The 1.6 vol% and 2.5 vol% TiNi/6061Al composites were fabricated by permanent mold casting for investigating the effect of heat treatment on tensile strength for composites. The tensile strength without T6 treatment at 293 K was increased with increasing the volume fraction of TiNi fiber and at 363 K the higher the pre-strain, the higher the tensile strength. The tensile strength of the composite with $T_{6}$ treatment at 293 K was found to increase with increasing both the amount of pre-strain and the volume fraction of TiNi fiber and was higher than that without $T_{6}$ treatment. It should be noted that the tensile strength 2.5vol%TiNi/6061Al composites rolled at a 38% reduction ratio was the maximum value of 298 MPa. The tensile strength of composites decreased with increasing the reduction ratio over 38% because of the rupture of TiNi fiber.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.10a
• /
• pp.127-130
• /
• 2002

The 2.5 vol% TiNi/6061Al composites were fabricated by permanent mold casting, and its microstructures and tensile test for the cold rolled composites with maximum 50% reduction ratio were investigated. In the case of TiNi fiber with 2mm interval in preform, the interface bonding of fabricated composites were good. EPMA analysis results were found the small amount of Mg, Si segregated interface of diffusion layer. Transverse section of TiNi fiber was decreased with increasing reduction ratio and 40% reduction ratio was observed microcrack from TiNi fiber. And the tensile strength of composites at 38% reduction ratio was 194MPa. In the case of over 38% reduction ratio, the decrease of the tensile strength was due to TiNi fiber rupture by excess working. The fracture mode was appeared brittle fracture with increasing reduction ratio

• Korean Journal of Materials Research
• /
• v.12 no.12
• /
• pp.955-961
• /
• 2002

2.7vol%TiNi/6061 Al composites with TiNi shape memory alloy as reinforcement were fabricated by vacuum hot press. It was investigated by OM, SEM, EPMA and XRD analysis for the behavior of diffusion layer formation on various heat treatment condition. Thickness of diffusion layer was increased proportionally according to heat treatment time. The layer was formed by the mutual diffusion of TiNi and Al. The diffusion rate from TiNi fiber to Al matrix was faster than that of reverse diffusion path. The more diffused layer was formed in Al matrix. The diffusion at interface layer was consisted of $A1_3$Ti, $Al_3$Ni analyzed by EPMA, XRD results.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.2
• /
• pp.99-107
• /
• 2009

This study produced a design curve and fatigue limit for a variation in volume ratio and reduction ratio of TiNi/Al composites. In many cases, stress-life curve does not indicate fatigue limit, so it was presented by probabilistic-stress-life curve. Goodman diagram was used to analyze the fatigue strength of materials with a finite life determined by repeated load and the fatigue strength of endurance limit with an infinite life. The fatigue experiment was conducted using the scenk-type plane bending specimen in same shape. The result of the fatigue test, which had been conducted under consistent stress amplitude, was examined. (i) The optimal condition for TiNi/Al in accordance with hot pressing (ii) Impacts of fatigue limit caused by a variation in reduction ratio and volume ratio of TiNi/Al composites (iii) Probability distribution for fatigue limit of TiNi/Al2024 and TiNi/Al6061.

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1057-1062
• /
• 2001

We investigated the change of mechanical properties for TiNi shape memory alloy by heat treatment. 6061Al matrix composites with TiNi shape memory alloy as reinforcement were fabricated by vacuum casting. TiNi alloy has the maximum tensile strength at 673K treated and there is no change of tensile strength and hardness at 448K treated. The composites, prepared by vacuum casting, showed good interface bonding by vacuum casting. It was about 3$\mu\textrm{m}$ of thickness of the diffusion layer. Tensile strength of the composite was in higher than that of 6061Al alloy as increased value of about 70MPa at room temperature and about 110MPa at 363K. We thought that the increase of the tensile strength at 363K was due to reverse transformation of the TiNi shape memory alloy.

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1028-1034
• /
• 2001

The 2.5 vol% TiNi/6061Al composites were fabricated by permanent mold casting. The microstructures and tensile test for the cold rolled composites with maximum 50% reduction ratio were investigated. In the case of TiNi fiber with 2mm interval in preform, the interface bonding of fabricated composites were good, interface diffusion layer of this composites was made by the mutual diffusion. Transverse section of TiNi fiber was decreased with increasing reduction ratio and longitudinal section of TiNi fiber showed multiple wave phenomenon. And the tensile strength of composites at 38% reduction ratio was the most high. In the case of over 38% reduction ratio, the decrease of the tensile strength was due to TiNi fiber rupture by excess working. The fracture mode was appeared brittle fracture with increasing reduction ratio.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.11a
• /
• pp.94-94
• /
• 2000

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.11a
• /
• pp.95-95
• /
• 2000

• Korean Journal of Materials Research
• /
• v.9 no.4
• /
• pp.419-427
• /
• 1999

TiNi shape memory alloy was shape memory heat-treated and investigated its mechanical properties with the variation of prestrain. Also 6061 Al matrix composites with TiNi shape memory alloy fiber as reinforcement have been fabricated by Permanent Mold Casting to investigate the microstructures and interface properties. Yield stress of TiNi wire was the most high in the case of before heat-treatment and then decreased as increasing heat-treatment time. In each heat-treatment condition, the yield stress of TiNi wire was not changed with increasing the amount of prestrain. The interface bonding of TiNi/6061Al composite was fine. There was a 2$\mu\textrm{m}$ thickness of diffusion reaction layer at the interface. We could find out that this diffusion reaction layer was made by the mutual diffusion. The diffusion rate from Al base to TiNi wire was faster than that of reverse diffusion and the amount of the diffusion was also a little more than that of reverse.

• Journal of Korea Foundry Society
• /
• v.18 no.6
• /
• pp.534-540
• /
• 1998

6061Al-matrix composite with TiNi shape memory fiber as reinforcement has been fabricated by Permanent Mold Casting to investigate the mechanical properties of the smart composites. The composites have showed good interface bonding as a result of the analysis of SEM and EDX. The smartness of composite is given due to the shape memory effect of the TiNi fiber which generates compressive residual stresses in the matrix material when heated after being prestrained. The tensile strength of the composites was tested at temperatures between $90^{\circ}C$ and room temperature with increasing amount of pre-strain, and it showed that the tensile strength at $90^{\circ}C$ was higher than that of the room temperature. Especially, the tensile strength of the composite increases with increasing pre-strain. It showed that hardness of matrix was higher than that of common 6061Al alloy.