• Korean Chemical Engineering Research
• /
• v.55 no.5
• /
• pp.586-592
• /
• 2017

In this study, acrylic resins with solids content of 75% were prepared by addition polymerization of n-butyl acrylate (BA), methyl methacrylate (MMA), 2-hydroxypropyl methacrylate (HPMA) and acetoacetoxyethyl methacrylate (AAEM) monomers. At this time, the glass transition temperature ($T_g$) of the acrylic resin was changed to 20, 30 and $40^{\circ}C$, and the hydroxyl value (OH value) was changed to 60, 90 and 120. As a result, the viscosity of acrylic resin increased with increasing $T_g$ and hydroxyl (OH) value. The synthesized acrylic resin was designed to have a high cross-link density to maintain high elasticity and high durability. The crosslinked acrylic resin was used to prepare an acrylic urethane clear coating by curing reaction with a block isocyanate (Desmodur BL-3175). The physical properties of the clear paints were analyzed by measuring viscosity, adhesion, pencil hardness and $60^{\circ}$ specular gloss. Acrylic urethane clear coatings were prepared as specimens and evaluated for various properties to be applied as top coatings for coil coating. The prepared coatings were excellent in adhesion, excellent in $60^{\circ}$ specular gloss and pencil hardness, and eco-friendly.

• Corrosion Science and Technology
• /
• v.14 no.5
• /
• pp.213-217
• /
• 2015

Recently, household electronic industries require environmentally-friendly and highly functional steels in order to enhance the quality of human life. Customers especially require both excellent corrosion and abrasion resistant anti-fingerprint steels for digital TV panels. Thus POSCO has developed new functional electro-galvanized steels, which have double coated layers with organic-inorganic composites on the zinc surface of the steel for usage as the bottom chassis panel of TVs. The inorganic solution for the bottom layer consists of inorganic phosphate, magnesium, and zirconium compounds with a small amount of epoxy binder, and affords both improved adhesion properties by chemical conversion reactions and corrosion resistance due to a self-healing effect. The composite solution for the top layer was prepared by fine dispersion of organic-inorganic ingredients that consist of a urethane modified polyacrylate polymer, hardener, silica sol and a titanium complex inhibitor in aqueous media. Both composite solutions were coated on the steel surface by using a roll coater and then cured through an induction furnace in the electro-galvanizing line. New anti-fingerprint steel was evaluated for quality performance through such procedures as the salt spray test for corrosion resistance, tribological test for abrasion resistance, and conductivity test for surface electric conductance regarding to both types of polymer resin and coating weight of composite solution. New composite coated anti-fingerprint steels afford both better corrosion resistance and abrasion properties compared to conventional anti-fingerprint steel that mainly consists of acrylate polymers. Detailed discussions of both composite solutions and experimental results suggest that urethane modifications of acrylate polymers of composite solutions play a key role in enhanced quality performances.

• Polymer(Korea)
• /
• v.37 no.4
• /
• pp.455-461
• /
• 2013

Mar behavior and visibility were investigated by applying a constant load to various gloss-coated urethane-acrylate surfaces. Using a area-contact scratch tip which can apply a relatively low stress level to the coated surfaces, the mar damages were generated on the surfaces. When evaluating the mar-induced damage by means of delta-gloss (${\Delta}G$) and delta-luminance (${\Delta}L$) with existing test methodologies, an increase in constant load on the same gloss-coated surface leads to an increase in ${\Delta}G$ and ${\Delta}L$. However, these are not suitable for evaluating and comparing the surface damages of different gloss-coated samples because of a disagreement between the measured values and the mar visibility. It is shown that new mar test assessment proposed in this work not only can be used to quantitatively evaluate the mar damage, but also accounts for the correlation that the increases of the normalized gloss and luminance on coated surfaces correspond with an increase in the mar visibility.

• Clean Technology
• /
• v.12 no.1
• /
• pp.19-25
• /
• 2006

In this study, photo-cuarable urethane methacrylate oligomers were synthesized from polyether type polyol (PP series, GP series), isocyanate (2,4-toluene diisocyanate) and hydroxy acrylate (hydroxypropyl methacrylate). We measured basic property including color, viscosity and refractive index of resulting urethane methacrylate. Also we measured tensile strength, elongation, and Young's modulus after photo curing. Photo curing speed was investigated using photo-DSC (TA instrument). In the case of similar polyol structure, as the molecular weight of polyol is increased, tensile strength, Young's modulus, curing rate were decreased, but elongation was increased. As the number of functionality of urethane methacrylate oligomer is increased, tensile strength, Young's modulus, curing rate were increased, but elongation was decreased.

• Applied Chemistry for Engineering
• /
• v.20 no.1
• /
• pp.52-61
• /
• 2009

In this study, TAPEH (t-amyl peroxy 2-ethyl hexanoate) was selected for the reaction initiator which is a core factor for developing acrylic polyol binder. Tone M100 (caprolactone acrylate), 4HBA (4-hydroxy butyl acrylate), and 2HEMA (2-hydroxy ethyl methacrylate) were used for hydroxy-monomers. To check the applicability of raw materials mentioned above into the binders of 2 components acrylic polyurethane paint and reduce the VOC, the reactivity and film performance by different kinds of aliphatic polyisocyanate hardeners which are already generalized were reviewed. As the Tin-based catalyst has been regulated, the comparison test of reactivity and performance between the conventional catalyst and non-toxic metal catalyst recommended as the alternative was conducted as well. As a result, we were able to obtain the basic data which are necessary for applying 2 components high solid polyurethane paint and also reached a conclusion that it can be applied for developing new paints in terms of high performance, workability and environmental care.

• Journal of the Korean Electrochemical Society
• /
• v.6 no.2
• /
• pp.98-102
• /
• 2003

Urethane acrylate oligomer was synthesized and used in a gel polymer electrolyte (GPE) and then its electrochemical performances were evaluated. $LiCoO_2/GPE/graphite$ cells were prepared and their performances depending on discharge currents and temperatures were evaluated. The precursor containing $5 vol\%$ curable mixture had a low viscosity relatively. ionic conductivity of the gel polymer electrolyte at room temperature and $-20^{\circ}C$ was ca. $5.9\times10^{-3}S{\cdot}cm^{-1}\;and\;1.4times10^{-3}S{\cdot}cm^{-1}$, respectively. GPE showed good electrochemical stability up to potential of 4.5V vs. RLi/Li^+.\;LiCoO_2/GPE/graphite$ cell showed a good high-rate and low-temperature performance.

• Applied Chemistry for Engineering
• /
• v.5 no.5
• /
• pp.857-861
• /
• 1994

UV curable hybrid systems have been investigated in the urethane acrylate based formulations where potentially irritant acrylate monomers have been substituted by vinyl ethers. Generally, among the systems studied, coating properties of hybrid system are superior to those of free radical hut inferior to those of cationic systems. When the content of acrylic oligomer is above 70%, however, hybrid system could render an excellent combination of coating and curing properties which outperforms both cationic and free radical systems. Photo-DSC has been used to follow the progress of crosslinking of various coating systems. Results imply that the critical factors in determining the curing rates of coating formulations are different depending upon the formulation characteristics. In the same type of hybrid formulations, the monomer/oligomer ratio rather than photoinitiator efficiency is the critical factor determining the curing rate of the systems.

• Polymer(Korea)
• /
• v.24 no.3
• /
• pp.389-398
• /
• 2000

Transparent, abrasion resistant coatings with 4~13 ${\mu}{\textrm}{m}$ thickness were prepared by spin-coating on polycarbonates with organic/inorganic hybrid solutions, followed by UV curing and heat treatment at 12$0^{\circ}C$ for 12 hours. The coating solutions were composed of inorganic phase and organic phase in 0:100, 20:80, 30:70, 50:50, 80:20 wt% ratios, respectively, mixed with photoinitiator, senaitizer and surfactant. The inorganic phase was formed by sol-gel reaction of TEOS and silane coupling agent MPTMS in 1 : 2 or 2 : 1 molar ratios, the organic phase consisted of difunctional urethane acrylate oligomeric resin, multifunctional acrylate TMPTA and HDDA in 4 : 3 : 3 wt% ratio. The coating systems were investigated by FT-IR, $^{29}$ Si-NMR spectra. In addition, TGA/DSC for thermal analysis and SEM, AFM observation for coated surface were examined. Gererally, the homogeneity of phases, the surface smoothness of coating and abrasion resistance were improved with the higher content of inorganic component. Namely, coating system with below 10 $\AA$ surface roughness and T$_{g}$ of 15$0^{\circ}C$ showed only 10% decrease in light transmittance after abrasion test, whereas uncoated polycarbonate substrate exhibited 46% decrease..

• Proceedings of the Korean Society of Soil and Groundwater Environment Conference
• /
• 2002.09a
• /
• pp.183-186
• /
• 2002

Experiments in the batch soil/aqueous systems were conducted to compare the sorption onto soil and extraction efficiency of sorbed phenanthrene in the presence of the micelle-forming anionic surfactant(SDS) or the micelle-like amphiphilic nano-sized polyurethane particles. Micelle-like amphiphilic nano-sized polyurethane(APU) particles synthesized from amphiphilic urethane acrylate anionomers(UAA) could solubilize phenanthrene within their hydrophobic interiors as the same way that surfactants micelles did in aqueous phase.

• Journal of the Semiconductor & Display Technology
• /
• v.16 no.1
• /
• pp.45-51
• /
• 2017

Poly(urethane acrylate) siloxane oligomers with Interpenetrating polymer netwoked nanoparticles were prepared to synthesize hard coating solution by reaction with diisocyanates. The diisocyanate combined siloxane hard coating solution showed more flexibility than the siloxane solution. In addition, diisocyanate resulted in improvement of curl property and surface hardness in the siloxane solution. Of the used diisocyanates, isophorone diisocyanate and acryloyloxy ethyl diisocyanate were good for UV hard coating solution. This effect will decrease brittleness in the siloxane solution using for plastic display plate.