The creep life of 9Cr1MoVNb steel, in terms of Larson-Miller parameter(LMP), was evaluated by small punch(SP) creep simulation and verified by uniaxial creep test. By employing the elastoplastic FEM(finite element method), the small punch creep behaviors associated with various friction coefficients were simulated to identify a real friction phenomena. The friction coefficient, ${\mu}$=0.7, determined by comparing deflection history was used in the small punch creep simulation to find the equivalent stresses with which the relationship between punch load and uniaxial creep stress was found. The creep life was then predicted by the LMP, which was the relationship among the rupture time, temperature, and stress. Finally, the LMP calculated by SP-creep simulation was compared with that had computed by the uniaxial creep test and fairly matched LMPs were found.

• Journal of the Korean Society for Precision Engineering
• /
• v.30 no.8
• /
• pp.809-814
• /
• 2013

The relationship between the small-punch creep test and the conventional creep test was investigated experimentally using a method similar to that of the Monkman-Grant relationship. Uniaxial and small-punch creep rupture tests were carried out on 9Cr-2W ferritic steel (Commercial Grade 92 steel: X10CrWMoVNb 9-2) at elevated temperatures. From the relation derived in the same manner as the Monkman-Grant relation, a correlation between the displacement rate in response to the small-punch creep test and the strain rate in the uniaxial creep test was found, and the creep life was calculated using this relation. Furthermore, the failure modes of the small punch creep test specimens were investigated to show that the fracture was caused by creep.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.111-116
• /
• 2001

Small punch-creep(SP-Creep) test technique has been applied for evaluating the creep characteristics for high temperature materials. However, in order to evaluate the damage and predict the remaining life, it is necessary to establish a quantitative correlation between SP-Creep and uniaxial-creep test results. This paper presents analytical and experimental results of useful correlation between SP-Creep and uniaxial-creep properties for 9Cr1MoVNb steel at $600{\sim}650^{\circ}C$ in terms of stress(load) and activation energy during creep deformation. Especially, the activation energy obtained from SP-Creep test is linearly related to that from uniaxial-creep test at $650^{\circ}C$ as follows: $Q_{sp-p}{\fallingdotseq}1.37\;Q_{TEN},\;Q_{sp-{\sigma}}{\fallingdotseq}1.53\;Q_{TEN}$.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1994.10a
• /
• pp.74-79
• /
• 1994

The log-log presentation of stress versus Larson-Miller parameter is obtained by uniaxial tensile test instead of the long time creep test. The used material for example calculations is SUS304 stainless steel. The temperature of the uniaxial tensile test can be determined by the Larson-Miller parameter of the design stress and the 0.1hr's rupture time of the uniaxial tensile test. The rupture time at the design temperature and stress can be determined by the Larson-Miller parameter of the stress. The average creep rate is the total deformation of the tensile test divided by the rupture time at the design stress and temperature. The liner trend and the order of the data of the average creep rate by this method is almost same as that of experimental results.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.99-104
• /
• 2000

This paper describes the high temperature creep characteristics for virgin material of 9Cr1MoVNb steel using small punch creep(SP-Creep) test technique which is developing recently. In addition, the several results of SP-Creep test are compared with that of 2.25Cr- 1Mo steel which is widely used as boiler materials and that of conventional uniaxial creep test. The obtained SP-Creep curves show the creep behaviors of three regimes like that obtained from conventional uniaxial creep test, and SP-Creep properties are definitely depended on applied load and test temperature. The correlation of SP-Creep rate and creep rupture life with applied load has been determined like the correlation between creep rate/rupture life and stress in uniaxial creep test, and also is satisfied with Power law. The creep rupture times of newly 9Cr1MoVNb steel are higher than those of 2.25Cr1Mo steel at the same creep temperature and applied loading condition, and the decrease extent of creep rupture life with loads is very lower compared with 2.25Cr1Mo steel.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.12
• /
• pp.2565-2573
• /
• 2002

A basic research was performed to ensure the usefulness of Small Punch-creep(SP-creep) test for residual life evaluation of heat resistant components effectively. This paper presents analytical results of initial stress and strain distributions in SP specimen caused by constant loading for SP-creep test and its experimental correlations with uniaxial creep(Ten-creep) test on 9Cr1MoVNb steel. It was shown that the initial maximum equivalent stress, ${\sigma}_{eq{\cdot}max}$ from FE analysis was correlated with steady-state equivalent creep strain rate, ${\epsilon}_{qf-ss'}$ rupture time, $t_r$, activation energy, Q and Larson-Miller Parameter, LMP during SP-creep deformation. The simple correlation laws, ${\sigma}_{sp}-{\sigma}_{TEN}$, $P_{sp}-{\sigma}_{TEN}\; and\; Q_{sp}-Q_{TEN}$ adopted to established a quantitative correlation between SP-creep and Ten-creep test data. Especially, the activation energy obtained from SP-creep test is linearly related to that from Ten-creep test at $650^{\circ}C$ as follows : $Q_{SP-P}\;{\risingdotseq}\;1.37 \;Q_{TEN},\; Q_{SP-{\sigma}}{\risingdotseq}1.53\; Q_{TEN}$.

• Korean Journal of Metals and Materials
• /
• v.48 no.11
• /
• pp.965-973
• /
• 2010

The small punch creep (SPC) test has recently received much attention as a new alternative to the conventional uniaxial creep test because it needs only a miniature-sized specimen directly detached from an operating system or component without any serious sampling damages. However, it is difficult to obtain the equivalent uniaxial creep data directly from the SPC data. As a specimen is deformed by a punch in the SPC test, the test result is sensitive to the friction between them. Finite element analyses with various friction coefficients was performed and showed a tendency of increased SPC life with an increased friction coefficient. The necking position predicted by the SPC simulation with a proper friction coefficient showed good agreement with that observed from the real SPC test. Finally, a noble method to convert the SPC load and displacement rate into the equivalent uniaxial creep stress and strain rate, respectively, was established in this study.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.43-48
• /
• 2000

In this study, a small punch creep(SP-Creep) test using miniaturized specimen$(10{\times}10{\times}0.5mm)$ has been described for the development of the newly semi-destructive creep test method for high temperature structural components such as headers and tubes of boiler turbine casino and rotor and reactor vessel. The SP-Creep testing technique has been applied to 2.25Cr-1Mo(STBA24) steel used widely as boiler tube material and the creep test temperature are varied at $550^{\circ}C{\sim}600^{\circ}C$. The overall deformations of SP-Creep curves are definitely depended with applied load and creep test temperature and show the creep behaviors of three steps like conventional uniaxial creep curves. The steady state creep rate${\delta}_{ss}$ of SP-Creep curve for miniaturized specimen increases with increasing creep temperature, but the exponential value with creep loading is decreased. The activation energy$(Q_{spc})$ during SP-Creep deformation with various test temperatures shows 605.7kJ/mol that is g.eater than 467.4kJ/mol reported in uniaxial creep test. This may be caused by the difference of stress states during creep deformation In two creep test. But from the experimental results, e.g. SP-Creep curve behaviors, the steady state creep rate${\delta}_{ss}$ with creep temperature, and the exponential value(n) with creep loading, it can be summarized that the SP-Creep test may be a useful test method to evaluate the creep properties of the heat resisting material.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.12
• /
• pp.1995-2001
• /
• 2001

In this study, a small punch creep(SP-Creep) test using miniaturized specimen(10${\times}$10${\times}$0.5mm) is described to develop the new creep test method for high temperature structural materials. The SP-Creep test is applied to 2.25Cr-lMo(STBA24) steel which is widely used as boiler tube material. The test temperatures applied for the creep deformation of miniaturized specimens are between 550∼600$^{\circ}C$. The SP-Creep curves depend definitely on applied load and creep temperature, and show the three stages of creep behavior like in conventional uniaxial tensile creep curves. The load exponent of miniaturized specimen decreases with increasing test temperature, and its behavior is similar to stress exponent behavior of uniaxial creep test. The creep activation energy obtained from the relationship between SP-Creep rate and test temperature decreases as the applied load increases. A predicting equation or SP-Creep rate for 2.25Cr-lMo steel is suggested. and a good agreement between experimental and calculated data has been found.

• International Journal of Concrete Structures and Materials
• /
• v.9 no.3
• /
• pp.337-343
• /
• 2015

Previous studies have shown that the drying shrinkage of recycled aggregate concrete (RAC) is greater than that of natural aggregate concrete (NAC). Drying shrinkage is the fundamental reason for the cracking of concrete, and tensile creep caused by the restraint of drying shrinkage plays a significant role in the cracking because it can relieve the tensile stress and results in the delay of cracking occurrence. However, up till now, all research has been focusing on the compressive creep of RAC. Therefore, in this study, a uniaxial restrained shrinkage cracking test was executed to investigate the tensile creep properties caused by the restraint of drying shrinkage of RAC. The mechanical properties, such as compressive strength, tensile splitting strength, and Young's modulus of RAC were also investigated in this study. The results confirmed that the tensile creep of RAC caused by the restraint of shrinkage was about 20-30 % larger than that of NAC.