900 nm), the CVD-grown graphene electrodes have a higher/flatter transmittance in the visible to IR region and are more robust under bending. Nevertheless, the lowest sheet resistance of the currently available CVD graphene electrodes is higher than that of ITO. Here, we report an ingenious strategy, irradiation of MeV electron beam (e-beam) at room temperature under ambient condition, for obtaining size-homogeneous gold nanoparticle decorated on graphene. The nano-particlization promoted by MeV e-beam irradiation was investigated by transmission electron microscopy, electron energy loss spectroscopy elemental mapping, and energy dispersive X-ray spectroscopy. These results clearly revealed that gold nanoparticle with 10 ~ 15 nm in mean size were decorated along the surface of the graphene after 1.5 MeV-e-beam irradiation. A chemical transformation and charge transfer for the metal gold nanoparticle were systematically explored by X-ray photoelectron spectroscopy and Raman spectroscopy. This approach advances the numerous applications of graphene films as transparent conducting electrodes.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.47 no.3
• /
• pp.577-592
• /
• 2023

In this study, nanofiber-based textile sensors were developed for motion detection and monitoring. Poly(vinylidene fluoride) (PVDF) nanofibers containing zinc oxide (ZnO) nanoparticles and silver nanowires (AgNW) were fabricated using electrospinning. PVDF was chosen as a piezoelectric polymer, zinc oxide as a piezoelectric ceramic, and AgNW as a metal to improve electric conductivity. The PVDF/ZnO/AgNW nanocomposite fibers were used to develop a textile sensor, which was then incorporated into an elbow band to develop a wearable smart band. Changes in the output voltage and peak-to-peak voltage (V_p-p) generated by the joint's flexion and extension were investigated using a dummy elbow. The β-phase crystallinity of pure PVDF nanofibers was 58% when analyzed using Fourier transform infrared spectroscopy; however, the β-phase crystallinity increased to 70% in PVDF nanofibers containing ZnO and to 78% in PVDF nanocomposite fibers containing both ZnO and AgNW. The textile sensor's output voltage values varied with joint-bending angle; upon increasing the joint angle from 45° to 90° to 150°, the V_p-p value increased from 0.321 V_p-p to 0.542 V_p-p to 0.660 V_p-p respectively. This suggests that the textile sensor can be used to detect and monitor body movements.

• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.1418-1419
• /
• 2011

차세대 전력 반도체인 고전압 GaN 쇼트키 장벽 다이오드의 역방향 특성을 개선하기 위해서 열 산화공정이 제안되었다. AlGaN/GaN 에피탁시 위에 쇼트키 장벽 다이오드 구조가 제작되었으며, 쇼트키 컨택은 증착 후 $450^{\circ}C$에서 산화되었다. 열 산화공정이 메사 측벽의 AlGaN 및 GaN 표면에 $AlO_x$ 및 $GaO_x$를 형성하여 표면으로 흐르는 누설전류를 억제한다. 표면 및 GaN 버퍼를 통한 누설전류는 열 산화 공정 이후 100 ${\mu}m$-너비당 51.3 nA에서 24.9 pA로 1/2000 배 수준으로 감소하였다. 표면 산화물 형성으로 인하여 생성된 Ga-vacancy와 Al-vacancy는 acceptor로 동작하여 surface band bending을 증가시켜 쇼트키 장벽 높이를 증가시킨다. 애노드-캐소드 간격이 5 ${\mu}m$인 제작된 소자는 0.99 eV의 높은 쇼트키 장벽 높이를 획득하여, -100 V에서 0.002 A/$cm^2$의 낮은 누설전류를 확보하였다. 애노드-캐소드 간격이 5에서 10, 20, 50 ${\mu}m$로 증가되면 소자의 항복전압은 348 V에서 396, 606, 941 V로 증가되었다. 열 산화공정은 전력용 GaN 전자소자의 누설전류감소와 항복전압 증가를 위한 후처리 공정으로 적합하다.

• Journal of Industrial and Engineering Chemistry
• /
• v.68
• /
• pp.399-405
• /
• 2018

We report the fabrication of organic field-effect transistors (OFETs) via spray coating of electrochemically exfoliated graphene (EEG) and conducting polymer hybrid as electrodes. To reduce the roughness and sheet resistance of the EEG electrodes, subsequent coating of conducting polymer (poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS)) and acid treatment was performed. After that, active channel layer was developed by spin coating of semiconducting poly(3-hexylthiophene) on the hybrid electrodes to define the bottom gate bottom contact configuration. The OFET devices with the EEG/PEDOT:PSS hybrid electrodes showed a reasonable electrical performances (field effect mobility = $0.15cm^2V^{-1}\;s^{-1}$, on/off current ratio = $10^2$, and threshold voltage = -1.57V). Furthermore, the flexible OFET devices based on the Polydimethlsiloxane (PDMS) substrate and ion gel dielectric layer exhibited higher electrical performances (field effect mobility = $6.32cm^2V^{-1}\;s^{-1}$, on/off current ratio = $10^3$, and threshold voltage = -1.06V) and excellent electrical stability until 1000 cycles of bending test, which means that the hybrid electrode is applicable to various organic electronic devices, such as flexible OFETs, supercapacitors, organic sensors, and actuators.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1997.06a
• /
• pp.13-17
• /
• 1997

The densification of $Al_2$O$_3$/15v/o ZrO$_2$ (Zirconia Toughened Alumina: ZTA) to the 99% of theoretical density was attempted by controlling the processing parameters affecting the each processing step i.e., milling, spray-drying, forming and pressureless sintering. The ZTA processed under the identical conditions showed a large variation in the green and sintered densities, and the mechanical properties. The deviation of 4-point bending strength was more than 100MPa for the ZTA with ~99% of theoretical density. Moreover, the relative green and sintered densities were deviated greatly from the average value. This low reproducibility could be caused by the variation of spray-dried granule properties. Thus, the effect of yield strength and morphology of spray-dried ZTA granule on the green and sintered densities and the mechanical properties needs to be studied in detail. The objective of this work is to fine out the optimum condition of compaction pressure and compaction method depending on the properties of spray-dried granules.

• Advances in concrete construction
• /
• v.10 no.1
• /
• pp.71-79
• /
• 2020

Ultra-high-performance concrete (UHPC) is recognized as a promising material in future civil engineering projects due to its outstanding mechanical and durability properties. However, the lack of local UHPC materials and official standards, especially for prestressed UHPC structures, has limited the application of UHPC. In this research, a large-scale prestressed bridge girder composed of nonproprietary UHPC is produced and investigated. This work has two objectives to develop the mixing procedure required to create UHPC in large batches and to study the flexural behavior of the prestressed girder. The results demonstrate that a sizeable batch of UHPC can be produced by using a conventional concrete mixing system at any precast factory. In addition, incorporating local aggregates and using conventional mixing systems enables regional widespread use. The flexural behavior of a girder made by this UHPC is investigated including flexural strength, cracking pattern and development, load-deflection curve, and strain and neutral axis behaviors through a comprehensive bending test. The experimental data is similar to the theoretical results from analytical methods based on several standards and recommendations of UHPC design.