• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.225-229
• /
• 1996

In this study, in order to develop outdoor insulating materials, SIN(simultaneous interpenetrating polymer network) was introduced to Epoxy resin and the environment resistance was investigated. The single network structure specimen(E series) formed of Epoxy resin alone and simultaneous interpenetrating polymer network specimen (EM series) in which epoxy resin was taken as the first network and methyl methacrylate resin as the second network were manufactured. Ten kinds of specimens were manufacture by filler (SiO$_2$) content. SEM were utilized in order to confirm their network structure changes, and AC voltage dielectric strength was measured. Also, UV-test and tracking test were carried out investigate the environment resistance characteristic. Therefore the variations of network structure were happened as a result of SEM test, and it was confirmed that simultaneous interpenetrating polymer network specimens were more excellent than single network structure specimens.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.605-608
• /
• 1999

We report investigations on a Pentacene thin film as a component for active layer of Organic thin film transistors. Pentacene film was deposited by Organic Molecular Beam Deposition(OMBD) and Al electrode was deposoted by vacuum evaporation. Electrical characterization of Pentacene films were measured by the three-terminal contact resistance methods, as the results contact resistance between pentacene films and the Aluminium electrode is 5.064G$\Omega$. The Al contact with the pentacene shows the bottom contact resistance. From the current-voltage characteristics, electrical conductivity of the Pentacene film is found as ~ 10$^{-4}$ /cm. physical characterization of pentacene films were measured by UV-spectrum and Cyclic-Voltammetry method.

• Korean Journal of Mineralogy and Petrology
• /
• v.36 no.1
• /
• pp.1-17
• /
• 2023

On painting cultural properties to which Orpiment, a traditional yellow mineral pigment, is applied, the color's degeneration is frequently observed. To identify the cause of the degeneration, this study takes a look into orpiment and the various pigments that are mixed into it (Lead White, Lead Red, and Cinnabar) in powder and painting state. The pigment was mixed with Argyo glue and then applied to korean traditional paper and silk. Considering the possibility that alum causes the discoloration, it was applied to the specimen. With a UV tester, the powders and the painted specimens were subjected to a light resistance test in three phases (96 hour). Color changes were measured with a colorimeter and minerals, chemical composition and structural changes were analysed by XRD, SEM/EDS and Raman spectrometers. While the color change of pure Orpiment powder according to the light resistance test was small, the colored specimen became darker. The color change was large in the Orpiment colored on the silk and in the alum-treated specimen. In Orpiment powder was produced white arsenolite as altered orpiment after UV test. In the mixed powder of Orpiment and Lead White were detected only the constituent minerals of Orpiment and Lead White, and no altered substances were produced. Whereas after the UV test, orpiment and arsenolite, which were altered substances of orpiment, and the constituent minerals of Lead White were detected. In the case of mixing the two pigments in the powder state, darkening did not occur even by the UV test. However, the specimens colored with the mixed powder were darkened by the UV test. The color change of Orpiment was different depending on the mixed pigment and base material. The color change was greater in the case of alum treatment than in the case without alum treatment, and it was found that alum also had an influence on the color change of Orpiment.

• Polymer(Korea)
• /
• v.36 no.3
• /
• pp.287-294
• /
• 2012

ZnAl-LDH(layered double hydroxide) (Zn:Al=2:1 mole ratio) modified with stearic acid (SA) or oleic acid (OA) was synthesized by a coprecipitation method and compounded to SAN polymer at various contents. All the SAN composites were manufactured by a co-rotating twin-screw extruder and subsequently injection molded into several specimen. Morphology, transparency, and thermal resistance of these composites were evaluated by TEM, XRD(X-ray diffractometry), UV-Vis spectrophotometry, and thermogravimetric analysis. SAN nanocomposites containing OA-$Zn_2Al$ LDH showed better optical transmittance than SAN nanocomposites containing SA-$Zn_2Al$ LDH. All the SAN nanocomposites containing OA-$Zn_2Al$ LDH or SA-$Zn_2Al$ LDH exhibited improvement of thermal resistance at second stage of thermal oxidation. These results were explained by the fact that the interaction between organic modifier and polymer performed an important role in the property improvement of polymer nanocomposites.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.421-421
• /
• 2008

Generally, the polymer thick-film resistors for embedded organic or hybrid substrate are patterned by screen printing so that the accuracy of resistor pattern is not good and the tolerance of resistance is too high(${\pm}$20~30%). To reform these demerits, a method using Fodel$^{(R)}$ technology, which is the patterning method using a photosensitive resin to be developable by aqueous alkali-solution as a base polymer for thick-film pastes, was recently incorporated for the patterning of thermosetting thick-film resistor paste. Alkali-solution developable photosensitive resin system has a merit that the precise patterns can be obtained by UV exposure and aqueous development, so the essential point is to get the composition similar to PSR(photo solder resist) used for PCB process. In present research, we made the photopatternable resistor pastes using 8 kinds of epoxy acrylates and a conductive carbonblack (CDX-7055 Ultra), evaluated their developing performance, and then measured the resistance after final curing. To become developable by alkali-solution, epoxy acrylate oligomers with carboxyl group were prepared. Test coupons were fabricated by patterning copper foil on FR-4 CCL board, plating Ni/Au on the patterned copper electrode, applying the resistor paste on the board, exposing the applied paste to UV through Cr mask with resistor patterns, developing the exposed paste with aqueous alkali-solution (1wt% $Na_2CO_3$), drying the patterned paste at $80^{\circ}C$ oven, and then curing it at $200^{\circ}C$ during 1 hour. As a result, some test compositions couldn't be developed according to the kind of oligomer and, in the developed compositions, the measured resistance showed different results depending on the paste compositions though they had the same amount of carbonblack.

• Applied Chemistry for Engineering
• /
• v.10 no.4
• /
• pp.603-607
• /
• 1999

The polarization characteristics of poly(vinyl alcohol)-iodine complex, (PVA-KI system) prepared by the oxidation process of PVA film containing a potassium iodide (KI) were investigated. The UV-visible spectrum of the PVA-KI system polarizing film showed avsorption bands corresponding to $I^{-}$, $I{_3}{^-}$ and $I{_5}{^-}$ chromophoric species at 220 nm, 290~360 nm, respectively. The polarization efficiency and transmittance of PVA-KI system film were significantly influenced by oxidation time, stretching ratio and concentration of KI. The prepared polarizing film exhibited a high polarization efficiency(99.5%) and transmittance(45%). Especially, the heat resistance of the polarizing film was higher than that of a commercial PVA-$I_2$ polarizing film. It may be argued that the result should come from a difference in oxidation process of PVA polarizing film.

• Journal of the Korean Wood Science and Technology
• /
• v.28 no.1
• /
• pp.28-35
• /
• 2000

This paper deals with a coating technique for hardening surface layer of softwood(Larix leptolepis) flooring board to improve its surface properties such as hardness and abrasion resistance, Two coating methods were applied for surface hardening of the wood in this study. First, several functional monomers were added in UV-curing epoxy acrylate varnish. Secondly, unsaturated polyester varnish was used as under coat and acryl varnish including anti-abrasive agent was used as top coat. The hardness of the treated wood was similar to that of high density hardwood such as keruing by the first coating method. The abrasion resistance of the coated wood was greatly improved by the second method. Adhesion properties and impact resistance of the coated wood surface were also good. It was suggested that the well-coated softwood could be used as interior flooring board for heavy walking as substitute for hardwood.

• Journal of Surface Science and Engineering
• /
• v.50 no.5
• /
• pp.345-351
• /
• 2017

A double-layered anti-reflective coating with hydrophilic/abrasion-resistant properties was studied using anatase titanium dioxide($TiO_2$) and silicon oxycarbide($SiO_xC_y$) thin film. $TiO_2$ and $SiO_xC_y$ thin films were sequentially deposited on a glass substrate by DC sputtering and PECVD, respectively. The optical properties were measured by UV-Vis-NIR spectrophotometer. The abrasion-resistance and the hydrophilicity were observed by a taber abrasion tester and a contact angle analyzer, respectively. The $TiO_2/SiO_xC_y$ double-layer thin film had an average transmittance of 91.3%, which was improved by 10% in the visible light region (400 to 800 nm) than that of the $TiO_2$ single-layer thin film. The contact angle of $TiO_2/SiO_xC_y$ film was $6.9^{\circ}$ right after UV exposure. After 9 days from the exposure, the contact angle was $10.2^{\circ}$, which was $33^{\circ}$ lower than that of the $TiO_2$ single-layer film. By the abrasion test, $SiO_xC_y$ film showed a superior abrasion-resistance to the $TiO_2$ film. Consequently, the $TiO_2/SiO_xC_y$ double-layer film has achieved superior anti-reflection, hydrophilicity, and abrasion resistance over the $TiO_2$ or $SiO_xC_y$ single-layer film.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.34 no.2
• /
• pp.41-47
• /
• 2024

In this study, the resistance characteristics of semi-insulating SiC single crystals grown using the PVT method were investigated, considering the purity level of SiC source powders used in PVT growth and the cooling procedure after crystal growth. Two β-SiC powders with different purities were employed, and the cooling rate after growth was adjusted to achieve various resistance values. 4-inch HPSI-SiC ingots were grown using the PVT method, utilizing SiC powders with low nitrogen concentration and relatively high nitrogen concentration. These ingots were then subjected to different cooling procedures to modify the cooling rate. Transmission/absorption spectra and crystal quality of the grown crystals were analyzed through UV/VIs/NIR spectroscopy and X-ray rocking curve analysis, respectively. Additionally, electrical properties were investigated through non-contact resistivity analysis to identify the dominant factors influencing resistivity properties.

• Journal of Adhesion and Interface
• /
• v.6 no.3
• /
• pp.19-25
• /
• 2005

Synthetic rubber based pressure-sensitive adhesives (PSAs) usually containing SIS or SBS block copolymer, tackifier, plasticizer, and other additives are now widely used on various applications. As these PSAs are physically crosslinked and can be applied without the use of solvent, they are thermally processable and environmentally friendly. However these PSAs cannot be used in high temperature applications and in applications where solvent and chemical resistance properties are required. We developed the PSA adding UV curable system, such as thiol-ene system, to increase adhesion properties at elevated temperature. The adhesion properties such as probe tack, peel strength, shear adhesion failure temperature (SAFT) were evaluated. The probe tack test was conducted with varying probe materials and coating thickness of PSAs. Using the contact angle, the surface property of the cured PSAs was also observed.