Synthesis and Photopolymerization Kinetics of Polyether Urethane Methacrylate Oligomers

폴리에테르 우레탄 메타아크릴레이트 올리고머의 합성 및 광중합 동역학

  • Oh, Sungae (R&D Center, Miwon Commercial Co., Ltd.) ;
  • Park, Kwangbae (R&D Center, Miwon Commercial Co., Ltd.) ;
  • Park, Chanik (Department of Cosmeceutical Science, Daegu Haany University) ;
  • Bae, Won (R&D Center, Miwon Commercial Co., Ltd.)
  • 오성애 (미원상사(주) 연구소) ;
  • 박광배 (미원상사(주) 연구소) ;
  • 박찬익 (대구한의대학교 화장품약리학과) ;
  • 배원 (미원상사(주) 연구소)
  • Received : 2006.01.16
  • Accepted : 2006.02.14
  • Published : 2006.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, photo-cuarable urethane methacrylate oligomers were synthesized from polyether type polyol (PP series, GP series), isocyanate (2,4-toluene diisocyanate) and hydroxy acrylate (hydroxypropyl methacrylate). We measured basic property including color, viscosity and refractive index of resulting urethane methacrylate. Also we measured tensile strength, elongation, and Young's modulus after photo curing. Photo curing speed was investigated using photo-DSC (TA instrument). In the case of similar polyol structure, as the molecular weight of polyol is increased, tensile strength, Young's modulus, curing rate were decreased, but elongation was increased. As the number of functionality of urethane methacrylate oligomer is increased, tensile strength, Young's modulus, curing rate were increased, but elongation was decreased.

본 연구에서는 폴리에테르 계열의 폴리올과 이소시아네이트 (2,4-toluene diisocyanate) 그리고 하이드록시 아크릴레이트 (hydroxypropyl methacrylae)를 이용하여 광경화가 가능한 우레탄 메타아크릴레이트 계열의 올리고머를 합성하였다. 합성된 우레탄 메타아크릴레이트의 색상, 점도, 굴절율과 같은 기본적인 물성과 광경화후 필름에 대한 인장 강도, 신율, 영율 등을 측정하였다. 광경화 속도는 Photo-DSC를 이용하여 측정하였다. 유사한 폴리올 구조 내에서는 폴리올의 분자량이 증가하면 인장 강도, 영율, 광경화 속도는 감소하고 연신율은 증가하는 결과를 얻었다. 우레탄 메타아크릴레이트 올리고머의 관능기 숫자가 증가하면 인장 강도, 영율, 광경화 속도는 증가하고 반대로 연신율은 감소하는 결과를 얻게 되었다.

Keywords