• Proceedings of the Korean Geotechical Society Conference
• /
• 2000.11a
• /
• pp.353-360
• /
• 2000

We developed large diameter sampler (we called KICT type large diameter sampler) to obtain undisturbed clay and sand samples. In-situ test carried out in the In-Chon international airport and Kim-Hae. Also we obtained undisturbed sample with a hydraulic piston sampler in the nearly site and carried out unconfined compression test, consolidation test and triaxial test. The result, unconfined compression strength, secant modules, preconsolidation pressure and undrained shear strength of samples to obtain KICT type large diameter sampler are larger than that of samples to obtain hydraulic piston sampler. But failure strains and volume changes at the consolidation of samples to obtain KICT type large diameter sampler are smaller than that of samples to obtain hydraulic piston sampler

• Journal of The Korean Society of Agricultural Engineers
• /
• v.53 no.3
• /
• pp.83-91
• /
• 2011

This study aimed to investigate the engineering and environmental characteristics of phosphogypsum-cement-soil mixtures composed of phosphogypsum, soil, and a small amount of cement was analysed on the basis of the unconfined compression test, the tensile strength test, the freezing and thawing test, the wetting and drying test, SEM and EDS analysis, XRD analysis and Leaching test. The specimens were manufactured with soil, cement and phosphogypsum. The cement contents was 10 %, and the phosphogypsum contents was 10, 20, 30, and 40 % by the weight of total dry soil. Each specimen was manufactured after curing at constant temperature and humidity room for 3, 7 and 28 days, after which the engineering characteristics of phosphogypsum-cement-soil mixtures were investigated using the unconfined compression test, the tensile strength test, the freezing and thawing test, the wetting and drying test. The basic data were presented for the application of phosphogypsum-cement-soil mixtures as construction materials. To investigate the environmental characteristics, leaching test was performed and the leaching test results were far below than of regulatory requirement of Waste Management Act in Korea. Therefore the results show that phosphogypsum is environmentally safe and can be used as construction materials in environmental aspect.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.45 no.6
• /
• pp.144-152
• /
• 2003

Laboratory experiments were carried out to investigate the influence of pore water contamination on the treatment effect of sandy soil which was solidified by Portland cement. In the experiments, setting time of hydraulic cement that was mixed with contaminated mixing water was measured using Vicat equipment and observed the tendency of setting process with the kind of contaminants, organic or inorganic components. It was shown that organic contaminants of the mixing water affect largely on the initial setting process of hydraulic cement and inorganics, expecially heavy metals, did not affect on the initial setting process, otherwise it was appeared that setting time of the sandy soil that was contaminated with inorganic components was apparently faster than the sandy soil that did not include inorganic components even though organic concentrations was relatively low level (COD=200∼300) in the mixing water. The results of unconfined compression strength test (UCST) were well consistent with the results of Vicat equipment test.

• Geomechanics and Engineering
• /
• v.17 no.2
• /
• pp.195-206
• /
• 2019

The gypsiferous soils are significantly sensitive to moisture and the water has a severe destructive effect on them. Therefore, the effect of lime and silica fume addition on their mechanical properties, when subjected to water, is investigated. Gypsiferous soil specimens were mixed with 1, 2 and 3% lime and 1, 3, 5 and 7% silica fume, in terms of the dry weight of soil. The specimens were mixed at optimum moisture content and cured for 24 hours, 7 and 28 days. 86 specimens in the sizes of unconfined compression strength test mold were prepared to perform unconfined compressive strength and durability tests. The results proved that adding even 1% of each of these additives can lead to a 15 times increase in unconfined compressive strength, compared with untreated specimen, and this increases as the curing time is prolonged. Also, after soaking, the compressive strength of the specimens stabilized with 2 and 3% lime plus different percentages of silica fume was considerably higher than before soaking. The durability of the treated specimens increased significantly after soaking. Direct shear tests showed that lime treatment is more efficient than silica fume treatment. Moreover, it is concluded that the initial tangent modulus and the strain at failure increased as the normal stress of the test was increased. Also, the higher lime contents, up to certain limits, increase the shear strength. Therefore, simultaneous use of lime and silica fume is recommended to improve the geotechnical properties of gypsiferous soils.

• Journal of the Korean GEO-environmental Society
• /
• v.11 no.7
• /
• pp.33-43
• /
• 2010

The physical characteristics of the marine clay in the Korean Peninsula, specifically Pusan areas of the south coast of Korea, were previously studied and reliable data from harbor construction projects were used for the relationship analysis of geotechnical strength parameters. The sample of marine clay classified to ML, MH, CL, CH and ML-CL from USCS were included for the analysis while the samples classified to SC were excluded in order to raise the degree of data analysis. Geotechnical strength properties, such as undrained shear strength, sensitivity ratio, and effective friction angle were analyzed and evaluated using the data obtained from unconfined compression test, triaxial compression test and field vane test. Abnormal values were extracted through statistical analysis. Moreover, the reliability of the results was improved by performing the evaluation of disturbance. Linear regression analysis was used for the relationship analysis, between undrained shear strength and depth. The relationship equation between undrained shear strength and depth was derived from the analysis of unconfined and triaxial compression test data of samples obtained at same location. Consequently, The relationship between depth and undrained shear strength is $S_u=0.015148D+0.04624$ and the undrained shear strength derived from the triaxial compression test was estimated to be about 1.26 of derived from the unconfined compression test.

• The KSFM Journal of Fluid Machinery
• /
• v.19 no.3
• /
• pp.25-28
• /
• 2016

The Schmidt hammer test is one of the best nondestructive tests to measure the strength without breaking structures, which has been used to measure the strength of concrete structures in a simple way at construction sites. However, the future research is needed to apply Schmidt hammer in cold regions. This study is intended to investigate the correlation between unconfined compression test result of the oil storage facilities foundation taken at the King Sejong Antarctic Station and Schmidt hammer test result at the sample-taking site. Also, the equation for uniaxial compression strength using Schmidt hammer rebound value is proposed.

• Journal of Industrial Technology
• /
• v.29 no.B
• /
• pp.73-80
• /
• 2009

This paper is to investigate effect of B.G.I (Best Grouting Innovation) method on reinforcing ground. In this thesis, extensive literature review was performed to summarize theoretical backgrounds of grouting and to compare the applicability of different grouting methods. Unconfined compression test with specimen prepared by injecting different grouts of B.G.I, S.G.R and L.W methods and by changing the curing time were carried out to figure out characteristics of initial unconfined compression strength mobilized in the early stage. As results of test, the compression strength increases with curing times and specimen prepared with grouts of B.G.I method show greater values than others. On the other hands, the measured values of pH are in the range of 7-10 during tests. In field, preliminary construction to main construction at several sites were performed to confirm the effect of reinforcing the ground by application of B.G.I method. From the results of permeability test in field, SPT test and phenol reaction test, it was found that N values after grouting are greater than those before grouting and values of permeability in grouted ground is reduced significantly.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.22 no.3
• /
• pp.60-74
• /
• 1980

Soil-cement mixtures involve problems in it's durability in grain size distribution and mineral composition of the used soils as well as in cement content, compaction energy, molding water content, and curing. As an attempt to solve the problems associated with durability of weathered granite soil with cement treated was investigated by conducting tests such as unconfined compression test, it's moisture, immers, wet-dry and freeze-thaw curing, mesurement of loss of weight with wet-dry and freeze-thaw by KS F criteria and CBR test with moisture curing on the five soil samples different in weathering and mineral composition. The experimental results are summarized as follows; The unconfined compressive strength was higher in moisture curing rather than in the immers and wet-dry, while it was lowest in freeze-thaw. Decreasing ratio of unconfined compressive strength in soil-cement mixtures were lowest in optimum moisture content or in the dry side rather than optimum moisture content with freeze-thaw. The highly significant ceofficient was obtained between the cement content and loss of weight with freeze-thaw and wet-dry. It was possible to obtain the durability of soil-cement mixtures, as the materials of base for roads, containing above 4 % of cement content, above 3Okg/cm$_2$ of unconfined compressive trength with seven days moisture curing or 12 cycle of freeze-thaw after it, above 100% of relative unconfined compressive strength, 80% of index of resistance, below 14% of loss of weight with 12 cycle of wet-dry and above 1. 80g/cm$_2$ of dry density.

• Journal of Ocean Engineering and Technology
• /
• v.19 no.6 s.67
• /
• pp.44-49
• /
• 2005

This paper investigates strength characteristics and stress-strain behaviors of unreinforced and reinforced lightweight soils. Lightweight soil, composed of dredged soil, cement, and air-foam, was reinforced by a waste fishing net, in order to increase its compressive strength. Test specimens were fabricated by various mixing conditions, such as cement content, initial water content, air content, and waste fishing net; then, unconfined compression tests were carried out on these specimens. From the test results, it was shown that reinforced lightweight soil had different behavior after failure, even though it had similar behavior as unreinforced lightweight soil before failure. The test results also showed that stress became constant after peak strength in reinforced lightweight soil, while the stress decreased continuously in unreinforced lightweight soil. It was observed that the strength was increased due to reinforcing effect by the waste fishing net for most cases, except high water content greater than $218\%$. In the case of high water content, a reinforcing effect is negligible, due to slip between waste fishing net and soil particles. In reinforced lightweight soil, secant modulus (E50) was increased, due to the inclusion of waste fishing net.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.8 no.2
• /
• pp.105-110
• /
• 2008

Flowable fill is generally a mixture of sand, fly ash, a small amount of cement and water. Sand is the major component of most flowable fill with waste materials. Various materials, including two waste foundry sands(WFS), an anti-corrosive waste foundry sand and natural soil, were used as a fine aggregate in this study. Natural sea sand was used for comparison. The flow behavior, hardening characteristics, and ultimate strength behavior of flowable fill were investigated. The unconfined compression test necessary to sustain walkability as the fresh flowable fill hardens was determined and the strength at 28-days appeared to correlate well with the water-to-cement ratio. The strength parameters, like cohesion and internal friction angle, were determined for the samples prepared by different curing times. The creep test for settlement potential was conducted. The data presented show that by-product foundry sand, an anti-corrosive WFS, and natural soil can be successfully used in controlled low strength materials(CLSM), and it provides similar or better properties to that of CLSM containing natural sea sand.