• Carbon letters
• /
• v.26
• /
• pp.51-60
• /
• 2018

An electroless deposition method was used to modify the surface properties of rice husk ceramic particles (RHC) by depositing nano-nickel on the surface of the RHC (Ni-RHC). The dry tribological performances of aluminum matrix composite adobes containing different contents of RHC and Ni-RHC particles have been investigated using a micro-tribometer. Results showed that the Ni-RHC particles substantially improved both the friction and wear properties of the Ni-RHC/aluminum matrix adobes. The optimal concentration was determined to be 15 wt% for both the RHC and Ni-RHC particles. The improvements in the tribological properties of aluminum adobes including the Ni-RHC were ascribed to friction-induced peeling off of Ni coating and formation of protection layer on the wear zone, both of which led to low friction and wear volume.

• Tribology and Lubricants
• /
• v.9 no.2
• /
• pp.63-69
• /
• 1993

The wear properties of two types of $Si_3N_4$(silicon nitride) exposed to high and low humidity were examined experimentally for various sliding speed. Bearing steel was used as the disk material at pin-on-disk type sliding. Wear rates of pressureless sintered-plus-hot-isostatic pressed Si3N4 were slightly lower than those of pressureless sintered $Si_3N_4$. It was observed that adsorbed moisture and sliding speed markedly influenced the wear properties of $Si_3N_4$. The highest wear rate was obtained under the high humidity and low sliding speed condition. As the sliding speed was increased, wear rates were decreased and the humidity effect on the wear rates of $Si_3N_4$ was lowered. The result that the $Si_3N_4$ pin showed a high wear rate under the high humidity condition was explained by the property change due to the adsorbed moisture, plowing action by the hard particles of $Fe_2O_3$ from the disk, and the corrosion effect at $Si_3N_4$ surface. Increase in sliding speed was supposed to have reduced the humidity effect on wear rate of $Si_3N_4$ by raising the temperature of both the bearing steel disk and $Si_3N_4$ pin specimen.

• Tribology and Lubricants
• /
• v.31 no.1
• /
• pp.28-34
• /
• 2015

This paper addresses the problems of using anti-freeze lubricants for different machines that must function at extremely low temperatures during winter operation in the Republic of Sakha (Yakutia). We discuss the possibility of obtaining anti-freeze base oils from Talakan crude oil, an area with major oil and gas deposits of the Republic of Sakha, and also provide the trade and technological classification of Talakan crude oil. We propose two different schemes for processing Talakan crude oil: the fuel scheme (obtaining light and heavy fractions as a fuel oil) and the base oil scheme (obtaining light fractions and base oils). We investigate the influence of pour point depressants on alkyl-methacrylate base on the low-temperature properties of the fractions obtained from Talakan crude oil and Korean base oils, and establish the optimal concentration of pour point depressants. We compare the properties of these fractions with the low-temperature properties of Korean base oils and find that the commercial oil "Ravenol 0W-40" provides optimistic results. We obtain oil with a pour point of minus $50^{\circ}C$ and a viscosity index greater than 100. The Design of Experiment was used to establish the optimum composition of the pour point depressants and the base oil S-8 to obtain lubricant oil with a kinematic viscosity of 17 cSt, viscosity index of 208, and a pour point of minus $64^{\circ}C$.

• Tribology and Lubricants
• /
• v.26 no.4
• /
• pp.246-253
• /
• 2010

Friction characteristics of the brake friction materials without environmentally regulated ingredients were examined to find their role in the brake performance. Five friction materials were produced based on a nearcommercial formulation by changing the relative amount of potentially hazardous ingredients to health and environment, such as $Sb_2S_3$, potassium titanate, and brass fiber. Tribological properties of the friction materials were obtained using a scale dynamometer and Krauss type tribometer. Results showed that the excluded three ingredients played important synergetic effects on tribological properties in terms of fade resistance, wear resistance and friction effectiveness. In particular, brass fibers played important roles in the friction stability by providing excellent thermal diffusivity at the friction interface. Potassium titanate whiskers showed excellent fade resistance and wear resistance compared to the substituted barite. Antimony trisulfide, on the other hand, showed little effect on the high temperature fade resistance and wear resistance, while it increased friction effectiveness at moderate temperatures. The friction materials without the three ingredients showed severe fade, indicating antisynergy effects.

• Tribology and Lubricants
• /
• v.21 no.2
• /
• pp.71-76
• /
• 2005

This paper compares of mechanical tensile properties of 6 kinds of copper foil. The beam lead made with copper foil. Different from other package type such as plastic package, Chip Size Package has a reliability problem in beam lead rather than solder joint in board level. A new tensile loading system was developed using voice-coil actuator. The new tensile loading system has a load cell with maximum capacity of 20 N and a non-contact position measuring system based on the principle of capacitance micrometry with 0.1nm resolution for displacement measurement. Strain was calculated from the measured displacement using FE analysis. The comparison of mechanical properties helps designer of package to choose copper for ensuring reliability of beam lead in early stage of semiconductor development.

• Tribology and Lubricants
• /
• v.28 no.3
• /
• pp.117-123
• /
• 2012

Tribological properties of hybrid type friction materials were studied. Hybrid friction materials were produced by combining non-steel(NS) and low-steel(LS) type friction materials. The emphasis of the investigation was given to possible synergistic effects from the two different friction materials, in terms of friction stability at high temperatures and the amplitude of friction oscillation, also known as stick-slip at low sliding speeds. The high temperature friction test results showed that the friction effectiveness of the hybrid friction material was well sustained compared to LS and NS friction materials. Wear resistance of the hybrid type was similar to LS friction materials. Examination of the rubbing surfaces after tests revealed that the friction characteristics of the hybrid friction material were attributed to the wear debris produced from low-steel friction materials, which were migrated to the surface of the non-steel friction material, forming new contact plateaus. The stick-slip amplitude and its frequency were pronounced when non-steel friction material was tested, while hybrid and low-steel types showed relatively small stick-slip amplitudes. These results suggest possible improvement of tribological properties by designing a hybrid composite of low-steel and non-steel friction materials.

• KSTLE International Journal
• /
• v.10 no.1_2
• /
• pp.1-5
• /
• 2009

This paper reports an investigation on nanotribological properties of silicon nanochannels coated by a diamond-like carbon (DLC) film. The nanochannels were fabricated on Si (100) wafers by using photolithography and reactive ion etching (RIE) techniques. The channeled surfaces (Si channels) were then further modified by coating thin DLC film. Water contact angle of the modified and unmodified Si surfaces was examined by an anglemeter using the sessile-drop method. Nanotribological properties, namely friction and adhesion forces, of the Si channels coated with DLC (DLC-coated Si channels) were investigated in comparison with those of the flat Si, DLC-coated flat Si (flat DLC), and Si channels, using an atomic force microscope (AFM). Results showed that the DLC-coated Si channels greatly increased hydrophobicity of silicon surfaces. The DLC coating and Si channels themselves individually reduced adhesion and friction forces of the flat Si. Further, the DLC-coated Si channels exhibited the lowest values of these forces, owing to the combined effect of reduced contact area through the channeling and low surface energy of the DLC. This combined modification could prove a promising method for tribological applications at small scales.

• Tribology and Lubricants
• /
• v.23 no.2
• /
• pp.66-72
• /
• 2007

[ $MoS_2$ ], is a well-known metal sulfide applied as solid lubricants and an additive to prolong the life of sintered bearings under severe conditions. However, the high price of $MoS_2$ limited its wide application. This study is aimed to investigate the possibility far application to solid lubricants for $Cu_2S$ as a substitute of $MoS_2$. Bronzes added $Cu_2S$ and $MoS_2$, are produced by powder metallurgy in this study, and then evaluated their friction and wear properties., as well as sintered bronze. The sliding wear test using pin-on-disc type machine, was conducted at several sliding speeds for three type test pieces sintered bronzes added $Cu_2S$ and $MoS_2$, and sintered bronze without lubricants. Addition of $Cu_2S$ to bronze leads to relatively good friction properties, although it is not so good as addition of $MoS_2$. However, the wear properies of sintered bronze added $Cu_2S$ are better than that of sintered bronze added $MoS_2$.

• Tribology and Lubricants
• /
• v.24 no.2
• /
• pp.96-103
• /
• 2008

PTFE is generally utilized as the form of composites with adding various fillers. The purpose of this paper lies on clarifying the friction and wear properties of the PTFE coating layer on steel. Especially, the effects of PTFE powder size for coating and surface roughness of the counter material on the properties are investigated. Sliding friction and wear tests are conducted at several sliding speeds by employing two types of PTFE coating layer using different powder sizes. One type of coating layer is composed of uniform fine powder, whereas the other type is made up of mixture powder of different sizes. As results, it is found that PTFE coating layer are effective to improve the wear resistance and to reduce the friction coefficient. It is clear that PTFE coating layers are abrasively removed by asperities of the counter material during sliding contact. However, PTFE coating layer with uniform fine powder shows somewhat better wear resistance than that with mixture powder of different sizes in low sliding speed region. It can be seen that the wear of the coating layer are drastically reduced because wear fragment from counter material are transferred to the coating layer. On the other hand, friction coefficient is shown not to be directly related with PTFE powder size in coating layer.

• Tribology and Lubricants
• /
• v.25 no.1
• /
• pp.61-65
• /
• 2009

Tribological properties of the semi-metallic friction materials containing different solid lubricants (graphite, $WS_2$, $MoS_2$) were investigated. The friction materials were fabricated with an experimental formulation and tested with gray cast iron disks. Results showed that graphite contributed to stabilize the friction coefficient during run-in processes. Also, graphite provided better fade resistance than that of $WS_2$ and $MoS_2$. At intermediate temperature ranges, however, friction materials with $WS_2$ or $MoS_2$ maintained higher friction effectiveness than that of graphite. On the other hand, friction materials containing $MoS_2$ showed increased wear rates than that with graphite or $WS_2$. Friction materials with proper combinations of two solid lubricants showed better friction and wear properties than that of the friction materials containing single solid lubricant.